• Journal of the Korean Vacuum Society
• /
• v.5 no.1
• /
• pp.6-13
• /
• 1996

The kinetics of native oxide formation on the (Al, Ga)As and (Cd, Mn)Te have been studied by X-ray photoelectron spectroscopy(XPS) and Auger electron spectroscopy(AES). The regrowth of native oxide after 3keV Ar ion sputter etch and deionized water etch has been studied. The previous report exhibited that the native oxide on CdTe and GaAs can be removed completely by deionzied(DI) water only[1]. On the other hand, the airgrown native oxide on (Al, Ga)As become nonhomogeneous and the regrown native oxide on (Cd,Mn)Te can be partially removed.

• Proceedings of the KIEE Conference
• /
• 1988.07a
• /
• pp.319-323
• /
• 1988

For finding the effects of As on $TiSi_2$ formation, sputter deposited Ti film on Si substrates implanted with various doses of As have been rapid thermal annealed in Ar atmosphere at temperatures of 600-900$^{\circ}C$ for 20 sec. The sheet resistance of Ti-Silicides was examined with 4-point probe, the thickness with ${\alpha}$-step, and the As dopant behavior in Si substrates with ASR. The thickness of Ti-Silicides decreased with increasing As doping, but Ti-Silicides sheet resistance increased with increasing it. However, the critical concentration effect reported by Park et al. was not observed. We observed that the thickness of native oxide increase with increasing As doping. Thus, we concluded that native oxide act as a "barrier" for the Si diffusion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.2
• /
• pp.125-130
• /
• 2000

Two step growth of reduced pressure chemical vapor eposition has been successfully developed to achieve in-situ phosphorus-doped silicon epilayers, and the characteristic evolution on their microstructures has been investigated using scanning electron microscopy, transmission electron microscopy, and secondary ion mass spectroscopy. The two step growth, which employs heavily in-situ P doped silicon buffer layer grown at low temperature, proposes crucial advantages in manipulating crystal structures of in-situ phosphorus doped silicon. In particular, our experimental results showed that with annealing of the heavily P doped silicon buffer layers, high-quality epitaxial silicon layers grew on it. the heavily doped phosphorus in buffer layers introduces into native oxide and plays an important role in promoting the dispersion of native oxides. Furthermore, the phosphorus doping concentration remains uniform depth distribution in high quality single crystalline Si films obtained by the two step growth.

• Economic and Environmental Geology
• /
• v.19 no.2
• /
• pp.85-96
• /
• 1986

The Bupyeong Silver mine which is located approximately 35km west of Seoul is currently the leading silver producer in Korea. The deposits occur as stockwork deposits hosted in Jurassic pyroclastic rocks. Occurrences of ore deposits and mineral paragenesis suggest a division of mineralization into four stages: Stage I, deposition of iron oxide and base metal sulfides; Stage II, deposition of tin oxide and silverm inerals; stage III, deposition of native silver and other silver minerals; Stage IV, formation of pyrite bearing siderite veinlets, Silver minerals in ore are native silver, argentite, freibergite, pyrargyrite, canfieldite, polybasite, dyscrasite and Ag-Fe-S mineral. The most important silver mineral is native silver among them. Chemical composition of important silver minerals were determined by electron probe microanalyser. Assay, size and modal analyses for floatation products were carried out. In floatation products, relative proportion of native silver for total important silver minerals have following ranges: feed, 64.7 to 74.74 wt.%; A-cleaner concentrate, 80.58 to 98.79 wt.%; and final tailing, 28.12 to 72. 57 wt. %. Average degree of liberation for native silver in feed and A-cleaner concentrate are 60.49% and 77.57% respectively. Negative relationship can be recognized between native silver and argentite in their abundance and behavior in floatation precesses.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.59 no.1
• /
• pp.130-133
• /
• 2010

Although many structures based on $SnO_2$ nanowires have been demonstrated, there is a limitation towards practical application due to the unwanted contact potential between the metal electrode and the $SnO_2$ nanowire. This is mostly due to the presence of the native oxide layer that acts as an insulator between the metal contact and the nanowire. In this study the contact properties between Ti/Au contacts and a single $SnO_2$ nanowire was compared to the electrical properties of a contact without the oxide layer. RIE(Reactive Ion Etching) is used to selectively remove the oxide layer from the contact area. The $SnO_2$ nanowires were synthesized by chemical vapor deposition (CVD) and dispersed on a $Si/Si_3N_4$ substrate. The Ti/Au (20nm/100nm) electrodes were formed bye-beam lithography, e-beam evaporation and a lift-off process.

• Journal of the Korean Electrochemical Society
• /
• v.20 no.1
• /
• pp.1-6
• /
• 2017

This study investigated the effect of surface pretreatment, which removes native Cu oxides on Cu seed layer, on subsequent Cu electro-/electroless deposition in Cu interconnection. The native Cu oxides were removed by using citric acid-based solution frequently used in Cu chemical mechanical polishing process and the selective Cu oxide removal was successfully achieved by controlling the solution composition. The characterization of electro-/electrolessly deposited Cu films after the oxide removal was then performed in terms of film resistivity, surface roughness, etc. It was observed that the lowest film resistivity and surface roughness were obtained from the substrate whose native Cu oxides were selectively removed.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.109-109
• /
• 2000

Recently, carbon nanotube has been investigating for field emission display ( (FED) applications due to its high electron emission at relatively low electric field. However, the growing of carbon nanotube generally requires relatively high temperature processing such as arc-discharge (5,000 ~ $20,000^{\circ}C$) and laser evaporation (4,000 ~ $5,000^{\circ}C$) methods. In this presentation, low temperature growing of carbon nanotube by plasma enhanced chemical vapor deposition (PECVD) using nickel catalyst which is compatible to conventional FED processing temperature will be described. Carbon n notubes with average length of 100 run and diameter of 2 ~ $3\mu$ill were successfully grown on silicon substrate with native oxide layer at $550^{\circ}C$using nickel catalyst. The morphology and microstructure of carbon nanotube was highly depended on the processing temperature and nickel layer thickness. No significant carbon nanotube growing was observed with samples deposited on silicon substrates without native oxide layer. This is believed due to the formation of nickel-silicide and this deteriorated the catalytic role of nickel. The formation of nickel-silicide was confirmed by x-ray analysis. The role of native oxide layer and processing parameter dependence on microstructure of low temperature grown carbon nanotube, characterized by SEM, TEM XRD and R없nan spectroscopy, will be presented.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1528-1530
• /
• 1997

As device size shrinks, contamination will increasingly affect the reliability and yield of device. Therefore, contaminants must be removed from the surfaces of Si wafers prior to each process. But it becomes out increasingly difficult to clean silicon surfaces with finer patterns by the conventional wet treatment because of the viscosity and surface tension of solutions. Hence, a damage less dry cleaning process is needed for the silicon surfaces. For the removal of Si native oxide by UV-enhanced dry cleaning. $F_2$ gas and $F_2/H_2$ mixed gas were applied. As a result of analysis, UV-enhnaced $F_2/H_2$ treatment is more suitable than UV-enhanced $F_2$ treatment for removal of native oxide on the surfaces of Si wafers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.504-509
• /
• 1999

In-situ cleaning and subsequent silicon epitaxial film growth were performed in a load-locked reactor equipped with Hg-grid UV lamp and PBN heater to obtain the smooth and contaminant-free underlying surface and develop low-temperature epitaxial film growth process. The removals of organic and native oxide were investigated using UV-excited $O_2$ and $NF_{3}/H_{2}$, and the effect of the surface condition was examined on the quality of silicon epitaxial film grown at temperature as low as $750^{\circ}C$. UV-excited gas phase cleaning was found to be effective in removing the organic and native oxide successfully providing a smooth surface with RMS roughness of 0.5$\AA$ at optimal condition. Crystalline quality of epitaxial film was determined by smoothness of cleaned surface and the presence of native oxide and impurity. Crystalline defects such as dislocation loops or voids due to the surface roughness were observed by XTEM.

• Korean Journal of Pharmacognosy
• /
• v.43 no.1
• /
• pp.85-93
• /
• 2012

181 kinds of local native plants were selected by its anti-inflammatorial folk medicinal uses and evaluated it antioxidative and inhibitory activity of nitric oxide (NO) production in lipopolysaccharide (LPS)-induced 264.7 macrophage cells. Among the 181 kinds of plants, 99 species showed potent antioxidative activities and 20 extracts showed inhibitory activity towards nitric oxide production by more than 70% at a concentration of $100{\mu}g/mL$. Therefore, these plants should be considered promising candidates for the treatment of inflammatory diseases accompanying overproduction of NO.