• Journal of Powder Materials
• /
• v.10 no.4
• /
• pp.262-269
• /
• 2003

Nano-sized Ni-ferrite powder was fabricated by spray pyrolysis process using the waste solution resulting from shadow mask processing. The average particle size of the powder was below 100 nm. The effects of the concentration of raw material solution, the nozzle tip size and air pressure on the properties of powder were studied. As the concentration increased, the average particle size of the powder gradually increased and its specific surface area decreased, but size distribution was much wider and the fraction of the Ni-ferrite phase greatly increased as the concentration increasing. As the nozzle tip size increased from 1 mm to 2 mm, the average particle size of the powder decreased. In case of 3 mm nozzle tip size, the average particle size of the powder increased slightly. On the other hand, in case of 5 mm nozzle tip size, average particle size of the powder decreased. Size distribution of the powder was unhomogeneous, and the fraction of the Ni-ferrite phase decreased as the nozzle tip size increasing. As air pressure increased up to 1 kg/$cm^2$, the average particle size of the powder decreased slightly, on the other hand, the fraction of the Ni-ferrite phase was almost constant. In case of 3kg/$cm^2$ air pressure, average particle size of the powder and the fraction of the Ni-ferrite phase remarkably decreased, but size distribution was narrow.

• Journal of Powder Materials
• /
• v.11 no.6 s.47
• /
• pp.493-502
• /
• 2004

In this study, nano-sized indium oxide powder with the average particle size below 100 nm is fab-ricated from the indium chloride solution by the spray pyrolysis process. The effects of the reaction temperature, the concentration of raw material solution and the inlet speed of solution on the properties of powder were studied. As the reaction temperature increased from 850 to $1000^{\circ}C$, the average particle size of produced powder increased from 30 to 100 nm, and microstructure became more solid, the particle size distribution was more irregular, the intensity of a XRD peak increased and specific surface area decreased. As the indium concentration of the raw material solution increased from 40 to 350 g/l, the average particle size of the powder gradually increased from 20 to 60 nm, yet the particle size distribution appeared more irregular, the intensity of a XRD peak increased and spe-cific surface area decreased. As the inlet speed of solution increased from 2 to 5 cc/min., the average particle size of the powder decreased and the particle size distribution became more homogeneous. In case of the inlet speed of 10 cc/min, the average particle size was larger and the particle size distribution was much irregular compared with the inlet speed of 5 cc/min. As the inlet speed of solution was 50 cc/min, the average particle size was smaller and microstructure of the powder was less solid compared with the inlet speed of 10 cc/min. The intensity of a XRD peak and the variation of specific area of the powder had the same tendency with the variation of the average par-ticle size.

• Economic and Environmental Geology
• /
• v.42 no.5
• /
• pp.501-507
• /
• 2009

Ordered single-walled hollow aluminogermanate (ALGE) nano-balls(NBs) and nano-tubes(NTs) have been self-assembled from the ALGE precursors having an Al/Ge ratio of 1.33 using simple pH-control. The hollow ALGE NBs with average monodisperse diameters of 5 nm and chemistry of Al/Ge=1.5~1.6 were formed through structural assembly in the ALGE solution (Al/Ge=1.33) highly basified to pH=13(Na/Al=28~30) and followed by immediate acidification to pH=9. When the basified solution(pH=13) were acidified to pH=4, ALGE S-NTs (Short-fiber nano-tubes) with diameters of 3.3 nm, 15~20 nm in length, and chemistry of Al/Ge=2.6~2.8 were successfully synthesized. Whereas the solution was basified to pH=9, and subsequently acidified to pH=4, L-NTs(Long-fiber nano-tubes) with >100 nm in length were synthesized for the first time. The self-assembly of the hollow NBs, S-NTs, and L-NTs form the ALGE precursors can be explained by the degree of $H^+$-dissociation of the -Ge-OH inner surfaces, which was controlled by amount of $Na^+$ and pH conditions of ALGE precursor solutions. This results indicate that target forms of ALGE nanomaterials can be synthesized by simple pH controls.

• Proceedings of the SCSK Conference
• /
• 2003.09a
• /
• pp.178-191
• /
• 2003

OMC is essentialiy necessary compound in sun goods as organic UV protecting products. But the skin-trouble problem is raising because of skin penetration of OMC. In this study, non-capsulated pure OMC was compared with Organic-Inorganic-Nano-hybrid OMC for skin penetration force and SPF degree. Organic- Inorganic Nano-Hybrid OMC is OMC trapped in the pore of the mesoporous silica synthesized by the sol-gel method after OMC is nanoemulsified in the system of the hydrogenated Lecithin/ Ethanol/caprylic/capric triglyceride/OMC/water. OMC- nano- emulsion was obtained by a microfluidizing process at 1000bar and then micelle size in the nanoemulsion solution is 100-200nm range. Mesoporous silica nano-hybrid OMC was prepared by the process; surfactant was added in dissolved OMC-Nanoemulsion, then the rod Micelle was formed. OMC-nanoemulsion was capsulated in this rod Micelle and then silica precursor was added in the OMC-nanoemulsion solution. Through the hydrolysis reaction of the silica precursor, mesoporous silica concluding OMC-Nanocapsulation was obtained. The nano-hybrid surface of this OMC-Nanoemulsion-Inorganic system was treated with polyalkyl-silane compound. OMC-Mesoporous silica Nano-hybrids coated with polyalkyl-silane compound show the higher sun protecting factor (SPF Analyzer: INDEX 10-15) than pure OMC and could reduce a skin penetration of OMC. The physico-chemical properties of these nano-hybrids measured on the SPF index, partical size, strcture, specific surface area, pore size, morphology, UV absorption, rate of the OMC dissolution using SPF Analyzer, Laser light scattering system, XRD, BET, SEM, chroma Meter, HPLC, Image analyzer, microfluidizer, UV/VIS. spectrometer.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.466-471
• /
• 2014

Hydrous zirconia particles were prepared from $ZrOCl_2$ aqueous solution using an electro-dialysis [ED] process. For the preparation of $(Zr,Y)(OH)_4$ precipitates, 3 mol% $YCl_3$ was added into $ZrOCl_2$ aqueous solution. During the hydrolysis of 0.5 mol/L $(Zr,Y)OCl_2$ solution at $90^{\circ}C$ a slurry solution was obtained. The ED process was used for the removal of chlorine from the slurry solution. Two kinds of slurry solution were sampled at the beginning and end of the ED process. The morphology of hydrous zirconia particles in the solution was observed using an inverted optical microscope and an FE-SEM. The hydrous zirconia particles were nano-crystalline, and easily coagulated with drying. Yttrium stabilized zirconia [YSZ] powder could be obtained by the calcination of $(Zr,Y)(OH)_4$ precipitates prepared from a $(Zr,Y)OCl_2$ solution by the ED process. The coagulated dry powders were shaped and sintered at $1500^{\circ}C$ for 2 h. The sintered body showed a dense microstructure with uniform grain morphology.

• Journal of the Korean Ceramic Society
• /
• v.53 no.3
• /
• pp.325-331
• /
• 2016

Anatase particles of titanium dioxide were prepared from $TiCl_4$ aqueous solution by using an electro-dialysis [ED] process. For the preparation of an aqueous solution of $TiCl_4$ precipitates, $TiCl_4$ liquid frozen in ice was transferred to a neck flask and then hydrolyzed using deionized [DI] $H_2O$. During the hydrolysis of the $TiCl_4$ solution at $0^{\circ}C$, a slurry solution of $TiOCl_2$ was obtained and the color changed from red to orange. The ED process was applied for the removal of chlorine content in the slurry solution. Two kinds of hydrolyzed slurry solution with lower [$Ti^{4+}$] and higher [$Ti^{4+}$] were sampled and the ED process was applied for the samples according to the removal time of [$Cl^-$]. With de-chlorination, the solution status changed from sol to gel and the color quickly changed to blue. Finally, white crystalline powders were formed and the phase was confirmed by XRD to be anatase crystallites. The morphology of the hydrous titania particles in the solution was observed by FE-SEM. The hydrous titania particles were nano-crystalline, and easily coagulated with drying.

• Advances in nano research
• /
• v.3 no.4
• /
• pp.207-223
• /
• 2015

Nanotechnology is considered the most important technological advancement in recent years, and it is utilized in all industries due to its potential applications. Almost all of the industries (food, agriculture, medicine, automotive, information and communication technologies, energy, textile, construction, etc.) reorganize their future in the light of nanotechnological developments. As the most important source of income of countries, the agriculture industry increases the use of nanotechnology products gradually as a solution to the problems encountered. Reducing the use of agricultural inputs (pesticides, herbicides, fertilizers, etc.) by increasing their efficiency utilizing nano-carriers, detecting the environmental conditions and development of the crops in the field simultaneously by making use of nanosensors, reducing the sample volume and the amount of analyte used thanks to nanoarrays, effective treatment of water resources through nano-filters, accelerating the development of crops by using nanoparticles are the prominent nanotechnological applications in the agriculture industry. This review presents information on the benefits of the recent developments in nanotechnology applications in the agriculture industry.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.11
• /
• pp.2029-2033
• /
• 2007

Hydrotalcite, layered double hydroxides (LDH), with hexagonal morphology has been rapidly synthesized by microwave reaction within 1 hour by urea hydrolysis from homogeneous solution. Different synthesis parameters, Mg/Al molar ratio, microwave reaction temperature and microwave power were systematically investigated. Pure hydrotalcite phase was obtained for Mg/Al ratios of 2:1 and 3:1, and higher reaction temperature gave higher crystallinity. The hydrotalcite synthesized at 600W power shows the highest crystallinity and more homogeneous crystal size distribution. The hydrotalcite samples were characterized by powder X-ray diffraction (XRD), simultaneous thermogravimetric/differential thermal analysis (TG/DTA), Fourier Transform Infrared (FT-IR) and Scanning electron micrograph (SEM).

• Journal of the Optical Society of Korea
• /
• v.18 no.3
• /
• pp.283-287
• /
• 2014

Square lattice nano-hole arrays with diameters and periodicities of 200 and 500 nm, respectively, are fabricated on InGaN/GaN blue light emitting diodes (LEDs) using electron-beam lithography and inductively coupled plasma reactive ion etching processes. Cathodoluminescence (CL) investigations show that light emission intensity from the LEDs with the nano-hole arrays is enhanced compared to that from the planar sample. The CL intensity enhancement factor decreases when the nano-holes penetrate into the multiple quantum wells (MQWs) due to the plasma-induced damage and the residues. Wet chemical treatment using KOH solution is found to be an effective method for light extraction from the nano-patterned LEDs, especially, when the nano-holes penetrate into the MQWs. About 4-fold CL intensity enhancement factor is achieved by the KOH treatments after the dry etching for the sample with a 250-nm deep nano-hole array.

• Journal of Welding and Joining
• /
• v.21 no.4
• /
• pp.39-45
• /
• 2003

Nano-TiO$_2$ photocatalytic coatings were deposited on the stainless steel 304(50$\times$70$\times$3mm) by the APS(Atmospheric Plasma Spraying). Photocatlytic reaction was tested in MB(methylene blue) aqueous solution. For applying nano-TiO$_2$ powders by thermal spray, the starting nano-TiO$_2$ powder with 100% anatase crystalline was agglomerated by spray drying. Plasma second gas(H$_2$) flow rate and spraying distance were used as principal process parameters which are known to control heat enthalpy(heat input). The relationship between process parameters and the characteristics of microstructure such as the anatase phase fraction and grain size of the TiO$_2$ coatings were investigated. The photo-decomposition efficiency of TiO$_2$ coatings was evaluated by the kinetics of MB aqueous solution decomposition. It was found that the TiO$_2$ coating with a lower heat input condition had a higher anatase fraction, smaller anatase grain size and a better photo-decomposition efficiency.