• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2003.10a
• /
• pp.95-96
• /
• 2003

Titanium carbide nano-tube and fibers were synthesized by self-propagating high temperature synthesis (SHS) method. The average diameters of the nano-tubes and nano-fibers are about 100 and 20 nm in diameter, respectively. the non-stoichiometric numbers of the titanium carbide determined by neutron diffractometry were 0.87 and 0.94.

• Journal of Powder Materials
• /
• v.17 no.5
• /
• pp.390-398
• /
• 2010

Aqueous gold nanoparticle dispersion was synthesized by chemical reduction method using diethanolamine as reducing agent and polyethyleneimine as dispersion stabilizer. The synthesis conditions for the stable dispersion of the gold nanoparticle suspension were determined by changing the amount of the reducing agent and dispersant during the wet chemical synthesis procedures. The face centered cubic lattice structure of the gold nanoparticles was confirmed by using X-ray diffraction and the morphologies of the nanoparticles were observed by transmission electron microscope. The synthesized gold nanoparticle dispersion was concentrated by evaporating the dispersion medium at room temperature followed by the addition of ethyleneglycol as humectant for the increase of the elastic properties to obtain gold nanoparticle inks for direct ink writing process. The line patterns were obtained with the gold nanoparticle inks during the writing procedures and the morphologies of the fine patterns were observed by scanning electron microscope.

• Journal of Powder Materials
• /
• v.13 no.6 s.59
• /
• pp.432-438
• /
• 2006

Aluminum nitride (AlN) nanopowders with low degree of agglomeration and uniform particle size were synthesized by carbothermal reduction of alumina and subsequent direct nitridization. Boehmite powder was homogeneously admixed with carbon black nanopowders by ball milling. The powder mixture was treated under ammonia atmosphere to synthesize AlN powder at lour temperature. The effect of process variables such as boehmite/carbon black powder ratio, reaction temperature and reaction time on the synthesis of AlN nanopowder was investigated.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.51-56
• /
• 2003

To investigate the effect of the parameters of the plasma arc discharge process on the particle formation and particle characteristics of the iron nano powder, the chamber pressure, input current and the hydrogen volume fraction in the powder synthesis atmosphere were changed. The particle size and phase structure of the synthesized iron powder were studied using the FE-SEM, FE-TEM and XRD. The synthesized iron powder particle had a core-shell structure composed of the crystalline $\alpha$-Fe in the core and the crystalline $Fe_3O_4$ in the shell. The powder generation rate and particle size mainly depended on the hydrogen volume fraction in the powder synthesis atmosphere. The particle size increased simultaneously with increasing the hydrogen volume fraction from 10% to 50%, and it ranged from about 45nm to 130 nm.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1328_1329
• /
• 2009

Nano porous indium tin oxide (ITO) powder was synthesized employing a new route sol-gel combustion hybrid method using Ketjen Black as a fuel. The nano porous ITO powder was composed of $SnCl_4$-98.0% and $In(NO_3)_3{\cdot}XH_2O$-99.999%, produce with a $NH_4OH$ with sol-gel method as a catalyst [1,2]. Crystal structures were examined by powder X-ray diffraction (XRD), and those results show shaper intensity peak at $25.6^{\circ}(2{\Theta})$ of $SnO_2$ by increased sintering temperature. A particle morphology as well as crystal size was investigated by scanning electron microscopy(FE-SEM), and the size of the nano porous powder was found to be in the range of 20~30nm. ITO films could controlled by nano porous powder at various sintering temperature in this paper[3,4]. The sol-gel combustion method was offered simple and effective route for the synthesis of nano porous ITO powder[5].

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.12
• /
• pp.852-856
• /
• 2014

$BaTiO_3$ nano powder can be synthesized by hydrate salt method at $120^{\circ}C$ in air. Decreasing the thickness of thick film, the nano dielectric particle is needed in electronic ceramics. However, the synthesis of $BaTiO_3$ nano particle at low temperature in air and their mechanism were not reported enough. And ultrasonic treatment can be tried because of low temperature process in air. Therefore, in this study, the $BaTiO_3$ nano powder was synthesised with the synthesis time and ultrasonic treatment at $120^{\circ}C$ in air. In the synthesis process, the effects of process were evaluated. From the experimental observation, the synthesis mechanism was proposed. The homogeneous $BaTiO_3$ particle was synthesised by KOH salt solution at $120^{\circ}C$ for 1hour. It was conformed that the ultrasonic treatment effected on the increase of synthesis rate. After cutting the salt powder using FIB, $BaTiO_3$ nano particles observed homogeneously in the cross-section of the salt particle.

• Journal of Powder Materials
• /
• v.14 no.2 s.61
• /
• pp.116-122
• /
• 2007

It is well known that thermal plasma process has lots of advantages such as high temperature and good quality for synthesis of nano particles. In this research, we attempt the synthesis of nano unitary and composite powder (Ag, Mg-Al, Zr-V-Fe) using transferred thermal plasma. Nano particles of metal alloy, ranging from 20 nm to 150 nm, have been synthesized by this process.

• Korean Journal of Materials Research
• /
• v.30 no.2
• /
• pp.93-98
• /
• 2020

Effective control of the heat generated from electronics and semiconductor devices requires a high thermal conductivity and a low thermal expansion coefficient appropriate for devices or modules. A method of reducing the thermal expansion coefficient of Cu has been suggested wherein a ceramic filler having a low thermal expansion coefficient is applied to Cu, which has high thermal conductivity. In this study, using pressureless sintering rather than costly pressure sintering, a polymer solution synthesis method was used to make nano-sized Cu powder for application to Cu matrix with an AlN filler. Due to the low sinterability, the sintered Cu prepared from commercial Cu powder included large pores inside the sintered bodies. A sintered Cu body with Zn, as a liquid phase sintering agent, was prepared by the polymer solution synthesis method for exclusion of pores, which affect thermal conductivity and thermal expansion. The pressureless sintered Cu bodies including Zn showed higher thermal conductivity (180 W/m·K) and lower thermal expansion coefficient (15.8×10^-6/℃) than did the monolithic synthesized Cu sintered body.

• Journal of Powder Materials
• /
• v.9 no.6
• /
• pp.433-440
• /
• 2002

Synthesis and compaction of Al-base nano powders by pulsed discharge method were investigated. The aluminum based powders with 50 to 200 nm of diameter were produced by pulsed wire evaporation method. The powders were covered with very thin oxide layer. The perspective process for the compaction and sintering of nanostructured metal-based materials stable in a wide temperature range can be seen in the densification of nano-sized metal powders with uniformly distributed hard ceramic particles. The promising approach lies in utilization of natural uniform mixtures of metal and ceramic phases, e.g. partially oxidized metal powders as fabricated in our synthesis method. Their particles consist of metal grains coated with oxide films. To construct a metal-matrix material from such powder, it is necessary to destroy the hard oxide coatings of particles during the compaction process. This goal was realized in our experiments with intensive magnetic pulsed compaction of aluminum nanopowders passivated in air.

• Applied Science and Convergence Technology
• /
• v.27 no.1
• /
• pp.14-18
• /
• 2018

In order to understand the mechanism of the synthesis of particles using a plasma torch, it is necessary to understand the reaction mechanisms using a computer simulation. In this study, we have developed a simulation method to combine the Lagrangian scheme to follow microparticles and a nodal method to treat nanoparticles categorized with different particle sizes. The Lagrangian scheme includes the Coulomb force which affects the dynamics of larger particles. In contrast, the nodal method is adequate for the nanoparticles because the charge effect is negligible for nanoparticles but the number of nanoparticles is much larger than that of microparticles. This method is helpful to understand the dynamics and growth mechanism of micro- and nano-powder mixture observed in the experiment.