• 한국재료학회지
• /
• 제18권3호
• /
• pp.117-122
• /
• 2008

Micro-sized bumps on a multi-layered build-up PCB were fabricated by pulse-reverse copper electroplating. The values of the current density and brightener content for the electroplating were optimized for suitable performance with maximum efficiency. The micro-bumps thus electroplated were characterized using a range of analytical tools that included an optical microscope, a scanning electron microscope, an atomic force microscope and a hydraulic bulge tester. The optical microscope and scanning electron microscope analyses results showed that the uniformity of the electroplating was viable in the current density range of $2-4\;A/dm^2$; however, the uniformity was slightly degraded as the current density increased. To study the effect of the brightener concentration, the concentration was varied from zero to 1.2 ml/L. The optimum concentration for micro-bump electroplating was found to be 0.6 ml/L based on an examination of the electroplating properties, including the roughness, yield strength and grain size.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.450-455
• /
• 2002

Cu-cored Sn-Ag solder balls were fabricated by coating pure Sn and Ag on Cu balls. The melting behavior and the solderability of the BGA joint with the Ni/Au coated Cu pad were investigated and were compared with those of the commercial Sn-Ag and Sn-Ag-Cu balls. DSC analyses clarified the melting of Cu-cored solders to start at a rather low temperature, the eutectic temperature of Sn-Ag-Cu. It was ascribed to the diffusion of Cu and Ag into Sn plating during the heating process. After reflow soldering the microstructures of the solder and of the interfacial layer between the solder and the Cu pad were analyzed with SEM and EPMA. By EDX analysis, formation of a eutectic microstructure composing of $\beta$-Sn, Ag$_3$Sn, ad Cu$_{6}$Sn$_{5}$ phases was confirmed in the solder, and the η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer was found to form at the interface between the solder and the Cu pad. By conducting shear tests, it was found that the BGA joint using Cu-cored solder ball could prevent the degradation of joint strength during aging at 423K because of the slower growth me of η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer formed at the solder, pad interface. Furthermore, Cu-cored multi-component Sn-Ag-Bi balls were fabricated by sequentially coating the binary Sn-Ag and Sn-Bi solders on Cu balls. The reflow property of these solder balls was investigated. Melting of these solder balls was clarified to start at the almost same temperature as that of Sn-2Ag-0.75Cu-3Bi solder. A microstructure composing of (Sn), Ag$_3$Sn, Bi and Cu$_{6}$Sn$_{5}$ phases was found to form in the solder ball, and a reaction layer containing primarily η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ was found at the interface with Ni/Au coated Cu pad after reflow soldering. By conducting shear test, it was found that the BGA joints using this Cu-core solder balls hardly degraded their joint shear strength during aging at 423K due to the slower growth rate of the η'-(Au, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer at the solder/pad interface.he solder/pad interface.

• 마이크로전자및패키징학회지
• /
• 제6권4호
• /
• pp.1-7
• /
• 1999

MCM-D 기판에 수동소자를 내장시키는 공정을 개발하였다. MCM-D 기판은 Cu/감광성 BCB를 각각 금속배선 및 절연막 재료로 사용하였고, 금속배선은 Ti/cu를 각각 1000$\AA$/3000$\AA$으로 스퍼터한 후 fountain 방식으로 전기 도금하여 3 um Cu를 형성하였으며, BCB 층에 신뢰성있는 비아형성을 위하여 BCB의 공정특성과 $C_2F_6$를 사용한 플라즈마 cleaning영향을 AES로 분석하였다. 이 실험에서 제작한 MCM-D 기판은 절연막과 금속배선 층이 각각 5개, 4개 층으로 구성되는데 저항은 2번째 절연막 위에 thermal evaporator 방식으로 NiCr을 600$\AA$증착하여 시트저항이 21 $\Omega$/sq가 되게 형성하였고. 인덕터는 coplanar 구조로 3, 4번째 금속배선층에 형성하였으며, 커패시터는 절연막으로 PECVD $Si_3N_4$를 900$\AA$증착한 후 1, 2번째 금속배선층에 형성하여 88nF/$\textrm {cm}^2$의 커패시턴스를 얻었다. 이 공정은 PECVD $Si_3N_4$와 thermal evaporation NiCr 공정을 이용함으로써 기존의 반도체 공정을 이용하여 MCM-D 기판에 수동소자를 안정적으로 내장시킬 수 있었다.

• 마이크로전자및패키징학회지
• /
• 제7권3호
• /
• pp.31-36
• /
• 2000

RF(radio Frequency)용 MCM(Multichip Module)-D 기판 내장형 인덕터를 개발하였다. MCM 기술은 고밀도 패키징 기술로서 주로 디지털회로에 많이 적용되어 왔으나, 최근에는 아날로그회로 및 디지털회로가 혼재된 혼성신호 및 초고주파 회로에도 적용되고 있다. 혼성신호에서는 능동소자 주변에 많은 수의 수동소자가 연결되므로 MCM-D 기판에 수동소자를 내장시키면 원가절감과 시스템의 크기 축소 및 경량화를 이를 수 있을 뿐 아니라, 성능과 신뢰성을 향상시킬 수 있다. 본 논문에서 MCM-D 기판은 Cu/감광성 BCB(Benzocyclobutene)를 각각 금속배선 및 절연막 재료로 사용하였고, 금속배선은 Ti/Cu를 각각 1000 $\AA$/3000 $\AA$으로 스퍼터한 후 fountain 방식으로 전기 도금하여 3 $\mu\textrm{m}$ Cu를 형성하였으며, 인덕터는 coplanar구조로 하여 기존의 반도체 공정을 이용하여 MCM-D기판에 인덕터를 안정적으로 내장시키고 전기적 특성을 측정하였다.

• 한국재료학회지
• /
• 제19권3호
• /
• pp.151-155
• /
• 2009

Micro-scale copper bumps for build-up PCB were electroplated using a pulse-reverse method. The effects of the current density, pulse-reverse ratio and brightener concentration of the electroplating process were investigated and optimized for suitable performance. The electroplated micro-bumps were characterized using various analytical tools, including an optical microscope, a scanning electron microscope and an atomic force microscope. Surface analysis results showed that the electroplating uniformity was viable in a current density range of 1.4-3.0 A/$dm^2$ at a pulse-reverse ratio of 1. To investigate the brightener concentration on the electroplating properties, the current density value was fixed at 3.0 A/$dm^2$ as a dense microstructure was achieved at this current density. The brightener concentration was varied from 0.05 to 0.3 ml/L to study the effect of the concentration. The optimum concentration for micro-bump electroplating was found to be 0.05 ml/L based on the examination of the electroplating properties of the bump shape, roughness and grain size.