• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.559-568
• /
• 2015

In this study, multi-component blended concrete mix with fly ash and ground granulated blast furnace slag according to 3 level of type of warter reduction agent (type of 0%, 8% and 16%) and 3 level of water-binder ratio (40%, 45% and 50%) was prepared for evaluation of effect of physical characteristics of concrete using multi-component blended binder according to warter reduction efficiency of warter reduction agent. In addition, concrete mix was carried out repetition test of three times in order to secure the reliability. As a result, compressive strength according to type of warter reduction agent was found that difference of strength was about 20% occurred, warter reduction efficiency of warter reduction agent was showed that a great influence on qualities of concrete. Therefore, reflected the effect of warter reduction efficiency of warter reduction agent, prediction model equations of compressive strength for multi-component blended concrete was proposed, it was found that more than 90% of the high correlation.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.2
• /
• pp.124-132
• /
• 2018

This research presents the results of an investigation on the characteristic of multi-component blended high fluidity mortars. The binder was blended ordinary Portland cement(OPC), ground granulated blast furnace slag(GGBFS), calcium sulfoaluminate(CSA) and ultra rapid setting cement(URSC). The GGBFS was replaced by OPC from 30%(P7 series), 50%(P5 series) and 70%(P3 series), CSA and URSC was 10% or 20% mass. The superplasticizer of polycarboxylate type were used. A constant water-to-binder ratio(w/b)=0.35 was used for all mixtures. Test were conducted for mini slump, setting time, V-funnel, compressive strength and drying shrinkage. According to the experimental results, the contents of superplasticizer, V-funnel and compressive strength increases with an increase in CSA or URSC contents for all mixtures. Moreover, the setting time and drying shrinkage ratio decrease with and increase in CSA or URSC. CSA decreased dry shrinkage but URSC had less effect. However, the mixed binders of CSA and URSC had a large effect of reducing drying shrinkage by complementary effect. This is effective for improving the initial strength of URSC, and CSA is effective for the expansion and improvement of long-term strength.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.140-143
• /
• 2004

Heat of hydration of concrete under different curing temperatures can be characterized with knowledge of the thermal activity, the heat rate at the reference temperature, and the total heat of hydration of the mixture. The so-called multi-component hydration model incorporates the effect of following variables: cement chemical composition, cement fineness, secondary cementitious powders, mixture proportions, and concrete properties. However, the model does not consider the use of silica fume as a secondary cementitious powder. Therefore, the model that quantifies the heat of hydration due to the use of silica fume is needed. In this thesis, the effects of silica fume on heat of hydration are evaluated and the influence on the heat of hydration are also quantified to be included in the model, so that the analysis using modified multi-component hydration model for silica fume concrete provides more accurate results than normal concrete.

• Journal of Ocean Engineering and Technology
• /
• v.26 no.3
• /
• pp.26-32
• /
• 2012

Recently, concrete using multicomponent blended cement has been required to increase the freeze-thaw and sulfate resistances of concrete structures exposed to a marine environment. Thus, the purpose of this study was to propose the use of concrete containing multicomponent blended cement as one of the alternatives for concrete structures exposed to a marine environment. For this purpose, batches of concrete containing ordinary portland cement (OPC), binary blended cement (OPC-G, G: ground granulated blast slag), ternary blended cement (OPC-GF, F: fly ash), and quaternary blended cement (OPC-GFM, M: mata-kaolin) were made using a water-binder ratio of 50%. Then, the durability levels, including thesulfate and freeze-thaw resistances, were estimated for concrete samples containing OPC, OPC-G, OPC-GF, and OPC-GFM. It was observed from the tests that the durability levels of the concrete samples containing OPC-G and OPC-GF were found to be much better than that of the concrete containing OPC. The optimum mixing proportions were a40% replacement ratio of ground granulated blast slag for the binary blended cement and a30% replacement ratio of ground granulated blast slag and 10% fly ash for the ternary blended cement.

• Journal of the Korea Concrete Institute
• /
• v.28 no.5
• /
• pp.593-600
• /
• 2016

The paper presented investigates the effects of kaolinite on strength properties of alkali-activated multi-component cement. The binders of this study was blended of ground granulated blast furnace slag (GGBFS), fly ash (FA), silica fume (SF) and kaolinite (KA). In this study, the specimens of combination of 20%~70% GGBFS, 10%~60% FA, 10% SF (constant ratio) and 10%~50% KA binder were used for strength properties tests. The water/binder ratio was 0.5. The binders (GGBFS + FA + SF + KA) was activated by sodium hydroxide (NaOH) and sodium silicate ($Na_2SiO_3$) was 10% by total binder weight (10% NaOH + 10% $Na_2SiO_3$). The research carried out is on the compressive strength, water absorption, ultrasonic pulse velocity (UPV) and X-ray diffraction (XRD). The compressive strength decreased as the contents of KA increase. One of the major reason for this is the low reactivity of KA compared with other raw materials used as precursors such as GGBFS or FA. The presence of remaining KA indicates that the initially used quantity has not fully reacted during hydration. Moreover, the results have indicated that increased of KA contents decreased UPV under all experimental conditions. The drying shrinkage and water absorption increased as the content of KA increase. Test result clearly showed that the strength development of multi-component blended cement were significantly dependent on the content of KA and GGBFS.

• Corrosion Science and Technology
• /
• v.4 no.3
• /
• pp.89-94
• /
• 2005

This paper presents the results of a study that was undertaken to optimize the ratio of the components of a new multi-component inhibitor blend composed of orthophosphate/ phosphonates/ acrylate copolymer/ isothiazolone. The effects of newly developed inhibitor on carbon steel dissolution in synthetic cooling water were studied through weight loss tests, electrochemical tests, scale tests, and micro-organism tests. The obtained results were compared to blank (uninhibited specimen) and showed that developed inhibitor revealed very good corrosion, scale, and micro-organism inhibition simultaneously. All measurements indicated that the efficiency of the blended mixture exceeded 90 %. The inhibitive effects arose from formation of protective films which might contain calcium phosphate, calcium phosphonate, and iron oxide. The nature of protective films formed on the carbon steel was studied by scanning electron microscopy (SEM) and auger electron spe ctroscopy (AES). Inhibitor used in this study appeared to have better performance for scale inhibition due to their superior crystal modification effect and excellent calcium carbonate scale inhibition properties. The effect of inhibitor on microorganisms was evaluated through minimum inhibitory concentration (MIC) test. All kinds of micro-organisms used in this study were inhibited under 78ppm concentration of inhibitor.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.565-566
• /
• 2009

Supplementary cementing materials (SCM), such as silica fume, slag, and low-calcium fly ash, have been widely used as mineral admixtures in high strength and high performance concrete. Due to the chemical and physical effect of SCM on hydration, compared with Portland cement, hydration process of cement incorporating SCM is much more complex. This paper presents a numerical hydration model which is based on multi-component concept and can simulate hydration of cement incorporating SCM. The proposed model starts with mixture proportion of concrete and considers both chemical and physical effect of SCM on hydration. Using this proposed model, this paper predicts the following properties of hydrating cement-SCM blends as a function of hydration time: reaction ratio of SCM, calcium hydroxide content, heat evolution, porosity, chemically bound water and the development of the compressive strength of concrete. The prediction results agree well with experiment results.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.735-738
• /
• 2004

In this study, it was founded to make the optimal mixture for producing concrete which is self-compacting, yet, and generates low heat of hydration by using fly ash, blast furnace slags and limestone powders as binders in addition to cement while using super-plasticizers and viscosity agents as admixture agents. The structural behaviors of the concrete produced with the selected mixture were compared with those of the concrete currently using for construction of nuclear power plants. The study shows that the blended high fluidity concrete including limestone is better in workability and durability than the concrete currently in use for nuclear power plants.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.739-742
• /
• 2004

In this study, it was founded to make the optimal mixture for producing concrete which is self-compacting, yet, and generates low heat of hydration by using flyash, blast furnace slags and limestone powders as binders in addition to cement while using super-plasticizers and viscosity agents as admixture agents. The structural behaviors of the concrete produced with the selected mixture were compared with those of the concrete currently using for construction of nuclear power plants. The study shows that the blended high fluidity concrete including limestone is better in workability and durability than the concrete currently in use for nuclear power plants.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.2
• /
• pp.49-56
• /
• 2006

The single droplet combustion characteristics of multicomponent fuel such as diesel-oxygenate and diesel-paraffin blends under high ambient temperature and atmospheric pressure were investigated in the study. The results of the study may be concluded as follows : In the combustion of diesel fuel droplet with additive of oxygenate and paraffin, the dimensionless droplet size of $(D/D_o)^2$ was linearly decreased with time. A fuel droplet with low boiling temperature additives and in high boiling temperature diesel fuel evaporates and burns faster than usual diesel fuel. This rapid burning may result from so-called "micro-explosion" and its burning intensity varies with the types of additives. The results above may suggest that rapid evaporation of oxygenate additive in the middle stage of combustion can contribute much to combustion improvement of blended fuels. When compared to ordinary diesel fuel, neat oxygenate and paraffin fuels show blue flame during entire combustion which prove smokeless combustion.