• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.157-158
• /
• 2022

A problem arose about the lack of strength of dry mortar for flooring. To solve the problem of lack of strength, a high-strength dry mortar was applied. However, problems arose about the increase in the amount of cracks. It is necessary to analyze the causes of the increase in the amount of cracking in high-strength dry mortar and take countermeasures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.501-504
• /
• 2006

Recycled aggregate mortar contains plenty of calcium hydroxide to improve the strength of blast furnace slag, although the surface mortar made of recycled aggregate deteriorates adhesion to cement paste and blast furnace slag has a low initial strength. Therefore, this study assumes that the combination with both recycled aggregate and blast furnace slag will produce a better performance. The results of the experiment show that dry mortar made of recycled aggregate provides with higher strength than wet mortar does at the 3-day and 7-day age, while lower at the 28-day age. It indicates that a large amount of cement mortar made of dry recycled aggregate has deteriorated adhesion strength. The mixes with 30% and 50% of blast furnace slag and 50% and 75% of recycled aggregate provide with much better strength at the 7-day age, although they usually have latent hydraulic property at the 28-day age. It indicates that calcium hydroxide($Ca(OH){_2}$) in recycled aggregate has affected ground granulated blast furnace slag.

• Journal of Korean Society of Rural Planning
• /
• v.11 no.3 s.28
• /
• pp.53-57
• /
• 2005

Up to recently building are constructed focusing on the convenience of residential condition. However, environmental-friendly materials is required for construction as people are spending more time inside buildings and causes of many problems like sick-building syndrome are known due to the noxious gases and polluted air originated from construction materials. Although loess(hwangtoh) is an environmental-friendly material, it has limitations in compressive strength far a construction material. The purpose of this study is to suggest the optimal ratio of loess(hwangtoh) mortar by tests of compressive strength comparing with standard strength of floor finishing mortar and evaluate the usability of loess(hwangtoh) mortar for floor finishing material through an impact test, a cracking test and a abrasion test. Based on the results of this study, 86% of loess(hwangtoh) and 14% of inorganic binder is suggested for the optimal mixture ratio of loess(hwangtoh) mortar. Moreover, the characteristics of loess(hwangtoh) is suitable for floor finishing material in impact, crack, abrasion.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.297-298
• /
• 2023

In the concrete industry, efforts are being made to reduce CO₂ emissions, and technologies that collect, store, and utilize CO₂ have recently been studied. This study analyzed the change in compressive strength after the accelerated carbonation test of Non-Sintered Cement(NSC) mortar. Type C Fly Ash and Type F Fly Ash were mixed in a 1:1 ratio and then mixed with Blast Furnace Slag fine powder to produce NSC. The mortar produced was cured underwater until the target age. In addition, an accelerated carbonation test was conducted under the condition of a concentration of 5 (±1.0%) of CO₂ gas for 14 days. The mortar compressive strength was measured before and after 14 days of accelerated carbonation test based on the 7th and 28th days of age. As a result of the experiment, the compressive strength was improved in all binder. In general, the compressive strength of NSC mortar subjected to the accelerated carbonation test was similar to that of Ordinary Portland Cement(OPC) mortar not subjected to the accelerated carbonation test.

• Journal of Microbiology and Biotechnology
• /
• v.20 no.4
• /
• pp.782-788
• /
• 2010

Microbiological calcium carbonate precipitation (MCP) has been investigated for its ability to improve the compressive strength of mortar. However, very few studies have been conducted on the use of calcite-forming bacteria (CFB) to improve compressive strength. In this study, we discovered new bacterial genera that are capable of improving the compressive strength of mortar. We isolated 4 CFB from 7 environmental concrete structures. Using sequence analysis of the 16S rRNA genes, the CFB could be partially identified as Sporosarcina soli KNUC401, Bacillus massiliensis KNUC402, Arthrobacter crystallopoietes KNUC403, and Lysinibacillus fusiformis KNUC404. Crystal aggregates were apparent in the bacterial colonies grown on an agar medium. Stereomicroscopy, scanning electron microscopy, and X-ray diffraction analyses illustrated both the crystal growth and the crystalline structure of the $CaCO_3$ crystals. We used the isolates to improve the compressive strength of cement-sand mortar cubes and found that KNUC403 offered the best improvement in compressive strength.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.3
• /
• pp.27-33
• /
• 2019

The purpose of this study is to provide and evaluate the tensile properties of masonry element such as tensile strength, strain, modulus of elasticity and stress-strain relationship through the direct tension test with varies of mortar strength. From the experiment, the tension fracture was observed along the interfaces between the brick and the mortar. Tension properties of masonry element was significantly affected by compressive strength of mortar, $f_m$, indicating that higher tensile strength and modulus of elasticity of masonry element were obtained with increase of $f_m$. The strain of a masonry element was inversely proportional to $f_m$ due to the lower ductility of a higher mortar strength. A tensile stress-strain relationship of masonry element was generalized based on the numerical analysis and the regression analysis using test data. The proposed model shows fairly good agreement with the test measurements.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.127-134
• /
• 2021

A hydrophobic emulsion consisting of PMHS and PVA was mixed into a cement mortar to observe changes in cement hydrate and microstructure, and to experimentally evaluate compressive strength and flexural strength. The hydrophobic emulsion was added with metakaolin and PVA fibers, and the stirring speed and sequence were adjusted to prepare a shell-concept hydrophobic emulsion. It was then mixed when mixing mortar to enhance filling of the internal pores and change of the hydrates. It was observed that the mortar mixed with a hydrophobic emulsion was filled with micropores and a coating film was formed on the surface of the hydrates by the emulsion. It was analyzed that the total pore area and porosity of the mortar mixed with the emulsion decreased from 30% to 60% compared to OPC, excluding the 50MK variable, which was extremely reduced and the median pore diameter decreased in some variables. It was also found that the compressive strength of the mortar mixed with emulsion 1% was increased up to 20%, but the strength of the mortar specimen mixed with 2% decreased to 50%.

• Advances in materials Research
• /
• v.11 no.2
• /
• pp.121-146
• /
• 2022

In the recent years, the use of agricultural waste in green cement mortar and concrete production has attracted considerable attention because of potential saving in the large areas of landfills and potential enhancement on the performance of mortar. In this research, microparticles of palm oil fuel ash (POFA) obtained from a multistage thermal and mechanical treatment processes of raw POFA originating from palm oil mill was utilized as a pozzolanic material to produce high-performance cement mortar (HPCM). POFA was used as a partial replacement material to ordinary Portland cement (OPC) at replacement levels of 0, 5, 10, 15, 20, 25, 30, 35, 40% by volume. Sand with particle size smaller than 300 ㎛ was used to enhance the performance of the HPCM. The HPCM mixes were tested for workability, compressive strength, ultrasonic pulse velocity (UPV), porosity and absorption. The results portray that the incorporation of micro POFA in HPCMs led to a slight reduction in the compressive strength. At 40% replacement level, the compressive strength was 87.4 MPa at 28 days which is suitable for many high strength applications. Although adding POFA to the cement mixtures harmed the absorption and porosity, those properties were very low at 3.4% and 11.5% respectively at a 40% POFA replacement ratio and after 28 days of curing. The HPCM mixtures containing POFA exhibited greater increase in strength and UPV as well as greater reduction in absorption and porosity than the control OPC mortar from 7 to 28 days of curing age, as a result of the pozzolanic reaction of POFA. Micro POFA with finely graded sand resulted in a dense and high strength cement mortar due to the pozzolanic reaction and increased packing effect. Therefore, it is demonstrated that the POFA could be used with high replacement ratios as a pozzolanic material to produce HPCM.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.217-219
• /
• 2012

In this study, the experiment was conducted in the level of mortar as one of the basic studies on pre-cast concrete which acceleration curing is not done. This study has the purpose to develop the strength of mortar into 20MPa within 6 hours in the condition of room temperature using admixtures which can accelerate C3S hydration reaction. In this experiment, W/C was fixed into 20%, PCE which can stimulate C3S was used as an accelerating admixture. From the results of this experiment, maximum content of accelerating admixture was 1%. Also, as more than 20MPa was measured through 6-hour compressive strength, it can be known that strength can be developed without steam-curing.

• Computers and Concrete
• /
• v.6 no.5
• /
• pp.391-401
• /
• 2009

This paper presents a study of the strength and chloride penetration of blended Portland cement mortar containing ground palm oil fuel ash (POA) and ground river sand (GS). Ordinary Portland cement (OPC) was partially replaced with POA and GS. Compressive strength, rapid chloride penetration test (RCPT) and chloride penetration depth of mortars were determined. The GS only asserted the packing effect and its incorporation reduced the strength and the resistance to chloride penetration of mortar. The POA asserted both packing and pozzolanic effects. The use of the blend of equal portion of POA and GS also produced high strength mortars, save cost and excellent resistance to chloride penetration owing to the synergic effect of the blend of POA and GS. For chloride depth, the mathematical model correlates well with the experimental results. The computer graphics of chloride depth of the ternary blended mortars are also constructed and can be used to aid the understanding and the proportioning of the blended system.