• 한국세라믹학회지
• /
• 제41권2호
• /
• pp.111-117
• /
• 2004

고순도 3Y-TZP에 알루미나를 0.3∼l.2wt%까지 첨가하여 attrition milling을 하고 slip-casting하여 시료를 제조하였다. 1390∼151$0^{\circ}C$까지 열처리하여 소결체의 소결특성을 기제적 물성과 미세구조 분석을 통하여 확인하였다. XRD를 이용하여 monoclinic-ZrO$_2$의 생성량을 정량적으로 확인하였으며, 147$0^{\circ}C$ 이장에서 열처리한 시료의 경우 m-ZrO$_2$의 생성으로 밀도의 저하를 보였으며, 비정상 입자성장을 유발하여 경도가 저하되었다. 알루미나의 첨가량이 0.9wt% 미만, 열처리 온도143$0^{\circ}C$에서 microhardness가 1360Hv 이상의 소결체를 제조할 수 있었다.

• 대한화학회지
• /
• 제61권2호
• /
• pp.57-64
• /
• 2017

Monoclinic $VO_2(M)$ nanoparticles codoped with 1.5 at. % W and 2.9 at. % Mg were synthesized by the hydrothermal treatment and post-thermal transformation method of $V_2O_5-H_2C_2O_4-H_2O$ with $Na_2WO_4$ and $Mg(NO_3)_2$. The composite thin film of the W/Mg-codoped $VO_2(M)$ with a commercial acrylic block copolymer was also prepared on PET substrate by wet-coating method. The reversible phase transition characteristics of the codoped $VO_2(M)$ nanoparticles and the composite film were investigated from DSC, resistivity and Vis-NIR transmittance measurements compared with the undoped and Wdoped $VO_2(M)$ samples. Mg-codoping into W-doped $VO_2(M)$ nanoparticles synergistically enhanced the transition characteristics by increasing the sharpness of transition while the transition temperature ($T_c$) lowered by W-doping was maintained. The codoped composite film showed the prominently enhanced NIR switching efficiency compared to only W-doped $VO_2(M)$ film with a lowered $T_c$.

• 한국표면공학회지
• /
• 제47권1호
• /
• pp.7-12
• /
• 2014

The characteristics of oxidation for the Zry-4 was measured in the $800^{\circ}C$ and high steam pressure (50 bar, 75 bar, 100 bar) conditions, using an apparatus for high pressure steam oxidation. The effect of accelerated oxidation by high-pressure steam was increased more than 60% in hydrogen-charged cladding than normal cladding. This difference between hydrogen charged claddings and normal claddings tends to be larger as the higher pressure. The accelerated oxidation effect of hydrogen charging cladding is regarded as the hydrogen on the metal layer affects the formation of the protective oxide layer. The creation of the sound monoclinic phase in Zry-4 oxidation influences reinforcement of corrosion-resistance of the oxide layer. The oxidation is estimated to be accelerated due to the creation of equiaxial type oxide film with lower corrosion resistance than that of columnar type oxide film. When tetragonal oxide film transformed into the monoclinic oxide film, surface energy of the new monoclinic phase reduced by hydrogen in the metal layer.

• 한국분말재료학회지
• /
• 제5권3호
• /
• pp.199-209
• /
• 1998

A new low melting inorganic binder, monoclinic $HBO_2$, has been developed for Selective Laser Sintering (SLS) of alumina powder by dehydration process of boron oxide powder in a vacuum oven at $120^{\circ}C$. It led to better green SLS parts and higher bend strength far green and fired parts compared to other inorganic binders such as aluminum and ammmonium phosphate. This appeared to be due to its low viscosity and better wettability of the alumina particle surface. A low density single phase ceramic, aluminum borate ($Al_{18}B_4O_{33}$), and multiphase ceramic composites, $A_{12}O_3-A_{14}B_2O_9$, were successfully developed by laser processing of alumina-monoclinic $HBO_2$ powder blends followed by post-thermal processing; both $Al_{18}B_4O_{33}$ and $A_{14}B_2O_9$ have whisker-like grains. The physical and mechanical properties of these SLS-processed ceramic parts were correlated to the materials and processing parameters. Further densification of the $A_{12}O_3-A_{14}B_2O_9$ ceramic composites was carried out by infiltration of colloidal silica, and chromic acid into these porous SLS parts followed by heat-treatment at high temperature ($1600^{\circ}C$). The densities obtained after infiltration and subsequent firing were between 75 and 80% of the theoretical densities. The bend strengths are between 15 and 33 MPa.

• 한국세라믹학회지
• /
• 제20권4호
• /
• pp.347-355
• /
• 1983

A batch mixture was prepared as 16mol% CaO-84mol% $ZrO_2$ of regeant-grade powder. The monoclinic Zirconia powder had an average particle size of $9.24 \mu\textrm{m}$ and calcium carbonate powder had a reported purity of 99.7 weight percent and mean particle size of TEX>$24, 37<\mu\textrm{m}$. The specimens were fired at 1400, 1500, 1650 and $1750^{\circ}C$ for 0. 3, 5 and 7 hours respectively. After fired the specimens were investigated using Scaning electron microscopy. Density Porosity Compressive strength Modulus of rupture and Thermal expansion were measured X-ray diffration analysis was also carried out. The results are as follows ; 1) As the firing temperature or soaking time was increased firing linear shrinkage apparent density compressive strength and modulus of rupture increased but apparent porosity decreased, 2) Cubic and monoclinic Zirconia was found at $1400^{\circ}C$ and cubic Ziconia found above $1500^{\circ}C$ 3) The specimens fired at 140$0^{\circ}C$ without soaking display thermal expansion curves by monoclinic〓tetragonal transformation and no tranformation was found at $1400^{\circ}C$ for 5hrs and above $1500^{\circ}C$. 4) The lattice parameter had constant value of 5.1345 $\AA$ through all the ranges of firing temperature 5) The higher the firing temperature was or the longer the soaking time was the larger the grain size was.

• 한국세라믹학회지
• /
• 제38권7호
• /
• pp.602-607
• /
• 2001

Zirconia powder containing 3 mol% yttria (3Y-PSZ) was casted on the cast iron substrate by plasma spraying method. Coated specimens were then heat treated at 500$\^{C}$ in nitrogen plasma. Wear tests were performed on nitrogen heat treated and non heat treated samples at temperatures from 25$\^{C}$ to 600$\^{C}$. Wear results showed that the friction coefficient and the wear loss of both the treated and the non-treated samples showed maximum value at 400$\^{C}$. These results were explained by low temperature thermal degradation due to the monoclinic transformation. Nitrogen plasma treatment significantly improved the tribological performance. The effect of nitrogen heat treatment on tribological behavior was explained by the increased micro-hardness and decreased monoclinic faction.

• 한국세라믹학회지
• /
• 제31권9호
• /
• pp.981-988
• /
• 1994

Crystallizable glasses with precipitation of celsian were prepared for the purpose of insulating dielectric layers for the devices such as integrated circuit substrates. Crystallization behavior of these glasses were studied by DTA, SEM, XRD analysis and by the measurement of dielectric properties. The base composition of the glass-ceramic consists in weight percent of 30% SiO2, 10% Al2O3, 26% BaO, 10% CaO, 10% ZnO, 8%TiO2 and 6% B2O3. 2-6 wt% Y2O3 were selected as the nucleating agent to promote monoclinic celsian formation. As a result, in barium-rich glasses containing 4~6wt% Y2O3 , monoclinic celsian was developed as major crystalline phase in the temperature range of 850~90$0^{\circ}C$. Also, the dielectric constant and quality factor of these glass-ceramics were about 9 and more than 1000, respectively.

• 전기학회논문지P
• /
• 제53권4호
• /
• pp.171-174
• /
• 2004

The $Ag_2Te$ crystal was grown by the Bridgman method. The $Ag_2Te$ crystal was an monoclinic structure with lattice constance a = $8.1686{\AA}$, b = $9.0425{\AA}$, c = $8.0065{\AA}$. Hall effect shows a n-type conductivity in the $Ag_2Te$ crystal. The electrical resistivity was 1.080e-$3{\Omega}cm$ and electron mobility was $-5.48{\times}10^3cm^2/V{\cdot}sec$ at room temperature(RT).

• E2M - 전기 전자와 첨단 소재
• /
• 제9권5호
• /
• pp.445-449
• /
• 1996

Structural and optical characteristics in Se thin film fabricated by EBE method had been studied. Se thin film was deposited with noncrystalline until substrate temperature of >$100^{\circ}C$ Color of its surface had red genealogy, and its optical energy band gap was about 2.45 eV. But Se film was grown with monoclinic at substrate temperature of over >$150^{\circ}C$ Also, color of its surface had gray genealogy, and its optical energy band gap was about 2.31 eV. Finally, after heat-treatment at >$150^{\circ}C$ for 15 min with substrate temperature of >$100^{\circ}C$ noncrystalline Se was proved to be hexagonal, and color of its surface had dark gray genealogy, and its optical energy band gap was about 2.06 eV. From the results, it was known that Se thin film for photoelectric device with the lowest optical energy band gap was accepted from hexagonal structure.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.1568-1571
• /
• 2005

We have evaluated thermal stability of a $BaAl_2Si_2O_8:Eu^{2+}$ $(BAS:Eu^{2+})$, which have polymorph property such as hexagonal, monoclinic structure depending upon firing temperature. When both polymorph $BAS:Eu^{2+}$ were baked in air at 500 $^{\circ}C$ for 30 min, the photoluminescence (PL) intensity of $monoclinic-BAS:Eu^{2+}$ was maintained of the initial intensity. However, the PL intensity of $hexagonal-BAS:Eu^{2+}$ decreased significantly, corresponding to about 34 %. From analyses of Rietveld refinement, the difference of thermal stability of both $BAS:Eu^{2+}$ can be ascribed to both crystal structure of host materials and the average interatomic distances between $Eu^{2+}$ ion and oxygen their crystal structure which plays a key role of shield for Eu2+ ions against oxidation atmosphere.