• 한국주조공학회지
• /
• 제22권3호
• /
• pp.121-129
• /
• 2002

According to the investigation of waste $CO_2$ molding sand in the 15 steel foundries in Busan and Gyeong area, about 1 ton of waste $CO_2$ molding sand per ton of steel castings production was produced In order to reduce amount of $Na_2O$, Loss of Boiling (L.O.B), Loss of Ignition (L.O.I), Conductivity and PH which are present in the waste $CO_2$ molding sand below the reclamation effect, more than 50% of elimination for reclamation was required. It was found that the waste $CO_2$ molding sand does not contain a harmful component designated by industrial waste materials. Reclamation of the waste $CO_2$ molding sand was practically achieved by an abrasive-dry reclamation process. According to bench time of the sodium silicate-bonded $CO_2$ molding sand, reduction of compressive strength and surface stability index(S.S.I) become slowdown. Therefore, the reclaimed sand could be allowed the reuse of molding sand in $CO_2$ molding process including core sand.

• 한국주조공학회지
• /
• 제25권4호
• /
• pp.173-178
• /
• 2005

The vacuum molding process is one of the clean-foundry molding-processes that can recycle molding sands repeatedly, because molding can be accomplished by introducing vacuum only among dry molding sands in flask. The effects of molding conditions such as sand grain fineness, vacuum pressure and coating thickness on the fluidity of A356 Al alloy were studied and the results was obtained that the fluidity length was decreased as the sand grain fineness number and coating thikness were decreased and the vacuum pressure was increased. A large amount of heat removal from the molten metal resulting from the vacuum suction during the vacuum molding process was the principal cause of this decrease in fluidity.

• Korean Chemical Engineering Research
• /
• 제44권2호
• /
• pp.136-148
• /
• 2006

주물공장에서는 주철을 녹여서 다양한 기계부품을 만든다. 다양한 기계부품을 만들기 위해 목형을 주물사에 넣은 후 주입구를 만들어 녹인 주철을 투입한다. 주물공장은 furan 공정을 포함해 많은 공정으로 이루어지며, 이 중 furan 공정은 목형에 주물사를 부어 넣는 공정이다. Furan 공정의 첫 단계는 주물사가 서로 엉겨 붙어 있게 하기 위해 접착성을 가지는 고분자 물질인 furan류를 주물사에 섞게 되고 녹은 주철이 목형으로 들어가는 것이며 고온에 의해 많은 유해 VOC류가 발생하게 된다. 또 공정조업에서 furan용 모래를 목형이 든 주물형틀에 부어 넣게 되고, 이때도 유독가스와 분진이 발생하게 되며 이 분진은 furan 물질을 포함하고 있어 조업자의 건강에 치명적인 요소가 되며, 이로 인해 조업기피현상이 심화되어 인력수급에 문제가 되고 나아가 사업 경영에 큰 걸림돌이 되고 있다. 본 연구는 이러한 조업기피의 원인을 제거하고 쾌적한 조업환경을 제공하기 위해 유해 VOC류와 집진을 동시에 수행할 수 있는 유해 VOC 및 분진 동시제거 시스템을 최적 설계하고 나아가 현장에 적용 설치하였다. 그 결과 설치 후 포름알데히드의 경우 VOC 0 ppm, 분진 $4{\mu}g/m^3$으로 조업환경이 개선되었으며, 조업자들의 조업 기피 요인을 해소하였다. 또한, 우리는 회사의 고용 문제를 해결하고, 작업의 생산성을 향상시킬 수 있었다.

• 한국주조공학회지
• /
• 제4권2호
• /
• pp.89-95
• /
• 1984

A Study on the Mechanical Properties of Molding Sand with Various Water/Clay Ratio A standard sample of molding sand was prepared by adding a various amount of bentonite, which has water/clay ratio from 0.4 to 0.6, into artificial sand, Hanyoung #6. The results obtained by measuring the room temperature properties of green mold are as follows. 1. This compressive strength of green molds which have 4% and 10% of bentonite decreased with increasing water/clay ratio, but the maximum strengths of 4.3 (psi) and 7.2 (psi) were observed in the samples with 6%, 8% bentonite respectively when the water/clay is 0.45. 2. The optimum water/clay ratio for strength and permeability increased from 0.4 to 0.5 with increasing clay. 3. The green compressive strength was proportional to the hardness. 4. Deformation increased with increasing water/clay ratio. 5. Flowability decreased with increasing water/clay ratio and clay content in molding sand.

• 한국주조공학회지
• /
• 제1권3호
• /
• pp.19-29
• /
• 1981

An emphasis has been placed on the importance of selecting a sand for furan sand process, which ie affected by the properties of sand. Investigations have been carried out to use the domestic artificial sands for the furan sand process. For laboratory investigations, the sands have been prepared and tested for chemical analysis, loss on ignition, sieve analysis, AFS grain fineness number, grain shape, PH value, acid demand, surface shape, theoretical surface area, moisture absorption, crushing durability and compressive strength and S. S. I. of molding sands. Most commercial sands have been found to be able to be used. The main requirement of the sands has been shown to be that 3 or 4 screen sands, AFS no.40-70 (or 100), of low acid demand, good surface area and good grain shape require less resin and catalyst to give an adequate strength.

• 한국주조공학회지
• /
• 제9권5호
• /
• pp.403-412
• /
• 1989

This study has been carried out to investigate into the properties of molding sands containing various core sands, $CO_2$, Shell, Furan, Pep Set and Cold Box, in the system sands using domestic active bentonite. The properties of system sands with 5% bentonite and 3% moistures containing baked core sands and no-baked core sands were varied by the ratio of core sands. The system sand containing no-baked core sands had been the poor bonding force and rough grain surface than those of the baked core sands. The L. O. I of system sand containing 30% organic binders core sands were more than inorganic binders core sands. It has been found that the no-baked core sands were necessary have to reclaim for using molding sand.

• 한국주조공학회지
• /
• 제4권1호
• /
• pp.5-11
• /
• 1984

Green compressive strength, permeability, deformation, flowability, compactability and green hardness values at room temperature are dependable on the grain distribution and grain shape. The results obtained under constant moisture (4% for sand) and bentonite (8% for sand) were as follows; 1. With decreasing grain size, surface area of sand grain was increased. 2. With decreasing grain size, coefficient of angularity was increased. 3. As surface area increased from $8926.43cm^2$ to $21211.16cm^2$ , green compressive strength was increased from $210.93\;g/cm^2$ to $449.98\;g/cm^2$, hardness was increased from 76.7 to 82.3, but permeability was decreased from $411.7\;{\frac{\;cc\;{\cdot}\;cm\;}{atm\;{\cdot}\;cm^2\;{\cdot}\;min.}}$ to $113.7\;{\frac{\;cc\;{\cdot}\;mm\;}{atm\;{\cdot}\;cm^2\;{\cdot}\;min.}}$ 4. As surface area increased from $8926.43\;cm^2$ to $21211.16\;cm^2$, flowability was decreased from 82.3% to 80.8%, deformation was decreased from $67.1\;cm\;{\times}\;10^{-3}$ to $54.6\;cm\;{\times}\;10^{-3}$, but compactability was increased from 44.8% to 54.3%. 5. Room temperature properties of molding sand were affected by variation of surface area.

• 한국주조공학회지
• /
• 제14권1호
• /
• pp.45-51
• /
• 1994

The possibility of using bulk talc as molding material was reviewed and tested with the measurement of thermal properties and computer simulations. The measured thermal conductivity and heat diffusivity($k{\rho}c$) of talc were $2.4W/m^{\circ}C$ and $6.6{\times}10^6J^2/m^4^{\circ}C^2s$, respectively. Thermal properties of talc could be ranked between those of sand mold and iron mold. Talc transforms into cristobalite and enstatite at $910^{\circ}C$, During the transformation volume and structure change, cracks appear on the surface and distortion occurs. Therefore talc can be used for molding material below $910^{\circ}C$ if carefully treated. Computer simulation was carried out to test whether talc insert could promote directional solidification in sand mold and iron mold. In sand mold, it was possible to achieve directional solidification of thin plate casting with the length to thickness ratio of 15, if both iron insert and talc insert were used. In iron mold, it was possible to achieve directional solidification only with talc insert.

• 한국정밀공학회지
• /
• 제2권3호
• /
• pp.41-46
• /
• 1985

The behavior of the burn-on in sand mold has been investigated by varying the pouring metal, bonding materials, additive materials and molding sand. The results obtained from thease experiments are as follows; 1) The burn-on layer of silica sand decreased in order of carbon steel, gray cast iron and stainless steel, and thease burn layer proceeded mostly by producing FeO. 2) The burning reaction of silica sand mold in carbon steel castings declined with increasingly bentonite content, but water-glass scarcely took part in the burn-on reaction. 3) The addition of feldspar and seacoal to silica sand promoted the inhibiting burn-on. 4) The burn-on layer of sand mold decreased of silica sand, chromite sand and olivine sand.

• 한국주조공학회지
• /
• 제43권1호
• /
• pp.37-40
• /
• 2023