• Journal of the Korean Ceramic Society
• /
• v.16 no.2
• /
• pp.69-76
• /
• 1979

This study attempted to characterize the powder and sintered specimen of Mn-Zn ferrite that was prepared by Hot Petroleum Drying Method. The results of the experiment were as follows: 1. The mixed sulfate powder prepared by Hot Petroleum Drying Method was homogeneous and very reactive. The ferrite formation of this powder occurred at lower temperature than the one prepared by Sulfate Dry Mixing Method. 2. The calcined oxide powder prepared by Hot Petroleum Drying Method was found to be agglomerated, and therefore it was very difficult to compact this powder. 3. The sintered density was 4.95g/㎤, 97% of the theoretical density, when the specimen was prepared by Hot Petroleum Drying method, calcined at 90$0^{\circ}C$ in air for 3h, sintered at 1,30$0^{\circ}C$ in air for 3h, and then cooled in nitrogen. 4. The discontinuous grain growth occurred at lower temperature in the specimen prepared by Hot Petroleum Dyring Method than in the one prepared by Sulfate Dry Mixing Method. The discontinuous grain growth was considered to be due to the presence of liquid formed by addition of CaO and $SiO_2$.

• Journal of the Mineralogical Society of Korea
• /
• v.12 no.2
• /
• pp.77-90
• /
• 1999

Characteristics and variations of chemical compositions in Co-rich crusts occurred in the EEZ of the Republic of Marshall Islands were reviewed. Correlation coefficient analysis, hierarchical cluster analysis, and Q-mode factor analysis for 62 samples were done in this study. All data were selected and gathered from the open file report of the cooperative cruise done by United States Geological Survey with Scripps Institute of Oceanography, University of Hawaii or Korea Ocean Research Development Institute. The average of crust thickness. Co content, and Ni content of 62 samples from the 21 seamounts were 30mm, 0.58 wt% and 0.40%, respectively. The mineral phases and associated elements assigned by correlation coefficients, cluster analysis and Q-mode factor analysis are following four. 1) CFA: P, Ca, CO2, Y, Sr: 2) Mn-oxide mineral: As, Mn, Co, Na: 3) Al-silicate mineral: Pd,Si, Al, Cu, Fe: 4) PGE-bearing mineral: Rh, Pt, Ir.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.374-378
• /
• 1999

Thin Films of BaYTiO system were Prepared by frequency (rf)/dc magnetron sputtering method. The preparation of target were accomplished by the mixed oxide method, and their composition consisted of the $Ba_{0.997}$ $Y_{0.003}$Ti $O_3$+0.5 $SiO_2$+x $M_{n}$O(x=0, 0.073, 0.1, 0.127, 0.154). The average particle size of (Ba,Y)Ti $O_2$ system ceramics with Mn $O_2$ additives increases as the amount of MnO additives increase and reaches the maximum grain growth when the amount of MnO is 0.127(mol%).).).).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.407-410
• /
• 2000

(M $n_{l-x}$M $g_{l-x}$)F $e_{2+x}$ $O_4$(x=0.0, 0.025, 0.1, 0.2) for NTC(negative temperature coefficient) thermistor was prepared by calcining at 80$0^{\circ}C$ and sintering at from 1100 to 130$0^{\circ}C$ with 5$0^{\circ}C$ intervals while x was varied from 0.0 to 0.025, 0.1 and 0.2. The best linear property was obtained in the based specimen sintered at 120$0^{\circ}C$ with x=0.1 composition. Thermistor parameter, $B_{25~85^{\circ}C}$, was in the range of 5000~ 7300 [K]. Temperature coefficient of resistance, $\alpha$$_{25^{\circ}C}$, was -5.2 %/$^{\circ}C$. The results showed the possibility that Mn-Ni-Co based thermistor could be substituted by the composition used in this study was confirmed.med.d.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.181-182
• /
• 2015

본 실험에서는 PET 위 무전해 도금을 위한 대안 공정 개발을 목적으로 은(Ag)와 과망간산염($MnO_4{^-}$)를 사용하여 기존에 일반적으로 사용된 Sn/Pd의 Sensitization과 Activation process를 대체하는 기술을 연구했다. Palladium(Pd)의 경우 공정비용에서 높은 부분을 차지하기 때문에 이를 대신하여 Ag를 사용했으며, PET 표면의 전처리를 위해 Ultra Violet과 과망간 산염을 이용하여 표면의 친수성을 높였다. 과망간산염을 사용하여 표면을 전처리하는 과정에서 이산화망간($MnO_2$)과 알코올 작용기가 생성되는데 Ag activation 단계에서 촉매 생성에 중간 매개체 역할을 하는 것으로 사료된다. 이와 같은 결론을 도출 하기 위해서 표면 위 Ag의 화학적 구조 및 상 분석을 위해 XPS와 TEM이 사용되었으며 표면에서 Ag는 Ag-O와 같은 Silver oxide의 형태와 Ag-Mn-O와 같은 Compound로 무전해 도금을 위한 촉매 역할 하는 것으로 판단된다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.946-949
• /
• 2000

Amorphous MnO$_2$$.$ nH$_2$O in 1M KOH aqueous electrolyte proves to be an excellent electrode for a faradic electrochemical capacitor cycled between -0.5 and +1.0 versus Ag/AgCl. In order to observe morphology and crystalline structure of MnO$_2$powder, we analyzed it by XRD and SEM. The effect of oxidation treatment on MnO$_2$electrode was observed by different oxidation voltages. A maximum capacitance of 364F/g was obtained by 1.1V oxidation treatment. This capacitance was attributed solely to a surface redox mechanism

• Korean Journal of Materials Research
• /
• v.12 no.9
• /
• pp.712-717
• /
• 2002

New wet chemical method so called precipitation-evaporation method was suggested for preparing spinel structure lithium manganese oxide ($LiMn_2$$O_4$) for Li ion secondary battery. Using precipitation-evaporation method, $LiMn_2$$O_4$ cathode materials suitable for Li ion secondary batteries can be synthesized. Single spinel phase $LiMn_2$$O_4$ powder was synthesized at lower temperature compared to that of prepared by solid-state method. $LiMn_2$$O_4$ powder prepared by precipitation-evaporation method showed uniform, small size and well defined crystallinity particles. Li ion secondary battery using $LiMn_2$$O_4$ as cathode materials prepared by precipitation-evaporation method and calcined at $800^{\circ}C$ showed discharge capacity of 106.03mAh/g and discharge capacity of 95.60mAh/g at 10th cycle. Although Li ion secondary battery showed somewhat smaller initial capacity but good cyclic ability. It is suggested that electro-chemical properties can be improved by controlling particle characteristics by particle morphology modification during calcination and optimizing Li ion secondary battery assembly conditions.

• Korean Journal of Metals and Materials
• /
• v.49 no.4
• /
• pp.281-290
• /
• 2011

In order to gain better understanding of the selective surface oxidation and its influence on the galvanizability of a transformation-induced plasticity (TRIP) assisted steel containing 1.5 wt.% Si and 1.6 wt.% Mn, a model experiment has been carried out by depositing Si and Mn (each with a nominal thickness of 10 nm) in either monolayers or bilayers on a low-alloy interstitial-free (IF) steel sheet. After intercritical annealing at $800^{\circ}C$ in a $N_2$ ambient with a dew point of $-40^{\circ}C$, the surface scale formed on 590 MPa TRIP steel exhibited a microstructure similar to that of the scale formed on the Mn/Si bilayer-coated IF steel, consisting of $Mn_{2}SiO_{4}$ particles embedded in an amorphous $SiO_{2}$ film. The present study results indicated that, during the intercritical annealing process of 590 MPa TRIP steel, surface segregation of Si occurs first to form an amorphous $SiO_{2}$ film, which in turn accelerates the out-diffusion of Mn to form more stable Mn-Si oxide particles on the steel surface. During hot-dip galvanizing, particulate $Fe_{3}O_{4}$, MnO, and Si-Mn oxides were reduced more readily by Al in a Zn bath than the amorphous $SiO_{2}$ film. Therefore, in order to improve the galvanizability of 590 TRIP steel, it is most desirable to minimize the surface segregation of Si during the intercritical annealing process.

• Journal of the Mineralogical Society of Korea
• /
• v.23 no.4
• /
• pp.281-295
• /
• 2010

This paper deals with magnetic susceptibility, mineralogy, soil properties (pH, EC, CEC, loss on ignition), iron and manganese oxides, the content and partitioning of heavy metals (As, Cd, Cr, Cu, Ni, Pb, Zn), and their mutual relationship in the soil samples of an unpolluted, abandoned mine area, and industrial complex area. The various minerals derived from weathered bedrock were identified by X-ray diffraction in the unpolluted soil samples, except for the magnetic minerals. XRD analysis also revealed the existence of hematite and magnetite related to mine tailings and waste rocks in the abandoned mine area samples. The industrial complex area samples had carbonate minerals, such as calcite and dolomite, that might be due to anthropogenic deposition. The sum of the reducible, oxidizable, and residual fractions was over 80% for the abandoned mine area samples and over 50% for the industrial complex area samples using the sequential extraction method. The industrial complex area samples had a relatively high carbonate fraction that was associated with carbonate minerals. The content of aqua regia-extractable Fe, Mn, As, and Zn had a high positive correlation with the content of the dithionite-citrate-bicarbonate (DCB)-extractable method related to Fe/Mn oxide phases. The 54% and 58% of aqua regia-extractable Fe and As content, respectively, acted together with the concentrations of the DCB-extractable phases. Magnetic susceptibility values of total samples ranged from 0.005 to $2.131{\times}10^{-6}m^3kg^{-1}$. The samples including iron oxide minerals, such as hematite and magnetite, had a high magnetic susceptibility. The magnetic susceptibility showed a significant correlation with the heavy metals, Cd (r=0.544, p<0.05), Cr (r=0.714, p<0.01), Ni (r=0.645, p<0.05), Pb (r=0.703, p<0.01), and Zn (r=0.496, p<0.01), as well as Fe (r=0.608, p<0.01) and Mn (r=0.615, p<0.01). The aqua regia-extractable Fe and Mn content had a significant positive correlation with Cd, Cr, Cu, Ni, and Zn. However, the DCB-extractable Fe and Mn content had a significant positive correlation with As and Ni, indicating that the heavy metals were associated with Fe and Mn oxide minerals.

• Journal of Korean Society of Water and Wastewater
• /
• v.24 no.3
• /
• pp.341-349
• /
• 2010

It is well known that manganese is hard to oxidize under neutral pH condition in the atmosphere while iron can be easily oxidized to insoluble iron oxide. The purpose of this study is to identify removal mechanism of manganese in the D water treatment plant where is treating bank filtered water in aeration and rapid sand filtration. Average concentration of iron and manganese in bank filtered water were 5.9 mg/L and 3.6 mg/L in 2008, respectively. However, their concentration in rapid sand filtrate were only 0.11 mg/L and 0.03 mg/L, respectively. Most of the sand was coated with black colored manganese oxide except surface layer. According to EDX analysis of sand which was collected in different depth of sand filter, the content of i ron in the upper part sand was relatively higher than that in the lower part. while manganese content increased with a depth. The presence of iron and manganese oxidizing bacteria have been identified in sand of rapid sand filtration. It is supposed that these bacteria contributed some to remove iron and manganese in rapid sand filter. In conclusion, manganese has been simultaneously removed by physicochemical reaction and biological reaction. However, it is considered that the former reaction is dominant than the latter. That is, Mn(II) ion is rapidly adsorbed on ${\gamma}$-FeOOH which is intermediate iron oxidant and then adsorbed Mn(II) ion is oxidized to insoluble manganese oxide. In addition, manganese oxidation is accelerated by autocatalytic reaction of manganese oxide. The iron and manganese oxides deposited on the surface of the sand and then are aged with coating sand surface.