저온용 Mn-Cu계 촉매의 적정 적용온도를 파악하기 위해 다양한 조건에서 소성하였으며 소성한 촉매를 사용하여 반응온도, 유속 등에 따른 탈질효율 변화를 조사하였다. 실험결과 촉매의 전처리과정에서 바나듐-티타니아계 촉매보다 낮은 일정온도 이상으로 적용시 촉매의 산화가, pore 등에서 변화가 일어나며 궁극적으로 활성저하로 귀결됨을 알 수 있었다.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2004.11a
• /
• pp.443-444
• /
• 2004

• Clean Technology
• /
• v.21 no.2
• /
• pp.130-139
• /
• 2015

The NO oxidation process has been applied to improve a removal efficiency of NO included in exhaust gas. In this study, to produce a dry oxidant for the NO oxidation process, the catalytic H₂O₂ decomposition method was proposed. A variety of the heterogeneous solid-acidic Mn-based catalysts were prepared for the catalytic H₂O₂ decomposition and the effect of their physico-chemical properties on the catalytic H₂O₂ decomposition were investigated. The results of this study showed that the acidic sites of the Mn-based catalysts has an influence on the catalytic H₂O₂ decomposition. The Mn-based catalyst having the abundant acidic sites within the wide temperature range in NH₃-TPD shows the best performance for the catalytic H₂O₂ decomposition. Therefore, the NO oxidation efficiency, using the dry oxidant produced by the H₂O₂ decomposition over the Mn-based catalyst having the abundant acidic properties under the wide temperature range, was higher than the others. As a remarkable result, the best performances in the catalytic H₂O₂ decomposition and NO oxidation was shown when the Mn-based Fe₂O₃ support catalyst containing K component was used for the catalytic H₂O₂ decomposition.

• Clean Technology
• /
• v.29 no.3
• /
• pp.185-192
• /
• 2023

This study was conducted to obtain basic process simulation data before conducting pyrolysis experiments for the development of a thermochemical conversion system by recirculation of heat carrier and gases thereby. In this study, polypropylene (PP) was used as a pyrolysis sample material as an alternative to waste plastics, and fluid sand was used as a heat transfer medium in the system. Manganese (Mn) was chosen as the catalyst for the pyrolysis experiment, and the catalyst pyrolysis was performed by impregnating it in the sand. The basic properties of PP were analyzed using a thermogravimetric analyzer (TGA), and liquid oil was generated through catalytic pyrolysis under a nitrogen atmosphere at 600℃. The carbon number distribution of the generated liquid oil was confirmed by GC/MS analysis. In this study, the effects of the presence and the amount of Mn loading on the yield of liquid oil and the distribution of hydrocarbons in the oil were investigated. When Mn/sand was used, the residue decreased and the oil yield increased compared to pyrolysis using sand alone. In addition, as the Mn loading increased, the ratio of C₆~C₉ range gasoline in the liquid oil gradually increased, and the distribution of diesel and heavy oil with more carbon atoms than C₁₀ in the oil decreased. In conclusion, it was found that using Mn as a catalyst and changing the amount of Mn could increase the yield of liquid oil and increase the gasoline ratio in the product.

• Proceedings of the KAIS Fall Conference
• /
• 2011.05a
• /
• pp.320-322
• /
• 2011

저온에서의 탈질능력이 우수한 망간계 촉매를 바탕으로 수소-TPR 장치를 사용하여 저온에서의 활성을 파악하였다. 상기 결과를 바탕으로 주요 공정조건인 반응온도, 유속, 수분함량, 주입물 농도, 주입가스 중 수분함량 등에 대한 탈질능의 변화를 조사하였다. 실험결과 망간계 촉매의 경우 반응온도가 증가할수록 탈질능력은 감소하였으며 수분함량에 대해서도 탈질효율이 크게 영향을 받음을 알 수 있었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.9
• /
• pp.4250-4256
• /
• 2011

Mn catalyst promoted with Cu were prepared and tested for selective catalytic reduction of $NO_x$ with $NH_3$. Performance of each catalyst was investigated for $NO_x$ activity while changing temperature, space velocity, water content and $O_2$ concentration. Hydrogen conversion efficiency of catalyst was also measured in the $H_2$-TPR system. The inhibition effect of water on catalyst was investigated with the on-off control of water supply. High activity of Mn-Cu catalyst was observed for $160{\sim}260^{\circ}C$. It is found that increase of oxygen concentration acts as a promotor to the increase of catalyst activity but water content acts as a inhibitor.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.1
• /
• pp.100-109
• /
• 2016

In this study, the NO oxidation using dry oxidant produced by catalytic $H_2O_2$ conversion was conducted. It was shown that Mn-based $Fe_2O_3$ support catalyst has the best performance in the catalytic $H_2O_2$ conversion and its combined-NO oxidation. The reaction characteristics of NO oxidation was investigated by the various operation conditions such as $H_2O_2$ amount, oxidation temperature and space velocity. As a results, the oxidation efficiency of NO greatly depends on the oxidation reaction temperature, $H_2O_2$ amount and space velocity. The performance of NO oxidation was increased with increasing the oxidation temperature and $H_2O_2$ amount. Also, the performance of NO oxidation was decreased with increasing the space velocity.

• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.190-194
• /
• 2012

10 wt% Mn supported on various commercial $TiO_2$ catalysts were prepared by wet-impregnation method for the low temperature selective catalytic reduction (SCR) of NO with $NH_3$. A combination of various physico-chemical techniques such as BET, XRD, XPS and TPR were used to characterize these catalysts. MnOx surface densities on MnOx/$TiO_2$ catalyst were related to surface area. As MnOx surface density lowered with high dispersion, the SCR activity for low temperature was increased and the reduction temperature ($MnO_2$ ${\rightarrow}$ $Mn_2O_3$) of surface MnOx was lower. For a high SCR, MnOx could be supported on a high surface area of $TiO_2$ and should be existed a high dispersion of non-crystalline species.