• Journal of Korea Foundry Society
• /
• v.36 no.1
• /
• pp.10-17
• /
• 2016

Numerical analysis has been performed to evaluate effect of the shape variables such as core length, slot width and slot length on misrun in aluminum die casting process for motor rotor. The predictive method for misrun in diecasting process was established by comparing the result of numerical analysis and an actual motor rotor. Solidification modulus was introduced to predict quantitatively the castability of aluminum diecasting process for motor rotor. It was found that there are minimum critical solidification modulus and slot width to prevent misrun according to core length through diecasting limit diagram proposed using the predictive method. The critical solidification modulus and slot width increase as core length increases to prevent misrun of aluminum motor rotor in diecasting process. Based on the results, the design criteria of slot shape to prevent misrun of aluminum motor rotor with various core length were established.

• Journal of Korea Foundry Society
• /
• v.22 no.6
• /
• pp.309-314
• /
• 2002

The effect of mold density and evacuation on surface defect of high chromium cast iron upon EPC process was investigated. Under evacuation of $0.1{\sim}0.3$ atm, surface defects were carbon defect, burn on and misrun. Carbon defect was augmented by increasing mold density from 0.011 g/$cm^3$ to 0.03 g/$cm^3$ under evacuation of $0.1{\sim}0.3$ atm, but carbon defect was decreased by increasing evacuation from 0.1 to 0.3 atm. Burn-on wasn't found under evacuation of 0.1 atm regardless of mold density, but burn-on was augmented by increasing evacuation from 0.2 to 0.3 atm and decreased by reducing mold density. Misrun was only found under 0.1 atm evacuation and 0.011 g/$cm^3$ mold density.

• Journal of Korea Foundry Society
• /
• v.29 no.3
• /
• pp.138-143
• /
• 2009

Vacuum suction is applied to the mold during pouring in the inclined gravity die casting to remove defects such as misrun and gas porosity in the brake master cylinder. Casting defects are observed after solidification and their cause is analyzed by using the calculated results with commercial solidification and flow analysis code(ZCAST). The optimum vacuum suction is -2 cmHg, and when the start time of vacuum suction is 3 seconds after pouring, better filled result is obtained by holding it for 15 seconds. Reproducibility test under the optimum conditions attained from the above pouring tests is performed, and it is confirmed that these pouring conditions can be applied to the mass production immediately.

• Journal of Korea Foundry Society
• /
• v.41 no.2
• /
• pp.127-131
• /
• 2021

Based on its good compatibility with high-temperature environments, the Ti-48Al-2Cr-2Nb alloy is used for high-temperature materials of industrial equipment. In this study, a Ti-48Al-2Cr-2Nb alloy turbocharger turbine wheel was fabricated by a vacuum centrifugal casting method. The conditions that prevent misrun defects of the turbocharger turbine wheel blade from centrifugal casting using alumina molds were investigated. The microstructure of the alloy prepared by vacuum centrifugal casting was studied by means of optical microscopy (OM), with a micro-Vickers hardness analyzer (HV), by X-ray diffraction (XRD) and by SEM-EDS. The HV and SEM-EDS examinations of the as-cast Ti-48Al-2Cr-2Nb alloy showed that the thickness of the oxide layer (α-case) was typically less than 50 ㎛. At a high preheating temperature of 1,100℃, a moderate RPM of 260, and with an alumina mold with a large gate size, there were almost no misrun defects. Therefore, it was confirmed that a Ti-48Al-2Cr-2Nb alloy turbocharger turbine wheel with fewer misrun defects could be achieved through a high preheating temperature, a moderate RPM, a large gate size and an alumina mold to suppress the formation of alpha-case components.

• Journal of Korea Foundry Society
• /
• v.21 no.4
• /
• pp.253-259
• /
• 2001

There are many methods to produce metal foams, which can be classified into three groups according to the state of the starting metal i.e. liquid or powder or solid. Three types of defects such as cell closing, cell deformation or breakdown and cell misrun are thought to be occurred when we make the open cell aluminum foams by precision casting. Filling ability of the mold slurry between preform is related with cell closing, mold collapsibility is related with cell deformation or breakdown, mold temperature and pouring pressure are related with cell misrun. These factors can be evaluated by measuring slurry fluidity, burnout strength and permeability of the mold. Properties of the plaster mold were evaluated to find optimum mold conditions for high quality open cell aluminum foam in this study. Permeability was almost zero independent of burnout conditions, however, crack initiation was found on the surface of all specimens one or two minutes after taking out from the furnace. Crack has grown and disappeared with time. This crack may facilitate the mold filling when molten metal is poured, because of the improved mold permeability. It was considered that crack initiation and disappearance was closely related with temperature difference between the surface and inner part. Knocking-out the mold is a difficult problem due to the small cell size, because continuous mesh structure of the metal foam is not strong. It is not easy to remove molding material after pouring. We can expect that water quenching can facilitate the knocking-out the mold after solidification without damaging cell structures. Collapsed particles after water quenching became bigger with the increase in time.

• Journal of Korea Foundry Society
• /
• v.42 no.4
• /
• pp.209-217
• /
• 2022

In the present study, in order to prevent the misrun defects that occur during traditional brass casting, a method for selecting the proper casting process conditions is proposed. A learning model was developed and demonstrated to be able to learn the presence or absence of defects according to the casting process conditions and to predict the occurrence of defects depending on the certain process given. Appropriate process conditions were determined by applying the proposed method, and the determined conditions were verified through a comparison of different simulation results with additional conditions. With this method, it is possible to determine the casting process conditions that will prevent defects in the desired sand model. This technology is expected to contribute to realization of smart traditional brass farming workshops.

• Conservation Science in Museum
• /
• v.15
• /
• pp.4-25
• /
• 2014

Chuncheon National Museum currently own a bronze Buddhist gong that was discovered in 1987 at the Sudasa Temple site of in Suhangri, Pyeongchang. Significantly, showing many casting defects and areas where was repaired, the Gong offered crucial information about the casting technique. To better understand the production technique, scientific analysis was conducted on various aspects of the gong, including its materials, moulds, chaplets, and defects. Composition analysis revealed that the gong was composed primarily of copper ^71.6wt%, tin ^18.2wt%, and lead ^7.2wt%, along with about 1wt% of both arsenic and antimony. The lead content of the chaplets was higher than that of the gong, and the lead content was the highest in the solder, which was used to fill holes after casting. Surface analysis, based on the parting line, indicated that the gong was most likely produced with the sand casting process. Radiography and close examination of the surface disclosed various casting defects ^{e.g., Cold Shut, Surface Folds, Misrun, and Blowholes Adjacent to Chaplets} and their possible causes. The casting defects of a few holes were filled with soft solder.

• Journal of Korea Foundry Society
• /
• v.31 no.5
• /
• pp.274-283
• /
• 2011

The vacuum die casting is a promising candidate of the stamping process for fabrication of fuel cell bipolar plate due to its advantages, such as precision casting, mass production and short production time. This study proposes vacuum die casting process to fabricate bipolar plates in fuel cell. Bipolar plates were fabricated under various injection conditions such as molten metal temperature and injection velocity. Also, according to injection velocity conditions, simulation results of MAGMA soft were compared to the experimental results. In case of melt temperature $650^{\circ}C$, misrun occurred. When the melt temperature was $730^{\circ}C$, mechanical properties were low due to dendrite microstructure. Injection velocity has to set at more than 2.0 m/s to fabricate the sound sample. When melt temperature, injection velocity (Fast shot), and vacuum pressure are $700^{\circ}C$, 2.5 m/s and 30 kPa respectively, sample had good formability and few casting defects. Simulation results are mostly in agreement with experimental results.

• Journal of Conservation Science
• /
• v.38 no.3
• /
• pp.234-242
• /
• 2022

The study aimed to investigate the split casting method based on the recreation of the iron-seated Buddha (ISB) statue (number 1971) in the Chuncheon Museum. The statue was designed using three-dimensional scan data and reduced to half-size. Using the existing research results, the ISB statue was created by mold production and split casting. The mold was prepared by mixing sand and clay at a ratio of 3:4 and 1:3 on the outside and inside, respectively, and then casting was done. Various casting defects were observed in the ISB casting and similar shapes were seen. The casting defects included veining or finning, misrun, open or external shrinkage, surface or subsurface blowholes, surface pinholes, and shift. The microstructures were identified as branch-shaped dendrite and pearlite organizations, and black graphite was observed between the cementite organizations. The study findings may be relevant in exploring traditional casting and manufacturing techniques of ISB and may aid in the production of the original form of ISB.