• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2006.05a
• /
• pp.105-109
• /
• 2006

본 연구는 Karr column을 이용하여 희토류 염화물 수용액상에서 비희토성분인 철의 분리에 대한 기초 연구로서, 아민계 추출제인 Alamine336을 이용하여 염화물 수용액상에서 유기상의 농도, 염소이온 농도, 염산 농도에 따른 철 성분의 분리특성을 파악 하였다. Batch 실험결과 추출제 농도가 증가함에 따라 철성분 제거율이 급격히 상승하였으며, 염산 및 염소이온 농도의 경우도 유사한 결과를 나타내었다. Batch 실험을통해 확인된 불순물(Fe)을 추출하기위한 최적 조건은 염산농도 2M, 추출제 농도 0.1M, 상비 1, 추출시간 30분으로서, 이때 희토류 염화물 수용액상의 철 성분 함량은 0.7ppm 이하로서 제거율은 99.9%였다. 또한 최적의 batch 실험조건에서 반응시간(=체류시간)을 변화시키며 실험한 결과, 반응시간 60분의 조건에서 batch 실험과 유사한 결과를 얻을 수 있었다.

• Resources Recycling
• /
• v.31 no.2
• /
• pp.12-19
• /
• 2022

The study was conducted to develop a vanadium recovery process using reduction pre-treatment in the Vanadium TitanoMagnetite (VTM) The sample for the research was provided by the Gwan-in Mine in Pocheon, Gyeonggi-do. The vanadium content of the sample is 0.54 V₂O₅% and vanadium is concentrated mainly in magnetite and ilmenite. Magnetic separation of the sample can increase vanadium content up to 1.10 V₂O₅%. To increase the vanadium content further, reduction pre-treatment was performed, which is a process of concentrating vanadium present in the iron by reducing iron in magnetite using carbon(C). Based on this reduction pre-treatment, the magnetic separation process was developed, which achieved a vanadium grade of 1.31V₂O₅% and 79.68% recovery. In addition, XRD analysis of the vanadium concentrate before and after reduction and the final vanadium concentrate was performed to confirm the behavior of vanadium by reduction pre-treatment.

• 한국지구물리탐사학회:학술대회논문집
• /
• 2003.11a
• /
• pp.637-641
• /
• 2003

Abrasive powders were recovered from electrical industry sludge by simple physical separation for their recycling. The raw electrical industry sludge was filter pressed, dried, dispersed and then classified by air classifier at various conditions. The three kinds of particles with different particle size distribution were classified by controlling rotor speed and air volumes of the classifier. The recovered abrasive powders, which are classified at 5,000,9000 and 13,000 rpm of rotor speed, are almost same properties to raw pumice, garnet and rouge powders, respectively. The results of particle size analysis, X-ray diffraction and SEM observation show that the recovered powders can be reused as an abrasive powders.

• Resources Recycling
• /
• v.21 no.2
• /
• pp.3-8
• /
• 2012

In the points of the environmental conservation and the recirculating utilization of limited resources, it is very important to recover valuable metals like Au, Ag, Pd, Cu, Sn, Ni, Co, and Li used as industrial raw materials from urban ores. From now, many processes have been developed for recovering the valuable metals contained in urban ores and some of them have been operated commercially. In the paper, pyrometallurgical processes developed for reclaiming valuable metals from urban ores will be briefly introduced.

• Journal of Powder Materials
• /
• v.15 no.3
• /
• pp.234-238
• /
• 2008

Al-Cu alloy nano powders have been produced by the electrical explosion of Cu-plated Al wire. The porous nano particles were prepared by leaching for Al-Cu alloy nano powders in 40wt% NaOH aqueous solution. The surface area of leached powder for 5 hours was 4 times larger than that of original alloy nano powder. It is demonstrated that porous nano particles could be obtained by selective leaching of alloy nano powder. It is expected that porous Cu nano powders can be applied for catalyst of SRM (steam reforming methanol).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.386-387
• /
• 2006

This study is about the recycling technology of scrap a PCB(printed circuit board) produced in home appliances or automobile industry. And we develop the recycling technology of cooper (Cu)which is contained to leaching solution. In stead of electrolytic collecting in existing sulphuric atmosphere, we apply process using the ammonia solution which is used in economizing energy. So m the process of electrolyzing scrap a PCB through the leaching and separation, we examine the effect of the nickel contained to the solution and the cooper degree of purity which is changed according to current density.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.10a
• /
• pp.330-334
• /
• 2005

본 연구에서는 유해 중금속을 다량 함유하고 있는 산업폐기물의 고화 처리에 사용되는 칼슘설포알루미네이트(4CaO $3Al_2O_3\;SO_4$ 이후부터 CSA로 기입)의 제조를 위해 철강부산물인 압연 슬러지를 활용하여 그 특성에 대해 조사하였다. 본 연구에서는 철강 부산물인 압연슬러지 외에 석회석 미분물, 인산부산 석고를 혼합하여 칼슘알루미네이트 상을 합성하였다. 합성 결과 소성온도 $1250^{\circ}C$에서부터 CSA가 합성되었고, 이와 함께 칼슘실리케이트$(2CaO\;SiO_2)$와 칼슘알루미노페라이트($4CaO\;Al_2O_3\;Fe_2O_3$)도 함께 합성되었다. CSA 합성에 미치는 중금속 영향을 관찰한 결과 원료의 중금속이 CSA 합성 온도를 낮추는 효과가 있는 것으로 나타났다. CSA를 이용한 철강산업 폐기물의 중금속 고용 처리 연구에서도 본 실험에서 합성된 CSA가 폐기물의 중금속 고화 처리에 효과가 있는 것으로 나타났다.

• Journal of the Mineralogical Society of Korea
• /
• v.21 no.4
• /
• pp.443-450
• /
• 2008

나노튜브 형상의 할로이사이트는 화장품 약물 등 활성물질의 방출시간을 연장하는데 응용할 수 있는 천연 나노광물이다. 할로이사이트를 이용한 활성물질 적재 방출 제어기술을 최초로 등록한 1997년 미국 특허를 필두로 2007년에는 비타민과 글리세린 등의 기능효과제를 광범위하게 포함하는 기능성화장품 제조기술에 대한 특허가 출원되었다. 학술 논문으로서는 화장품 보다 서방형 약물전달 기술에 관한 연구가 주로 발표되고 있다. 최근 화장품용 분체에 단순한 기재로서의 역할뿐만 아니라 기능성을 추가로 부여하고 있다. 특히, 할로이사이트는 기능성 화장성분의 전달 속도를 제어할 수 있으며 다른 분체보다 밀도가 낮아 팩 크림 로션류의 기재로 적합하다. 따라서 나노튜브형 할로이사이트를 활용한 나노캐리어 기술은 최근 화장품 유형별 시장점유율에서 2위로 부상한 기능성화장품 분야의 핵심기술로 성장할 것으로 기대된다.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.05a
• /
• pp.178-182
• /
• 2005

본 연구에서는 추출제가 함유된 추출레진$(75{\sim}150{\mu}m)$으로 채워진 저압액체크로마토그래피를 이용하여 용리온도$(20{\sim}60^{\circ}C)$와 유속$(1.41{\sim}7.04cm/min)$에 따른 Dy와 Ho의 분리특성을 조사하였다. 용리액인 HCl의 농도는 $0.25{\sim}0.5mol/L$가 적절한 것으로 판단되며, HCl $0.5mol/L$ 이상에서는 분리효과가 거의 없었다. 일정한 용리액 농도에서 유속이 느릴수록, column의 온도가 높을수록 분리도와 해상도는 개선되었으며, 유속이 느릴수록 용리액의 소모량은 감소, 분리시간은 증가하였다. 적정조건인 용리온도 $60^{\circ}C$, 유속 7.04cm/min, HCl 0.25mol/L에서 분리도는 ${\alpha}_{Dy}^{Ho}=1.36$로 가장 높았다.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.05a
• /
• pp.147-151
• /
• 2005

실리콘 잉곳의 절단공정에서 발생하는 폐실리콘 슬러지는 실리콘과 실리콘카바이드 등의 유가자원이 함유되어 있는데, 본 연구에서는 폐실리콘 슬러지 중의 실리콘 분말을 효과적으로 분리, 회수하는 방법에 대해 검토하였다. 폐실리콘 슬러지는 상당량의 절삭유와 소량의 철분말이 포함되어 있는데 절삭유는 유기 용매에 용해시켜 효과적으로 분리하였고, 철분말은 자력선별에 의해 제거하였다. 절삭유와 철성분이 제거된 잔사인 실리콘과 실리콘 카바이드의 혼합 분말로부터 초음파 분산 선별법을 사용하여 실리콘 분말을 효율적으로 분리회수 하였다.