• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.25-30
• /
• 2001

The purpose of this study is to present a basic data about the workability of high strength concrete to apply to a field of construction work. The main parameters are as follows; environmental temperature, elapsed time and the use of mineral admixture or not under the same mixing proportions. From the result, Adding amounts of superplasticizer to get a target slump were different in the respective temperature condition. Slump loss according to elapsed time was influenced by environmental temperature. the amount of superplasticizer and the slump loss were decreased by using mineral admixture(garnet powder) and by making concrete under lower temperature.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.5
• /
• pp.55-60
• /
• 2004

This study was performed to evaluate the early estimation of compressive strength of concrete using mineral admixture by refrigeration curing method. It was a method of early decision for the property of concrete after the curing age 28days through the refrigeration curing at $-18{\pm}3^{\circ}$ for five hours. The test result was fixed connection between the curing age 28days and 31hours by the compressive strength test through the standard curing and refrigeration curing. Accordingly, it can be reduced the mistake of construction work by forecasting the property of concrete through the refrigeration curing.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.95-101
• /
• 1999

This study was performed to evaluate the characteristics of workability and strength of the concrete containing mineral admixtures such as flyash, blast furnace slag, zeolite powder. As a result, considering their workability and strength, the optimum replacement ratio of them to plain concrete were obtained for each ternary admixture. This increased compressive strength was ascribed to both the closer parkinof fine particles and pozzolan reactivity of powders. This work showed that could be effectively utilized as a blending material without any decrease in the strength of early hydration stage. On the other hand, we found that the compressive strength at early ages ternary ordinary and high strength concrete untill 7 days was small, but that ternary concrete at 28days was highly increased about 31% and 15% extent.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.225-228
• /
• 2006

To clarify the one body behavior of reinforcing bar and concrete, it is important to investigate bond characteristics between two materials. Bond strength is decided by applied force and interface area between reinforcing bar and concrete. And, the resultant force of chemical adhesive force, frictional force, and mechanical interaction are to be main factors. Property of concrete influences on chemical adhesive force and frictional force; bond strength is decreased by corrosion of reinforcing bar, as the result, durability is also decreased. In this study, to confirm bond characteristics with property of concrete, w/c ratio and blending of mineral admixture were selected as the main test parameters. The results obtained from this study will be used as the basic data for bond characteristics with corrosion.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.209-210
• /
• 2009

In constuction work, the early compressive strength in reference to the demolding time of side forms is significant on reducing the construction time and improving the economical efficiency. Therefore, this study is investigated the effect of the kind and replacement ratio of mineral admixture on the development of early strength.

• International Journal of Concrete Structures and Materials
• /
• v.6 no.1
• /
• pp.31-40
• /
• 2012

Self-consolidating concrete (SCC) is a recently developed innovative construction material. SCC fills in a formwork without any vibrating consolidation, which allows us to eventually achieve robust casting. However, high formwork lateral pressure exerted by SCC is a critical issue regarding its application as cast-in-place concrete. In order to control the risk caused by high formwork pressure, a comprehensive prediction model for the pressure was previously proposed, investigated, and validated with various SCC mixtures. The model was originally designed to simulate the intrinsic pressure response of SCC mixtures while excluding other extrinsic influencing factors such as friction and flexibility of the formwork. The model was then extended to consider extrinsic factors such as friction between SCC mixtures and formwork. In addition, other interesting topics for peak formwork pressure and mineral admixture effects were summarized in the paper.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.107-113
• /
• 2003

The rheology properties of cement paste with variation of quantity and type of mineral admixture were investigated. The rheology of the paste was assessed by using a HAAKE Rotovisco(RT 20) rheometer having cylindrical serrate spindle. The results were as follows: The viscosity and the yield stress of cement paste were decreased by the only replacement of 10% BFS(blast furnace slag) or the only replacement of 30% FA(fly ash), whereas SF(silica fume) increased them as the replacement quantity was increased. Increasing the dosage of HRWR(high-range water reducer), the rheology properties were improved significantly in cement paste with the replacement of SF. In addition, rheology properties of two ingredient blended pastes, such as BFS(20%)-SF(5%), FA(20%)-SF(5%), were improved more than those of three ingredient blended paste, BFS(20%)-FA(20%)-SF(5%).

• Magazine of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.43-47
• /
• 2012

• Computers and Concrete
• /
• v.32 no.2
• /
• pp.185-206
• /
• 2023

This article aimed to explore the optimization of mineral admixtures and retarding admixture for high-performance concrete. In essence, fresh concrete can be regarded as a mixture in which both coarse and fine aggregates are suspended in a cement-based matrix paste. Based on this view, the test procedure was divided into three progressive stages of binder paste, mortar, and concrete to explore their rheological behavior and mechanical properties respectively. At each stage, there were four experimental control factors, and each factor had three levels. In order to reduce the workload of the experiment, the Taguchi method with an L9(3⁴) orthogonal array and four controllable three-level factors was adopted. The test results show that the use of the Taguchi method effectively optimized the composition of high-performance concrete. The slump of the prepared concrete was above 18 cm, and the slump flow was above 50 cm, indicating that it had good workability. On the other hand, the 28-day compressive strength of the hardened concretes was between 31.3-59.8 MPa. Furthermore, the analysis of variance (ANOVA) results showed that the most significant factor affecting the initial setting time of the fresh concretes was the retarder dosage, and its contribution percentage was 62.66%. On the other hand, the ANOVA results show that the most significant factor affecting the 28-day compressive strength of the hardened concretes was the water to binder ratio, and its contribution percentage was 79.05%.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.3
• /
• pp.282-290
• /
• 2013

In this study, the adjustment range of mixture factor with replacement mineral admixture was reviewed to secure the mixture change data of high volume concrete compared to general concrete. When changing the concrete mix to high volume concrete within the universal concrete mixing, the adjustment range of mixture to ensure optimum quality is as follows. Unit-water content is $20{\sim}30kg/m^3$ downward. Fine aggregate ratio dropped by approximately 1% when W/B was reduced by 5%, and it is reduced by approximately 0.12% when there is a 5% increase in the total replacement rate. When the FA replacement rate was increased by 5%, the AE agent was approximately 20% to 30% higher compared with the conventional one. When the FA and BS replacement rate rose by 5%, W/B was reduced by about 1 to 4%.