• Journal of the Korea Concrete Institute
• /
• v.23 no.5
• /
• pp.609-615
• /
• 2011

MgO concrete containing lightly burnt MgO powder at $850{\sim}1,000^{\circ}C$ may have a long-term expansibility characteristic. Such expansibility of MgO concrete can compensate the shrinkage at later ages since the hydration of the MgO is very slow. However, the addition of MgO delays the initial hydration of cement and increases the setting time of cement. Also, the porosity and pore-size distribution of the MgO concrete are different from OPC concrete. Therefore, in order to use MgO in practice, both mechanical and durability properties of MgO concrete should be carefully examined. In this study, durability tests on carbonation, freezing-thawing, and diffusion of chloride were carried out after 56 days of underwater curing at $20^{\circ}C$ to compare durability characteristics of 5% MgO-mixed concrete with those of OPC concrete. The results showed that MgO concrete shows a greater durability than the concrete with no MgO, because the micro structure in the MgO concrete is much denser due to its expansibility characteristic.

• Tribology and Lubricants
• /
• v.34 no.3
• /
• pp.84-92
• /
• 2018

Bearings are essential for reducing vibration and wear, in order to achieve high durability and increase longevity. White metal treatment of tilting pads via centrifugal casting method has the possibility of increasing durability. However, this manufacturing method has drawbacks such as long processing time, high defect rate, and harmful health effects. Laser cladding deposition technique is a powerful method that can address these issues by decreasing the processing time and providing good adhesion. In this study, we suggest optimum conditions for laser cladding deposition that can be used in industrial applications. We deposited a soft white metal layer on SCM440 that is primarily used in shafts to minimize wear of bearing pads. During the laser deposition process, we controlled factors such as laser power, powder feed rate, and laser head speed to determine the optimum conditions. In addition, we measured the hardness using micro Vickers, and performed field emission scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, and friction tests to investigate the mechanical properties and surface characteristics for different parameters. Based on the experimental results, we suggest that laser power, powder feed rate, and laser head speed of 1.3 kW, 2.5 rpm, and 10 mm/s, respectively, constitute the optimum conditions for producing white metals using laser cladding.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.1
• /
• pp.7-12
• /
• 2017

3YSZ + (x) $Al_2O_3$ composites (x = 20, 40, 60, 80 wt%) were fabricated and the influences of particle sizes of $Al_2O_3$ on their microstructures and mechanical properties were investigated with XRD, SEM, vickers hardness and fracture toughness. $Al_2O_3$-3YSZ composites containing $Al_2O_3$ powder of a $0.3{\mu}m$ and an $1.0{\mu}m$, which are here in after named as $Al_2O_3$($0.3{\mu}m$)-3YSZ and $Al_2O_3$($1.0{\mu}m$)-3YSZ, respectively, were made by mixing raw materials, uni-axial pressing and sintering at $1,400^{\circ}C$, $1,500^{\circ}C$, and $1,600^{\circ}C$. $Al_2O_3$($0.3{\mu}m$)-3YSZ composites show the higher density and the better mechanical properties than $Al_2O_3$($1.0{\mu}m$)-3YSZ composites. The Vickers hardness of the $Al_2O_3$($0.3{\mu}m$)-3YSZ composites show a peak value of 1,997 Hv at the content of 60 wt% $Al_2O_3$, which is a slightly higher value in comparison with 1,938 Hv of the $Al_2O_3$($1.0{\mu}m$)-3YSZ composite. However, the fracture toughness of $Al_2O_3$-3YSZ composites monotonically increases with decreasing the content of $Al_2O_3$ without any peak values. $Al_2O_3$($0.3{\mu}m$)-3YSZ and $Al_2O_3$($1.0{\mu}m$)-3YSZ composites sintered at $1,600^{\circ}C$ have a maximum value of a $6.9MPa{\cdot}m^{1/2}$ and a $6.2MPa{\cdot}m^{1/2}$, respectively at the composition of containing 20 wt% $Al_2O_3$. It should be noticed that the mechanical properties and the sintering density of the $Al_2O_3$-3YSZ composites can be enhanced by using more fine $Al_2O_3$ powder due to their denser microstructure and smaller grain size.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.271-272
• /
• 2012

Bulk Metallic Glasses (BMGs or amorphous alloy) exhibit high strength and good corrosion resistance. Applications of thin films and micro parts of BMGs have been used a lot since its inception in the research of BMGs. However, Application and fabrication of BMGs are limited to make structural materials. Thin films of BMGs which is sputtered on the surface of structural materials by sputtering process is used to improve limits about application of BMGs. In order to investigate the difference of properties between designed alloys and thin films, we identified that thin films deposited on the surface that have the characteristic of the amorphous films and the composition of designed alloys. Zr-Cu (Cu=30, 35, 38, 40, 50 at.%) and Zr-Cu-Al (Al=10 at.% fixed, Cu=26, 30, 34, 38 at.%) alloys were fabricated with Zr (99.7% purity), Cu (99.997% purity), and Al (99.99% purity) as melting 5 times by arc melting method before rods 2mm in diameter was manufactured. In order to analyze GFA (Glass Forming Ability), rods were observed by Optical Microscopy and SEM and $T_g$, $T_x$, ($T_x$ is crystallization temperature and $T_g$ is the glass transition temperature) and Tm were measured by DTA and DSC. Powder was manufactured by Gas Atomizer and target was sintered using powder in large supercooled liquid region ($=T_x-T_g$) by SPS(Spark Plasma Sintering). Amorphous foil was prepared by RSP process with 5 gram alloy button. The composition of the foil and sputtered thin film was analyzed by EDS and EPMA. In the result of DSC curve, binary alloys ($Zr_{62}Cu_{38}$, $Zr_{60}Cu_{40}$, $Zr_{50}Cu_{50}$) and ternary alloys ($Zr_{64}Al_{10}Cu_{26}$, $Zr_{56}Al_{10}Cu_{34}$, $Zr_{52}Al_{10}Cu_{38}$) have $T_g$ except for $Zr_{70}Cu_{30}$ and $Zr_{60}Al_{10}Cu_{30}$. The compositions with $T_g$ made into powders. Figure shows XRD data of thin film showed similar hollow peak.

• Corrosion Science and Technology
• /
• v.6 no.4
• /
• pp.147-153
• /
• 2007

This study sought to investigate the reaction of Co-binder containing tungsten with molten zinc. Four kinds of Co-W alloys (pure, 10%W, 20%W, 30%W) were prepared using the powder metallurgy method. The specimens were immersion-tested in molten pure zinc baths at $460^{\circ}C$. To evaluate the corrosion property in molten zinc, the weight loss of the specimen was measured after the immersion tests at different immersion times (10~300 min.). Co-10%W alloys, compared with pure cobalt, showed no effect of tungsten addition on the reaction rate in molten zinc. The relationship between the weight loss and the square root of immersion period represents a straight line in both pure cobalt and Co-10%W alloy. The Co-Zn reaction layer in Co- 1O%W alloy consists of $\gamma2$, $\gamma1$, $\gamma$ and ($\beta1$ phases. The rate of weight loss significantly increases and the weight loss behavior is not well accord with the linear relationship as the tungsten content in the Co-W alloy increases. The $\beta1$ layer was not formed on the Co-20%W alloy and neither was a stable Co-Zn intermetallic compound layer found on the Co-30%W alloy. The main cause of increase in reaction rate with increasing tungsten content is related with the instability of the Co-Zn reaction phases as seen on micro-structural analysis.

• Nuclear Engineering and Technology
• /
• v.52 no.9
• /
• pp.1939-1944
• /
• 2020

Pool boiling heat transfer of a copper microporous coating was experimentally studied in borated water with a concentration of boric acid from 0.0 to 5.0 vol percent (vol%) to determine the effect of boric acid on boiling heat transfer in water. A high-temperature, thermally conductive microporous coating (HTCMC) was created by sintering copper powder with an average particle size of 67 ㎛ onto a 1 cm × 1 cm plain copper surface with a coating thickness of ~300 ㎛ within a furnace in a vacuum environment. The tests showed that the nucleate boiling heat transfer coefficient (NBHT) of HTCMC became slightly less enhanced as the concentration of boric acid increased but the NBHT coefficient values were still significantly higher than those of the plain surface. The critical heat flux (CHF) values from 0 to 1.0 vol% were maintained at ~2,000 kW/㎡, and then, they gradually decreased down to ~1,700 kW/㎡ as the concentration increased further to 5.0 vol%. It is believed that the micro-scale pores of the HTCMC were partially blocked by the high boric acid concentration during the nucleate boiling such that the small bubbles were not effectively created using the HTCMC reentrant cavities as the boric acid concentration increased.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.7
• /
• pp.467-472
• /
• 2015

Thermal batteries are primary power sources for military applications requiring high reliability, robustness and long storage life. Conventional electrodes for thermal batteries are prepared by compacting powder mixtures into pellets. Separator is composed of halide mixture, such as LiCl-KCl eutectic salt, blended with MgO to immobilize the molten salt. In order to increase the power density and energy density, the resistance of electrolyte should be reduced because the resistance of electrolyte is predominant in thermal batteries. In this study, wetting behaviors and impregnation weight of molten salts as well as the micro structures of ceramic felt were investigated to be applicable to thin electrolyte. Discharge performances of single cell with the ceramic separator impregnated by molten salt were evaluated also. Zirconia felt with high porosity and large pore outperformed alumina felt in wetting characteristics and molten salt impregnation as well as discharge performances. Based on the results of this study, ceramic felt separator impregnated with molten salt have revealed as an alternative of conventional thick MgO based separator with no conspicuous sign of thermal runaway by short circuit.

• Journal of the Korean Ceramic Society
• /
• v.56 no.6
• /
• pp.526-533
• /
• 2019

Indialite/cordierite glass-ceramics demonstrate excellent microwave dielectric properties such as a low dielectric constant of 4.7 and an extremely high quality factor Qf of more than 200 × 10³ GHz when crystallized at 1300℃/20 h, which are essential criteria for application to 5G/6G mobile communication systems. The glass-ceramics applied to dielectric resonators, low-temperature co-fired ceramic (LTCC) substrates, and direct casting glass substrates are reviewed in this paper. The glass-ceramics are fabricated by the crystallization of glass with cordierite composition melted at 1550℃. The dielectric resonators are composed of crystallized glass pellets made from glass rods cast in a graphite mold. The LTCC substrates are made from indialite glass-ceramic powder crystallized at a low temperature of 1000℃/1 h, and the direct casting glass-ceramic substrates are composed of crystallized glass plates cast on a graphite plate. All these materials exhibit excellent microwave dielectric properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.21-21
• /
• 2009

후막 광식각 기술을 이용하여 형성된 Ag 전극과 LTCC 기판 사이의 접착력을 향상시키기 위하여 무기 바인더로서 anorthite, diopside 및 MLS-62 glass frit을 첨가하여 감광성 Ag paste를 제조하였다. 소성 후의 glass pool effect를 감소시키기 위해 attrition mill을 통하여 미세 glass 분말을 준비하였다. Glass frit은 Ag powder의 5vol%~25vol%의 함량으로 첨가하여 감광성 Ag paste를 제조하였고 패턴 형성 후 $850^{\circ}C$에서 1시간 소결하였다. 전극과 기판 사이의 접착력은 micro-ball shear test 법으로 측정하였으며, Ag 전극 부착력은 glass frit의 함량 증가에 따라 증가하다가 감소하는 경향을 보이는데, 이는 과량의 glass frit 첨가로 인한 전극 내부에 액상 풀의 형성에 기인한 것으로 보여진다. Ag 전극의 면저항은 glass frit의 함량이 증가함에 따라 $0.13m{\Omega}{/\square}$에서 $2.06m{\Omega}{/\square}$까지 증가하는 경향을 나타내었다. 소성 전후의 전극 패턴의-수축율은 $100{\mu}m$의 선폭을 기준으로 glass frit의 첨가랑이 증가할수록 43.3%에서 35.0%로 감소하였으며, 그 결과 최소 선폭 $25{\mu}m$의 미세 전극 패턴의 형성이 가능하였다.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.5
• /
• pp.65-70
• /
• 2008

Asphalt concrete pavements are susceptible to deformation and failure compared to cement concrete pavements. Epoxy is commonly used to enhance the bonding and durability of structures. Based on this concept, an epoxy and ceramics combined mixture was developed and applied to the field to estimate the pavement performance, Laboratory and field performance tests were conducted to observe the applicability of epoxy and ceramics composite materials compared to the conventional one. In this research, the epoxy and ceramics composite mixturewas used in two ways. 7 mm and 15 mm of thin surface layers using the mixture were constructed on cement and asphalt concrete pavements, respectively, after surface treatment. 12 months of field performance surveys were conducted to observe the resistances to the crack and deformation. According to the field performance tests, epoxy and ceramics combined mixture showed better bonding and field performances than the conventional one.