• Applied Chemistry for Engineering
• /
• v.8 no.5
• /
• pp.709-714
• /
• 1997

$TiO_2$ hydrate coating on mica in an aqueous solution of $TiOSO_4$ by the hydrolysis using ammonia water studied with emphasis on coating conditions for a uniform coating. For the uniform coating of $TiO_2$ film on mica surface, it was found that smaller mica particles were coated more uniformly compared to larger particles. It was necessary to suppress the rate of formation of hydrated $TiO_2$ particles in solution, which were deposited on mica and generate irregular coating. It was also necessary to control precipitation yield by varying the reaction temperature to obtain uniform coating. More uniform coating was obtained with higher precipitation yield. A uniform dense film was formed when mica particles of average size of $14.7{\mu}m$ is used for mica slurry solution, of which pH is 2.5, and the factor of acidity of $TiOSO_4$ solution is 291, and the solution was kept at $80^{\circ}C$ for 3 hours. The morphology of $TiO_2$ film formed on mica was little affected by firing at $900^{\circ}C$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.1
• /
• pp.888-894
• /
• 2015

Inorganic composite particles have excellent physical and chemical characteristics and have been applied in various industries. Recently, many studies have examined the optical properties, such as light scattering, refraction, transmission characteristics, by coating organic-inorganic materials on a substrate, such as mica. Mica is widely applied as a pigment, plastics, painted products, and ceramics because of its high chemical stability, durability and non-toxicity. Magnesium oxide has a range of properties, such as high light transmittance, corrosion resistance and non-toxicity, and it is used as an optical material and polymer additives. To use the optical properties of mica and magnesium oxide, mica was coated with magnesium hydroxide by a dissolution and recrystallization process. In this study, the optimal conditions for the haze value of the particles were found by adjusting the amount of precursors and pH. Magnesium hydroxide layers were formed on the surfaces of mica and converted to MgO after calcination at $400^{\circ}C$ for 4 h. The results showed that the value of MgO-coated mica haze can be controlled easily by the amount of the magnesium hydroxide and pH. The optical properties of the inorganic composite powder were analyzed using a hazemeter and the highest haze value was 85.92 % at pH 9. The physicochemical properties of the synthesized composite was analyzed by SEM, XRD, EDS, and PSA.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.32 no.3 s.58
• /
• pp.141-148
• /
• 2006

This study is intended to analyze the impact of PMMA on color changes comparatively by making 2 types of cheek color items with red-color pigments: one containing PMMA, which is one of the recently developed circular polymers and used when producing color make-up items that have aero powder as the chief ingredient, and the other without it. To accomplish the purpose, we have reviewed literature on raw materials that have aero powder as the chief ingredient. Also, after making compounds of PMMA and pigments lot aero powder, such as Talc, Mica, OMC Talc As, Mica As, we examined them compared to those without PMMA using spectrophotometer, a questionnaire survey, and Digital camera. Besides, the particles were analyzed using SEM. As a result of the analysis, cosmetics containing PMMA represent more vivid and rich colors, putting on one's face softly. Since the entire specific surface area of PMMA is large enough to absorb oil evenly, it yields vivid and rich colors. But, Mica, one of natural pigments, shows a result as opposed to that of Mica As, one of silicon-compounded pigments, suggesting that pearl effect may possibly causes defused reflection. Based on these findings, it is expected that cosmetics will have more vivid colors, or improved color presentation, as well as the softer sense of touch when a circular polymer of PMMa is added to the manufacturing process of color make-up items.

• Journal of Advanced Navigation Technology
• /
• v.14 no.1
• /
• pp.49-56
• /
• 2010

Severe energy constraints and the low power consumption require the significance of the energy efficient error control mechanisms in wireless sensor network (WSN). In this paper, an automatic repeat request (ARQ) methodology for the analysis of error control schemes in WSN is presented such that the effects of packet length, the modulation scheme and the interference effect of the wireless channel are investigated. Moreover, an analyis of ARQ error control is provided by considering two major architectures for wireless sensor network, i.e., Mica2 and MicaZ sensor nodes. And the throughput performance of WSN with asynchronous FSK signal and DSSS-OQPSK signal with selective repeat ARQ scheme are analyzed in multiple interference environment, and the probability of receiving a correct bit and packet from target node to sink node is evaluated as a function of the channel parameter, the number of wireless sensor node, and the spreading factor.

• Korean Journal of Metals and Materials
• /
• v.50 no.7
• /
• pp.523-530
• /
• 2012

We investigated the experimental method that uses the homogeneous precipitation method to prepare mica flakes-coated rutile-type titania pearlescent pigment with urea as a precipitant. $TiO_2$ particles exhibit a high reflection of lights and optical properties with chemical stabilities, so they are appropriate for coating on luminescent pigments (mica). The coating principle of mi ca coated titania with various thicknesses was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and tested by spectrophotometer. Mica with a particle size in the range of $40-60{\mu}m$ was suspended in water, and metal sulphates and urea were added to the mixture, which was heated to boiling. The change in pH was continuously followed. The metal oxide and crystal structure were affected by the conditions of $TiOSO_4$ concentration and reaction time with a sintering temperature the range of $800-1100^{\circ}C$.

• Journal of Adhesion and Interface
• /
• v.15 no.1
• /
• pp.9-13
• /
• 2014

The purpose of this work is to investigate the specific gravity, thermal, and mechanical property changes of polypropylene (PP)/mica composites before and after solid-state extrusion. On increasing the filler content, the specific gravity of the composites increased. The specific gravity of the oriented specimen containing filler in PP matrix is found to be much smaller than that of pre-specimen due to the formation of more microvoids. The presence of microvoids in the case of oriented composite specimen significantly affected the tensile and flexural properties of the composites. Both flexural strength and modulus of the composites showed maxima when the mica contents was 10 wt%, regardless of the orientation via solid state extrusion.

• Korean Journal of Metals and Materials
• /
• v.49 no.5
• /
• pp.367-373
• /
• 2011

This paper studies the experimental method that uses the homogeneous precipitation method to prepare mica flakes coated with anatase-type titania pearlescent pigment with urea as precipitant. The optimum technology parameters, the chemical composition, the microstructure, and the color property of resulting pigments are discussed. The coating principle of mica coated titania with various coating thickness is analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy(TEM) and tested by spectrophotometer analysis. The colored nanocrystalline pigments with different morphology and coating thickness 45-170 nm were prepared by homogeneous precipitation treatment of $TiOSO_4$(titanum oxysulfate) aqueous solutions. Characterizations on the pigments show that the pearlescent effects of the pigments depend mainly on mica size, thickness of the metal oxide deposit, its chemical composition, and crystal structure.

• Economic and Environmental Geology
• /
• v.40 no.6
• /
• pp.771-784
• /
• 2007

This study shows the weathering characteristics of mica-schist affected by faulting and metamorphism through laboratory tests. Frozen-thaw test, which simulate the physical-chemical weathering processes in the laboratory, shows the important influence of foliation developed in mica-schist, resulting in $20{\sim}40%$ reduction of UCS according to weathering grade of rock. Slaking durability test was carried out for different weathering grade rock specimens and indicated that the specimens from fault area had a low durability index compared to other relatively fresh samples. XRD analysis allowed to estimate the dynamic evolution of mineral composition through wet-dry cycle in which the chlorite was the most important mineral leached out during slaking test. The creep test indicated that the main deformation produced along the foliation plane. The compacted clay minerals between discontinuity planes influence on the discontinuity shearing properties and result in a big difference between peak shear strength and residual strength. The results of laboratory tests on mica-schist show the possibility of a important deformation along the foliation plane or discontinuity.

• Polymer(Korea)
• /
• v.31 no.5
• /
• pp.428-435
• /
• 2007

The thermomechanical property, morphology, and gas permeability of nanocomposites of ultra high molecular weight polyethylene (UHMWPE) with two different organoclays are compared. Hexamethylene benzimidazole-mica ($C_{16}BIMD-Mica$) and Cloisite 25A were used as reinforcing fillers in the formation of UHMWPE hybrid films. Dispersions of organoclays with UHMWPE were carried out by using the solution intercalation method at different organoclay contents to produce nano-scale composites. Transmission electron microscopy (TEM) micrographs show that some of the clay layers are dispersed homogeneously within the polymer matrix on the nano-scale, although some clay particles are agglomerated. We also found that the addition of only a small amount of organoclay is enough to improve the thermomechanical property and gas barrier of the UHMWPE hybrid films. In general, Cloisite 25A is more effective than $C_{16}BIMD-Mica$ in increasing both the thermomechanical property and the gas barrier in a UHMWPE matrix.

• The Journal of Engineering Geology
• /
• v.28 no.4
• /
• pp.593-603
• /
• 2018

The most of groundwater with high U-concentration occur in the Jurassic granite of Gyeonggi massif and Ogcheon belt, and some of them occur in the Cretaceous granite of Ogcheon belt. On the contrary, they do not occur in the Jurassic granite of Yeongnam massif and the Cretaceou granite of Gyeongsang basin. The Jurassic and Cretacous granite, the host rock of high U-groundwater, were resulted from parental magma with high ratio of crustal material and highly differentiated product of fractional crystalization. These petrogenetic characteristics explain the geological evidence for preferential distribution of uraniferous groundwater in each host rock. It were reported recently that high U-content, low Th/U ratio and soluble mineral occurrence of uraninite in the two-mica granite of Daejeon area which have characteristics of S-type peraluminous and highly differntiated product. It is the mineralogical-geochemical evidences supporting the fact that the two-mica granite is the effective source of uranium in groundwater. The biotite granite and two-mica granite of Jurassic age were reported as biotite granite in many geological map even though two-mica granite occur locally. This fact suggest that the influence of two-mica granite can not be ignored in uraniferous groundwater hosted by biotite granite.