• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.3
• /
• pp.120-123
• /
• 2005

The 5 mol% ZnO doped $LiNbO_3$ film and the 2 mol% MgO doped $LiNbO_3$ film were grown on the $LiNbO_3$ (001) substrate by liquid phase epitaxy (LPE) method with $Li_2CO_3-V_2O_5$ flux system. The crytsallinity and the lattice mismatch between $Zn:LiNbO_3$, film and $Mg:LiNbO_3$, film were analyzed by x-ray rocking curve (XRC). In addition, the ZnO and MgO distribution in the cross-section of the multilayer thin films was observed using electron probe micro analyzer (EPMA).

• Korean Journal of Crystallography
• /
• v.4 no.2
• /
• pp.74-85
• /
• 1993

Single crystals of LiNbO3 have found extensive application in electro-optic and nonlinear optic devices. However, laser-induced refartive index inhomogeneities, which have been labeled opical damage impose limits on device optical damage in LiNbO3 is imporved if more than 4.5 rml% MgO is added to the melt The laser damage thrueshold increased as much as 100 times better then that of undoped crystals. The MgO doped cystal has thus been urterlsiv81y studied since then. In the study, Mgo:LiNbOs(MLA) single crystals dopsd with 0, 2.5, 5.0, 7.5, 10.0 mol% MgO have been grown by the czocrualski technique. The metls were prepared in the platinum crluible and 15∼20mm diameter crystals were grown with a length of 20∼30mm in a resitance heater. The growth rate was 2.5mm/hr, the rotation speed 15rpn. Before sawing MLN single crystals were annealed for 24 hours under atmosphere at a temperature of 1080℃. After sawing, we have found an annual ring cross section of MNA crystals only in the direction of perpendicilar to the c-axis. Nonuniform dispusion of MgO was pointed out that the cuties of the state of oxide were strongly affected by oxygen partial pressure in.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.3
• /
• pp.401-406
• /
• 1998

For the applications in optical waveguides and devices, LiNbO_3$ single crystals need to overcome the weakness of optical damage due to the inhomogeneities of laser-induced refractive index. This problem can be solved by doping of Mg in LiNbO_3$ and proton exchange of LiNbO_3$. In this study, to understand the mechanism of optical damage resistance in LiNbO_3$, the changes of lattice defects in LiNbO_3$ caused by MgO doping and acid treatment were observed indirectly by $OH^-$ absorption bands using a FT-IR spectrophotometer. The effect of lattice defects on temperature, heat-treatment and polishing were also investigated. It is shown that MgO doping increases optical damage resistance by generating the defects of $Mg_{Nb}^{2+}$ in the lattice of LiNbO_3$, and that proton exchange by implantation of $H^+$ ion in the hexagonally closest packed oxygen layers on the surface of LiNbO_3$, makes lattice defects, which diffuse into the crystal after heat-treatment above $400^{\circ}C$.

• Korean Journal of Optics and Photonics
• /
• v.4 no.1
• /
• pp.84-89
• /
• 1993

Spatial homogenity of Mg (4 mole %):LiNb$O_3$ is investigated by studying the characteristic of Second Harmonic Generation in Mg:LiNb$O_3$ as a function of temperature and DC Electric Field. It is found that the temperaturs at which the intensity of the second harmonic is reduced to the first zero from its maximum for the phase matching condition is shifted linearly to the strength of DC Electric field applied to optic axis of Mg:LiNb$O_3$. From these results, the electro-optic coefficient of Mg:LiNb$O_3$ is estimated to be higher than that of Congruent LiNb$O_3$ by a factor of 1.5.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.1
• /
• pp.1-4
• /
• 1991

The applicability of $LiNbO_{3}$ as a substrate for fabrication of Ti-indiffused waveguide electro-optic devices is limited. Ti diffuses comparatively in congruently melting $LiNbO_{3}$; the Curie temperature of this material is too low to permit diffusion temperatures much above $1100^{\circ}C$ without the necessity of re-poling the crystal. Both of hese difficulties could be eliminated by incorporating certain dopants in $LiNbO_{3}$. Crystals of $LiNbO_{3}$ doped with Ti and Mg were grown and evaluated. The electroptic coefficients and birefringence of $LiNbO_{3}$ doped crystals were measured at ${\lambda}=.6328$ and $1.32\;$\mu{m}$. Curie temperatures were measured. The Curie temperature of both undoped and Ti-doped $LiNbO_{3}$ was $1130^{\circ}C$; that for Mg-doped $LiNbO_{3}$ was $30^{\circ}$ higher. From these data, a composition for the crystals was estimated. Thermogravimetric data confirmed this estimate and showed that the composition of Mg : $LiNbO_{3}$ was $49.3{\pm}0.2mole%\;Li_{2}O$ ; the composition of the undoped and Ti : $LiNbO_{3}$ samples was $48.6{\pm}0.2mole%$. Diffusion of Ti into both Mg-doped and Ti-doped $LiNbO_{3}$ crystals was studied as a function of $Li/NbO_{3}$ ratio and temperature.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.20-22
• /
• 1999

The effect of dopant and stoichiometry on the physical and optical properties of $LiNbO_{3}$ were studied. We prepared three samples, undoped, MgO doped $LiNbO_{3}$ with congruent composition and near-stoichiometric $LiNbO_{3}$. Dielectric constant and transmittance in UV/VIS/IR light range were measured. The results showed that the features for high [Li]/[Nb] were similar to those for low [Li]/[Nb] but with high [Mg].

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.1
• /
• pp.1-10
• /
• 1995

Congruent $LiNbO_3$ single crystals and $LiNbO_3$ : Mg single crystals, having high resistance to optical damage, doped with MgO to the levels of 2.0, 5.0 and 7.0 mol% were grown successfully by CZ method and optical damage of each crystal was measured by compen. sation method. With doping level reaching about 5 mol%, there was an abrupt change in the features of optical absorption edge and $OH^-$ absorption band. From these data, we confirmed indirectly the threshold in MgO doping level. When the MgO doping amount reaches about 5 mol% in the melt, $Mg^{2+}$ occupies Nb site and becomes $Mg_{Nb}^{2+}$, resulting in the sharp increase of optical damage resistance. The optical damage resistance of $LiNbO_3$ : Mg was improved more than three times when MgO amount in the melt reaches 5 mol%.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.447-453
• /
• 1999

Congruent $LiNbO_3$ crystals with doped Mg and codoped with Mn or Fe were grown by the Czochralski method. It is known that the physical properties of $LiNbO_3$ depend strongly on the addition of Mg and transition metals. This is established by studying the following properties; XRD patterns, the phase transition temperature, energy of the fundamental absorption edge, the shape of the absorption band of the $OH^-$ vibration and lines of the ESR of $Fe^{3+},\; Mn^{2+}$. The position of the UV absorption edge and the shape and peak point of the absorption band of the $OH^-$ vibrational band changed monotonously up to a critical concentration of $Mg^{2+}$ ions. The mechanism of the incorporation of Mg ions changes at this concentration. The transition temperature was estimated by measuring the dielectric temperature behavior up to $1230^{\circ}C$ in a frequency range of 100Hz to 10MHz. EPR of $Mn^{2+}\;and\; Fe^{3+}$ ions were employed to investigated the Mg doping effects in the $LiNbO_3$ crystal. The increase of linewidths and the asymmetry of signals were observed in all crystals. New signals of $Fe^{3+}$ arising from the new centers were observed I the heavily Mg-doped crystals.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.4
• /
• pp.532-542
• /
• 1996

The electrical and optical properties of the annealed $LiNbO_{3}$ single crystal with congruently melting composition and MgO or ZnO doped $LiNbO_{3}$ single crystal grown by the FZ method. The electrical and optical properties such as electrical conductivity, dielectric constant (Curie temperature), electro-mechanical coupling factor, optical transmittance and refractive indices of the grown crystals were measured and the nonlinear refractive indices of the grown crystals were calculated theoretically. The doping effects of MgO and ZnO were investigated by comparing the electrical and optical properties of the undoped $LiNbO_{3}$ single crystal and those of the $LiNbO_{3}$ single crystals doped with MgO or ZnO.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.2
• /
• pp.129-134
• /
• 1995

Bulk properties of single crystals $KMnCl_3$ undoped and Mg- doped $LiNbO_3$ were examined by using the neutron scattering technique. This study shows that the good -looking samples by polarized light have to be examined by the. neutron scattering to ensure the bulk properties of single crystal. Large mosaic spread in KMnCb indicated the crystal is not in a single domain. Many parts are relatively randomly directed against crystal axis with close angle each other. For the small mosaic spread of Li~ in the scattering pattern, it is found that some large domains have close orientations. Mg doped Li~ is turned out to be a well grown one.