• Transactions of the Korean Society of Automotive Engineers
• /
• v.14 no.5
• /
• pp.73-78
• /
• 2006

In this paper, creep tests of Mg-Zn-Mn and Mg-Zn-Mn-Ca alloys, which were casted by mold with Mg-3%Zn-1%Mn and Mg-3%Zn-1%Mn-0.2%Ca, were done under the temperature range of 473-573K and the stress range of 23.42-78.00Mpa. The activation energies and the stress exponents were measured to investigate the creep plastic deformation of those alloys, and the rupture lifes of Mg-Zn-Mn alloy were also measured to investigate the fracture behavior. From the results, the activation energy of Mg-Zn-Mn and Mg-Zn-Mn-Ca alloys under the temperature range of 473-493K were measured as 149.87, 145.98KJ/mol, respectively, and the stress exponent were measured as 5.13, 6.06 respectively. Also the activation energies Mg-Zn-Mn and Mg-Zn-Mn-Ca alloys under the temperature range of 553-573K were obtained as 134.41, 129.22KJ/mol, respectively, and tress exponent were obtained as 3.48, 4.63, respectively. Finally stress dependence of rupture life and the activation energy of rupture life of Mg-Zn-Mn under the temperature range of 473-493K was measured as 8.05, 170.0(KJ/mol), respectively, which were a little higher than the results of steady state creep.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.1
• /
• pp.12-17
• /
• 2005

Effects of Zn and Zr additions on the microstructure and mechanical properties of Al-5%Mg-1%Mn alloys were investigated. As Zn content increased in the Al-Mg-Mn-Zn alloys, the tensile strength and ductility of as-cast alloys rather decreased while the tensile strength of the heat-treated alloys significantly increased mainly due to the precipitation of fine $MgZn_2$ phases. Small amount of Zr was added to the 3%Zn alloy to further enhance the mechanical properties, and it appeared to increase the strength and ductility, especially in as-cast state.

• Korean Journal of Materials Research
• /
• v.26 no.11
• /
• pp.628-634
• /
• 2016

The cold rolling workability and mechanical properties of two new alloys, designed and cast Al-5.5Mg-2.9Si and Al-7Mg-0.9Zn alloys, were investigated in detail. The two alloy sheets of 4 mm thickness, 30 mm width and 100 mm length were reduced to a thickness of 1 mm by multi-pass rolling at ambient temperature. The rolling workability was better for the Al-7Mg-0.9Zn alloy than for the Al-5.5Mg-2.9Si alloy; in case of the former alloy, edge cracks began to occur at 50% rolling reduction, and their number and length increased with rolling reduction; however, in the latter alloy, the sheets did not have any cracks even at higher rolling reduction. The mechanical properties of tensile strength and elongation were also better in the Al-7Mg-0.9Zn alloy than in Al-5.5Mg-2.9Si alloy. Work hardening ability after cold rolling was also higher in the Al-7Mg-0.9Zn alloy than in the Al-5.5Mg-2.9Si alloy. At the same time, the texture development was very similar for both alloys; typical rolling texture developed in both alloys. These differences in the two alloys can primarily be explained by the existence of precipitates of $Mg_2Si$. It is concluded that the Al-7Mg-0.9Zn alloy is better than the Al-5.5Mg-2.9Si alloy in terms of mechanical properties.

• Journal of Powder Materials
• /
• v.12 no.4 s.51
• /
• pp.303-308
• /
• 2005

Various kinds of Mg-Zn-Ca base alloys were rapidly quenched via melt spinning process. The meltspun ternary and quaternary alloy ribbons were heat-treated, and then the effects of additional elements on age hardening behavior and phase change of precipitates were investigated using Vickers hardness tester, XRD, and TEM equipped with EDS system. In ternary alloys, age hardening was mostly due to the distribution of $Mg_6Ca_2Zn_3$ and $Mg_2Ca$. The stable phases of precipitates were varied according to the aging temperature and the alloy composition. With the increase of Ca content, $Mg_2Ca$ precipitates were detected more than $Mg_6Ca_2Zn_3$ precipitates. In quaternary alloys, the precipitates taken from Mg-Zn-Ca-Co were identified as new quaternary phase, whereas those taken from Mg-Zn-Ca-Zr as MgZnCa containing Zr. In general, the ternary alloy showed higher peak hardness and thermal stability than the quaternary considering the total amounts of the solutes. It implies that the structure of precipitate should be controlled to have the coherent interface with the Mg matrix.

• Journal of Korea Foundry Society
• /
• v.35 no.6
• /
• pp.155-162
• /
• 2015

The effect of Sr addition on mechanical and bio-corrosion properties of as-cast Mg-3wt.%Zn-0.5wt.%Ca-xwt.%Sr (x = 0.3, 0.6, 0.9) alloys were examined for application as biodegradable implant material. The microstructure, mechanical properties and corrosion resistance of the as-cast Mg-Zn-Ca-Sr alloys were characterized by using optical microscopy, scanning electron microscopy, tensile testing and electrochemical measurement in Hank's solution. The as-cast alloys contained ${\alpha}$-Mg and eutectic $Ca_2Mg_6Zn_3$ phases, while the alloys contained ${\alpha}$-Mg, $Ca_2Mg_6Zn_3$ and Mg-Zn-Ca-Sr intermetallic compound when the Sr addition was more than 0.3 wt.%. The yield strength, ultimate tensile strength and elongation increased with the increasing of Sr content up to 0.6 wt.% but decreased in the 0.9 wt.% Sr-added alloy, whereas the corrosion resistance of 0.3 wt.% Sr-added alloy was superior to other alloys. It was thought that profuse Mg-Zn-Ca-Sr intermetallic compound deteriorated both the mechanical properties and corrosion resistance of the as-cast alloy.

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.462-466
• /
• 1998

Interest in rapid solidification of magnesium alloys stems from the fact that conventional ingot metallurgy alloys exhibit poor strength, ductility, and corrosion resistance. Such properties can be improved by microstructural refinement via rapid solidification processing. Mg-5wt%Zn alloys have been produced as continuous strips by melt overflow technique and the strips were consolidated by hot extrusion. The yield stress, tensile strengh and ductility obtained in asextruded Mg-5wt%Zn alloy were ${\sigma}_{0.2}=152\;MPa$, ${\sigma}_{T.S{\cdot}}=263\;MPa$ and ${\varepsilon}=21.8%$. In order to evaluate the influence of additional elements on mechanical properties, Th and Zr were added in rapidly solidified Mg-5wt%Zn alloy. An 130% increase in yield stress of as-extruded Mg-5wt%Zn-3wt%Th-1wt%Zr alloy was attributed to grain refinement by rapid solidification and elemental addition.

• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.4
• /
• pp.223-229
• /
• 2023

This work was intended to investigate the effects of Zn content on microstructure and hardness of discontinuous precipitates (DPs) produced by continuous cooling (CC) in Mg-8%Al-X%Zn alloys with 0%, 0.5% and 1% of Zn contents (wt%). The DPs in the alloys possessed a wide range of (α+β) interlamellar spacings, which is attributed to the different transformation temperatures during CC. The higher Zn content resulted in the lower level of interlamellar spacings of the DPs, along with thinner and larger volume fraction of β phase layer in the DPs. It is noted that the DPs in the alloy with higher Zn content exhibited higher hardness, and that the ratio of increase in hardness of the DPs to that of the as-cast state was also increased with increasing Zn content. The reason was discussed on the basis of microstructural differences of the DPs in the Mg-8%Al-X%Zn alloys.

• Journal of Korea Foundry Society
• /
• v.18 no.3
• /
• pp.283-288
• /
• 1998

Interest in rapid solidification of magnesium alloys stems from the fact that conventional ingot metallurgy alloys exhibit poor strength, ductility, and corrosion resistance. Such properties can be improved by microstructural refinement via rapid solidification processing. In this study, Mg-Zn alloys have been produced as continuous strips by melt overflow technique. In order to evaluate the influence of additional elements on the grain refinement and mechanical properties, Th and Zr were added in rapidly solidified Mg-5wt%Zn alloy. Then the microstructual observations were undertaken with the objective of evaluating the grain refinement as function of the cooling rate and the additional elements. The tremendous increase in hardness of Mg-Zn base alloys was mainly due to the refinement of the grain structure by the effect of rapid solidification and alloying elements. The formation of intermetallic phases on the grain boundaries may have a positive effect on the corroion resistance. Therefore, despite competition from many other developments, the rapid solidification processing of magnesium alloys emerges as a valuable method to develop superior and commercially acceptable magnesium alloys.

• Journal of Korea Foundry Society
• /
• v.24 no.6
• /
• pp.340-346
• /
• 2004

The plan for obtaining a good combination of strength and castability appeared feasible and the following observations were made. 1. In Al-12Mg-6.6Zn-xSi alloys, more primary $Mg_2Si$ phase formed with reduced $Al_3Mg_2$ phase, as Si content is necessary for an effective solution heat treatment because the solidus temperature is very low silicon contents. 2. A high tensile strength could be obtained in the heat-treated Al-12Mg-5.5Zn-5Si alloy attributed in the heat-treated Al-12Mg-5.5Zn-5Si alloy attributes to fine $MgZn_2$ particles that precipitated uniformly in the matrix. 3. Al-12Mg-5.5Zn-Si alloys showed excellent casting capabilities such as hot cracking resistance and fluidity compared to the reference commercial alloys. 4. The wear resistance of Al-12Mg-5.5Zn-5Si alloy was superior to that of A7075 alloy, and even higher resistance is expected if the morphology and size of primary $Mg_2Si$ phase is carefully controlled.

• Journal of Korea Foundry Society
• /
• v.32 no.2
• /
• pp.86-90
• /
• 2012

Aluminium-silicon based casting alloys have received an attention for high electrical and thermal conductivity applications, however relatively low conductivity of Al-Si alloys often limits the application. Efforts have been made to develop new high conductivity aluminium casting alloys containing no or less silicon. In this study Al-Zn-Fe based alloys were selected as the new alloys, and the effect of Mg additions on their properties and casting characteristics were investigated. As the magnesium content was increased, the tensile strength of Al-2Zn-0.2Fe based alloy was remarkably increased, while the electrical conductivity was deteriorated. It was observed that the fluidity of the alloys was generally inversely proportional to the Mg content but the hot cracking resistance was rather proportional to it. Cooling curve analyses were carried out to measure the actual solidification range and dendrite coherency temperature.