• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.131-135
• /
• 1988

The microstructural changes in partially stabilized MgO-ZrO2 alloys during heat treatment and mechanical properties of ZrO2(Y2O3)/Al2O3 systems have been studied. 9mol% MgO-ZrO2 powders were sintered at 1800$^{\circ}C$ for 4 hours and these specimens were aged at 1420$^{\circ}C$ and 1100$^{\circ}C$ secondly. These specimens have high thermal shock resistance and high toughness. The bend strength of Y-PSZ/Al2O3 composites conventially sintered were increased by HIP from 650MPa to 980MPa.

• Journal of the Korean Ceramic Society
• /
• v.54 no.3
• /
• pp.222-227
• /
• 2017

Flake-type micro hollow silica was synthesized by precipitation method using an $Mg(OH)_2$ inorganic template and sodium silicate and ammonium sulfate as the silica precursors. We investigated the effects of the silica precursor concentration on the shape, shell thickness, and surface of the hollow silica. When the concentration of the silica precursor was 0.5 M, the hollow silica had a smooth and translucent thin shell, but the shell was broken. On the other hand, the shell thickness of the hollow silica changed in the range of 12 nm to 18 nm with the increase of the precursor concentration from 0.7 M to 1.1 M. Simultaneously, unintended spherical silica satellites were created on the shell surface. The number of satellites and the size rose according to the increased concentration of silica precursor. The reason for the formation of spherical silica satellites is that the $NH_4OH$ nucleus generated in the synthesis of hollow silica acted as another silica reaction site.

• Journal of the Korean Ceramic Society
• /
• v.56 no.3
• /
• pp.256-268
• /
• 2019

In this research, some mechanical properties of Al₂O₃-based composites containing nanoSiC and nanoMgO additives, including elasticity modulus, hardness, and fracture toughness, have been evaluated. Micron-sized Al₂O₃ powders containing 0.08 wt.% nanoMgO particles have been mixed with different volume fractions of nanoSiC particles (2.5 to 15 vol.%). Untreated samples have been sintered by using hot-press technique at temperatures of 1600 to 1750℃. The results show significant increases in the mechanical characteristics with increases in the sintering temperature and amount of nanoSiC particles, with the result that the elasticity modulus, hardness, and fracture toughness were obtained as 426 GPa, 21 GPa, and 4.5 MPa.m^1/2, respectively.

• Journal of the Korean Society for Precision Engineering
• /
• v.23 no.8 s.185
• /
• pp.100-107
• /
• 2006

The objective of this research is to investigate the electromagnetic interference(EMI) shielding characteristics of fiber reinforced composites. We fabricated glass and carbon fiber reinforced composites filled with metal powder and nano carbon black. The measurements of shielding effectiveness(SE) were carried out frequency range 300MHz - 1GHz for commercial purposes such as electric or telecommunication devices. The return loss and loss due to absorption were also measured as a function of frequency in the micro wave(300MHz-1GHz) region. It is observed that the SE of the composites is the frequency dependent, increase with the increases in filler loading. The Mg metal powder filled composite showed higher SE compared to that of carbon black. The Mg metal powder/epoxy composite was shown to exhibit up to 40dB of SE. The results indicates that the composite having higher filler loading can be used for the purpose of EMI shielding as well as for some microwave applications.

• Food Science and Biotechnology
• /
• v.17 no.4
• /
• pp.850-856
• /
• 2008

White, red, and extruded ginsengs were studied against 8 strains of food-borne pathogens and/or food spoilage microorganisms. The ginseng powders were extracted with different extractants and screened for antimicrobial activity using the disc diffusion and broth dilution techniques. The results showed that the yield of extraction was higher with increase of aqueous solution content and temperature. Preliminary screening revealed that the red ginseng extracts were most active, that has been found to be highly effective against all tested microbe except Listeria monocytogenes. Moreover, Bacillus subtilis has shown highly susceptible, which the diameters of inhibition zone values of 28 extracts were between 7 and 14 mm. The minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) recorded for the different crude ginseng extracts against microorganism using ranged from 6.25 to 100 mg/mL, indicated that the methanol extract of ginseng were more effective than ethanol and water extracts. The 60% methanol extract of red ginseng had the greatest effects against B. subtilis with MIC and MBC values at 6.25 mg/mL.

• Korean Journal of Food Science and Technology
• /
• v.38 no.4
• /
• pp.513-520
• /
• 2006

Spray-dried (SD) and freeze-dried (FD) takju powders were stored at 5, 15 and $25^{\circ}C$, and various quality characteristics such as moisture, amino nitrogen, color value, total viable cell count, total sugar, reducing sugar organic acid, and flavor compounds were measured for 50 days at 10-day intervals. After 50 days of storage, the moisture content was increased from an initial 6.64% to 7.24-7.38% in the SD powder, and from an initial 4.86 to 5.43-5.61% in the FD powder. pH, total acid content and total viable cell counts were slightly increased. Organic acid content was decreased in the SD powder from an initial 3,949.9 mg% to 805.9-922.3 mg%, and in the FD powder from an initial 5,171.5 mg% to 3,646.0-4,110.2 mg%. Amino nitrogen content was increased in the SD powder from an initial 1.2% to 1.9-2.2% and in the FD powder from an initial 1.9% to 2.2-2.5%. Total sugar and reducing sugar contents were increased in the SD powder from an initial 17.2% and 4.0% to 25.9-27.3% and 5.8-6.9%, and in the FD powder from an initial 19.1% and 5.2% to 29.2-30.2% and 8.3-8.8%, respectively. With increasing storage time, L and b values in the SD powder increased slowly, while L value in the FD powder tended to decrease and b value tended to increase. About 20 major volatile flavor components were identified in the SD and FD powders by GC-MS and all such component levels were decreased with increasing storage time.

• Journal of Radiation Protection and Research
• /
• v.26 no.1
• /
• pp.7-12
• /
• 2001

Sintered LiF:Mg,Cu,Na,Si thermoluminescence (TL) pellets were developed for application in radiation dosimetry. In the present study, the TL dosimetric properties of LiF:Mg,Cu,Na,Si TL pellets have been investigated for emission spectrum, dose response, energy response, and fading characteristics. LiF:Mg,Cu,Na,Si TL pellets were made by using a sintering process, that is, pressing and heat treatment from TL powders. Photon irradiations for the experiments were carried out using X-ray beams and a $^{137}Cs$ gamma source at the Korea Atomic Energy Research Institute (KAERI). The average energies and the dose were in the range of 20-662 keV and $10^{-6}-10^{-2}\;Gy$, respectively. The glow curves were measured with a manual type TLD reader(System 310, Teledyne) at a constant nitrogen flux and a linear heating rate. For a constant heating rate of $5^{\circ}C\;s^{-1}$, the main dosimetric peak of glow curve appeared at $234^{\circ}C$, the activation energy was 2.34 eV and frequency factor was $1.00{\times}10^{23}$. TL emission spectrum is appeared at the blue region centered at 410 nm. A linearity of photon dose response was maintained up to 100 Gy. The photon energy responses relative to $^{137}Cs$ response were within ${\pm}20%$ at overall photon energy region. The fading of TL sensitivity of the pellets stored at the room temperature was not found for one year.

• Journal of the Korean Ceramic Society
• /
• v.24 no.4
• /
• pp.329-334
• /
• 1987

Diffusion of SO4-- ion in hardened cement paste with slag and siliceous powders such as silica fume and white carbon was investigated. Ca(OH)2 from hardenend cement paste was dissolved by sea-water and then gypsum was formed from the reaction of Ca++ in hardenend cement paste and SO4-- ions in MgSO4 solution. A part of the gypsum by reaction with calcium aluminate hydrates formed ettringite. Amounts of SO4-- ions passed through hardened cement paste was less than that of Cl- ions(Dcl-) in hardened cement paste were 0.1∼0.6${\times}$10-11$\textrm{cm}^2$/sec and 1∼4${\times}$10-8$\textrm{cm}^2$/sec respectively.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.152-156
• /
• 2007

Tungsten carbide powder was synthesized by SHS (self-propagating high-temperature synthesis). Except $WO_{3}$, each concentration of raw material ($WO_{3},\;Mg,\;NaCl,\;Na_{2}CO_{3},\;C$) was investigated. Final product was characterized by XRD and SEM. X-ray data demonstrated that the $NaCl+Na_{2}CO_{3}$ combined mixture has superiority in the WC formation process. Single phase and submicrometer WC powder was synthesized at the temperature below $1600^{\circ}C$. The role of sodium salts in combustion process was discussed, and chemical mechanism of WC formation was proposed. WC powder prepared by salt-assisted combustion synthesis has a size $0.2{\sim}3\;{\mu}m$ and low agglomeration degree.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.95-95
• /
• 2003

최근, 대면적 평판표시소자 제작을 위한 전기발광 (EL; electroluminescence)소자용 소재로서 GaN 분말을 적용하고자 하는 연구가 진행되고 있다. 이와 같이 GaN 분말을 EL 소재로 사용하기 위해서는 원하는 파장의 빛을 발광할 수 있도록 특정의 불순물을 첨가하여야 할 필요가 있다. Mg이 첨가된 GaN 분말의 합성과 특성에 대한 연구가 있었으며, 희토류 원소가 첨가된 GaN 분말의 특성이 보고된바 있다. 본 논문에서는 GaOOH 분말을 출발물질로 채택하여 Zn가 첨가된 GaN 분말을 합성하고 광학적인 특성을 조사하였다. Zn가 첨가된 GaN 분말을 합성하기 위하여, 우선 CaOOH 분말 1g과 일정량의 ZnO 또는 Zn(NO$_3$)$_3$를 함께 섞어 유발에서 습식 혼합한 후 건조시켰다. Ga에 대한 Zn의 몰 비는 0.1부터 30 까지 변화시켰다. 반응온도는 900~110$0^{\circ}C$의 범위에서 변화시켰고, 반응시간은 1~4시간 범위에서 변화시켰으며, NH$_3$의 유량은 400 sccm으로 하였다. X선 회절분석장치를 사용하여 결정구조를 확인하였고, Zn의 첨가에 따른 광학적 특성은 10 K의 온도에서 광루미네센스(PL; photoluminescence)를 측정하여 평가하였다.