• 한국주조공학회지
• /
• 제27권5호
• /
• pp.198-202
• /
• 2007

In the present study, the high temperature mechanical properties and creep resistance of Mg-Zn-Y-Ca alloys has been investigated. The Mg-4Zn-0.8Y alloy consists of ${\alpha}$-Mg matrix and icosahedral quasicrystalline phase. Calcium addition into Mg-4n-0.8Y based alloy results in the formation of ${\tau}(Ca_{2}Mg_{6}Zn_{3})$ and $Mg_{2}Ca$ as the second solidification phases. Creep properties of the Mg-Zn-Y and Mg-Zn-Ca based alloys measured at applied stresses between 65 MPa and 85 MPa are significantly improved with adding calcium and yttrium, respectively. The improved creep resistance is due to the formation of thermally stable $Mg_{2}Ca$ phase.

• 한국동물학회지
• /
• 제10권2호
• /
• pp.1-8
• /
• 1967

토끼의 골격근 homogenate에서 23,000$\times$G, 60 분간의 원심분리와 얻은 근 microsome의 ATPase 활성, 근수축에 대한 이완작용, 및 Ca 의 흡수작용을 여러 가지 조건에서 측정하였다. ATPase 활성은 Ca++ Mg++ 양 이온의 존재에 의하여 활성화되며 , 5 mM Mg++ 의 존재하에서는 Ca++ 의 최적농도는 0.1mM이다. Oxalate의 존재하에서는 1 mM 의 Ca++ 이 최적농도이므로 oxalate의 작용은 불용성 Ca-oxalate의 작용은 불용성 Ca-oxalate를 microsome vesicle so 및 medium 내에 침전시켜 유리 Ca++ 농도를 저하시키는 것이라고 생각된다. Microsome의 이완작용은 조제후 120 시간까지 시간에 따라 감소되어 가나, 그이 ATPase 활성은 거의 변화가 없는 것으로 보아 Ca++ + Mg++ -의존성 ATPase 는 이완작용에는 직접 관련이 없는 것으로 해석된다. Oxalatedmlwhswo는 microsome의 Ca++ 흡수량을 현저히 증대시키며 동시에 흡수포화에 도달하는 시간을 지연시킨다. Oxalate의 이러한 효과도 Ca-oxalate의 형성에 기인하는 것으로 해석된다. Microsome 내에 축적되는 Ca 의 량은 ATP 농도가 커질수록 많아진다. 그러나 축적된 Ca 의 량과 ATP 농도사이에 화학정량론적 관계는 없는 것같다.

• 한국토양비료학회지
• /
• 제23권2호
• /
• pp.107-113
• /
• 1990

주요(主要) 석회물질(石灰物質)이 해성염토(海成鹽土)의 제염(除鹽)에 주는 효과(效果)를 밝히기 위(爲)하여 염토(鹽土)가 함유(含有)하는 Na + Mg와 당량(當量)의 Ca를 탄산(炭酸)칼슘, 수산화(水酸化)칼슘, 규산(珪酸)칼슘 또는 석고(石膏)로 시용(施用)하여 유리원통시험(圓筒試驗)을 실시(實施)하였다. 최상층(最上層) 1/10염토(鹽土)에 석회물질(石灰物質) 반량(半量)을 혼합(混合)하고 남은 반량(半量)을 표면(表面)에 덮은 후 (後) 증류수(蒸溜水)를 주가(注加)하면서 연속적(連續的)으로 3차에 걸쳐 여과수(濾過水)를 받아 세척(洗滌)한 층별토양(層別土壤)과 함께 분석(分析)하였는 바 그 결과(結果)는 아래와 같다. 1. $CaSO_4$는 투수(透水)와 제염(除鹽)(Na)을 용역(容易)하게 하였으나 Mg를 하층(下層)에 집적(集積)시켰다. 2. $Ca(OH)_2$, $CaCO_3$, $CaCO_3$는 표층(表層)에 Mg를 침전(沈澱)시키고, 하위층(下位層)에서 Mg를 세탈(洗脫)하였는데, 특(特)히 표층직하(表層直下)에서 더 세탈(洗脫)하였다. 이 세탈(洗脫)은 $Ca(OH)_2$처리(處理)에서 가장 현저(顯著)했고, $CaSiO_2$, $CaCO_3$의 순서(順序)로 약(弱)해졌다. 3. 치환성(置換性) Na의 해리(解離)에 더한 석회(石灰)의 알칼리성(性)은 토양(土壤)의 pH를 높였으며, 투수속도(透水速度)를 낮추고 Na의 제염(除鹽)을 저해(沮害)하였다. 이 영향(影響)은 $Ca(OH)_2$처리(處理)에서 더 컸다. 4. 세탈(洗脫)된 토양(土壤)의 pH는 치환성(置換性) Na 및 Mg와 다음 회부관계(回復關係)를 보였다. $$pH=7.77+0.489Na/\sqrt{Mg}\;r=0.845^{**}$$.

• 한국광물학회지
• /
• 제5권2호
• /
• pp.102-108
• /
• 1992

장군광산의 산화망간광석에서 자연산 (Ca, Mg)-부서라이트를 발견하였는바, 이는 퇴적 또는 변성기원이 능망간석의 표성 풍화에 의해 형성되었다. 부서라이트는 란시아이트와 함께 세립의 부서라이트-란시아이트 염편을 이룬다. 이 (Ca, Mg)-부서라이트-란시아이트는 엽상의 작은 결정으로 산출되나. 이는 세립의 다카넬라이트 집합체 주위에 침전되어 있다. 전자현미분석 결과, 장군 광산의 (Ca, Mg)-부서라이트는 ($Ca_{.08}Mg_{.07}Mn_{.05}6{2+})Mn_{.89}^{4+}O_2{\cdot}1.46H_2O$의 화학식을 갖는다. 상대습도의 조절 및 가열에 의한 탈수실험과 상대습도 조절에 의한 재수화 실험에의하면, (Ca, Mg)-부서라이트는 90${\circ}C$에서 완전히 탈수되며 27%만이 재수화된다. 상대습도 26%에서의 (40$^{\circ}C$로 가열한 경우와 일치하는) 탈수현상은 9.86${\AA}$ 회절선의 9.60${\AA}$으로의 감소 및 강도의 감소로 특징지워진다. 이는 층간의 매우 약하게 결합된 물분자의 방출에 기인한다. 40$^{\circ}C$에서 90$^{\circ}C$까지의 가열에 의한 탈수현상은 001 회절선이 9.60${\AA}$에서 7.42${\AA}$까지 점이적 이동으로 특징지워진다. 이는 층간에 약하게 결합되어 있는 물분자의 방출에 의한 것이다.

• 소성∙가공
• /
• 제26권5호
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• 한국콘텐츠학회논문지
• /
• 제2권1호
• /
• pp.120-124
• /
• 2002

본 연구에서는 주조법으로 제조한 Mg-Ca 합금의 전기 화학적 특성을 알아보고자 하였다. 연구결과에 의하면 전기화학적 특성이 불순물의 화학조성과 매우 밀접한 관계가 있으며, 칼슘 첨가 전ㆍ후 뚜렷한 미세구조 변화가 있음이 관찰되었다. 본 연구로부터 적은 양의 칼슘이 첨가되면 마그네슘 합금의 미세구조적 변화를 통하여 우수한 전기화학적 특성이 얻어질 수 있음이 확인되었다.

• 한국주조공학회지
• /
• 제27권3호
• /
• pp.131-134
• /
• 2007

[ $SF_6$ ] gas that is used as a protective cover gas for Mg and Mg alloys during melting and casting has extremely high greenhouse effect. CaO added Mg alloys could maintain their original mechanical properties and original abilities such as fluidity and hot tearing susceptibility. The ignition temperature increased with increasing CaO addition under ambient atmosphere and nitrogen atmosphere. The minimum amount of $SF_6$ gas decreased by 0.13 wt%CaO added AZ91D Mg alloy in the sealed condition.

• 한국재료학회지
• /
• 제6권11호
• /
• pp.1121-1126
• /
• 1996

(Pb0.63Ca0.37)ZrO3 세라믹에 MgO와 SrO를 첨가하여 Ca를 Mg와 Sr 이온으로 치환하였을 때의 고주파 유전특성에 대해 연구하였다. Ca 이온의 일부를 Mg 이온으로 치환시킨 경우에는 A-O결합에 의한 분극의 증가로 인하여 유전상수는 직선적으로 증가하지만 품질계수는 감소한다. 또한 Ca 이온을 Sr 이온으로 치환시킨 경우에는 결합길이의 증가로 인해 분극이 감소되어 유전상수와 품질계수가 감소한다. 고주파용 유전재료의 설계에 있어서 관용인자와 이온결합성의 평가가 중요하다.

• 한국주조공학회지
• /
• 제23권5호
• /
• pp.251-256
• /
• 2003

Effects of Ca addition on grain refinement, microstructure and mechanical properties of AZ31 Mg alloy were investigated. Due to Ca addition to Mg alloy (AZ31), the microstructure was refined, the quantity of $Mg_{17}Al_{12}$phase was reduced, and new $Al_2Ca$ phase was formed. The tensile property of AZ31 was increased with the minor addition of Ca, but was decreased rapidly over 0.2 wt.% of Ca content. The $Al_2Ca$ phase was considered to be detrimental to the mechanical property of AZ31 Mg alloy.

• 생물환경조절학회지
• /
• 제7권3호
• /
• pp.246-252
• /
• 1998

1995년 경남지역에서 양액재배 원수로 사용되고 있는 77개 농가의 지하수 중의 무기성분 농도를 분석한 결과는 다음과 같다. 지하수의 깊이는 10~500m, pH는 6.2~8.4, EC는 0.11~1.44dS/m이었다. 1 liter당 무기성분의 평균함량은 N $H_{4}$-N 0.3mg, N $O_{3}$-N 3.1mg, P $O_{4}$$^{3-}$ 0.5mg, $Ca^{2＋}$ 25.4mg, $Mg^{2＋}$ 11.5mg, $Na^{＋}$ 21.7mg, C $l^{-}$ 42.6mg, S $O_{4}$$^{2-}$ 72.5mg였다. 지하수의 pH와 $Mg^{2＋}$(0.34$^{**}$ ), $Ca^{2＋}$(0.33$^{**}$ ) 및 EC(0.29$^{**}$ ) 사이에 유의적인 정(＋)의 상관을 보였다. 또한 EC와 $Na^{＋}$(0.68$^{**}$ ), $Ca^{2＋}$(0.67$^{**}$ ), S $O_{4}$$^{2-}$(0.62$^{**}$ ), $Mg^{2＋}$(0.60$^{**}$ ), N $H_{4}$-N(0.36$^{**}$ ), C $l^{-}$(0.53$^{**}$ ) 및 $K^{＋}$(0.26$^{**}$ ) 간에도 유의적인 정(＋)의 상관을 보였다..