• Proceedings of the Membrane Society of Korea Conference
• /
• 2002.05a
• /
• pp.59-61
• /
• 2002

No Abstract, See Full-text

• Membrane Journal
• /
• v.14 no.2
• /
• pp.173-184
• /
• 2004

For the application of direct methanol fuel cell (DMFC), sulfonated polystyrene/teflon (PS/PTFE) composite membranes were developed by changing monomer ratio of styrene and DVB. The composite membranes were prepared as follows: first, the monomer mixtures consisting of styrene, divinyl benzene and AIBN were impregnated in porous PTFE film and then, polymerized under 8$0^{\circ}C$ to give PS/PTFE membranes. Finally, the membranes were reacted with chlorosulfonic acid in 1,2-dichloroethane to give the sulfonated composite membranes. The measurements of ATR-FTIR, SEM, solvent uptake test and ion exchange capacity (IEC) were done for the resulting membranes before or after sulfonation, respectively, which showed the composite membranes with proper crosslinking degree and sulfonic acid content were prepared well as a function of styrene/DVB ratio. ion conductivity and methanol permeability were studied for the sulfonated membranes. It was found that with decreasing the ratio of styrene/DVB, methanol permeability decreased from $6.6{\times}10^{-7}∼1.3{\timas}10^{-7}$ $\textrm{cm}^2$/s, which are much lower values than that of Nafion$^{(R)}$117($1.02{\times}10^{-6}$ $\textrm{cm}^2$/s). Under the same monomer condition, ion conductivity decreased from 0.11 S/cm ($25^{\circ}C$) to 0.08 S/cm ($25^{\circ}C$), which are similar or a little higher values compared with $Nafion^{(R)}117 (1.02{\times}10^{-6}$ $\textrm{cm}^2$/s, 0.0824 S/cm). These two results confirmed the composite membranes prepared could be applied successfully to DMFC.C.

• Membrane Journal
• /
• v.14 no.2
• /
• pp.117-125
• /
• 2004

Proton exchange membrane composed of PVA/PAM/ZrP was prepared and effect of PAM and ZrP contents on properties and performance of the membrane were investigated. PAM as a crosslinking agent was mixed into PVA solution with different concentration (7∼11 wt%) and the PVA/PAM solution was cast to prepare PVA/PAM crosslinked membrane. The membrane was treated in the solution of zirconyl chloride and phophoric acid to make a PVA/PAM/ZrP composite membrane. Methanol permeability, ion conductivity, swelling and ion exchange capacity of the membranes with different ZrP concentration were $10^{-8}∼l0^{-6}$ $\textrm{cm}^2$/sec, $10^{-3}~10^{-2}$ S/cm, 0.26∼1.17 g $H_2O$/g membrane and 2.59∼5.1 meq/g membrane, respectively. Hethanol permeability and ion conductivity of the PVA/PAM/ZrP membrane were improved by 18% and 23%, respectively, compared to those of the PVA/PAM membrane.

• Membrane Journal
• /
• v.18 no.4
• /
• pp.274-281
• /
• 2008

Covalent-crosslinked sulfonated poly(arylene ether sulfone) (SPAES) copolymers were synthesized copolymerization technique and additionally crosslinked with divinylbenzene (DVB). To optimize the reaction condition, a concentration of crosslinking agent and a reaction time were varied in the ranges of $30{\sim}90\;v/v%$ and $30{\sim}720\;min$. The properties of the crosslinked membranes were investigated by SEM, TGA and the measurement of proton conductivity. It was found that the proton conductivity of crosslinked membranes decreased depending on a degree of crosslinking while water uptake and methanol permeability reduced.

• Clean Technology
• /
• v.11 no.3
• /
• pp.141-146
• /
• 2005

The composite membranes were made by grafting using supercritical carbon dioxide (scCO2) impregnation and polymerization procedures. The membranes were synthesized by changing amount of monomer. The polypropylene grafted polystyrene sulfonic acid (PP-g-pssa) membranes were characterized with various methods. The morphology and structure of PP-g-pssa membranes were analyzed with scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). As amount of monomer was increased, ion conductivity, cell performance was increased and methanol permeability was decreased. However PP-g-pssa membranes with 1.5g monomer and over had similar values of methanol permeability, ion conductivity and cell performance.

• Membrane Journal
• /
• v.16 no.1
• /
• pp.9-15
• /
• 2006

PVA/SSA/HPA composite membranes were prepared by the addition of SSA as a crosslinking agent and HPA such as PWA or SiWA. The water uptake decreased and the IEC increased as the HPA contents increased in PVA/SSA/HPA composite membranes. XRD results showed that HPA distributed well into the composite membranes as the HPA concentration increased, and SiWA dispersed better than PWA in the composite membranes. TGA results showed that PVA/SSA composite membranes were more heat-resistant than PVA due to the crosslinking of PVA, and the heat stability of the composite membranes improved much more as the concentration of HPA increased. The methanol barrier property of PVA/SSA/HPA composite membranes was superior to Nafion, and the methanol permeability of the composite membranes decreased as the concentration of HPA increased.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.1
• /
• pp.433-440
• /
• 2016

Composite membranes were prepared by the solution casting method from sulfonated poly(etheretherketone)(sPEEK) and imidazole and phosphotungstic acid(PWA) to enhance the electrolytic properties of the membrane. TGA measurements showed that physical crosslinking due to acid-base interactions improved the thermal resistance to the desulfonation of sulfonic acid groups of the composite membrane and the addition of PWA enhanced the resistance to thermal decomposition of the composite membrane. The acid-base interaction decreased the water uptake, proton conductivity and methanol permeability of the sPEEK/imidazole composite membranes. The addition of PWA increased the proton conductivities while it decreased the water uptake and methanol permeability of sPEEK/imidazole/PWA composite membranes. Therefore, the selectivity of the composite membranes was enhanced by the addition of PWA.

• Membrane Journal
• /
• v.16 no.4
• /
• pp.286-293
• /
• 2006

Porous asymmetric membranes based on PVdF as a nascent membrane were prepared by using a phase inversion method. PVdF ion conductive composite membranes were finally made by introducing $SO_3{^-}$ from sulfuric acid after cross-linked PS with various DVB contents in the pores of PVdF. Final PVdF composite membranes were characterized by FTIR, SEM, EDS to verify $SO_3{^-}$. It was revealed that the solvent contents and ion exchange capacity (IEC) decreased with increase of the degree of cross-linking. As the degree of crosslink increases both the electric conductivity and methanol permeability decreased, which was showing the better values than Nafion 117. When DVB content was 8%, its electric conductivity ($5.58{\times}10^{-5}S/cm$) was similar to Nafion 117 ($6.03{\times}10^{-5}S/cm$). But the lower methanol permeability ($1.0{\times}10^{-6}cm^2/sec$) than that of Nafion 117 was obtained.

• Advances in materials Research
• /
• v.13 no.3
• /
• pp.243-251
• /
• 2024

The asymmetric polylactic acid (PLA) membrane was prepared via phase inversion method using non-solvent induced separation (NIPS) technique. This study aims to synthesized as well as to characterize the PLA membrane and evaluating the membrane performance on water flux and permeability. In addition, this research also studied the removal performance of methylene blue dye. The polymer solution has been prepared using 12 wt.% of PLA and dissolved in 88 wt.% of Dimethylacetamide (DMAc) as a solvent. Then, the cast film was immersed in different ratio of coagulant bath medium (distilled water: methanol: ethanol) ranging from 100:0:0, 75:25:0, 75:0:25 and 75:12.5:12.5, respectively). Several characterizations were performed which include, membrane contact angle and membrane porosity. Performance PLA membranes were determined in terms of water flux and permeability at 1 bar transmembrane pressure using dead-end permeation cell. Finally, methylene blue (MB) removal efficiency was tested at the same transmembrane pressure. The findings revealed that the increase of alcohol concentration in coagulant bath resulted in higher porosity and lower contact angle. In short, MB dye rejection efficiency is also closely related to the amount of alcohol ratio used in coagulant baths. Increases in concentration of methanol and ethanol in coagulant bath medium increases the membrane porosity thus increased in efficiency of methylene blue rejection.

• Membrane Journal
• /
• v.15 no.4
• /
• pp.272-280
• /
• 2005

In this study, asymmetric polysulfone membranes were prepared by the phase inversion method and the casting solutions were containing N-methyl-2-pyrrolidone (NMP) as a solvent. Deionized water and various alcohols(methanol, ethanol, and propanol) were used as a coagulation medium in preparing asymmetric polysulfone membranes. This study investigates the effect of alcohol coagulants having different solubility parameters as a pore-former on the construction of porous structures and their pure water permeation properties. Asymmetric polysulfone membranes immersed in the pure alcohol coagulation bath solution showed the typical sponge-like structures and the reduced water permeability as compared with those of polysulfone membranes precipitated in the pure water coagulation bath solution. In the water/alcohol mixtures, asymmetric polysulfone membranes showed the finger-like structures with the sponge-like structures. Therefore, the sponge-like structure of polysulfone membrane was formed under the delayed demixing systems while the porosity of membrane was decreased significantly. The water permeability of polysulfone membrane precipitated in the pure water coagulant showed 164 [$L/m^2hr$] at 14.7 psi. In case of polysulfone membranes prepared in the pure methanol and ethanol coagulant, they showed the water permeability of 56 and 30 [$L/m^2hr$], respectively.