• 대한금속재료학회지
• /
• 제49권8호
• /
• pp.657-663
• /
• 2011

This study represents the results of the peel strength and surface morphology according to the preprocessing times of polyimide (PI) in a Cu/Ni/PI structure flexible copper clad laminate production process based on the polyimide. Field emission scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy were used to analyze the surface morphology, crystal structure, and interface binding structure of sputtered Ni, Cu, and electrodeposited copper foil layers. The surface roughness of Ni, Cu deposition layers and the crystal structure of electrodeposited Cu layers were varied according to the preprocessing times. In the RF plasma times that were varied by 100-600 seconds in a preprocessing process, the preprocessing applied by about 300-400 seconds showed a homogeneous surface morphology in the metal layers and that also represented high peel strength for the polyimide. Considering the effect of peel strength on plastic deformation, preprocessing times can reasonably be at about 400 seconds.

• Corrosion Science and Technology
• /
• 제20권5호
• /
• pp.308-314
• /
• 2021

Neutron dose level at bottom head of a reactor pressure vessel (RPV) was calculated using reactor vessel neutron transport for a Korean nuclear power plant A. At 34 EFPY with a 40-year (2042) design life after plating repair, irradiation fast neutron effect was 6.6x10¹⁵ n/cm². As helium(He) gas can be generated by Ni only at 1/10⁶ level of 5 × 10²¹ n/cm², He generation possibility in the Ni plating layer is very little during 40 years of operation (2042, 34 EFPY). Thermal neutrons can significantly affect the generation of He from Ni metal. At 10 years after a repair, He can be generated at a level of about 0.06 appm, a level that can add general welding repair without any consideration. After 40 years of repair, 9.8 appm of He may be generated. Although this is a rather high value, it is within the range of 0.1 to 10 appm when welding repair can be applied. Clad repair by Ni electroplating technology is expected to greatly improve the operation efficiency by improving the safety and shortening the maintenance period of the nuclear power plant.

• 대한전자공학회논문지SD
• /
• 제47권4호
• /
• pp.69-74
• /
• 2010

알루미늄 양극산화(aluminum anodization)의 선택적인 적용을 통하여 DRAM 소자를 위한 새로운 패키지 기판을 제작하였다. 에폭시 계열의 코어(core)와 구리의 적층 형태로 제작되는 일반적인 패키지 기판과는 달리 제안된 패키지 기판은 아래층 알루미늄(aluminum), 중간층 알루미나(alumina, $Al_2O_3$) 그리고 위층 구리(copper)로 구성된다. 알루미늄 기판에 양극산화 공정을 수행함으로써 두꺼운 알루미나를 얻을 수 있으며 이를 패키지 기판의 유전체로 사용할 수 있다. 알루미나층 위에 구리 패턴을 배치함으로써 새로운 2층 금속 구조의 패키지 기판을 완성하게 된다. 또한 알루미늄 양극산화를 선택적인 영역에만 적용하여 내부가 완전히 채워져 있는 비아(via) 구조를 구현할 수 있다. 패키지 설계 시에 비아 인 패드(via in pad) 구조를 적용하여 본딩 패드(bonding pad) 및 볼 패드(ball pad) 상에 비아를 배치하였다. 상기 비아 인 패드 배치 및 2층 금속 구조로 인해 패키지 기판의 배선 설계가 보다 수월해지고 설계 자유도가 향상된다. 새로운 패키지 기판의 주요 설계인자를 분석하고 최적화하기 위하여 테스트 패턴의 2차원 전자기장 시뮬레이션 및 S-파라미터 측정을 진행하였다. 이러한 설계인자를 바탕으로 모든 신호 배선은 우수한 신호 전송을 얻기 위해서 $50{\Omega}$의 특성 임피던스를 가지는 coplanar waveguide(CPW) 및 microstrip 기반의 전송선 구조로 설계되었다. 본 논문에서는 패키지 기판 구조, 설계 방식, 제작 공정 및 측정 등을 포함하여 양극산화 알루미늄 패키지 기판의 특성과 성능을 분석하였다.