• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.1
• /
• pp.143-179
• /
• 1989

To observe the bonding behavior of palladium-based alloys to porcelain; 1. Pd-Co binary alloy with the higher cobalt content, 2. Pd-Co binary alloy with the lower cobalt content, 3. Pd-Ag-Sn ternary alloy, 4. Pd-Ag binary alloy, 5. Pd-Cu-Au ternary alloy and 6. Pd-Cu binary alloy were made as 6 groups of experimental alloys. Each group of alloy was divided into 4 sub-groups such as one sub-group that was not degassed and three sub-groups that degassed for 5 minutes, 10 minutes and 15 minutes. On each specimen, weight changes after degassing, morphological changes of oxide layer by changing the degassing time, compositional changes at metal-ceramic interface and bond strength of metal-ceramic measured with planar shear test were observed and compared. The results of the present study allow the following conclusions to be drawn: 1. The alloy showing the greatest bond strength was Pd-Cu alloy without gold and bond strength was decreased by alloying gold to them. 2. Although Pd-Co alloy showed the most prominent oxidation behavior, bond strength of them to porcelain was not greatly high by the formation of porosities at metal-ceramic interfaces. 3. Likewise tin, cobalt formed the peaks on line profiles at metal-ceramic interface, however copper did not exhibit such peaks on line profiles. 4. Mainly, oxide layer on Pd-Co alloy was composed with cobalt, and for Pd-Co alloy with higher cobalt content the rise of bond strength was not significant by increased degassing time. 5. On Pd-Ag alloy not containing tin, during degassing for 15 minutes silver content was increased at metal-ceramic interface. 6. As an oxidized element, tin formed the oxide layers that widen their area by increasing the degassing time, while cobalt and copper showed the morphological changes of particle or crystal on oxide layer.

• The Journal of the Korea Contents Association
• /
• v.21 no.3
• /
• pp.602-608
• /
• 2021

For the comparison of bond strength between the Co-Cr alloy and ceramic, which are clinically used, test samples made with a traditional casting method as a control group), and Milling and SLM(3d printing group) samples were made as an experimental group. The metal-ceramic bond strength was measured with a universal testing machine. For the measurement, a three-point bending test was conducted. After the bond strength was measured, metal-ceramic interface was observed. According to the test result, casting group had 53.59 MPa, milling group had 45.90 MPa, and 3d printing group had 58.34 MPa. There was no statistical significance. With regard to failure pattern, most of the samples in two groups, showed mixed failure. This study showed a clinically applicable value when measuring the bond strength of alloy-ceramic material with an alloy produced by 3D printing.

• Journal of Technologic Dentistry
• /
• v.35 no.2
• /
• pp.89-95
• /
• 2013

Purpose: The purpose of this study was to evaluate bond strength of Metal Disk alloy and casting alloy. Methods: Metal specimens were divided into 4 groups for each alloy. Three point flexural test were used to measure the bond strength of CAD/CAM metal alloy and casting alloy. Statistical analysis was done using the Statistical Package for Social Sciences version 19.0 for Windows. As for the analysis methods, the study used Kruskal-Wallis test. Results: The average bonding strengths of Group 1 to porcelain was $36.7{\pm}9.90$ MPa, Group 2 to porcelain was $37.68{\pm}4.51$ MPa, Group 3 to porcelain was $36.43{\pm}6.57$ MPa, Group 4 to porcelain was $42.88{\pm}6.81$ MPa, Each group was not significantly different. Conclusion: Bond strength of Casting alloy is equal to or higher than bond strength of CAD/CAM Metal Disk alloy. Alloy clinical bond strength is 25 MPa, So CAD/CAM Metal Disk alloy can be used as dental material.

• Journal of Technologic Dentistry
• /
• v.38 no.2
• /
• pp.69-77
• /
• 2016

Purpose: This study was to evaluate the shear bond strength of ceramic fused to Ni-Cr alloy(Alophaloy) by heat treatment. Methods: The specimens were divided into 5 groups according to heat treatment conditions prior to porcelain application. Eighteen specimens from each group were subjected to the shear load a universal testing machine using a 0.1mm/min cross-head speed and two specimens from each group were observed with SEM and EDX line profile. Results: The observation of the oxide film on the metal surface by SEM photograph showed a coarsening with an increasing degassing hold time. The diffusion of metal oxide was observed farther from the opaque layer in the heat treated specimen than no heat treated specimen. The shear bond strength measured highest to A5(55.23MPa) in the 10min holding group and measured lowest from A1(24.38MPa) in the no heat treated group, and there was a significant difference(p<0.05). Conclusion: The shear bond strength of Ni-Cr alloy improved in the heat treatment compared to the no heat treatment specimen.

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.5
• /
• pp.620-639
• /
• 1999

Indirect composite resins are used as an popular effective esthetic material in prosthetic dentistry, often with metallic substructure that provides support for restorations. Recently, new indirect composite resins as a substitute of ceramic have been developed. These resins provide good esthetics, with a wide range of hue and chroma. And the flexural strength of those is in the range of 120-150MPa, Which is higher than that of feldspathic Ceramic, and similar th that of Dicor. Although it has many merits, one of the major clinical problems of composite resins is the bond failure between metal and resin due to insufficient interfacial bond strength. The purpose of this study was to evaluate shear bond strength of the reinforced indirect composite resin to dental alloys. Three different composite resin systems($Artglass^{(R)},\;Sculpture^{(R)},\;Targis^{(R)}$) as test groups and ceramic($VMK\;68^{(R)}$) as control group were bonded to Ni-Cr-Be alloy($Rexillium\;III^{(R)}$) and gold alloy(Deva 4). All specimens were stored at $^37{\circ}C$ distilled water for 24 hours and the half of specimens were thermocycled 2000 times at temperature from $5^{\circ}C\;to\;60^{\circ}C$. The shear bond strengths of reinforced indirect composite resins to dental alloys were measured by using the universal testing machine, and modes of debonding were observed by stereoscope and scanning electron microscope. The results were as follows: 1 The shear bond strengths of reinforced indirect composite resins to dental alloys were approximately half those of ceramic to dental alloys(P<0.01). 2. There was no significant difference between the shear bond strength of several reinforced indirect composite resins to metal. 3. Alloy type did not affect on the shear bond strengths of resin to metal, but the shear bond strengths of ceramic to gold alloys were higher than those of ceramic to Ni-Cr alloys(P<0.05). 4. The shear bond strengths of Artglass and Targil to gold alloys were significantly decreased after thermocycling treatment(P<0.01). 5. Sculpture showed cohesive, adhesive, and mixed failure modes, but Artglass and Targis showed adhesive or mixed failures. And ceramic showed cohesive and mixed failures.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.7
• /
• pp.4329-4335
• /
• 2014

This study examined the effects of the shear bond strength when the surface condition of the metal and zirconia, each being the lower structures, was different when determining the bond strength (metal group) of the metal lower structure with upper ceramics, and the shear bond strength (zirconia group) of zirconia lower structure with the upper ceramics in prosthetic appliances of metal-ceramic crown and zirconia-ceramic crowns. The metal groups were divided into a total of four groups: the group with no condition on the metal surface(NM), the group with sand-blasting(SM), the group with applied opaque ceramics(OM), and the group with applied opaque ceramics and sand-blasting(SOM). The zirconia groups were also separated into four groups: the group with no condition(NZ), the group with sand-blasting(SZ), the group treated with ZirLiner on the zirconia surface(LZ), and the group applied with ZirLiner along and sand-blasting(SLZ). To examine the effects on the shear bond strength according to the surface condition of each of the four metal and zirconia groups, SPSS was used to conduct one-way ANOVA. For metal-ceramic crowns, it would be best to apply opaque ceramics after sand-blasting on the surface of the metal, the lower structure. For zirconia-ceramic crowns, it is recommended to apply the ZirLiner after sand-blasting on the surface of zirconia, the lower structure.

• The Journal of Advanced Prosthodontics
• /
• v.1 no.3
• /
• pp.129-135
• /
• 2009

STATEMENT OF PROBLEM. Zirconia-based restorations have the common technical complication of delamination, or porcelain chipping, from the zirconia core. Thus the shear bond strength between the zirconia core and the veneering porcelain requires investigation in order to facilitate the material's clinical use. PURPOSE. The purpose of this study was to evaluate the bonding strength of the porcelain veneer to the zirconia core and to other various metal alloys (high noble metal alloy and base metal alloy). MATERIAL AND METHODS. 15 rectangular ($4\times4\times9mm$) specimens each of zirconia (Cercon), base metal alloy (Tillite), high noble metal alloy (Degudent H) were fabricated for the shear bond strength test. The veneering porcelain recommended by the manufacturer for each type of material was fired to the core in thickness of 3mm. After firing, the specimens were embedded in the PTFE mold, placed on a mounting jig, and subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.5mm/min until fracture. The average shear strength (MPa) was analyzed with the oneway ANOVA and the Tukey's test ($\alpha$= .05). The fractured specimens were examined using SEM and EDX to determine the failure pattern. RESULTS. The mean shear strength ($\pm\;SD$) in MPa was 25.43 ($\pm\;3.12$) in the zirconia group, 35.87 ($\pm\;4.23$) in the base metal group, 38.00 ($\pm\;5.23$) in the high noble metal group. The ANOVA showed a significant difference among groups, and the Tukey' s test presented a significant difference between the zirconia group and the metal group. Microscopic examination showed that the failure primarily occurred near the interface with the residual veneering porcelain remaining on the core. CONCLUSION. There was a significant difference between the metal ceramic and zirconia ceramic group in shear bond strength. There was no significant difference between the base metal alloy and the high noble metal alloy.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.2
• /
• pp.117-127
• /
• 1991

The purpose of this study was to evaluate the effect of surface treatment of fractured metal-ceramic crown on bond strength of porcelain repair resin. The specimens were divided into two groups for metal specimens add five groups for porcelain specimens by surface treatment methods. the metal specimens were treated by 2 methods. : micro-sandblasting with $50{\mu}m$ aluminum oxide and grinding with diamond bur. The porcelain specimens were treated by 5 methods : micro-sandblasting with $50{\mu}m$ aluminum oxide, grinding with diamond bur, etching with porcelain etching agent, combination of micro-sandblasting and etching procedure, and combination of grinding and etching procedure. After surface treatment, each specimen was bonded with composite resin and the bond strength was measured and the surface texture was observed by scanning electromicroscope(SEM). The results were as follows : 1. There was significant difference in shear bond strength between metal specimen and prorcelain specimen. 2. Bood strength of metal specimens treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting. 3. Bond strength of porcelain specimen treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting and porcelain etching agent. 4. There was no significant difference in shear bond strength between the group treated with diamond bur and combined treatment groups respectively. 5. The large undercuts were observed in group treated with diamond bur by SEM.

• Journal of Technologic Dentistry
• /
• v.33 no.4
• /
• pp.299-306
• /
• 2011

Purpose: This study aimed to investigate the shear bond strength by manufacturing the veneering porcelain on the IPS e.max $ZirCAD^{(R)}$ zirconia core, using the layering technique and heat-pressing technique, and to evaluate the clinical stability by comparing to the conventional metal ceramic system. Methods: The Schmitz-Schulmeyer test method was used to evaluate the core-veneer shear bond strength of zirconia core ceramic(IPS e.max $ZirCAD^{(R)}$) and their manufacture recommended two veneering ceramic systems(IPS e.max $ceram^{(R)}$, IPS e. max $ZirPress^{(R)}$). A metal ceramic system(Bellabond $plus^{(R)}$, VITA $VM13^{(R)}$) was used as a control group for the two all ceramic system test groups. The maximum loading and shear bond strength was measured. The average shear strength(MPa) was analyzed with the one-way ANOVA and the Tukey's test(${\alpha}$=.05). The fracture specimens were examined using Microscope to determine the failure pattern. Results: The mean shear bond strengths(SD) in MPa were MBSB control 43.62(2.13); ZBSB 18.65(1.76); ZPSB 18.89(1.54). The shear strengths of the zirconia cores were not significantly different(P>.05). Microscope examination showed that zirconia specimens presented mixed failure, and base metal alloy specimens showed adhesive failure. Conclusion: There was no siginificant different between the layering technique and the heat pressing technique in the veneering methods on the zirconia cores. None of the zirconia core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.

• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.1
• /
• pp.31-47
• /
• 1989

The purpose of this study was to evaluate the chemical bond strength of successively recast Pd-Ag ceramic alloys with porcelain and to investigate changes of quantity of trace elements at the metal-porcelain interface. Porcelain was fired as usual manner on the each successively recast specimen. Rectangular planar shear test was performed and bond strength was measured by Instron universal testing machine. Diffusion of trace elements at the each interface was observed by ESCA (Electron Spectroscopy for Chemical Analysis). The obtained results were as follows : 1. Chemical bond strength was significantly decreased after second recasting. But in case of first recasting, there was no significant decrease of bond strength statistically (p<0.05). 2. Bond strength was not significantly decreased in each generation, when fifty percents new alloy was added (p<0.05). 3. Ag, Sn and In were observed at the porcelain interface. But Pd was not observed. 4. The quantity of Ag, In ions were progressively increased at the metal-porcelain interface as the casting was repeated. Silver ion was most significantly increased.