• Journal of Technologic Dentistry
• /
• v.31 no.2
• /
• pp.45-52
• /
• 2009

Esthetic restorations have been widely used in dental practice, although many studies have focused on the development and improvement of all ceramic restorations. The success of esthetic restorations depends primarily on an optimal bond strength between various veneered ceramics and core materials for esthetic restorations. The purpose of this study was to compare the shear bond strength between various veneered ceramics and core materials for esthetic restorations. 30 metal cores and 20 zirconia cores were fabricated and divided into five groups according to veneered ceramic materials such as Creation porcelain powder, Cercon Ceram Kiss, and IPS e.max ZirPress. Thirty spacimens were prepared using Creation porcelain powder, veneered 3mm height and 3mm in diameter, over the metal cores (n=10). Twenty specimens were prepared using Cercon Ceram Kiss and Zirpress, veneered 3mm height and 3mm in diameter, over the zirconia cores (n=10). The shear bond strength test was performed in a universal testing machine with a crosshead speed of 1mm/min. Ultimate shear bond strength data were analyzed with One-way ANOVA and the Scheffe's test (p=.05). Within the limits of this study, the following conclusions were drawn: The mean shear bond strengths (MPa) were: 18.44 for Uni metal VH/Creation (NCUC); 18.72 for Heraenium/Creation (NCHC); 16.23 for Wirobond C/Creation (NCWC); 13.88 for Zirconia core/$110{\mu}m$ $Al_2O_3$ sandblasting/Cercon Ceram Kiss (ZS110P); 14.61 for Zirconia core/No surface treatment/IPS e.max ZirPress (ZNTH). The mean shear bond strength for NCUC (Uni metal VH/Creation), NCHC (Heraenium/Creation) and NCWC (Wirobond C/Creation) were significantly superior to ZS110P (Zirconia core/$110{\mu}m$ $Al_2O_3$ sandblasting/Cercon Ceram Kiss) and ZNTH(Zirconia core/No surface treatment/IPS e.max ZirPress) (p<0.05).

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.6
• /
• pp.732-746
• /
• 2003

Statement of problem. Soft lining materials, also referred to as tissue conditioning materials, tissue heating materials, relining materials, soft liners or tissue conditioners, were first introduced to dentistry by a plastic manufacturer in 1959. Since the introduction of the materials to the dental field, their material properties have been continually improved through the effort of many researchers. Soft lining materials have become widely accepted, particularly by prosthodontists, because of their numerous clinical advantages and ease of manipulation. Unfortunately, few reports have been issued upon the topic of increasing the bond strength between the base metal alloy used in cast denture bases and PMMA soft liner modified with 4-META, nor upon the pattern of debonding and material change in wet environment like a intra oral situation. Purpose. The purposes of this study were comparing the bond strength between base metal alloy used for the cast denture bases and PMMA soft liner modified with 4-META, and describing the pattern of debonding and material property change in wet environment like the intraoral situation. Material and Methods. This study consisted of four experiments: 1. The in vitro measurement of shear bond strength of the adhesive soft liner. 2. The in vitro measurement of shear bond strength of the adhesive soft liner after 2 weeks of aging. 3. A comparison of debonding patterns. 4. An evaluation the Relation time of modified soft liner. The soft liner used in this study was commercially available as Coe-soft (GC America.IL.,USA), which is provided in forms of powder and liquid. This is a PMMA soft liner commonly used in dental clinics. The metal primer used in this study was 4-META containing primer packed in Meta fast denture base resin (Sun Medical Co., Osaka, Japan). The specimens were formed in a single lap joint desist which is useful for evaluating the apparent shear bond strength of adhesively bonded metal plate by tensile loading. Using the $20{\times}20mm$ transparent grid, percent area of adhesive soft liner remaining on the shear area was calculated to classify the debonding patterns. To evaluate the change of the initial flow of the modified adhesive soft liner, the gelation time was measured with an oscillating rheometer (Haake RS150W/ TC50, Haake Co., Germany). It was a stress control and parallel plate type with the diameter of 35mm. Conclusion. Within the conditions and limitations of this study, the following conclusions were drawn as follows. 1. There was significant increase of bond strength in the 5% 4-META, 10% 4-META containing groups and in the primer coated groups versus the control group(P<0.05). 2. After 2 weeks of aging, no significant increase in bond strength was found except for the group containing 10% 4-META (P<0.05). 3. The gelation times of the modified soft liner were 9.3 minutes for the 5% 4-META containing liner and 11.5 minutes for the 10% 4-META liner. 4. The debonding patterns of the 4-META containing group after 2 weeks of aging were similar to those of immediaely after preparation, but the debonding pattern of the primer group showed more adhesive failure after 2 weeks of aging.

• Journal of Technologic Dentistry
• /
• v.33 no.4
• /
• pp.299-306
• /
• 2011

Purpose: This study aimed to investigate the shear bond strength by manufacturing the veneering porcelain on the IPS e.max $ZirCAD^{(R)}$ zirconia core, using the layering technique and heat-pressing technique, and to evaluate the clinical stability by comparing to the conventional metal ceramic system. Methods: The Schmitz-Schulmeyer test method was used to evaluate the core-veneer shear bond strength of zirconia core ceramic(IPS e.max $ZirCAD^{(R)}$) and their manufacture recommended two veneering ceramic systems(IPS e.max $ceram^{(R)}$, IPS e. max $ZirPress^{(R)}$). A metal ceramic system(Bellabond $plus^{(R)}$, VITA $VM13^{(R)}$) was used as a control group for the two all ceramic system test groups. The maximum loading and shear bond strength was measured. The average shear strength(MPa) was analyzed with the one-way ANOVA and the Tukey's test(${\alpha}$=.05). The fracture specimens were examined using Microscope to determine the failure pattern. Results: The mean shear bond strengths(SD) in MPa were MBSB control 43.62(2.13); ZBSB 18.65(1.76); ZPSB 18.89(1.54). The shear strengths of the zirconia cores were not significantly different(P>.05). Microscope examination showed that zirconia specimens presented mixed failure, and base metal alloy specimens showed adhesive failure. Conclusion: There was no siginificant different between the layering technique and the heat pressing technique in the veneering methods on the zirconia cores. None of the zirconia core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.

• Journal of Technologic Dentistry
• /
• v.33 no.1
• /
• pp.37-45
• /
• 2011

Purpose: Heat pressed ceramics, used for all ceramic restorations, have the additional advantage of being technically less change through using of the lost-wax technique. Conceptually, combining the ceramic with the clinically proven reinforcing ability of a metal framework would be advantageous; however, cause of mismatching of fusion between ceramics and metal frameworks which from differences of casting temperature and coefficient of thermal expansion, pressed ceramics could not be used with a metal framework. The purpose of this study was to compare shear bond strength of press-to metal ceramic to porcelain fused non precious metal and feldspatic porcelain fused non precious metal. Methods: The 30 metal specimens were casted in a porcelain fused non precious metal nickel-chromium alloy. They were divided into 3 groups by surface treatment and applied ceramic: $125{\mu}m$ aluminium oxide sandblasting and veneered feldspatic porcelain (group FP), $125{\mu}m$ aluminium oxide sandblasting and had press-to-metal ceramic applied (group PC), porcelain bonder (gold bonder) fused on surface of metal specimens and had press-to-metal ceramic applied (group PCG). In each group 10 metal specimens were used. The press-to-metal ceramic applied 20 specimens had ash-free wax pattern applied, the metal-wax complexes invested, and were pressed with heat press ceramic. All specimens were subjected to shear bond strength test at a crosshead speed of 1.0 mm/min. Results: The results of measured in Mean SD and data were analyzed by one-way AVOVA (p= .05) and Tukey HSD test (p= .05).: group FP $16.090{\pm}1.841$ MPa, group PC $12.620{\pm}1.8256$ MPa, group PCG $10.920{\pm}0.9283$, significant differences between all groups (p < .05). Significant differences were found in each between group FP and group PC, group FP and group PCG (p < .05). Conclusion: The shear bond strength of press-to-metal ceramic to porcelain fused non precious metal was described higher in unused gold bonder group than used gold bonder groups.

• The korean journal of orthodontics
• /
• v.22 no.2 s.37
• /
• pp.289-296
• /
• 1992

The purpose of this study was to evaluate and compare the shear bond strengths and failure sites of metal brackets bonded with chemically cured adhesive and light-cured adhesive. 10 brackets were bonded on prepared enamel surfaces with $Transbond^{circledR}$ (Unitek/3M; U.S.A.) light-cured orthodontic adhesive and another 10 brackets were bonded with $Ortho-one^{\circledR}$ (Bisco:U.S.A.) chemically cured orthodontic adhesive. 24 hours after bonding, the Instron universal testing machine was used to measure the shear bond strengths. The failure sites were examined under streoscopic microscope. The results were as follows: 1 . The mean shear bond strength of metal brackets bonded with light-cured adhesive was lower than that of metal brackets bonded with chemically cured adhesive, but the difference was not statistically significant (p < 0.05). 2. Regardless of the type of adhesives, the brackets were failed primarily at the bracket base-adhesive interface. 3. Bonding of metal brackets with light-cured adhesive is considered to be clinically acceptable.

• The Journal of Korean Academy of Prosthodontics
• /
• v.55 no.3
• /
• pp.264-271
• /
• 2017

Purpose: The purpose of this study is to investigate the differences in bond strength of four different indirect composites to the gold alloy and Ni-Cr alloy according to type of metal surface treatment after water storage. Materials and methods: Type IV gold alloy and Ni-Cr alloy were used for casting alloy while four types of indirect composite resins (Gradia, Tescera Sinfony and in;joy) were used in this study. Metal specimens were produced by casting and total of 240 specimens (60 specimens per one indirect composite group) were prepared. After bonding indirect composite resin and undergoing 24 hours of polymerization, customized jig was attached to the metal specimen and shear bond strength were measured using universal testing machine. Also, differences in shear bond strength before and after water storage for 240 hours were also measured. Results: In the measurement of shear bond strength according to the metal surface treatments, bead group showed high strength followed by loop and flatting group (P<.05). After being stored in water bath for 240 hours, Gradia showed statistically significant high bond strength compared to other indirect composite resins in all groups (P<.05). Conclusion: Shearbond strength was found to be different according to type of metal surface treatment and type of metal used after storage in water. Further studies need to be developed for clinical practices as three are still problems of microleakage, stain or wear.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.5
• /
• pp.343-348
• /
• 2015

PURPOSE. The purpose of this study was to evaluate the bond strength of composite resin on the fracture surface of metal-ceramic depending on the repair systems and surface roughening methods. MATERIALS AND METHODS. A total of 30 disk specimens were fabricated, 15 of each were made from feldspathic porcelain and nickel-chromium base metal alloy. Each substrate was divided into three groups according to the repair method: a) application of repair system I (Intraoral Repair Kit) with diamond bur roughening (Group DP and DM), b) application of repair system I with airborne-particle abrasion (Group SP and SM), and c) application of repair system II (CoJet Intraoral Repair System, Group CP and CM). All specimens were thermocycled, and the shear bond strength was measured. The data were analyzed using the Kruskal-Wallis analysis and the Mann-Whitney test with a significance level of 0.05. RESULTS. For the porcelain specimens, group SP showed the highest shear bond strength ($25.85{\pm}3.51MPa$) and group DP and CP were not significantly different. In metal specimens, group CM showed superior values of bond strength ($13.81{\pm}3.45MPa$) compared to groups DM or SM. CONCLUSION. Airborne-particle abrasion and application of repair system I can be recommended in the case of a fracture localized to the porcelain. If the fracture extends to metal surface, the repair system II is worthy of consideration.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.2
• /
• pp.117-127
• /
• 1991

The purpose of this study was to evaluate the effect of surface treatment of fractured metal-ceramic crown on bond strength of porcelain repair resin. The specimens were divided into two groups for metal specimens add five groups for porcelain specimens by surface treatment methods. the metal specimens were treated by 2 methods. : micro-sandblasting with $50{\mu}m$ aluminum oxide and grinding with diamond bur. The porcelain specimens were treated by 5 methods : micro-sandblasting with $50{\mu}m$ aluminum oxide, grinding with diamond bur, etching with porcelain etching agent, combination of micro-sandblasting and etching procedure, and combination of grinding and etching procedure. After surface treatment, each specimen was bonded with composite resin and the bond strength was measured and the surface texture was observed by scanning electromicroscope(SEM). The results were as follows : 1. There was significant difference in shear bond strength between metal specimen and prorcelain specimen. 2. Bood strength of metal specimens treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting. 3. Bond strength of porcelain specimen treated with diamond bur was higher than that treated with $50{\mu}m$ aluminum oxide sandblasting and porcelain etching agent. 4. There was no significant difference in shear bond strength between the group treated with diamond bur and combined treatment groups respectively. 5. The large undercuts were observed in group treated with diamond bur by SEM.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.12
• /
• pp.434-439
• /
• 2020

Selective laser melting (SLM) manufactures an alloy using laser as a heat source, and has recently been introduced in the dental industry. However, there is a lack of analytical research on metal-ceramic restorations achieved by SLM. This study evaluates and compares the metal-ceramic bond strength of Co-Cr alloys produced by selective laser melting and casting methods. Co-Cr samples required for this study were produced through the sintering process of ceramics, by applying the SLM and CAST methods. The metal-ceramic bond strength was measured by applying the shear bond strength test. In order to determine the area fraction of adherent ceramic, Si content of the specimen was measured using scanning electron microscopy SEM/ EDS. Results of the metal-ceramic bond strength and AFAC were analyzed by t-test (α = 0.05). No significant difference was observed comparing the bond strength of SLM and CAST Co-Cr alloys (P> 0.05). However, the SLM group had much better ceramic adherence than the CAST group (P < 0.001). Moreover, oxidation characteristics were similar for both SLM and CAST Co-Cr alloys, but metal structures were different. These results imply that although the bond of ceramic and Co-Cr alloy is not related to the manufacturing method, SLM alloys impart better ceramic adherence. This indicates that alloys made with SLM can be used to fabricate upper implant prostheses in the future. In particular, it is expected to overcome the shortcomings of the CAST method, and save time and cost.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.2
• /
• pp.110-117
• /
• 2017

PURPOSE. This laboratory study assessed the effect of different dentin cleaning procedures on shear bond strength of resin cements for recementing prosthesis. MATERIALS AND METHODS. A $4{\times}4$ flat surface was prepared on the labial surface of 52 maxillary central incisors. Metal frames ($4{\times}4{\times}1.5mm$) were cast with nickel-chromium alloy. All specimens were randomly divided into 2 groups to be cemented with either Panavia F2.0 (P) or RelyX Ultimate (U) cement. The initial shear bond strength was recorded by Universal Testing Machine at a crosshead speed of 0.5 mm/min. Debonded specimens were randomly allocated into 2 subgroups (n = 13) according to the dentin cleaning procedures for recementation. The residual cement on bonded dentin surfaces was eliminated with either pumice slurry (p) or tungsten carbide bur (c). The restorations were rebonded with the same cement and were subjected to shear test. Data failed the normality test (P < .05), thus were analyzed with Mann Whitney U-test, Wilcoxon signed rank test, and two-way ANOVA after logarithmic transformation (${\alpha}=.05$). RESULTS. The initial shear bond strength of group P was significantly higher than group U (P = .001). Pc and Uc groups presented higher bond strength after recementation compared to the initial bond strength. However, it was significant only in Pc group (P = .034). CONCLUSION. The specimens recemented with Panavia F2.0 provided higher bond strength than RelyX Ultimate cement. Moreover, a tungsten carbide bur was a more efficient method in removing the residual resin cement and increased the bond strength of Panavia F2.0 cement after recementation.