• Korean Journal of Materials Research
• /
• v.28 no.3
• /
• pp.159-165
• /
• 2018

In order to increase the efficiency of the sputtering method widely used in thin film fabrication, a dc sputtering apparatus which supplies both high frequency and magnetic field from the outside was fabricated, and cobalt thin film was fabricated using this apparatus. The apparatus can independently control the applied voltage, the target-substrate distance, and the target current, which are important parameters in the sputtering method, so that a stable glow discharge is obtained even at a low gas pressure of $10^{-3}$ Torr. The fabrication conditions using the sputtering method were mainly performed in $Ar+O_2$ mixed gas containing about 0.6 % oxygen gas under various Ar gas pressures of 1 to 30 mTorr. The microstructure of Co thin films deposited using this apparatus was examined by electron diffraction pattern and X-ray techniques. The magnetic properties were investigated by measuring the magnetization curves. The microstructure and magnetic properties of Co thin films depend on the discharge gas pressure. The thin film fabricated at high gas pressure showed a columnar structure containing a large amount of the third phase in the boundary region and the thin film formed at low gas pressure showed little or no columnar structure. The coercivity in the plane was slightly larger than that in the latter case.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.81-84
• /
• 2004

The NiCr is an important material for present thin-film resistor application owing to its low TCR and thermal stability. In this work, the NiCr thin films were deposited on coming glass substrate by reactive magnetron sputtering and the annealing at temperatures range from 300 to $500^{\circ}C$ for 20 min in vacuum. X-ray, AFM, $R_s$(surface leakage current) have been used to study the structural and electrical properties of the NiCr thin films. The high precision NiCr thin films resistor with TCR(temperature coefficient of resistance) of less then $10\;ppm/^{\circ}C$ was obtained under in in-situ annealing at $300^{\circ}C$ on Cr buffer layer substrate. It is clear that the NiCr thin-films resistor electrical properties are low TCR related with it's annealing and buffer layer condition. NiCr thin film resistor having a good thermal stability and low TCR properties are expected for the application to the dielectric material of passive component.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.29-29
• /
• 2008

Platinum Thin films were deposited on $Al_2O_3$ by Rf magnetic Sputtering. The physical and electrical characteristics of these films were analyzed under various deposition conditions(Ar gas pressure, input power, substrate temperature.) and annealing condition. The deposition rate was increased with increasing the input power but not increased linear. In the other factor, The Pt thin films property was associated with resistance. so lower resistance had more and more good Pt thin films condition. For the purpose of this study, we will get the best Pt thin film characteristics.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.387-387
• /
• 2013

Currently, the flash memory and the dynamic random access memory (DRAM) have been used in a variety of applications. However, the downsizing of devices and the increasing density of recording medias are now in progress. So there are many demands for development of new semiconductor memory for next generation. Magnetic random access memory (MRAM) is one of the prospective semiconductor memories with excellent features including non-volatility, fast access time, unlimited read/write endurance, low operating voltage, and high storage density. MRAM is composed of magnetic tunnel junction (MTJ) stack and complementary metal-oxide semiconductor (CMOS). The MTJ stack consists of various magnetic materials, metals, and a tunneling barrier layer. Recently, MgO thin films have attracted a great attention as the prominent candidates for a tunneling barrier layer in the MTJ stack instead of the conventional Al2O3 films, because it has low Gibbs energy, low dielectric constant and high tunneling magnetoresistance value. For the successful etching of high density MRAM, the etching characteristics of MgO thin films as a tunneling barrier layer should be developed. In this study, the etch characteristics of MgO thin films have been investigated in various gas mixes using an inductively coupled plasma reactive ion etching (ICPRIE). The Cl2/Ar, CH3OH/Ar, and CH4/Ar gas mix were employed to find an optimized etching gas for MgO thin film etching. TiN thin films were employed as a hard mask to increase the etch selectivity. The etch rates were obtained using surface profilometer and etch profiles were observed by using the field emission scanning electron microscopy (FESEM).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.6
• /
• pp.486-492
• /
• 1998

The amorphous Co-based magnetic films have a large saturation flux density, a low coercive force, and a zero magnetostriction constant. Therefore, they have been studied for application to magnetic recoding heads and micro magnetic devices. However, it was found that the magnetic anisotropy was changed for each film fabrication processes. In this study, we investigated how to control the anisotropy of sputtered amorphous $Co_{89}Nb{8.5}Zr{2.5}$ films. After deposition, the rotational field annealing ant the uniaxial field annealing were performed under the magnetic field of 1.5 kOe. the annealing was done at the temperature range from 400 to $600^{\circ}C$ for one hour. As-deposited amorphous $Co_{89}Nb{8.5}Zr{2.5}$ thin film had saturation magnetization ($4\piM_5$) of 0.8 T, coercive force($_IH_C$) of 1.5 Oe, and anisotropy field($H_k$) of 11 Oe. The amorphous $Co_{89}Nb{8.5}Zr{2.5}$ thin films annealed by rotational field annealing at $500^{\circ}C$ for one hour was found to be isotropy, and $4\piM_5$ of 0.9 T was obtained from these films, Also, the magnetic anisotropy of as-deposited films could be controlled by uniaxial field annealing at $400^{\circ}C$ for one hour. Anisotropy field($H_k$) of 17 Oe and $4\piM_5$ of 1.0 T were obtained by this method.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.255-259
• /
• 2011

The thickness dependence of magnetic properties was experimentally investigated in nanocrystalline Fe-Hf-N thin films fabricated by a RF magnetron sputtering method. In order to investigate the thickness effect on their magnetic properties, the films are prepared with different thickness ranges from 90 nm to 330 nm. It was revealed that the coercivity of the thin film increased with film thickness. On the contrary, the saturation magnetization decreased with film thickness. On the basis of the SEM and TEM, an amorphous phase forms during initial growth stage and it changes to crystalline structure after heat treatment at $550^{\circ}C$. Nanocrystalline Fe-Hf-N particles are also generated.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.2
• /
• pp.11-14
• /
• 2004

YBCO thin films have good characteristics for current limiting materials due to compact size and high current carrying capability. But the irregularities and the extreme thin thickness of YBCO films cause some difficulties in simultaneous quench and thermal shock protection. In order to solve these problems, vertical magnetic field generated from solenoid coil was applied to the YBCO element. And also to minimize the inductance caused by the serial connection of magnetic field source with superconducting elements, magnetic field source was separated from the power lines adapting protective current transformer. In this study, electric field-current (E-I) and quench characteristics of YBCO films were analyzed both by electrical measuring method and observations of bubble propagation. From the experiment results, it was revealed that the magnetic fields generated by surrounding coil could induce the uniform quench distribution for all stripes of current limiting units and finally simultaneous quenches were realized in all serial connection of YBCO elements. In addition, the separation of magnetic field source form electrical network could be good solution for simultaneous quench of YBCO films without any unnecessary effect caused by serial connection.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.06a
• /
• pp.194-194
• /
• 2003

As a result of the recent miniaturization an enhancement in the performance of thin film inductors and thin film transformers, there are increased demands for the thin films with high magnetic permeability in the high frequency range, high saturation magnetization, in high electrical resistivity, and low coercive force. In order to improve high frequency properties, we will investigate anisotropy field by shape and size of pattern. The Fe-Al-O thin films of 16mm and 1 $\mu\textrm{m}$ thickness were deposited on Si wafer, using RF magnetron reactive sputtering technique with the mixture of argon and oxygen gases. The fabricating conditions are obtained in the working partial pressure of 2mTorr, O$_2$ partial pressure of 5%, input power of 400W, and Al pellets on an Fe disk with purity of 99,9%. Magnetic properties of the continuous films as followed: the 4$\pi$M$\_$s/ of 19.4kG, H$\_$c/ of 0.6Oe, H$\_$k/ of 6.0Oe and effective permeability of 2500 up to 100㎒ were obtained. In this work, we expect to enhance effect of magnetic anisotropy on patterned of Fe-Al-O thin films.

• Journal of the Korean Ceramic Society
• /
• v.45 no.9
• /
• pp.556-560
• /
• 2008

The effects of Nb and Co ion substitution on the dielectric and magnetic properties of the multiferroic $BiFeO_3$ thin films have been investigated. Heteroepitaxial $BiFeO_3$ thin films were deposited by Pulsed Laser Deposition method. Nb substitution decreased the leakage current by 6 orders of magnitude and Co substituted $BiFeO_3$ thin films showed an enhanced magnetization, 2 times larger than that of un-substituted $BiFeO_3$. Through the co-substitution of Co and Nb, $BiFeO_3$ thin films with a low leakage current and an enhanced magnetization could be obtained.

• Journal of the Korean Magnetics Society
• /
• v.11 no.4
• /
• pp.168-172
• /
• 2001

Co-Zn ferrite thin films grown on thermally oxidized silicon wafers were fabricated by a sol-gel method. Magnetic and structural properties of Co-Zn thin films were investigated by using x-ray diffractometer (XRD), atomic force microscopy (AFM), auger electron spectroscopy (AES) and a vibrating sample magnetometer (VSM). Co-Zn ferrite thin films annealed at 400 $^{\circ}C$ presented have only a single phase spinel structure without any preferred crystallite orientation. Their surface roughness of Co-Zn ferrite thin films was shown as less than 3 nm and the grain size was about 40 nm for annealing temperatures over 600 $^{\circ}C$. A moderate saturation magnetization of Co-Zn ferrite thin films for recording media was obtained in this study and there is no significant difference of their magnetic property with those external fields of parallel and perpendicular to planes of the films. The maximum value of the coercivity was obtained as 1,900 Oe for Co-Zn ferrite thin film annealed at 600 $^{\circ}C$.