• Proceedings of the Korean Magnestics Society Conference
• /
• 2004.06a
• /
• pp.116-117
• /
• 2004

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1288-1289
• /
• 2006

Innovative SMC with low iron loss was made from iron powders with evaporated MgO insulation coating. The coating had greater heat-resistance than conventional phosphatic insulation coating, which enabled stress relieving annealing at higher temperature. Magnetic properties of toroidal samples (OD35mm,ID25mm, t5) were examined. The iron loss at 50Hz for Bm = 1.5T was lower 50% of conventional SMC and was almost the same with silicon iron laminations(t0.35). It became clear that MgO insulation coating has enough heat resistance and adhesiveness to powdersurface to obtain innovative SMC with low iron loss.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1191-1192
• /
• 2006

Eventhough Fe-6.5 wt.% Si alloy shows excellent magnetic properties, magnetic components made of the alloy are not totally because of its extremely low ductility. In order to overcome this demerit of alloy, 6.7 wt.% Si alloy powders were produced by gas atomization and then post-processed to form magnetic cores. By doing so, the total core loss could be minimized by reducing both hysteresis and eddy current loss. From our experiments, we were able to achive a core loss of $390mW/cm^3$ at 0.1 T and 50 kHz through proper processes and a permeability $\mu_{eff}$ of 68 at low frequency.

• Journal of the Speleological Society of Korea
• /
• no.78
• /
• pp.9-15
• /
• 2007

The materials showing high structure dispersion with functional properties were developed on the quartz base and those were obtained by mechano-chemical reaction technology. Depending on the processing conditions and subsequent applications the materials produced by mechano-chemical reaction show concurrently magnetic, dielectric and electrical properties. The obtained magnetic-electrical powders classified by aggregate complex of their features as segnetomagnetics, containing a dielectric material as a carrying nucleus, particularly the quartz on that surface one or more layers of different compounds were synthesized having thickness up to 1050nm showing magnetic, electrical properties and others. The similarity of the structure of surface layers of quartz particles subjected to mechano-chemical processing and nano-structure cluspol (clusters in a polymer matrics) material was alsoconfirmed by the fact that the characteristics of ferromagnetic quartz of insulating nano-composite powder were changed with time, after its preparing process was completed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.264-267
• /
• 2005

Soft magnetic iron powders have been coated with polyester or phenol resin. And the coated powder (soft magnetic composite) have been pressed into ring type core over the pressure of 870 MPa. Green density, magnetic flux density, permeability, core loss of the samples were measured to look at the effect of the coating materials and the amount of them. Green density is increased with the amount of coating materials and shows the maximum value, 6.5 $g/cm^3$ at 5 w/o, but decreased over it. And lowest value of the core loss is showed for the 5 w/o coated samples.

• Journal of Welding and Joining
• /
• v.20 no.1
• /
• pp.76-82
• /
• 2002

In these days, many advanced nations have enforced import restrictions against things emitting electromagnetic wave which has report that it is so harmful. In general, electromagnetic wave is composed of electric wave and magnetic wave. The reflection of electromagnetic wave is mainly reflected by conductive materials and the magnetism loss is generated by magnetic ferrite. The magnetism loss of ferrite is separated by eddy current loss, residual magnetism loss and hysteresis loss. Thermal sprayed coating is intended to manufacture because of simple processes and high efficient electromagnetic wave shielding. The high efficient thermal sprayed coatings were made from the magnetic ferrite materials that characterizes absorption of electromagnetic wave, and the electric conductive materials that characterize emitting of electromagnetic wave. This study was manufactured thermal sprayed coatings to improve absorption-efficiency, and measured the electromagnetic wave shielding efficiency. As the experimental results, high electromagnetic wave shield efficiency was obtained at wave frequency 2GHz to thermal sprayed ferrite coatings manufactured by size distribution range of spray powders, $38~88\mu\textrm{m}$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.218-218
• /
• 2012

Recently, hexagonal manganites have attracted much attention because of the coexistence of ferroelectricity and antiferromagnetic (AFM) order. The crystal structure of hexagonal manganites consists of $MnO_5$ polyhedra in which $Mn^{3+}$ ion is surrounded by three oxygen atoms in plane and two apical oxygen ions. The Mn ions within Mn-O plane form a triangular lattice and couple the spins through the AFM superexchange interaction. Due to incomplete AFM coupling between neighboring Mn ions in the triangular lattice, the system forms a geometrically-frustrated magnetic state. Among hexagonal manganites, $YMnO_3$, in particular, is the best known experimentally since the f states are empty. In addition, for applications, $YMnO_3$ thin films have been known as promising candidates for non-volatile ferroelectric random access memories. However, $YMnO_3$ has low magnetic order temperature (~70 K) and A-type AFM structure, which hinders its applications. We have synthesized $YMn1_{-x}Cr_xO_3$ (x = 0, 0.05 and 0.1) samples by the conventional solid-state reaction. The powders of stoichiometric proportions were mixed, and calcined at $900^{\circ}C$ for $YMn1_{-x}Cr_xO_3$ for 24 h. The obtained powders were ground, and pressed into 5-mm-thick disks of 1/2-inch diameter. The disks were directly put into the oven, and heated up to $1,300^{\circ}C$ and sintered in air for 24 h. The phase of samples was checked at room temperature by powder x-ray diffraction using a Rigaku Miniflex diffractometer with Cu $K{\alpha}$ radiation. All the magnetization measurements were carried out with a superconducting quantum-interference-device magnetometer. Our experiments point out that the Cr-doped samples show the characteristics of a spin-glass state at low temperatures.

• Korean Journal of Materials Research
• /
• v.15 no.8
• /
• pp.508-513
• /
• 2005

[ $TiO_2-Fe_2O_3$ ] nanocomposite powders for magnetic photocatalyst were synthesized by sol-gel process, in which $TiO_2$ photocatalytic layer was formed on the surface of $\gamma-Fe_2O_3$ magnetic core. Transmission electron microscopy (TEM) observation and X-ray diffractometry (XRD) analysis revealed that$\gamma-Fe_2O_3$ nanoparticles, $10\~20nm$ in diameter, were coated by $TiO_2$ shell of 5nm in thickness and $TiO_2$ was anatase phase. Also hydroxyl group (-OH) used to decompose organic compounds was detected by Fourier transformation infrared spectrometry(FT-IR) analysis. UV-Visible spectrophotometry results showed that light absorption occurred in the wavelength range of $400\~700 nm$, and the band gap energy $(E_g)$ of powder was 1.8 eV. Finally it was found that the coercivity $(H({ci})$ and saturation magnetization $(M_s)$ of the powder were 79 Oe and 14.8 emu/g, respectively as experimental vibrating sample magnetometer (VSM) measurements.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.12a
• /
• pp.285-285
• /
• 2003

• Proceedings of the Korean Magnestics Society Conference
• /
• 2003.12a
• /
• pp.365-365
• /
• 2003