• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1930-1932
• /
• 2005

Colloidal Silica(CS)/methyltrimethoxy silane(MTMS) and CS/MTMS/epoxy silane(Es) sol solutions were prepared in variation with synthesizing parameters such as kinds of CS, kinds of silane and reaction time. In order to understand its physical and chemical properties, sol-gel coating films on glass were fabricated. In the case of CS/MTMS sol, the coating films had high contact angle and more enhanced flat surface than those in the case of CS/MTMS/ES sol. Also, the coating films obtained from single CS had a better flat surface than those obtained from mixed CS. In the case of thermal stability, thermal dissociation of CS/MTMS and CS/MTMS/ES sol-gel coating films did not occur up to $550^{\circ}C$ and $440^{\circ}C$ respectively. The thickness of coating films obtained from CS/MTMS sol increased than those of CS/MTMS/ES sol. In addition, the coating films obtained from single CS were more thicker than those obtained from mixed CS.

• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.822-826
• /
• 2005

Colloidal Silica (CS)/methyltrimethoxysilane (MTMS) and CS/MTMS/epoxysilane (ES) sol solutions were prepared using various synthesizing parameters such as reaction time and types of CS and silane. In order to understand their physical and chemical properties, sol-gel coating films on glass were fabricated. In the case of the CS/MTMS sol, the coating films had high contact angle and more enhanced flat surface than the CS/MTMS/ES sol. In the case of thermal stability, thermal degradation of the CS/MTMS and CS/MTMS/ES coating films did not occur up to $550^{\circ}C$ and $440^{\circ}C$, respectively. The coating films prepared from the CS/MTMS sol were thicker than those of the CS/MTMS/ES sol. In addition, the coating films prepared from single CS were thicker than those of mixed CS. Hardness of the coating films prepared from CS/MTMS increased by adding ES. In case of the mixed CS, the hardness decreased by adding ES.

• Applied Chemistry for Engineering
• /
• v.9 no.5
• /
• pp.634-638
• /
• 1998

Monodisperse, spherical $PMSQ/TiO_2$ composite fine powders were prepared by modified sol-gel process where 300 nm $TiO_2$ fine powders were used as seed particles for hetero-condensation with hydrolyzed MTMS (Methyltrimethoxysilane). The reaction was carried out under $N_2$ atmosphere at ambient temperature using $NH_3$ as a catalyst. Methanol was used as a solvent. Powder was obtained by the filtration of the solution with a glass filter and washing with acetone. The stirring rate, reaction temperature, $[H_2O]/[MTMS]$ and $[MTMS]/[TiO_2]$ ratio were varied to investigate shapes and sizes of particles. Monodisperse particles of $1-2{\mu}m$ diameter were obtained with [MTMS]=0.2 M, $[NH_3]=0.6M$, $[H_2O]/[MTMS]=100$, $[MTMS]/[TiO_2]=10-50$ at ambient temperature with mild stirring condition. These composite particles had a contact angle of almost 180 degree contact angle with water, which proves their excellent hydrophobicity. The study of UV absorption spectra showed that they have UV protecting effect.

• Korean Chemical Engineering Research
• /
• v.56 no.3
• /
• pp.327-334
• /
• 2018

Water-repellent coating solutions were prepared by sol-gel method using tetraethoxysilane (TEOS) and methyltrimethoxysilane (MTMS) as precursors. The solutions were spin-coated on a cold-rolled steel sheet and thermally cured to prepare a non-fluorine water-repellent coating films. The effects of molar ratios of MTMS/TEOS, water concentration and ammonia concentration on the hydrophobic properties of the coating films were studied. The contact angle of water on coating films prepared by varying the molar ratio of MTMS/TEOS to 1~20 showed a maximum value of $108^{\circ}$ when the MTMS/TEOS molar ratio was 10. With increasing water content, the coating films showed the larger contact angles and the better the water repellency. As the amount of ammonia added was increased, the contact angles of coating films were increased, showing the better the water repellency. It is considered that the larger the amount of ammonia added, the larger the size of the silica particles generated, which increases the surface roughness of the silica particles, thereby increasing the water repellency.

• Polymer(Korea)
• /
• v.29 no.3
• /
• pp.242-247
• /
• 2005

Two kinds of colloidal silica(CS)/silane sol solutions were prepared in variation with synthesizing parameters such as kinds of CS, ratio of CS to silane and reaction time. Such sol solutions were obtained from 1034A Cs/methyl-trimethoxysilane(MTMS) and HSA CS/MTMS solutions. In the case of 1034A CS/MTMS CS/silane sol, coating film had high contact angle and more enhanced flat surface than those in the case of HSA CS/MTMS sol. In the case of thermal stability, thermal dissociation of 1034A CS/MTMS sol did not occur up to $550^{circ}$. The thickness of coating film obtained from 1034A CS/MTMS sol increased with increasing the amount of MTMS. The hardness of coating films obtained from 1034A CS/MTMS sol decreased with increasing the amount of MTMS. Surface free energy of CS/silane sol-gel coating film decreased with increasing amount of MTMS.

• Applied Chemistry for Engineering
• /
• v.30 no.3
• /
• pp.358-364
• /
• 2019

To improve the optical characteristics and antifouling of anti-reflective coating (AR) films, various AR coating films were prepared by varying the mixing ratio of tetraethylorthosilicate (TEOS)/base and methyltrimethoxysilane (MTMS)/acid hybrid solution. Prepared AR coating films were characterized by UV-Vis spectroscopy, contact angle analyzer, atomic force microscope (AFM), FT-IR and pencil scratch hardness test. In an AR coating film that prepared from the hybrid solution with a 10 wt% MTMS/acid solution, the glass substrate showed an excellent optical property (97.2% transmittance), good antifouling ($121^{\circ}$ water contact angle and $90^{\circ}\;CH_2I_2$ contact angle) and moderate mechanical strength (pencil hardness of 4 H). In particular, it is considered that the good antifouling was due to the well dispersion of the methyl group ($-CH_3$), derived from a small amount of MTMS/acid solution in the hybrid solution, on the substrate surface. From results of the pencil hardness test, the mechanical strength of AR coating film was improved as the content of MTMS/acid solution increased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.05b
• /
• pp.150-153
• /
• 2004

CS HSA, 1034A와 TMOS, MTMS 실란 간의 졸겔 반응조건이 코팅도막의 특성에 미치는 영향을 조사하기 위하여 CS 종류, CS 대비 TMOS/MTMS의 함량비, 반응시간 등을 달리하여 졸을 합성하고, 합성된 졸을 slide glass에 코팅한 후 $300^{\circ}C$에서 경화시킨 도막의 특성들을 조사하였다. CS 대비 MTMS의 함량 증가와 더불어 접촉각이 증가할 것으로 예상되지만 CS의 종류, 실란함량, 반응시간 등에 따라 증가하는 모양은 상당히 차이가 있었고 HSA CS계 보다는 1034A CS계로 제작된 도막에서 MTMS 함량과 접촉각과의 상관성이 다소 우수하였다. 표면거칠기는 HSA CS계인 경우에 반응시간과 MTMS 함량에 따라 민감하게 변했지만 1034A CS계에서는 HSA계의 졸에 비해 표면 거칠기가 향상되어 반응시간과 MTMS 함량의 조건에 영향을 받지 않고 표면조도와 균질성이 우수하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.82-85
• /
• 2004

Colloidal Silica(CS) HSA/2327과 methyltrimethoxysilane(MTMS), 1034A와 tetramethoxysilane(TMOS)/MTMS 간의 졸겔 반응조건이 코팅도막의 특성에 미치는 영향을 조사하기 위하여 CS종류, CS 대비 TMOS/MTMS의 함량비, 반응시간 등을 달리하여 졸을 합성하고, 합성된 졸을 slide glass에 코팅한 후 $300^{\circ}C$에서 경화시킨 도막의 특성들을 조사하였다. HSA/2327/MTMS에 의한 졸로부터 제조된 코팅도막은 졸 반응시간 의존성이 거의 없으며 반응초기부터 접촉각이 상당히 안정되어 있고 특히 낮은 MTMS 함량을 가진 졸들이 더욱 안정된 표면물성을 보였다. 1034A/TMOS/MTMS에 의해서 제조된 코팅도막은 적절한 소수성의 형성과 표면조도의 향상과 더불어 안정된 접촉각 양상을 나타내었다. 표면거칠기는 HSA/2327 혼합 CS계에 의해서는 반응시간이 길고 MTMS 함량이 높아질 때 비교적 표면조도가 나빠지는데 반응시간과 더불어 약간씩 증가하는 경향을 보였다. 1034A CS계에서는 반응시간과 MTMS 함량의 조건에 영향을 받지 않고 표면조도와 균질성이 우수하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.404-405
• /
• 2008

In this work, we investigated the effect of the functionalized SWNT-polymer composites for increasing sensitivity and imparting selectivity to nanotube sensors. To do this, CNT -based gas sensors were fabricated with two types of dispersed SWNT solution involving different polymer resin of TEOS (Tetraethyl orthosilicate) or MTMS (Methyl trimethoxysilane) which is blended to adhere to substrate well. As the surfaces of TEOS and MTMS surrounding SWNTs remain functionalized to -OH and $-CH_3$ groups respectively after hardening, gas adsorption will be affected differently according to the type of gases. In the experiment, we examined the response of electrical conductance for alcohol vapour gas. As the result, the conductance in the sensors using TEOS decreased considerably while that of MTMS was nearly invariable.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05b
• /
• pp.33-36
• /
• 2005

Colloidal Silica(CS)/silane sol solutions were prepared in variation with synthesizing parameters such as ratio of CS to silane and reaction time. In the case of LHSA CS/tetramethoxysilane(TMOS)/methyltrimethoxysilane(MTMS) CS/silane sol, coating film had stable contact angle with increasing reaction time excepting for 48hours. Also, the LHSA CS/TMOS/MTMS coating film had more enhanced flat surface with increasing the amount of MTMS and increasing reaction time. In the case of thermal stability, thermal dissociation of LHSA CS/MTMS sol did not occur up to $550^{\circ}C$.