• Transactions of the Korean hydrogen and new energy society
• /
• v.18 no.2
• /
• pp.157-163
• /
• 2007

During PEMFC operation, low current and low humidity conditions accelerate the degradation of perfluorosulfonic acid membrane. But, there have been no studies that clearly explain why these conditions accelerate the membrane degradation. In this study, the hydrogen permeability through the membrane, I-V polarization of MEA, fluoride emission rate(FER) in effluent water were measured during cell operation under low current densities and low relative humidity(RH). The experimental results were evaluated with oxygen radical mechanism the most commonly known for membrane degradation. It seems that low RH of anode is a good condition for $H{\cdot}$ radical formation on the Pt catalyst and the low current condition accelerates the $H{\cdot}$ to form $HO_2{\cdot}$ radical attacking the polymer membrane.

• Korean Chemical Engineering Research
• /
• v.61 no.4
• /
• pp.517-522
• /
• 2023

A chemical/mechanical durability test of polymer membrane evaluation method is used in which air and hydrogen are supplied to the proton exchange membrane fuel cell (PEMFC) and wet/dry is repeated in the open circuit voltage (OCV) state. In this protocol, when wet/dry is repeated, voltage increase/decrease is repeated, resulting in electrode degradation. When the membrane durability is excellent, the number of voltage changes increases and the evaluation is terminated due to electrode degradation, which may cause a problem that the original purpose of membrane durability evaluation cannot be performed. In this study, the same protocol as the department of energy (DOE) was used, but oxygen was used instead of air as the cathode gas, and the wet/dry time and flow rate were also increased to increase the chemical/mechanical degradation rate of the membrane, thereby shortening the durability evaluation time of the membrane to improve these problems. The durability test of the Nafion 211 membrane electrode assembly (MEA) was completed after 2,300 cycles by increasing the acceleration by 2.6 times using oxygen instead of air. This protocol also accelerated degradation of the membrane and accelerated degradation of the electrode catalyst, which also had the advantage of simultaneously evaluating the durability of the membrane and the electrode.

• Transactions of the Korean hydrogen and new energy society
• /
• v.32 no.5
• /
• pp.315-323
• /
• 2021

The air-cooled proton exchange membrane fuel cells (PEMFC) stacks, which is widely used in small-sized PEMFC, have a problem in that durability is weaker than that of the water-cooled type. Because the cathode is open to the atmosphere and the structural problem of the air-cooled stack, which is difficult to maintain airtightness, is highly likely to form a hydrogen/air boundary during start-up/shut-down (SU/SD). Through the accelerated durability evaluation of the 20 W air-cooled PEMFC stack, the purpose of this study was to find out the cause of the degradation of the stack and to contribute to the improvement of the durability of the air-cooled PEMFC stack. In this study, it was possible to evaluate durability in a relatively short time by reducing 20-30% of initial performance by repeating SU/SD 1,000 to 1,200 times on an air-cooled PEMFC stack. After disassembling the stack, each cell was divided into two and the performance analysis showed that the electrode degradation was more severe in the anode outlet membrane electrode assembly (MEA), which facilitates air inflow as a whole, than in the inlet MEA. It was shown that the cathode Pt was dissolved/precipitated to deteriorate the polymer ionomer inside the membrane.

• Journal of Ocean Engineering and Technology
• /
• v.36 no.3
• /
• pp.168-180
• /
• 2022

The IMO has decided to proceed with the early introduction of EEDI Phase 3, a CO₂ emission regulation to prevent global warming. Measures to reduce CO₂ emissions for ships that can be applied immediately are required to achieve CO₂ reduction. We set six different CO₂ emission scenarios according to the type of ship and fuel, and designed a monoethanolamine-based CO₂ capture process for ships using a rate-based model of Aspen Plus v10. The simulation model using Aspen Plus was validated using pilot plant operation data. A ship inevitably tilts during operation, and the performance of a tilted column decreases as its height increases. When configuring the conventional CO₂ capture process, we considered that the required column heights were so high that performance degradation was unavoidable when the process was implemented on a ship. We applied a parallel column concept to lower the column height and to enable easy installation and operation on a ship. Simulations of the parallel column confirmed that the required column height was lowered to less than 3 TEU (7.8 m).

• Korean Chemical Engineering Research
• /
• v.54 no.1
• /
• pp.6-10
• /
• 2016

Until a recent day, degradation of PEMFC (Proton Exchange Membrane Fuel Cells) has been mainly studied in unit cell. But operation and degradation of real PEMFC going along in stack instead of unit cell. Therefore in this work, ADT (Accelerated Degradation Test) of PEMFC was done in stack and the result from stack's test was compared with that of unit cell. The polymer electrolyte membrane was degraded by repeated electrochemical and mechanical degradation method among several ADT methods. Current densities of MEA at 0.6V decreased in stack and unit cell, 28.4% and 27.8% respectively after ADT for 312 hours. Hydrogen crossover current densities of membrane increased in stack and unit cell, 16.8% and 15.2% respectively after ADT for 312 hours. The result of ADT in stack was similar that of ADT in unit cell, which showed that ADT method of unit cell was available to the stack.

• Korean Chemical Engineering Research
• /
• v.52 no.6
• /
• pp.695-700
• /
• 2014

Proton Exchange Membrane Fuel Cells (PEMFC) can generate hydrogen and oxygen from water by electrolysis. But the electrode and polymer electrolyte membrane degrade rapidly during PEM water electrolysis because of high operation voltage over 1.7V. In order to reduce the rate of anode electrode degradation, unsupported $IrO_2$ catalyst was used generally. In this study, Pt/C catalyst for PEMFC was used as a water electrolysis catalyst, and then the degradation of catalyst and membrane were analysed. After water electrolysis reaction in the voltage range from 1.8V to 2.0V, I-V curves, impedance spectra, cyclic voltammograms and linear sweep voltammetry (LSV) were measured at PEMFC operation condition. The degradation rate of electrode and membrane increased as the voltage of water electrolysis increased. The hydrogen yield was 88 % during water electrolysis for 1 min at 2.0V, the performance at 0.6V decreased to 49% due to degradation of membrane and electrode assembly.

• Korean Chemical Engineering Research
• /
• v.45 no.4
• /
• pp.345-350
• /
• 2007

During PEMFC operation, OCV(open circuit voltage) and low humidity conditions accelerate the degradation of perfluorosulfonic acid membrane. There have been no studies that clearly explain why these conditions accelerate the membrane degradation. In this study, the hydrogen permeability through the membrane, I-V polarization of MEA, fluoride emission rate(FER) and $H_2O_2$ concentration in condensed water were measured during cell operation under OCV and low relative humidity(RH). The experimental results were evaluated with oxygen radical mechanism the most commonly known for membrane degradation. It seems that low RH of anode is a good condition for $H{\cdot}$ radical formation on the Pt catalyst and the OCV condition accelerate the $H{\cdot}$ to form $HO_2{\cdot}$ radical attacking the polymer membrane.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.288-294
• /
• 2009

Various polymer electrolyte membrane fuel cell (PEMFC) startup procedures were tested to explore possible techniques for reducing performance decay and improving durability during repeated startup-shutdown cycles. The effects of applying a dummy load, which prevents cell reversal by consuming the air at the cathode, on the degradation of a membrane electrode assembly (MEA) were investigated via single cell experiments. The electrochemical results showed that application of a dummy load during the startup procedure significantly reduced the performance decay, the decrease in the electrochemically active surface area (EAS), and the increase in the charge transfer resistance ($R_{ct}$), which resulted in a dramatic improvement in durability. After 1200 startup-shutdown cycles, post-mortem analyses were carried out to investigate the degradation mechanisms via various physicochemical methods including FESEM, an on-line $CO_2$ analysis, EPMA, XRD, FETEM, SAED, FTIR. After 1200 startup-shutdown cycles, severe Pt particle sintering/agglomeration/dissolution and carbon corrosion were observed at the cathode catalyst layer when starting up a PEMFC without a dummy load, which significantly contributed to a loss of Pt surface area, and thus to cell performance degradation. However, applying a dummy load during the startup procedure remarkably mitigated such severe degradations, and should be used to increase the durability of MEAs in PEMFCs. Our results suggest that starting up PEMFCs while applying a dummy load is an effective method for mitigating performance degradation caused by reverse current under a repetition of unprotected startup cycles.

• Applied Chemistry for Engineering
• /
• v.30 no.6
• /
• pp.659-666
• /
• 2019

Proton exchange membrane fuel cells (PEMFCs) generate electricity by electrochemical reactions of hydrogen and oxygen. PEMFCs are expected to alternate electric power generator using fossil fuels with various advantages of high power density, low operating temperature, and environmental-friendly products. PEMFCs have widely been used in a number of applications such as fuel cell vehicles (FCVs) and stationary fuel cell systems. However, there are remaining technical issues, particularly the long-term durability of each part of fuel cells. Degradation of a carbon supported-platinum catalyst in the anode and cathode follows various mechanistic origins in different fuel cell operating conditions, and thus accelerated stress test (AST) is suggested to evaluate the durability of electrocatalyst. In this article, comparable protocols of the AST durability test are intensively explained.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.98.2-98.2
• /
• 2011

For optimal performance of a proton exchange membrane fuel cell (PEMFC), the membrane electrode assembly (MEA) requires hydration, and the membrane's conductivity depends on water content. A humidifier is required to ensure that the reactant gas, usually hydrogen and air, is hydrated before entering the fuel cell. Dry membrane operation or improper hydration causes performance degradation. Typically, the humidification of a fuel cell is carried out by means of an internal or external humidifier. A membrane humidifier is applied to the external humidification of transportation or residential power generation fuel cell due to its convenience and high performance. In this study, The experiments were constructed with a plate-type membrane humidifier in terms of geometric parameters and operating parameters. The results show that the temperature and pressure, the channel length, the membrane thickness and gas flow rate are critical parameters affecting the performance of the humidifier.