• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.278-284
• /
• 1999

The effect of TiO$_2$addition has been studied on the power loss, density, initial permeability, resistivity, and microstructure of Mn-Zn ferrites. TiO$_2$addition increased the density of sintered body and decreased of the initial permeability. Activation energy for electron hopping as well as electrical resistivity increased with TiO$_2$addition. The toroidal core sintered at 1150 $^{\circ}C$ with 1.5 wt% of TiO$_2$demonstrated the power loss of 83 mW/㎤ at 1 MHz, 25 mT, 8$0^{\circ}C$. However, the same specimen sintered at 120$0^{\circ}C$ lead to the power loss, 1168 mW/㎤ at 1 MHz, 25 mT, 8$0^{\circ}C$ and developed an exaggerated grain growth.

• Journal of fish pathology
• /
• v.35 no.2
• /
• pp.241-246
• /
• 2022

White spot syndrome virus (WSSV) is a prevalent and virulent pathogen affecting cultured whiteleg shrimp (Litopenaeus vannamei) in Korea. In this study, seven monoclonal antibodies (mAbs) (10A12, 16C3, 17G4, 21G5, 22C4, 23B6 and 24G6) were produced by using purified WSSV. The reactivity of these mAbs was analysed by Western blot (WB), indirect immunofluorescence (IIF), and lateral flow immunochromatographic assay (LFIA). WB analysis demonstrated that three mAbs (17G4, 22C4, and 23B6) reacted specifically to VP28 with an approximate molecular weight of 24 kDa, mAb 16C3 reacted with approximately 17 kDa. IIF analysis demonstrated specific fluorescence signals on gill tissues of WSSV-infected shrimp, with five mAbs (10A12, 16C3, 22C4, 23B6, and 24G6), pleopods from WSSV-infected shrimp were used for LFIA, where, two mAbs (21G5 and 22C4) exhibited positive reaction. In conclusion, it can be inferred that the mAbs usage and specificity depends on the nature of assay used for diagnosis.

• Journal of Food Hygiene and Safety
• /
• v.34 no.2
• /
• pp.199-204
• /
• 2019

This study aimed to generate a probability distribution model based on temperature data of frozen food storage facility as input variables for microbial risk assessment (MRA). We visited 8 food-handling businesses to collect temperature data from their cold storage warehouses. The overall mean temperature inside the storage facilities was $-20.48{\pm}3.08^{\circ}C$, with 20.4% of the facilities having above $-18^{\circ}C$, with minimum and maximum temperature values of -10.3 and $-25.80^{\circ}C$ respectively. Temperature distributions by space locations of natural and forced convection were $-22.57{\pm}0.84$ and $-17.81{\pm}1.47^{\circ}C$, $-22.49{\pm}1.05$ and $-17.94{\pm}1.44^{\circ}C$, and $-22.68{\pm}1.03$ and $-18.08{\pm}1.42^{\circ}C$ in the upper (2.4~4 m), middle (1.5~2.4 m), and lower (0.7~1.5 m) shelves, respectively. Probability distributions from the temperature data were obtained using the program @RISK. Statistical ranking was determined using goodness of fit to determine the probability distribution model. Our results show that a log-normal distribution [5.9731, 3.3483, shift (-26.4281)] is most appropriate for relative MRA conduction.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.34 no.2
• /
• pp.91-97
• /
• 2001

The effects of sudden changes of water temperature (WT) on the stress response and physiological change of the cultured olive flounder in large (FL) and small (FS) size, and fat cod (FC) were examined by manipulating WT (2 types) in a flow through seawater culture system with 6 tanks (water vol. 270 L/tank). The WT was decreased from $20^{\circ}C$ to $10^{\circ}C$ within 5 hours ($2^{\circ}C/hour$) and maintained at $10^{\circ}C$ for 21 hours (Exp. I), and it was raised from $20^{\circ}C$ to $30^{\circ}C$ within 5 hours and maintained at $30^{\circ}C$ for 21 hours (Exp.II). In Exp. I, the levels of blood hematocrit at 5 hours ($10^{\circ}C$) in FS was significantly decreased from $13.5\pm2.0\%\;to\;11.3\pm2.3\%$, but FC at 2.5 hours ($15^{\circ}C$) ($19.0\pm0.3\%\;to\;23.2\pm3.8\%$) was increased, The blood hemoglobin concentration of all fish in Exp, II was significantly increased until 8 hours after raising WT from $20^{\circ}C$ to $30^{\circ}C$. In Exp. I and II , the levels of plasma cortisol in FL, FS and FC was changed from $5.2\pm8.5ng/mL,\;4.4\pm4.5ng/mL\;and\;2.7\pm0.4ng/mL$, respectively, before sudden drop and rise of WT. The levels of plasma cortisol of in FL ($164.0\pm53.1ng/mL$) and FC ($207.9\pm25.4ng/mL$) were significantly increased by the lowering WT sharply during whole experiment. The FL ($12.6\pm2.0ng/mL$) and FS ($4.0\pm3.9ng/mL$) showed no significant differences in cortisol level according to sudden rise of WT (5 hours). But it in FC ($44.7\pm18.2ng/mL$) was increased. In Exp. I, the plasma glucose levels of all fish groups were decreased after 5 hours ($10^{\circ}C$), The plasma lactic acid concentration of FL and FS showed no significant differences until 5 hours after raising WT from $20^{\circ}C$ to $30^{\circ}C$, But it in FC was significantly increased with WT raise.

• Journal of Electrochemical Science and Technology
• /
• v.6 no.3
• /
• pp.95-105
• /
• 2015

In the present work, Carbon supported Pt₁₀₀, Pt₈₀Sn₂₀, Pt₈₀Ni₂₀ and Pt₈₀Sn₁₀Ni₁₀ electrocatalysts with different atomic ratios were prepared by ethylene glycol-reduction method to study the electro-oxidation of ethanol in membraneless fuel cell. The electrocatalysts were characterized in terms of structure, morphology and composition by using XRD, TEM and EDX techniques. Transmission electron microscopy measurements revealed a decrease in the mean particle size of the catalysts for the ternary compositions. The electrocatalytic activities of Pt₁₀₀/C, Pt₈₀Sn₂₀/C, Pt₈₀Ni₂₀/C and Pt₈₀Sn₁₀Ni₁₀/C catalysts for ethanol oxidation in an acid medium were investigated by cyclic voltammetry (CV) and chronoamperometry (CA). The electrochemical results showed that addition of Ni to Pt/C and Pt-Sn/C catalysts significantly shifted the onset of ethanol and CO oxidations toward lower potentials. The single membraneless ethanol fuel cell performances of the Pt₈₀Sn₁₀Ni₁₀/C, Pt₈₀Sn₂₀/C and Pt₈₀Ni₂₀/C anode catalysts were evaluated at room temperature. Among the catalysts investigated, the power density obtained for Pt₈₀Sn₁₀Ni₁₀/C (37.77 mW/cm² ) catalyst was higher than that of Pt₈₀Sn₂₀/C (22.89 mW/cm² ) and Pt₈₀Ni₂₀/C (16.77 mW/ cm² ), using 1.0 M ethanol + 0.5 M H₂SO₄ as anode feed and 0.1 M sodium percarbonate + 0.5 M H₂SO₄ as cathode feed.

• Journal of Adhesion and Interface
• /
• v.15 no.4
• /
• pp.169-173
• /
• 2014

The effect of filler sizes on the thermal diffusivity of Nylon 66/SiC composites was investigated. By loading 60 vol% of SiC fillers on Nylon 66, the thermal diffusivity of the composites increased more than 10 times than that of unfilled Nylon 66 and the thermal diffusivity of composites with filler sizes of $24{\mu}m$ and $76{\mu}m$ increased to $2.2{\times}10^{-2}cm^2/sec$ and $1.75{\times}10^{-2}cm^2/sec$, respectively. It is speculated that the smaller filler size ($24{\mu}m$) of SiC is more favorable for the formation of thermal conductive path that the larger size ($76{\mu}m$) of filler composites. The thermal diffusivity of Nylon 46/SiC 400 (60 vol%) composites was $1.61{\times}10^{-2}cm^2/sec$ that was lower than that of Nylon 66/SiC (60 vol%) composites.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.891-896
• /
• 2003

Novel fabrication technique was developed for high strength Reaction-Bonded SiC (RBSC) hot gas filter for use in IGCC (Integrated Gasification Combined Cycle) system. The room and high temperature fracture strengths for Si-melt infiltrated reaction-bonded SiC were 50-123, and 60-66 MPa, respectively. The average pore size was 60-70 $\mu\textrm{m}$ and the porosity was about 34 vol％. RBSC infiltrated with molten silicon showed improved fracture strength at high temperature, as compared to that of clay-bonded SiC, due to SiC/Si phase present within SiC phase. The thickness for SiC/Si phase was increased with increasing powder particle size of SiC from 10 to 34 $\mu\textrm{m}$. Pressure drop with dust particles showed similar response as compared to that for Schumacher type 20 filter. The filter fabricated in the present study showed good performance in that the filtered powder size was reduced drastically to below 1 $\mu\textrm{m}$ within 4 min.

• Investigative Magnetic Resonance Imaging
• /
• v.10 no.1
• /
• pp.20-25
• /
• 2006

Purpose : To evaluate the NMR relaxation properties of newly developed high performance paramagnetic complexes. Materials and methods : 4-aminomethylcyclohexane carboxylic acid (0.63g, 4 mmol) was mixed with the suspension solution of DMF (15mL) and DTPA-bis-anhydride (0.71g, 2 mmol) to synthesize the ligand. The ligand was then mixed with Gd2O3 (0.18g, 0.5 mmol) to synthesize Gd-chelate. For the measurement of magnetic relaxivity of paramagnetic compounds, the compounds were diluted to 1mM and then the relaxation times were measured at 1.5T(64 MHz). Inversion-recovery pulse sequence was employed for T1 relaxation measurement and CPMG(Carr-Purcell-Meiboon-Gill) pulse sequence was employed for T2 relaxation measurement. Using MATLAB(Version 7.1) program, T1 magnetic relaxation map, R1 map, T2 magnetic relaxation map and R2 map were developed to represent magnetic relaxation time and magnetic relaxivity as image. Results : Compared to $R1=4.9mM^{-1}sec^{-1}$ and $R2=4.8mM^{-1}sec^{-1}$ of Omniscan (Gadodiamide), which is commercially available paramagnetic MR agent, R1 of SUK090(Gd-C32H74N5O24) was $12.46mM^{-1}sec^{-1}$ and R1 of SUK091(Gd-C34H78N5O24) was $12.77mM^{-1}sec^{-1}$. However, R1 of SUK092(Gd-C30H56N5O17) was decreased to $2.09mM^{-1}sec^{-1}$. In case of R2, SUK090(Gd-C32H74N5O24) was $8.76mM^{-1}sec^{-1}$ and SUK091(Gd-C34H78N5O24) was $7.60mM^{-}1sec^{-1}$ whereas SUK092(Gd-C30H56N5O17) was decreased to $1.82mM^{-1}sec^{-1}$. Conclusion : Among three new paramagnetic complexes, SUK090(Gd-C32H74N5O24) and SUK091(Gd-C34H78N5O24) showed higher T1, T2 magnetic relaxation rates than that of commercially available paramagnetic MR agent and thus expected to have more contrast enhancement effect.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.5 no.1
• /
• pp.63-69
• /
• 1997

The role of L-glutamic acid, a precursor of $C_5$ ALA biosynthetic pathway, on the production of 5-aminolevulinic acid (ALA) has been described in cells of Rhodospirillum rubrum N-1. To the Lascelles basal medium the addition of both 30 mM L-glutamicacid and 20 mM levulinic acid (LA) provided to increase the extracellular ALA yield up to 40 fold (76 mg/l). By the addition of both 60 mM glycine and succinic acid, precursorsof $C_4$ ALA biosynthetic pathway, at middle log phase of cell growth ALA yield was increased 27 fold (52 mg/l) although the celt growth was inhibited to a certain extent.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.2
• /
• pp.304-313
• /
• 2004

Xylitol, a five-carbon natural sugar alcohol, is widely used non-cariogenic sugar substitute. In present study, the effects of xylitol on the expression of mRNA for glucosyltransferase which synthesizes glucan from sucrose were detected by Fluorescent in situ hybridization (FISH) and flow cytometry. FITC fluorescences for mRNA of gtfB, gtfC and gtfD were decreased further with increasing concentration of xylitol from 1% to 10% when detected by FISH. Flow cytometric analysis also showed that the expression of gtfB, gtfC and gtfD was increased by the addition of sucrose and decreased by the addition of xylitol to BHI broth containing 1% sucrose. In conclusion, the expression of gtfB, gtfC and gtfD mRNA was decreased by the addition of xylitol.