• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.7
• /
• pp.510-514
• /
• 2013

In order to prevent heat loss that occurs through the glass, low-emissivity (Low-E) coating methods with good insulating properties and high transmittance were used. InGaZnO/Ag/InGaZnO (IGZO/Ag/IGZO) multilayer thin films have been deposited on XG glass substrate by RF magnetron sputtering. Depending on the different thickness of Ag in multilayer films, the structural and optical properties of Low-E multilayer films were analyzed. By XRD analysis results, the multilayer thin films were observed to be amorphous structure regardless of Ag thickness. According to the AFM results, surface morphology of the multilayer films was observed and compared. Using UV-VIS spectroscopy, low emissivity property has been observed clearly with the transmittance of higher than 85% at visible range and lower than 30% at IR range.

• Electrical & Electronic Materials
• /
• v.8 no.4
• /
• pp.504-508
• /
• 1995

The purpose of this research is to study on characteristics of corona ignitor which was designed for ignition of plasma, used at hard coating, surface treatment and thin film preparation, at high pressure. Corona ignitor composed of hollow type inner electrode and ring type external electrode. Though corona voltage increased with increasing distance between electrodes, corona discharge can be controlled stably. The gas flow in hollow type inner electrode and the construction between electrodes affect a length of corona flame and corona phenomenon. It is possible to ignite the . plasma, usually generated at low pressure(10 Torr), at high pressure(100 Torr) by corona ignitor.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.07a
• /
• pp.133-155
• /
• 2002

1. Quasicrystalline powders shows exotic physical and mechanical p properties 2. Applications: structural application: strengthening particles for composites C Coating application: wear resistance, low friction coefficient 3. For thermal spaying: material loss during process should be c considered to control chemical composition of deposit 4. Friction coefficient is strongly dependent on contact geometry F Friction coefficient from pin on plate: 0.1-0.2 Friction coe야icient from flat on plate: about 0.46. 5. Quasicrystalline materials show lower friction coefficient but higher w wear rate than corresponding values of $Cr_20_3$ coated layer. 6. Amorphous coating seems to be promising

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.11
• /
• pp.7667-7671
• /
• 2015

Recently, Zinc coating is often used with environment friendly features and high performance. Generally The coating temperature is one of main factors for determining coating thickness and coating ability, so the optimal coating temperature is strongly required. In this paper, the thermo-flow simulation considering the air flow inside the coating rooms for analyzing the temperature distributions of Zinc spray coating room was performed. Two spray coating rooms, preheating room and drying room were all modeled by SolidWorks program and the temperature distributions were analyzed by Flow simulation program. The analysis results were verified with the measured data by thermal image camera. The characteristics of temperature distributions of the first spray room and the second spray room were understood and the results showed that the temperatures of two spray coating room were low compared with the target temperature $25^{\circ}C$. To the exclusion of heater addition, the simulation with all the same conditions exclusive the exhaust fan was performed, which showed that the temperatures of the first and the second spray rooms increased by $6.2^{\circ}C$ and $5.8^{\circ}C$. This analysis can be applicable for designing a new spray coating room for improving performance.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.34 no.5
• /
• pp.18-38
• /
• 2002

A previous study on the model coatings based on latex-bound plastic pigment coatings (1) has been extended to latex-bound No. 1 clay, ultra-fine ground calcium carbonate (UFGCC), and clay-carbonate pigment mixture coatings, which are being widely used in the paper industry. The latex binder used was a good film-forming, monodisperse S/B latex or 0.15$\mu\textrm{m}$. No. 1 clay was representative of plate-like pigment particles, whereas UFGCC was of somewhat rounded rhombohedral pigment particlel. Both of them had negatively skewed triangular particle size distributions having the mean particle suet of 0.7${\mu}{\textrm}{m}$ and 0.6$\mu\textrm{m}$, respectively. Their packing volumes were found to be 62.5% and 657%, respectively. while their critical pigment volume concentrations (CPVC's) were determined to be 52.7% and 50.5% ( average of 45% caused by the incompatibility and 55.9% extrapolated) by coating porosity, respectively. Each pigment/latex coating system has shown its unique relationship between coating properties and pigment concentrations, especially above its CPVC. Notably, the clay/latex coating system hat shown higher coating porosity than the UFGCC/latex system at high pigment concentrations above their respective CPVC's. It was also found that their coating porosity and gloss were inter-related to each other above the CPVC's, as predicted by the theory. More interestingly, the blends of these two pigments have shown unique rheological and coating properties which may explain why such pigment blends are widely used in the industry. These findings have suggested that the unique structure of clay coatings and the unique high-shear rheology of ground calcium carbonate coatings can be judiciously combined to achieve superior coatings. Importantly, the low-shear viscosity of the blends was indicative of their unique packing and coating structure, whereas their high-shear rheology was represented by a common mixing rule, i.e., a viscosity-averaging. Transmission and scanning electron and atomic force microscopes were used to probe the state of pigment / latex dispersions, coating surfaces, freeze fractured coating cross-sections, and coating surface topography. These microscopic studies complemented the above observations. In addition, the ratio, R, of CPVC/(Pigment Packing Volume) has been proposed as a measure of the binder efficiency for a given pigment or pigment mixtures or as a measure of binder-pigment interactions. Also, a mathematical model has been proposed to estimate the packing volumes of clay and ground calcium carbonate pigments with their respective particle size distributions. As well known in the particle packing, the narrower the particle size distributions, the lower the packing volumes and the greater the coating porosity, regardless of particle shapes.

• The Korean Journal of Ceramics
• /
• v.2 no.1
• /
• pp.1-10
• /
• 1996

Transparent conducting $SnO_2$-based thin films have been coated on float substrates such as fused quartz, and ceramic fiber cloths such as the Nexel and E-glass cloth from tin alkoxides by the sol-gel technique. Also, thin films of alternating layers of $SnO_2$ and $SiO_2$ have been fabricated by dip coating. The sheet resistance and average visible transmittance of the films were investigated in the aspect of the applications as transparent electrodes such as liquid crystal displays, photo-detectors and solar cells. The Nextel and E-glass cloths coated with antimony-doped tin oxide (ATO) had sheet resistance of as low as $20 \;ohm/{\Box}$ and $120ohm/\;{\Box}$, respectively. The promotion effects of additives as $La_2O_3$ and Pt on the ethanol gas sensing properties of the films were investigated in the aspects of the applications as an alcohol sensor and a breath alcohol checker. Possible evidence of quantum well effects in the oxide multilayers of $SnO_2$ and $SiO_2$ was investigated.

• Textile Coloration and Finishing
• /
• v.20 no.1
• /
• pp.1-7
• /
• 2008

The study has attempted to introduce a new coating than the conventional standardized method of spray, padding and roll coating. The study has focused on finding condition for separating water and organic layer in marble bath and surface effects according to kind of raw hide. It was found that dyestuff-free was to be used in water layer and the input amount of initial insoluble pigment to be added in marble bath should be adjusted following the change of surface area of the marble bath in order to get efficient marble effect while preventing coagulation of water and organic layers. Eventually, amorphous high value-added leather could be obtained treated in process other than the conventional standardized method. Even raw hides of low grades($C{\sim}E$ grades) could be processed into amorphous marble effect that could conceal or shield surface scratches by the colorant, which eventually eliminated necessity of using excessive amount of chemicals in the coating process leading to achieving high quality marble leather of natural look.

• Structural Engineering and Mechanics
• /
• v.82 no.2
• /
• pp.163-172
• /
• 2022

Zinc-rich epoxy (ZRE) is used to overcome corrosion problems in reinforced concrete (RC) beams and coat steel rebars to protect them from humidity and chlorides. An extra coating layer of Sikadur-31 epoxy (SDE) is utilised to increase bond strength because the use of ZRE reduces the bond strength between concrete and steel rebars. However, the low melting point of SDE indicates that concrete specimens are vulnerable to fire. An experimental investigation on flexural performance of RC beams incorporating ZRE-SDE coating of steel rebars that were destroyed by fire is performed in this study. Twenty beams of five concrete mixes with different cementitious contents were tested to compare fire exposure for coated and uncoated rebars of the same beams at room temperature and determine the optimal cementitious content. Scanning electron microscopy (SEM) was also applied to investigate characteristics of fired mixture samples. Results showed that the use of SDE-ZRE at room temperature improves flexural strengths of the five mixes compared with uncoated rebars with percentages ranging from 8.5% to 12.3%. All beams with SDE-ZRE lost approximately 50% of their flexural strength due to firing. Moreover, the mix incorporating SF (silica fume) of 15% and cement content of 400 kg/m³ introduces optimum behaviour compared with other mixes. All results were supported and verified by the SEM analysis and compressive strength of cubic specimens of the same mixes.

• Korean Journal of Materials Research
• /
• v.17 no.1
• /
• pp.1-5
• /
• 2007

GaN thin fan were grown by spin coated colloidal GaOOH precursor. Polycrystalline GaNs with crystalline size of $10{\sim}100nm$ were grown on $SiO_2$ substrate. The shape of crystallite above $900^{\circ}C$ had the hexagonal plate and column type. X-ray diffraction patterns for them correspond to those of the hexagonal wurtzite GaN. With increasing droplets. i.e, thickness of deposited layers, XRD intensity increased. PL (photoluminescence) spectrum consisted with an weak near band-edge emission at 3.45 eV and a broad donor-acceptor emission band at 3.32 eV. From the low temperature PL measurement on GaN grown at $800^{\circ}C$ that the shallow donor-acceptor recombination induced emission was more intense than the near band-edge excitonic emission.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1996.02a
• /
• pp.102-102
• /
• 1996

This paper represents a new type low power High Frequency technological ion source (HF TIS) for ion - beam processing: the surface modification of materials, cleaning of surface, sputtering, coating of thin films, and polishing. The operational principle of HF TIS is based on the excitation of electrostatic waves in plasma located in the external magnetic field. Low power HF TIS with diameter 92 rom gives the opportunity to obtain beams of inert and chemically reactive gases with currents range from 5 to 150 mA (current density $0.015\;~\;3.5\;mA/\textrm{m}^2$) and ion beam energy 100 ~ 2500 eV at a HF power level 10 ~ 150 W. Three grid concave type ion optical system (IOS) is used for extraction and formation ofion beam.n beam.