• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.1
• /
• pp.29-35
• /
• 2004

The effect of low tempering in a temperature range of $150{\sim}400^{\circ}C$ on corrosion resistance in 420J2 stainless steel austenitized at $1000^{\circ}C$ was investigated by the application of salt spray test, electrochemical pitting test in 3.5% NaCl solution and DL-EPR test for intergranular corrosion in 0.5M $H_2SO_4$+0.01M KSCN solution. In salt spray test, good corrosion resistance was obtained in a tempering temperature range of $150{\sim}250^{\circ}C$. Pitting potential was increased to the tempering temperature of $250^{\circ}C$, but decreased with the increase of temperature up to $400^{\circ}C$ And it was thought that the degradation of pitting corrosion resistance showed at the tempering temperature of around $400^{\circ}C$ was due to the precipitation of $Cr_7C_3$ of $M_7C_3$ type. The degree of sensitization showed increasing tendency with the increase of tempering temperature, and also Cr depletion phenomena were observed in the vicinity of grain boundary.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.4
• /
• pp.249-255
• /
• 2018

High temperature and low temperature gaseous nitriding was performed in order to study of the surface hardening and wear properties of the nitrided AISI 410 Martensitic stainless steels. High temperature gaseous nitiridng (HTGN) was carried out using partial pressure $N_2$ gas at $1,100^{\circ}C$ for 10 hour, and Low temperature gaseous nitiridng (LTGN) was conducted in a gas mixture of NH3 and N2 at $470^{\circ}C$ for 10 hour. The nitrided samples were characterized by microhardness measurements, optical microscopy and scanning electron microscopy. The phases were identified by X-ray diffraction and nitrogen concentration was analyzed by GD-OES. The HTGN specimen had a surface hardness of about $700HV_{0.1}$, $350{\mu}m$ of case depth. A ${\sim}50{\mu}m$ thick, $1,250HV_{0.1}$ hard nitrided case formed at the surface of the AISI 410 steel by LTGN, composed nitrogen supersaturated expanded martensite and ${\varepsilon}-Fe_{24}N_{10}$ iron nitrides. Additionally, the results of the wear tests, carried out LTGN specimen was low friction coefficient and high worn mass loss of ball. The increase in wear resistance can be mainly attributed to the increase in hardness and to the lattice distortion caused by higher nitrogen concentration.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.159-159
• /
• 2007

In order to reduce a signal delay in ULSI, low resistive metal and intermetal dielectric material of low dielectric constant are required. Ordered mesoporous silica film is proper to intermetal dielectric due to its low dielectric constant and superior mechanical properties. In this study, ordered mesoporous silica films was synthesized using TEOS (tetraethoxysilane) / MTES (methyltriethoxysilane) mixed silica precursor and Brij-$76^{(R)}$ surfactant. These films had the porosity of 40% and dielectric constant of 2.5. To lower dielectric constant, the ordered mesoporous silica films were surface-modified by HMDS (hexamethyldisilazane) treatment. HMDS substituted -OH groups on the surface of silica wall for -Si$(CH_3)_3$ groups. After the HMDS treatment, ordered mesoporous silica films were calcined at various calcination temperatures. Through the investigation, it was concluded that the proper calcination temperature is necessary as aspects of structural, electrical, and mechanical properties.

• KOREAN JOURNAL OF CROP SCIENCE
• /
• v.39 no.6
• /
• pp.571-576
• /
• 1994

This study was conducted to determine the effects of embryo age, growth regulators, low temperature treatment on regeneration, plant growth, and heading in immature embryo culture of Barley. Shoot and root development was more in older than in younger excised embryos, and more in a medium without kinetin than in one with kinetin. The rate of survival was higher on medium without growth regulators and lower on medium with kinetin 5 mg/L because of retarded plant growth. Embryo age and media did not completely replace low temperature treatment. Twenty- and 14 day-old embryos responded by flowering after 4 weeks of vernalization. Embryo culture at 14- and 20 days after anthesis coupled with 4-week cold treatment shortens generation time of barley. When 20 day immature embryos of barley (cv. Olbori) was treated low temperature treatment for 4 weeks, the rate of heading was better than the other treatment.

• Journal of the Korean Ceramic Society
• /
• v.49 no.3
• /
• pp.236-240
• /
• 2012

The reticulated carbon foam have been used for their excellent properties in terms of thermal management which is getting important in industrial field currently. In this study, we measure the mechanical properties of the reticulated carbon foam which is heat-treated at various temperature from the prepared low-density phenol foam. Simultaneously, we observe microstructures with high resolution transmission microscope and measure the residual oxygen content of carbon foams to figure out the relationship between the apparent change of properties such as weight loss and linear shrinkage during heat treatment. In conclusion, the carbon foam heat-treated at $1400^{\circ}C$ shows the highest strength, and the mechanical behavior is believed to be strongly related to the creation of nano-size graphite crystals from the amorphous carbon during heat treatment. On the other hand, it is turned out that the weight loss occurred at the temperature under $1400^{\circ}C$ comes from the elimination of oxygen in the form of $CO_2$ or CO, but no evidence is found on weight loss mechanism at the temperature above $1400^{\circ}C$.

• Journal of Soil and Groundwater Environment
• /
• v.16 no.3
• /
• pp.10-16
• /
• 2011

The experimental studies for remediation of diesel contaminated soils were performed using subcritical water in laboratory scale. Contaminated soils from industrial area and artificially contaminated soils were utilized for soil remediation. Experimental system was composed for subcritical water to flow upward through the soil packed column for extracting contaminants. 10 g of contaminated soil was packed into the column and water flow rate was 2 mL/min. To evaluate the effects of temperature, pressure and treatment time on the removal efficiency, temperature was changed from 100$^{\circ}C$ to 350$^{\circ}C$, pressure from 50 bar to 220 bar and treatment time at the predetermined temperature from 0 min to 120 min. The purification efficiency increased as temperature increased. However, the effect of pressure and treatment time was low. Temperature 250$^{\circ}C$, pressure 50 bar and treatment time 30 min were selected for optimal operating condition for this study.

• Journal of the Korean Society for Heat Treatment
• /
• v.19 no.4
• /
• pp.219-224
• /
• 2006

Silver paste with low sintered temperature has been developed in order to apply electronic parts, such as bus electrode, address electrode in PDP (Plasma Display Panel) with large screen area. In this study, nano-sized silver particles with 10-30 nm were synthesized from silver nitrate ($AgNO_3$) solution by chemical reduction method and silver paste with low sintered temperature was prepared by mixing silver nanoparticles, conventional silver powder with the particle size 1.6 um and Pb-free frit. Conductive thick film from silver paste was fabricated by screen printing on alumina substrate. After firing at $540^{\circ}C$, the cross section and surface morphology of the thick films were analyzed by FE-SEM. Also, the sheet resistivity of the fired thick films was measured using the four-point technique.

• Textile Coloration and Finishing
• /
• v.24 no.2
• /
• pp.131-137
• /
• 2012

para-Aramid fibers were treated by low-temperature plasma to improve the adhesion. The surface of para-aramid fibers were treated with gaseous plasma of several discharge power and treatment time in oxygen gas at 1Torr pressure. The treated fibers at low-temperature plasma were taken oxygen-containing functional groups and micro-crator on the surface. The modified fibers were measured by dynamic contact angle analyzer and XPS(X-ray photoelectron spectroscopy). The Interfacial adhesion properties of aramid fabric and polyurethane resin were determined by T-peel test. The surface of aramid fibers were observed by FE-SEM photographs. It was found that surface modification and chemical component ratio of the aramid fibers were improved wettability and adhesion characterization.

• Membrane and Water Treatment
• /
• v.15 no.1
• /
• pp.1-9
• /
• 2024

Biological nutrient removal is gaining increasing attention in wastewater treatment plants; however, it is adversely affected by low temperatures. This study examined temperature effects on nutrient removal and morphological stability of the granular and denitrifying phosphorus accumulating organisms (PAO and DPAO, respectively) using sequencing batch reactors (SBRs) at 5, 10, and 20 ℃. Lab-scale SBRs were continuously operated using anaerobic-anoxic and anaerobic-oxic cycles to develop the PAO and DPAO granules for 230 d. Sludge granulation in the two SBRs was observed after approximately 200 d. The average removal efficiency of soluble chemical oxygen demand (SCOD) and PO₄^3--P remained >90% throughout, even when the temperature dropped to 5 ℃. The average removal efficiency of NO₃^--N remained >80% consistently in DPAO SBR. However, nitrification drastically decreased at 10 ℃. Hence, the removal efficiency of NH₄⁺-N was decreased from 99.1% to 54.5% in PAO SBR. Owing to the increased oxygen penetration depth at low temperatures, the influence on nitrification rates was limited. The granule in DPAO and PAO SBR was observed to be unstable and disintegrated at 10 ℃. In conclusion, morphological characteristics showed that changed conversion rates at low temperatures in aerobic granular sludge altered both nutrient removal efficiencies and granule formation.

• Food Science of Animal Resources
• /
• v.34 no.1
• /
• pp.115-121
• /
• 2014

This study explored the effects of water or brine (2% NaCl, w/v) immersion thawing combined with ultrasound treatment (40 kHz, 150 W) on the quality characteristics of pork. Ultrasound treatment of pork was conducted in two cold media (at $4^{\circ}C$), water and 2% (w/v) brine, respectively. Because the ultrasound treatment caused temperature increase in the media from $4^{\circ}C$ to $16^{\circ}C$, the qualities of pork thawed by ultrasound were compared with those thawed by immersion either in water or brine where the temperature was being maintained at either $4^{\circ}C$ (low temperature control) or $17^{\circ}C$ (high temperature control). The ultrasound treatment resulted in rapid thawing of pork where the thawing rate was similar to those thawed in the $17^{\circ}C$ media. For quality characteristics, ultrasound-treated pork in brine had an advantage of less cooking losses when comparing to the control. In particular, ultrasound treatment in brine exhibited the lowest shear force (or highest tenderness) among the freezing/thawing treatments. Although the ultrasound processing in brine caused discoloration of the pork, this thawing technique had potential to be applied as a commercial thawing technology for frozen foods.