• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2003.11a
• /
• pp.91-94
• /
• 2003

Ceramic femoral heads in the total hip replacement have been developed to reduce the polyethylene liner wear. Alumina and zirconia (3Y-TZP) are using in clinical application worldwide and there are many good test reports. However, alumina has a risk of catastrophic failure, and zirconia has the low temperature degradation in spite of enhanced fracture toughness. Recently, novel zirconia/alumina composite having low temperature degradation-free character and high fracture tough . was developed and it leads the lower wear 3f polyethylene than alumina and zirconia. In the present study, in order to optimise the microstructure of low temperature degradation (LTD)-free zirconia/alumina composite for the best wear resistance of polyethylene, various compositions of (LTD)-free zirconia/alumina composites were fabricated, and the sliding wear of UHMWPE against these novel composites were examined and compared with that against alumina and zirconia ceramics used for total hip joint heads.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2004.11a
• /
• pp.355-361
• /
• 2004

Ceramic femoral heads in the total hip replacement have been developed to reduce the polyethylene liner wear, Alumina and zirconia (3Y-TZP) having the excellent tribological properties are coupled against acetabular cups of polyethylene and are used in clinical application worldwide. However, alumina has a risk of catastrophic failure, and zirconia has the low temperature degradation in spite of enhanced fracture toughness. Recently, novel zirconia/alumina composite is very attractive due to the low temperature degradation (LTD)-free character and high fracture toughness. In the present study, we focus on the wear of ceramic on ceramic, which are able to be used as femoral heads and acetabular cups. Therefore, LTD-free zirconia/alumina composites with three compositions are made in a form of disk and cylinder, and the wear of the composites is performed on pin-on-disk type wear tester. The wear is conducted with or without lubricant. All the composites fabricated with the different composition show the good wear resistance.

• Tribology and Lubricants
• /
• v.21 no.5
• /
• pp.216-220
• /
• 2005

The sliding wear behaviors of three different compositions of novel low temperature degradation-free zirconia/alumina (LTD-free Z/A) composites were examined in a ceramic-ceramic contact pair. The wear tests were performed by using a pin-on-disk type wear tester in a linear reciprocal sliding motion with a line contact in both dry and bovine serum lubricated conditions at room temperature. From the results of dry sliding wear tests, Z/A#1((5.3Y, 4.6Nb)-TZP/80 $vol\%Al_2O_3$) showed the best wear resistance among three kinds of LTD-free Z/A composites. For the bovine serum lubricated sliding wear tests, wear was too little to be measured for all kinds of Z/A composites. These novel LTD-free Z/A composites having excellent wear resistance demonstrated a potential as the alternative materials for the ceramic-ceramic contact pairs of femoral head and acetabular liner in total hip replacement.

• Journal of Technologic Dentistry
• /
• v.34 no.2
• /
• pp.83-93
• /
• 2012

Purpose: The objective of this study is to find out physical properties and the flexural strength changed by the low temperature degradation of the block which is needed to make bio-prosthetic dentistry which is better than feldspar affiliated ceramic made by building up ceramic powder and also to apply this to the clinical use of zirconia monolithic all-ceramic crown. Methods: Flexural strength of each sample was evaluated before and after the Low Temperature Degradation, and physical properties of the Tetra Zirconia Block containing 3mol % was evaluated as well. The average and standard deviation of each experimental group were came out of the evaluation. Statistical package for social science 18.0 was used for statistics. Results: The average density of the monolithic all-ceramic crown was $6.0280{\pm}0.0147g/cm$, the relative density was 99.01 %. When the sample was sintered at $1480^{\circ}C$ the diameter of average particle was $396.62{\pm}33.71nm$. All the samples had no monolithic peak after XRD evaluation but only had tetragonal peak. There were statistically significant differences in the result of flexural strength of the samples evaluated after and before the low temperature degradation, the flexural strength before the low temperature degradation was $1747.40{\ss}{\acute{A}}$, at the temperature of $130^{\circ}C$ the flexural strength after the low temperature degradation was 1063.99MPa (p<0.001). There was statistically significant difference in the result of strength of 1020.07MPa after the low temperature degradation at the temperature of $200^{\circ}C$ (p<0.001). Conclusion: The block which was made for this evaluation possesses such an excellent strength among dental restorative materials that it is thought to have no problems to use for tetragonal zirconia polycrystal.

• New & Renewable Energy
• /
• v.17 no.1
• /
• pp.19-32
• /
• 2021

Photovoltaic (PV) panels are generally treated as the most dependable components of PV systems; therefore, investigations are necessary to understand and emphasize the degradation of PV cells. In almost all specific deprivation models, humidity and temperature are the two major factors that are responsible for PV module degradation. However, even if the degradation mode of a PV module is determined, it is challenging to research them in practice. Long-term response experiments should thus be conducted to investigate the influences of the incidence, rates of change, and different degradation methods of PV modules on energy production; such models can help avoid lengthy experiments to investigate the degradation of PV panels under actual working conditions. From the review, it was found that the degradation rate of PV modules in climates where the annual average ambient temperature remained low was -1.05% to -1.16% per year, and the degree of deterioration of PV modules in climates with high average annual ambient temperatures was -1.35% to -1.46% per year; however, PV manufacturers currently claim degradation rates of up to -0.5% per year.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.415-417
• /
• 2009

A low temperature decal (LTD) transfer method is tried to fabricated hydrocarbon (HC) membrane based MEA. Sandwiched structures of outer ionomer/catalyst/carbon coating/substrate, which had been developed for Nafion membrane, are used for transfer of catalyst to the HC membrane. Performances of the HC MEA before and after 500hr continuous operation are compared and it is found that a severe delamination occurs at the interface between the HC membrane and the catalyst layer, which is the main reason of the low performance and its degradation. The delamination is due probably to the different nature of HC membrane to the Nafion ionomer. A substitutional method, therefore, is suggested to overcome this. In such a way, the outer ionomer process is removed and the low transfer rate of catalyst by skipping the ionomer process is compensated with optimization of other process variables such as transfer time or temperature. The resulting performance is superior to the original LTD method, which can be explained in terms of low resistive components both in ohmic and kinetic.

• Journal of Welding and Joining
• /
• v.26 no.1
• /
• pp.50-55
• /
• 2008

A low alloy-steel(2.25Cr-1.0Mo) has been widely used for boiler piping, header and tubes in high temperature and pressure conditions of the thermal power plant. It is common knowledge that the repair welding is permitted two or three times by customary practice rule, but there is no regulation to limit the number of repair welding base on the study heat-affected zone(HAZ), which is the weakest zone when repair welding is under taken, by experiments about the metallographic degradation and mechanical properties. Therefore, this study aims to verify the reliability of 5 times repair welding through conducting the experimental observation in the mechanical and the metallographic change on HAZ varying repair welding times. In results of the experiments, it is concluded that the reliability was kept in HAZ even up to the fifth repairs.

• Journal of dental hygiene science
• /
• v.14 no.1
• /
• pp.29-34
• /
• 2014

The purpose of this study was to evaluate the influence of low temperature degradation (LTD) on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP). The push-shear bond test method was used to investigate the core-veneer bonding strength of industrially manufactured Y-TZP core ceramic and manufacturer recommended veneering ceramic. Four groups from ceramic-zirconia specimens (n=28; n=7 per group) were assigned into four experimental aging conditions, namely storage in an autoclave at $134^{\circ}C$ for 0, 3, 5, 10 hours. Bonding strength was obtained using a universal testing machine with crosshead speed 0.5 mm/min. Data were statistically analyzed using one-way ANOVA and Tukey's test (${\alpha}=0.05$). In bonding strength test, the group which was treated with LTD showed lower bonding strength than no treated group. The ceramic-zirconia bonding strength was affected by LTD (p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in LTD with treated Y-TZP groups.

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.3
• /
• pp.111-118
• /
• 1998

The intrinsic degradation behavior of $(V_{0.53}Ti_{0.47})_{0.925}Fe_{0.075}$ alloy with BCC structure and the two plateau regions (the low and high plateau region) has been investigate during the temperature-induced hydrogen absorption-desorption cycling (thermal cycling). After 400 thermal cycles between room temperature and $600^{\circ}C$ under 10atm $H_2$, the total reversible hydrogen absorption capacity decreased by about 40%. From thermal desorption analysis it was found that the degradation behavior at each plateau region was different. In addition, XRD analysis showed that the crystal structure of the sample in de-hydrided state was changed from BCC to BCT after degradation, and that of the sample in hydrided state it was maintained as FCC although peaks were broadened after degradation. From the result of static isothermal hydrogenation treatment it were found that crystal structure change from BCC to BCT was caused by the thermal energy. TEM analysis showed that the peak broadening was due to the formation of an amorphous phase in FCC matrix.

• Computers and Concrete
• /
• v.33 no.5
• /
• pp.605-619
• /
• 2024

The increase of reclaimed asphalt pavement (RAP) content in recycled asphalt concrete (RAC) is accompanied by the degradation of low-temperature cracking resistance, which has become an obstacle to the development of RAC. This paper aims to reveal the meso-scale mechanisms of the low-temperature fracture behavior of RAC and provide a theoretical basis for the economical recycling of RAP. For this purpose, micromechanical heterogeneous peridynamic model of RAC was established and validated by comparing three-point bending (TPB) test results against corresponding numerical simulation results of RAC with 50% RAP content. Furthermore, the models with different aggregate shapes (i.e., average aggregates circularity (${\bar{C_r}}=1.00$, 0.75, and 0.50) and RAP content (i.e., 0%, 15%, 30%, 50%, 75%, and 100%) were constructed to investigate the effect of aggregate shape and RAP content on the low-temperature cracking resistance. The results show that peridynamic models can accurately simulate the low-temperature fracture behavior of RAC, with only 2.9% and 13.9% differences from the TPB test in flexural strength and failure strain, respectively. On the meso-scale, the damage in the RAC is mainly controlled by horizontal tensile stress and the stress concentration appears in the interface transition zone (ITZ). Aggregate shape has a significant effect on the low-temperature fracture resistance, i.e., higher aggregate circularity leads to better low-temperature performance. The large number of microcracks generated during the damage evolution process for the peridynamic model with circular aggregates contributes to slowing down the fracture, whereas the severe stress concentration at the corners leads to the fracture of the aggregates with low circularity under lower stress levels. The effect of RAP content below 30% or above 50% is not significant, but a substantial reduction (16.9% in flexural strength and 16.4% in failure strain) is observed between the RAP content of 30% and 50%. This reduction is mainly attributed to the fact that the damage in the ITZ region transfers significantly to the aggregates, especially the RAP aggregates, when the RAP content ranges from 30% to 50%.