• 한국세라믹학회지
• /
• 제24권3호
• /
• pp.227-234
• /
• 1987

With the content of ZnO varing from 10.5 to 47.4 wt%, the crystallization of lithium zinc silicate glass was investigated by DTA, XRD, and SEM. In this work P2O5 was used as nucleation agent. The crystallization temperature was found to increase with the content of ZnO and the microstructure of formed crystalling phases was studied through the scanning electron microscopy. According to the XRD analysis, the crystal phases formed are summarized as follows. 1) The major phases are lithium orthosilicate, lithium disilicate and quartz at 10.5 wt% ZnO. 2) Lithium zinc silicate polymorphous and cristobalite occur in the composition varying 21.3 to 30.8 wt% ZnO. 3) At composition containing 47.4wt% ZnO some quantity of willemite is formed.

• The Journal of Advanced Prosthodontics
• /
• 제12권3호
• /
• pp.150-156
• /
• 2020

PURPOSE. The aim of this study was to evaluate the effect of different surface finishing processes on the color stabilities of lithium disilicate glass-ceramics, zirconia-reinforced lithium silicate ceramics, and resin nanoceramics after artificial ageing. MATERIALS AND METHODS. 216 samples were prepared from 3 different CAD/CAM materials (LAVA Ultimate, IPS e.max CAD, VITA Suprinity) with A1 HT color at a size of 14 × 12 mm and a thickness of 0.5 ± 0.05 mm. Color measurements of the samples were performed with a spectrophotometer using color parameters and CIE Lab color system on a gray backing between baseline color and after 5000 cycles of artificial ageing in 4 stages (i.e. the first measurement before the treatment, the second measurement after polishing, the third measurement after cement application, and the fourth measurement after artificial ageing). The results were evaluated using the Variance analysis and Fisher's LSD test. RESULTS. Resin nanoceramics (LU) exhibited higher color change values than zirconia-reinforced lithium silicate (VS) and lithium disilicate (EC) ceramics after artificial ageing. Manual polishing and glazing resulted in similar color change for LU and VS (P>.05). In the EC group, glazing provided statistically different results as compared to the manual polishing and control groups (P<.05). Among the ceramic groups, color change values of the subgroup, which was treated by glazing, of the zirconia-reinforced lithium silicate (VS) and lithium disilicate (EC) samples were below the clinically acceptable level (ΔE < 3.5). CONCLUSION. The lowest color change for all stages was observed in Vita Suprinity.

• The Journal of Advanced Prosthodontics
• /
• 제12권4호
• /
• pp.181-188
• /
• 2020

PURPOSE. The effect of core design on the fracture resistance of zirconia-lithium disilicate (LS2) bilayered crowns for anterior teeth is evaluated by comparing with that of metal-ceramic crowns. MATERIALS AND METHODS. Forty customized titanium abutments for maxillary central incisor were prepared. Each group of 10 units was constructed using the same veneer form of designs A and B, which covered labial surface to approximately one third of the incisal and cervical palatal surface, respectively. LS2 pressed-on-zirconia (POZ) and porcelain-fused-to-metal (PFM) crowns were divided into "POZ_A," "POZ_B," "PFM_A," and "PFM_B" groups, and 6000 thermal cycles (5/55 ℃) were performed after 24 h storage in distilled water at 37 ℃. All specimens were prepared using a single type of self-adhesive resin cement. The fracture resistance was measured using a universal testing machine. Failure mode and elemental analyses of the bonding interface were performed. The data were analyzed using Welch's t-test and the Games-Howell exact test. RESULTS. The PFM_B (1376. 8 ± 93.3 N) group demonstrated significantly higher fracture strength than the PFM_A (915.8 ± 206.3 N) and POZ_B (963.8 ± 316.2 N) groups (P<.05). There was no statistically significant difference in fracture resistance between the POZ_A (1184.4 ± 319.6 N) and POZ_B groups (P>.05). Regardless of the design differences of the zirconia cores, fractures involving cores occurred in all specimens of the POZ groups. CONCLUSION. The bilayered anterior POZ crowns showed different fracture resistance and fracture pattern according to the core design compared to PFM.

• 대한치과보존학회:학술대회논문집
• /
• 대한치과보존학회 2007년도 Autumn Scientific Meeting(the 128th) of Korean Academy of Comservative Dentistry
• /
• pp.645-645
• /
• 2007

• 한국세라믹학회지
• /
• 제18권3호
• /
• pp.163-170
• /
• 1981

The crystallization of $Li_2O-SiO_2$ system glasses and the effect of phase separtion to crystal nucleation were studied. The crystallization temperatures of various glasses were determined by DTA and glasses were nucleation heat treated at the temperatures ranging from 45$0^{\circ}C$ to 5$25^{\circ}C$. These glasses were thengown at $700^{\circ}C$ to observable size in the optical microscope. Crystal nucleation rates of various glasses were obtained by estimating the number of crystals per unit volume. The main crystal phase of these glasses identified by X-ray diffraction was lithium disilicate ($Li_2O$.$2SiO_2$). It was found that the crystal nucleation rate of glass (19.5% $Li_2P$-80.5% $SiO_2$), the nearest composition to lithium disilicate, was higher than other glasses. The opalescence caused by phase separation was observed in the nucleation heat treated glass (16.3% $Li_2O$-83.7% $SiO_2$). The result from nucleation density measurement of this glass indicated that the nucleation was enhanced during early stage of phase separation. The molphologies of crystals in glasses and crystal growth rate at $600^{\circ}C$ were also discussed.

• The Journal of Advanced Prosthodontics
• /
• 제14권2호
• /
• pp.78-87
• /
• 2022

PURPOSE. This study aimed to compare the effect of different surface treatments and luting agent types on the shear bond strength of two ceramics to commercially pure titanium (Cp Ti). MATERIALS AND METHODS. A total of 160 Cp Ti specimens were divided into 4 subgroups (n = 40) according to surface treatments received (control, 50 ㎛ airborne-particle abrasion, 110 ㎛ airborne-particle abrasion, and tribochemical coating). The cementation surfaces of titanium and all-ceramic specimens were treated with a universal primer. Two cubic all-ceramic discs (lithium disilicate ceramic (LDC) and zirconia-reinforced lithium silicate ceramic (ZLC)) were cemented to titanium using two types of resin-based luting agents: self-cure and dual-cure (n = 10). After cementation, all specimens were subjected to 5000 cycles of thermal aging. A shear bond strength (SBS) test was conducted, and the failure mode was determined using a scanning electron microscope. Data were analyzed using three-way ANOVA, and the Tukey-HSD test was used for post hoc comparisons (P < .05). RESULTS. Significant differences were found among the groups based on surface treatment, resin-based luting agent, and ceramic type (P < .05). Among the surface treatments, 50 ㎛ air-abrasion showed the highest SBS, while the control group showed the lowest. SBS was higher for dual-cure resin-based luting agent than self-cure luting agent. ZLC showed better SBS values than LDC. CONCLUSION. The cementation of ZLC with dual-cure resin-based luting agent showed better bonding effectiveness to commercially pure titanium treated with 50 ㎛ airborne-particle abrasion.

• 대한치과보철학회지
• /
• 제57권2호
• /
• pp.134-141
• /
• 2019

목적: 본 연구에서는 리튬 디실리케이트-지르코니아 이중도재관과 단일구조 지르코니아로 제작된 구치부 고정성 임플란트 지지 보철물의 2년간의 임상적 결과를 비교하고자 하였다. 대상 및 방법: 2015년에서 2018년 사이 부산대학교 치과병원에 내원하여 치료받은 총 17명의 환자(남성: 12, 여성: 5)를 대상으로 60개의 구치부 고정성 임플란트 지지 보철물을 제작하였다(LP. Lithium disilicate pressed zirconia prostheses: n = 30, MZ. Monolithic zirconia prostheses: n = 30) 보철물 제작 후 2년간의 추적 관찰을 통해 임플란트 생존율, 변연골 흡수량, 치주낭 깊이, 치태지수, 출혈지수, 치석지수 및 합병증을 평가하였다. 결과: 모든 임플란트가 기능적 문제와 동요도 없이 100%의 생존율을 보였다. 변연골 흡수량은 관찰 12개월에 LP군이 MZ군 보다 더 적었으며 (P < .05), 임상 검사시 관찰 12개월의 치주낭 깊이 및 치석 지수는 LP군에서 더 높았다 (P < .05). 주된 합병증으로 MZ군에서 7개에서 1.5 mm 이상의 골흡수가 관찰되었으며, LP군에서 2개의 chipping이 관찰되었다. 결론: 본 연구의 한계 내에서, 구치부 임플란트 지지 보철물에서 리튬 디실리케이트가 프레스된 지르코니아 보철물은 단일구조 지르코니아 보철물과 함께 예지성 있는 치료방법으로 판단된다.

• 구강회복응용과학지
• /
• 제22권2호
• /
• pp.149-159
• /
• 2006

Statement of problem. Porcelain repair mainly involves replacement with composite resin, but the bond strength between composite resin and all-ceramic coping materials has not been studies extensively. Purpose. The objective of this study was to investigate the influence of composite resin and ceramic etching pattern on shear bond strength of Empress2 ceramic and observe the change of microstructure of ceramic according to etching methods. Material and methods. Eighty-five cylinder shape ceramic specimens (diameter 5mm, IPS Empress 2 core materials) embeded by acrylic resin were used for this study. The ceramic were specimens divided into sixteen experimental groups with 5 specimens in each group and were etched with phosphoric acid(37%, 65%) & hydrofluoric acid (4%, 9%) according to different etching times(30s, 60s, 120s 180s). All etched ceramic surfaces were examined morphologically using SEM(scanning electron microscopy). Etched surfaces of ceramic specimens were coated with silane (Monobond-S) & adhesive(Heliobond) and built up composite resin using Teflon mold. Accomplished specimens were tested under shear loading until fracture on universal testing machine at a crosshead speed 1mm/min; the maximum load at fracture(kg) was recorded. Shear bond strength data were analyzed with one way ANOVA and Duncan tests.(P<.05) Results. Maximum shear bond strength was $30.07{\pm}2.41(kg)$ when the ceramic was etched with 4% hydrofluoric acid at 120s. No significant difference was found between phosphoric etchant group and control group with respect to shear bond strength. Conclusion. Empress 2 ceramic surface was not etched by phosphoric acid, but etched by hydrofluoric acid.

• The Journal of Advanced Prosthodontics
• /
• 제8권2호
• /
• pp.75-84
• /
• 2016

PURPOSE. To evaluate the effect of various surface treatments on the surface structure and shear bond strength (SBS) of different ceramics. MATERIALS AND METHODS. 288 specimens (lithium-disilicate, leucite-reinforced, and glass infiltrated zirconia) were first divided into two groups according to the resin cement used, and were later divided into four groups according to the given surface treatments: G1 (hydrofluoric acid (HF)+silane), G2 (silane alone-no heat-treatment), G3 (silane alone-then dried with $60^{\circ}C$ heat-treatment), and G4 (silane alonethen dried with $100^{\circ}C$ heat-treatment). Two different adhesive luting systems were applied onto the ceramic discs in all groups. SBS (in MPa) was calculated from the failure load per bonded area (in $N/mm^2$). Subsequently, one specimen from each group was prepared for SEM evaluation of the separated-resin-ceramic interface. RESULTS. SBS values of G1 were significantly higher than those of the other groups in the lithium disilicate ceramic and leucite reinforced ceramic, and the SBS values of G4 and G1 were significantly higher than those of G2 and G3 in glass infiltrated zirconia. The three-way ANOVA revealed that the SBS values were significantly affected by the type of resin cement (P<.001). FIN ceramics had the highest rate of cohesive failure on the ceramic surfaces than other ceramic groups. AFM images showed that the surface treatment groups exhibited similar topographies, except the group treated with HF. CONCLUSION. The heat treatment was not sufficient to achieve high SBS values as compared with HF acid etching. The surface topography of ceramics was affected by surface treatments.

• The Journal of Advanced Prosthodontics
• /
• 제13권1호
• /
• pp.36-45
• /
• 2021

Purpose. To investigate the fracture resistance of monolithic CAD-CAM all-ceramic surveyed crowns with two different occlusal rest seat designs. Materials and Methods. Two maxillary first premolar were prepared for all-ceramic surveyed crowns with wide (2/3rd of buccolingual width of an unprepared tooth) or narrow (1/3rd of buccolingual width of an unprepared tooth) disto-occlusal rest seat (ORS) designs. Eighty monolithic CAD-CAM all-ceramic surveyed crowns were prepared and divided into 4 groups - Group CR, Composite resin material as a control; Group LDS, Lithium disilicate based material; Group ZIPS, zirconia-material (IPS ZirCAD); and Group ZLHT, zirconia- material (CeramillZolidht+). Crowns were cemented on an epoxy resin die with adhesive resin cement. The fracture resistance of crowns was tested with the universal machine. Univariate regression analysis was used. Results. The mean ± standard deviation of maximum failure force values varied from 3476.10 ± 285.97 N for the narrow ORS subgroup of group ZIPS to 687.89 ± 167.63 N for the wide ORS subgroup of group CR. The mean ± standard deviation of maximum force was 1075 ± 77.0 N for group CR, 1309.3 ± 283.9 N for group LDS, 3476.1 ± 285.97 N for group ZIPS, and 2666.7 ± 228.21 N for group ZLHT, with narrow occlusal rest seat design. The results of the intergroup comparison showed significant differences in fracture strength with various material groups and occlusal rest seat designs (P<.001). Conclusion. The zirconia-based all-ceramic surveyed crowns fractured at more than double the load of Lithium disilicate based crowns. The crowns with narrow base occlusal rest seat design had statistically significantly higher fracture resistance than surveyed crowns with wide occlusal rest seat design. The use of narrow occlusal rest seat design in CAD-CAM all ceramic surveyed crowns provides higher fracture resistance, and therefore narrow occlusal rest design can be used for providing esthetics with high strength.