• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.228-231
• /
• 1999

The preparation and electrical properties of LIPON electrolyte were investigated in order to fabricate all solid state thin film battery. The LIPON thin film was deposited by r.f. sputtering of Li$_3$PO$_4$ target in O$_2$-N$_2$ mixtures. The LIPON deposited at N$_2$+10% O$_2$ ratio had a conductivity at 25 $^{\circ}C$ of 1.8${\times}$10$\^$-6/S/cm. The ion conductivity of the LIPON films decreased as the O$_2$ content of the process gas increased.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.4
• /
• pp.255-261
• /
• 1997

Thin film batteries can be used as a micro power source for electronic in which minute power is needed. In this study, lithium phosphorous oxynitride(LIPON) thin films were deposited as an eletrolyte for lithium ion batteries using RF magentron sputtering of lithium phosphate in N2. Ti was also added into the LIPON films as a second network former to enhance the ioinc conductivity of the films. The optimum conditions for LIPON film deposition were sought and the electrolyte with the conductivity of $2.5 \times 10^{-6}$S/cm was obtained at the condition of RF power 4.4 W/$\textrm{cm}^2$, process pressure 10 mtorr and pure nitrogen ambience. Furthermore, the conductivity of LIPON films was increased from $2.5 \times 10^{-6}$S/cm to $8.6 \times 10^{-6}$S/cm by the doping of 2.4at.% Ti. It was also found that by adding Ti to LIPON films, Li content was increased and nitrogen content that reported having the cross-linking effect on LIPON films was also increased as confirmed XPS.

• 한국전기화학회:학술대회논문집
• /
• 2001.04a
• /
• pp.37-37
• /
• 2001

• Journal of the Korean Electrochemical Society
• /
• v.3 no.1
• /
• pp.44-48
• /
• 2000

Amorphous $V_2O_5$ cathode thin films were prepared by DC-magnetron sputtering at room temperature and the thin film rechargeable lithium batteries were fabricated with the configuration of $V_2O_5/LIPON/Li$ using sequential ex-situ thin film deposition techniques. The electrochemical characteristics of $V_2O_5$ cathode materials Prepared at 80/20 of $Ar/O_2$ ratio showed high capacity and cycling behaviors by half cell test. LIPON solid electrolytes films were prepared by RF-magnetron sputtering using the self-made $Li_3PO_4$ target in pure $N_2$ atmosphere, and it was very stable for lithium contact in the range of 1.2-4.0 V vs. Li. Metallic lithium were deposited on LIPON electrolyte by thermal evaporation methode in dry room. Vanadium oxide based full cell system showed the initial discharge capacity of $150{\mu}A/cm^2{\mu}m$ in the range of $1.2\~3.5V$.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.4
• /
• pp.219-223
• /
• 2000

All-solid state lithium rechargeable thin film batteries were fabricated with the configuration of$Cu_{0.5}V_2O_5/Lipon/Li$ using sequential thin film techniques. Copper vanadium oxide thin films and Lipon thin films were prepared by DC reactive dual source magnetron sputtering and RF magnetron sputtering, respectively. According to XRD analysis, we found out that copper vanadium oxide thin films were amorphous. The electrochemical behaviour of them was examined in half cell system using EC : DMC(1:1 in IM $LiPF_5$) liquid electrolyte. The ionic conductivity of Lipon thin film was $1.02\times10^{-6}S/cm$ at $25^{\circ}C$ and $Cu_{0.5}V_2O_5/Lipon/Li$ cell showed that the discharge capacity was about $50{\mu}Ah/cm^2{\mu}m$ beyond 500cyc1es.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.100-104
• /
• 2008

Titanium sheet metal substrates used in thin film batteries were wet etched and their surface area was increased in order to increase the discharge capacity and power density of the batteries. To obtain a homogeneous etching pattern, we used a conventional photolithographic process. Homogeneous hemisphere-shaped wells with a diameter of approximately $40\;{\mu}m$ were formed on the surface of the Ti substrate using a photo-etching process with a $20\;{\mu}m{\times}20\;{\mu}m$ square patterned photo mask. All-solid-state thin film cells composed of a Li/Lithium phosphorous oxynitride (Lipon)/$LiCoO_2$ system were fabricated onto the wet etched substrate using a physical vapor deposition method and their performances were compared with those of the cells on a bare substrate. It was found that the discharge capacity of the cells fabricated on wet etched Ti substrate increased by ca. 25% compared to that of the cell fabricated on bare one. High discharge rate was also able to be obtained through the reduction in the internal resistance. However, the cells fabricated on the wet etched substrate exhibited a higher degradation rate with charge-discharge cycling due to the nonuniform step coverage of the thin films, while the cells on the bare substrate demonstrated a good cycling performance.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.4
• /
• pp.181-185
• /
• 2005

Lithium cobalt oxide thin film cathode, having thickness of $2.9{\mu}m$ with area of $4cm^2$, was deposited on platinum patterned alumina substrate by radio frequency magnetron sputtering. Li/Co molar ratio, which is an important factor for battery performance, was measured as a function of argon working pressure and applied R.F. power. Constant current charge and discharge performances were characterized with high rate discharge and cycling behavior. Using AC impedance analysis, internal resistance of the thin film battery was measured and simulated by proposed equivalent circuit model.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.100-105
• /
• 2001

An all solid-state thin film battery (TFB) was fabricated by growing, undoped and Pt-doped vanadium oxide cathode film ( $V_2$ $O_{5}$ ) on I $n_2$ $O_3$: Sn coated glass, respectively. Room temperature charge-discharge measurements based on Li/Lipon/ $V_2$ $O_{5}$ full-cell structure with a constant current clearly shows that the Pt-doped $V_2$ $O_{5}$ cathode film is superior, in terms of cyclibility. X-ray diffraction (XRD) results indicate that the Pt doping process induces a more random amorphous structure than an undoped $V_2$ $O_{5}$ film. In addition to its modified structure, the Pt-doped $V_2$ $O_{5}$ film has a smoother surface than the undoped sample. Compared to an undoped $V_2$ $O_{5}$ film, the Pt doped $V_2$ $O_{5}$ cathode film has a higher electron conductivity. We hypothesize that the addition of Pt alters electrochemical performance in a manner of making more random amorphous structure and gives an excess electron by replacing the $V^{+5}$. Possible mechanisms are discussed for the observed Pt doping effect on structural and electrochemical properties of vanadium oxide cathode films, which are grown on I $n_2$ $O_3$: Sn coated glass.