• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.9 no.2
• /
• pp.163-170
• /
• 1997

Solubility on $(LiBr+CaCl_2)$ in water has been measured systematically and compared with those of pure LiBr. It has been observed that there exists optimum value of $CaCl_2(LiBr+CaCl_2)$ in solubility when total$(LiBr+CaCl_2)$ concentration is higher than 57wt%. As total concentration increases up to 65wt%, it is found that the optimum value also increases monotonically. From the experimental results, a master plot has been constructed, with which optimum ratio of LiBr to $CaCl_2$ can be found in terms of total concentration. Vapor pressure of $H_2O/(LiBr+CaCl_2)$ solution with optimum contents of $CaCl_2$ has been observed to be changed negligibly at relatiely low temperature. However, as temperature increases, it is found that increasement in vapor pressure is significant.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.503-508
• /
• 2005

A simple and effective method for the synthesis of LiMn$_{2}$O$_{4}$ powder as a cathode material for lithium secondary battery is reported. Micrometer size LiMn$_{2}$O$_{4}$ was prepared by combustion synthesis technique employing initial mixture of l.l LiNO$_{3}$ -1.3Mn-0.7MnO$_{2}$-1NaCl composition. Parametric study of the combustion process including molar ratio of Mn/MnO$_{2}$ and NaCl concentration were carried out under air atmosphere. The combustion products obtained were additionally heat treated at the temperature 900$^{\circ}C$ and the washed by distilled water. The results of charging-discharging characteristics revealed that LiMn$_{2}$O$_{4}$ cell synthesized in the presence of NaCl had a high capacity and much better reversibility than one formed without NaCl An approximate chemical mechanism for LiMn$_{2}$O$_{4}$ formation is proposed.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2009.11a
• /
• pp.346-346
• /
• 2009

산화물 형태 사용후핵연료의 효율적 처분 혹은 재활용을 위한 연구 가운데, 고온의 LiCl 용융염 중에서 전해환원하여 금속으로 환원시킨 후, 환원된 금속을 고온의 LiCl-KCl 용융염에서 전해정련하는 연구가 국내외적으로 활발하게 진행되고 있다. 전해환원을 위해 일정 농도 $Li_2O$가 LiCl 용융염에 첨가되며 $Li_2O$ 농도가 높으면 반응 재질의 부식성이 크게 증가하므로 일반적으로 우라늄 산화물은 1wt% 이하의 $Li_2O$ 농도에서 전해환원 된다. 우라늄 산화물의 전해환원 전위는 $Li_2O$의 전해환원 전위 보다 표준 상태를 기준으로 공정온도인 650 $^{\circ}C$ 에서 약 70 mV 정도 낮기 때문에 전해환원 과정에서 $Li_2O$ 의 환원으로 Li 금속이 생성될 가능성이 있으며 우라늄 산화물은 대부분 직접 전해환원 되지만 일부 Li에 의해 화학적으로 환원되기도 한다. 전해환원 공정에서 환원되지 않은 희토류 산화물은 전해정련 공정에서 $UCl_3$와 반응하여 $UO_2$를 생성시켜 공정 효율을 떨어뜨린다. 따라서 전해환원 공정에서 가능하연 최대한 희토류 산화물을 금속으로 환원시키는 조건을 찾아내는 것이 바람직하고 이를 위해서 우선 전해환원 공정에서 희토류 산화물의 화학적 거동의 이해가 요구된다. 본 연구에서 열역학적 검토를 통하여 희토류 산화물의 환원 조건을 조사한 결과 희토류 산화물은 매운 낮은 $Li_2O$ 농도에서 Li에 의해 환원되고, 1wt% 이하의 $Li_2O$ 농도에서는 Sc와 Lu의 산화물이 $Li_2O$와 복합산화물을 형성하고 이들 복합산화물은 Li에 의해 환원되지 않는 것으로 나타났다. 또한 희토류 원소 별로 희토류 원소 산화물의 Li에 의한 환원 조건으로서 평형상태에서의 $Li_2O$ 농도 즉 환원 임계 $Li_2O$ 농도를 실험적으로 측정하였으며 1wt% $Li_2O$ 농도 이하에서 열역학적 해석과 동일하게 Sc와 Lu만이 복합산화물을 형성하여 Li에 의해 직접환원 되지 않는 것으로 관찰되었다.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2002.10a
• /
• pp.318-318
• /
• 2002

• Proceedings of the Korean Nuclear Society Conference
• /
• 2002.10a
• /
• pp.338.1-338
• /
• 2002

• Journal of Electrochemical Science and Technology
• /
• v.13 no.2
• /
• pp.279-291
• /
• 2022

In this report the thermochemical conversion of Sm₂O₃ to SmCl₃ using AlCl₃ in LiCl-KCl melt at 773 K is discussed. The final product was a mixture of SmCl₃, Al₂O₃, unreacted Sm₂O₃ and AlCl₃ in the chloride melt. The electrochemical attributes of the mixture was analyzed with cyclic voltammetry (CV) and square wave voltammetry (SWV). The crystallographic phases of the mixture were studied with X-ray diffraction (XRD) technique. The major chemical conversion was optimized by varying the effective parameters, such as concentrations of AlCl₃, duration of reaction and the amount of LiCl-KCl salt. The extent of conversion and qualitative assessment of efficiency of the present protocol were evaluated with fluorescence spectroscopy, UV-Vis spectrophotometry and inductively coupled plasma atomic emission spectroscopy (ICP-AES) studies of the mixture. Thus, a critical assessment of the thermochemical conversion efficiency was accomplished by analysing the amount of SmCl₃ in LiCl-KCl melt. In the process, a conversion efficiency of 95% was achieved by doubling the stoichiometric requirement of AlCl₃ in 50 g of LiCl-KCl salt. The conversion reaction was found to be very fast as the reaction reached equilibrium in 15 min.

• Korean Chemical Engineering Research
• /
• v.55 no.3
• /
• pp.379-384
• /
• 2017

An electrochemical reduction of a mixture of NiO and rare earth oxides has been conducted to increase the reduction degree of rare earth oxides. Cyclic voltammetry (CV) measurement was carried out to determine the electrochemical reduction behavior of the mixed oxide in molten LiCl medium. Constant voltage electrolysis was performed with various supplied charges to understand the mechanism of electrochemical reduction of the mixed oxide as a working electrode. After completion of the electrochemical reduction, crystal structure of the reaction intermediates was characterized by using an X-ray diffraction method. The results clearly demonstrate that the rare earth oxide was converted to RE-Ni intermetallics via co-reduction with NiO.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.1 no.1
• /
• pp.25-39
• /
• 2003

This study proposed a new electrolytic reduction technology that is based on the integration of simultaneous uranium oxide metallization and Li$_2$O electrowinning. In this electrolytic reduction reaction, electrolytically reduced Li deposits on cathode and simultaneously reacts with uranium oxides to produce uranium metal showing more than 99% conversion. For the verification of process feasibility, the experiments to obtain basic data on the metallization of uranium oxide, investigation of reaction mechanism, the characteristics of closed recycle of Li$_2$O and mass transfer were carried out. This evolutionary electrolytic reduction technology would give benefits over the conventional Li-reduction process improving economic viability such as: avoidance of handling of chemically active Li-LiCl molten salt increase of metallization yield, and simplification of process.

• Membrane Journal
• /
• v.12 no.2
• /
• pp.75-89
• /
• 2002

The effect of addition of inorganic salts in polyethersulfone (PES) polymer solution on the membrane formation and ultrafiltartion performance was studied through the thermodynamic and kinetic properties of casting solution. To control the thermodynamic and kinetic properties of casting solution, various inorganic salts $[CaC1_2, LiCl, LiClO_4, ZnC1_2 $and Mg(ClO_4)_2]$ were added in the PES/NMP solution. Variation of membrane morphology and performance of the resulting membranes with change of the salt type and content added in tasting solution were discussed using viscosity, coagulation value, light transmittance measurement, overall membrane porosity, ultrafiltration experiment and cross-sectional SEM image. For all kind of inorganic salts, according as increase of the salt content in casting solution, viscosity is increased, coagulation value becomes lower, top layer thickness below the skin surface is increased, bovine serum albumin(BSA) rejection decreased and pure water flux is increased except $CaC1_2$ and LiCl. In case of $CaC1_2$ and LiCl, it is found that when the salt content is increased, the formation of macrovoids is suppressed and the precipitation rate becomes slow while instantaneous demixing of precipitation type is maintained. However, in case of $LiClO_4$ and $Mg(ClO_4)_2,$ it is found that precipitation rate becomes faster.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.165-165
• /
• 2003