• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.2013-2015
• /
• 2005

In this paper, Effect of $BaSrTiO_3/Li_2CO_3$ on low temperature sintering and dielectric property of thick films has been investigated for variable capacitor on high frequency. The thick films were fabricated by the tape casting and then the structural and dielectric properties as a function of an addition composition ratio and sintering temperature were studied. For the thick film sintered at $1050^{\circ}C$, it was densified to 96% of $BaSrTiO_3$ theoretical density by the addition of 10 $wt{\cdot}%$ $BaSrTiO_3/Li_2CO_3$. Dielectric constant increased and Curie temperature lowered with the increased of $BaSrTiO_3/Li_2CO_3$ content, which probably can be explained by the substitution of $Ba^{3+},Li^{1+}$ on $RaTiO_3$ lattice. The tunability and dielectric loss of the $BaSrTiO_3/Li_2CO_3$ thick film, sintered at $1350^{\circ}C$, were about 26% and 0.234 at $10{\sim}15MHz$, respectively.

• Journal of the Institute of Electronics and Information Engineers
• /
• v.49 no.10
• /
• pp.128-134
• /
• 2012

The performance evaluation and fabrication of integrated-optic electric-field sensor utilizing $Ti:LiNbO_3$ asymmetric Mach-Zehnder intensity modulator with a push-pull lumped electrode and a plate-type probe antenna to measure an electric field strength is described. The modulator has a small device size of $46{\times}7{\times}1\;mm$ and operates at a wavelength $1.3{\mu}m$. The devices are simulated based on the BPM software and fabricated utilizing Ti-diffused $LiNbO_3$ channel optical waveguides. The minimum detectable electric field is 1.02 V/m and 6.91 V/m, corresponding to a dynamic range of ~35 dB and ~10 dB at the frequencies of 500 KHz and 5 MHz, respectively.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.7
• /
• pp.109-116
• /
• 1998

In this work was produced and analyzed a z-cut Ti:LiNbO$_{3}$ optical waveguide which applies for various optical devices.A waveguide channel with a thickness 8 .mu.m and a length 66,000.mu.m and a mach-zehnder interferometer type waveguide were fabricated at a diffusion temperature 1050.deg. C for 6-8hours in a wet $O_{2}$ environment. The resulting Ti:LiNbO$_{3}$ optical waveguide was measured to have a Ti-strip thickness of 950.angs. and low loss. Surfaces and cross-sections of a fabricated waveguide were analysed. The mode pattern anaysis revealed that the waveguide showed a single mode at a 1550nm wavelength. The effective dimension of the waveguide was calculated by measuring a gaussian profile; Wx=10.95.mu. and Wy=9.14.mu.m. a propagation loss, of 0.50dB/cm for a TM mode and 0.45dB/cm for a TE mode, was low enough to be accepatable for optical devices.

• Proceedings of the KAIS Fall Conference
• /
• 2000.10a
• /
• pp.173-177
• /
• 2000

인산염계 5Li₂O, 36CaO, 20TiO₂, 27P₂O/sub 5/의 조성을 선정하여 10K/min 승온속도로 1300℃에서 2시간동안 유지시켜 모유리를 제조하였고, 최적의 핵형성을 위해 610℃에서 20시간, 최고 결정성장을 위해 840℃에서 20시간 동안 열처리함으로써 LiTi₂(PO₄)₃상과 β-Ca₃(PO₄)₂결정상이 존재하는 Glass Ceramics를 제조하였고, 이를 1N-HCI용액에서 3일간 담지하여 β-Ca₃(PO₄)₂결정상을 용출시켜 LiTi₂(PO₄)₃상만이 존재하는 다공성 Glass Ceramics를 제조하였다.

• Electrical & Electronic Materials
• /
• v.10 no.7
• /
• pp.682-691
• /
• 1997

We have investigated the guided optical properties of a Ti:LiNbO$_3$optical waveguide which was fabricated by Ti-diffusion in an air atmosphere and proposed an effective polishing method of waveguide endfaces. And the results of guided optical mode and fabrication condition were obtained as follows; \circled1 propagation loss : 0.53 dB/cm \circled2 mode size : horizontal/vertical=12.5${\mu}{\textrm}{m}$ \circled3 mode mismatch : 1.7 dB \circled4 diffusion temperature : 105$0^{\circ}C$, time : 8 hours \circled5 atmosphere : air

• Journal of the Korean Electrochemical Society
• /
• v.13 no.4
• /
• pp.235-239
• /
• 2010

The $Li_4Ti_5O_{12}$/CNT composite is prepared by ultrasound associated sol-gel method. The prepared composite is characterized by SEM, TEM, XRD and TG analysis, and their electrochemical behaviors are investigated by cyclic voltammetry, electrochemical impedance spectroscopy and charge-discharge test in 1M $LiBF_4$/PC electrolyte. From the results, it is identified that the $Li_4Ti_5O_{12}$ nanoparticles coated on CNT surface have regular size with around 10~30 nm and spinel-framework structure. At the current rate of 20C, the discharge capacities of $Li_4Ti_5O_{12}$/CNT composites with CNT contents of 15, 30 and 50 wt% are 57, 63 and $48mAhg^{-1}$, respectively, which have similar value. The improved electrochemical behavior of the $Li_4Ti_5O_{12}$/CNT composite electrode is attributed to the addition of CNT with electronic conductivity.

• Journal of Electrochemical Science and Technology
• /
• v.1 no.1
• /
• pp.63-68
• /
• 2010

The $Li_4Ti_5O_{12}$/AC composite was prepared by sol-gel process with ultrasonication. The prepared composite was characterized by SEM, XRD and TG analysis, and their electrochemical behaviors were investigated by cyclic voltammetry, electrochemical impedance spectroscopy and charge-discharge test in 1M $LiBF_4$/PC electrolyte. From the results, the $Li_4Ti_5O_{12}$ particles coated on AC surface had an average particle size of 100 nm and showed spinel-framework structure. When the potential range of the $Li_4Ti_5O_{12}$/AC composite was extended from 0.1 to 2.5 V, redox peaks and electric double layer property were revealed. The initial discharge capacity of $Li_4Ti_5O_{12}$/AC composite was 218 mAh $g^{-1}$ at 1 C. The enhancement of discharge capacity was attributed to electric double layer of added activated carbon.

• Journal of Electrical Engineering and Technology
• /
• v.7 no.2
• /
• pp.207-211
• /
• 2012

Spinel-$Li_4Ti_5O_{12}$ was successfully synthesized by a solid-phase method at 800, 850, and $900^{\circ}C$ according to the $Li_4Ti_5O_{12}$ cubic spinel phase structure. To achieve higher EDLC energy density with the $Li_4Ti_5O_{12}$, the negative electrode of the hybrid supercapacitor was studied in this work. The electrochemical performances of the hybrid supercapacitor and EDLC were characterized by constant current discharge curves, c-rate, and cycle performance testing. The capacitance (1st cycle) of the hybrid supercapacitor and EDLC was 209 and 109 F, respectively, which is higher than EDLC. The capacitance of the hybrid supercapacitor decreases from 209 F to 101 F after 20 cycles when discharged at several specific current densities ranging from 1 to 10 A. In contrast, capacitance of the EDLC hardly decreases after 20 cycles. Results show that hybrid supercapacitor benefits from the high rate capability of supercapacitor and high capacity of the battery. Findings also prove that the hybrid supercapacitor is an energy storage device where the supercapacitor and the Li ion secondary battery coexist in one cell system.

• Korean Journal of Optics and Photonics
• /
• v.2 no.3
• /
• pp.149-152
• /
• 1991

We report a new method of fabricating a Ti:LiNb03 waveguide with no out-diffusion by coating the waveguide with $SiO_2$ thin film. It was coated before diffusion process, and the $LiO_2$ out-diffusion was prevented in the diffusion process. We compare the near field patterns of the guided modes between the typical waveguide and the waveguide fabricated by new method proposed here.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.930-935
• /
• 2004

$({Li}_{0.5}0{La}_{0.5}){TiO}_3$ (LLTO) solid electrolyte was grown on LiCo{O}_2 (LCO) cathode films deposited on $Pt/Ti{O}-2/Si{O}_2/Si$ substrate using pulsed laser deposition for all-solid-state lithium microbattery. LLTO solid electrolyte exhibits an amorphous phase at various deposition temperatures. LLTO films deposited at 10$0^{\circ}C$ showed a clear interrace without any chemical reaction with LCO, and showed an initial discharge capacity of 50 $\mu$Ah/cm$^2$-$\mu$m and capacity retention of 90 % after 100 cycles with Li anode in 1mol$ LiCl{O}_4$ in propylene carbonate (PC). The increase of capacity retention in LLTO/LCO structure than LCO itself was attributed to the structural stability of LCO cathode films by the stacked LLTO. The cells of LLTO/LCO with LLTO grown at $100^{\circ}C$ showed a good cyclic property of 63.6 % after 300 cycles. An amorphous LLTO solid electrolyte is possible for application to solid electrolyte for all-solid-state lithium microbattery.