• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.7
• /
• pp.112-119
• /
• 2009

The purpose of this study is to evaluate the evaluation of process yield performed by using Sn & Cu treatment on the surface to optimize process condition for Lead-free solder application. The materials which are used for the New Surface Treatment study are Semi-Dulling plating for high speed Sn/Cu alloy of Soft Alloy GTC-33 Pb free known as "UEMURA Method" and plating substrate is alloy 42.Especially in lead-free plating process, it is important to control plating thickness and Copper composition than Sn/Pb plating. Evaluated and controlled plating thickness $12{\pm}3um$, Copper composition $2{\pm}1%$, plating particle and visual inspection. The optimization of these parameters and condition makes it makes possible to apply Sn/Cu Lead-free solder from Sn/Pb alloy.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.481-486
• /
• 2002

We have investigated the effects of plating materials for Cu lead (Sn-lOPb, AwPdJNi, Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu) on properties of QFP joints using a Sn-8Zn-3Bi solder. The results were compared with the joints using Sn-3. 5Ag-0. 7Cu and Sn-37Pb solders. As a result, the joints with the Sn-3.5Ag, Sn-3Bi and Sn-0.7Cu plated Cu lead had the reliability comparable to those of the Sn-3.5Ag-0.7Cu and Sn-37Pb soldered joints with respect to the joint strength after the high temperature holding tests at 348K to 423k. In particular, the joint with the Sn-3.5Ag plated Cu lead had the best reliability. This is caused by the low growth rate of a Cu-Sn interfacial reaction layer that degrades the joint strength of the soldered joints. Consequently, the Sn-3.5Ag plating was found to be most feasible plating for the Sn-8Zn-3Bi soldered joint.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.1337-1342
• /
• 2008

The whisker grows at the plating of a lead frame so that it causes the serious problem like the short. To prove this case, many people have studied the cause and influence of the tin whisker growth. This study explains the grain size affects the growth of the whisker in the lead frame. By these studies about the whisker, the whisker growth is discovered by stresses generated by the intermetallic compound and CTE mismatch in both plating and base metal. The stresses or lattice defect generated in the plating process changes grain structure of plating. Consequently, these various stresses are stabilized by forming unspecified whiskers through lots of grain boundaries. Because the grain boundary is the path of the whisker growth, the smaller grain size exists, the more whiskers grow.

• Journal of the Korean institute of surface engineering
• /
• v.19 no.3
• /
• pp.92-108
• /
• 1986

An electroplating on the lead frame fabricated from domestic copper plate was studied experimentally. In this study, nickel was plated on the thin copper lead frame and silver layer was coated on the nickel film in the cyanide electrolyte. The effect of process variables such as current density, plating time, coating thickness and flow rate of electrolytic solution on the properties of coating was investigated. Some samples on each step were fabricated during electroplating. The results obtained from polarization measurement, observation of SEM photograph, adhesion test of coating and microhardness test are as follows. On silver plating, polarization resistance of potentiostatic cathodic polarization curve is reduced as the flow rate of Ag electrolytic solution increases. And above resistance is also reduced when the minor chemicals of sodium cyanide and sodium carbonate are added in potassium silver cyanide bath. The reduced polarization resistance makes silver deposition on the cathode easy. An increase in the current density and the coating thickness causes the particle size of deposit to coarsen, and consequently the Knoop microhardness of the coating decreases. On selective plating an increase in the flow rate of plating solution lead to do high speed plating with high current density. In this case, the surface morphology of deposit is of fine microstructure with high Knoop hardness. An increasing trend of the adhesion of coating was shown with increasing the current density and flow rate of electrolytic solution.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.211-213
• /
• 1999

In the future, restrictions are likely to be imposed on the use of lead in the electronics industry. In dealing with such a move, we have been developing Pb-free Sn-Ag plating process to replace presently available Sn-Pb process. In this paper, the result of a basic comparison test between Sn-Pb plating and Sn-Ag plating is reported.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.3 s.32
• /
• pp.1-7
• /
• 2004

Tin plating on component finishes may grow whiskers under certain conditions, which may cause failures in electronics equipment. To protect the environment, 'lead-free' among component finishes is being promoted worldwide. This paper presents the evaluation results of whiskers on two kinds of lead-free plating materials at the plating temperature and under the reliability test. The rising plating temperature caused increasing the size of plating grain and shorting the growth of whisker. The whisker was grown under the temperature cycling the bent type in matt Sn plating and striated type in malt Sn-Bi. The whisker growth in Sn-Bi plating was shorter than that in Sn plating. In FeNi42 leadframe, the $7.0{\~}10.0{\mu}m$ diameter and the $25.0{\~}45.0{\mu}m$ long whisker was grown under 300 cycles. In the 300 cycles of Cu leadframe, only the nodule(nuclear state) grew on the surface, and in the 600 cycles, a $3.0{\~}4.0{\mu}m$ short whisker grew. After 600 cycles, the ${\~}0.34{\mu}m$ thin $Ni_3Sn_4$ formed on the Sn-plated FeNi42. However, we observed the amount of $0.76{\~}1.14{\mu}m$ thick $Cu_6Sn_5$ and ${\~}0.27{\mu}m$ thin $Cu_3Sn$ intermetallics were observed between the Sn and Cu interfaces. Therefore, the main growth factor of a whisker is the intermetallic compound in the Cu leadframe, and the coefficient of thermal expansion mismatch in FeNi42.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.10a
• /
• pp.15-15
• /
• 1999

In chip plating, several parameters must be taken into consideration. Current density, solution concentration, pH, solution temperature, components volume, chip and media ratio, barrel geometrical shape were most likely found to have an effect to the process yields. The 3 types of barrels utilized in chip plating industry are the conventional rotating barrel. vibrational barrel (vibarrel), and the centrifugal type. Conventional rotating barrel is a close type and is commonly used. The components inside the barrel are circulated by the barrel's rotation at a horizontal axis. Process yield has known to have higher thickness deviation. The vibrational barrel is an open type which offers a wide exposure to electrolyte resulting to a stable thickness deviation. It rotates in a vertical axis coupled with multi-vibration action to facilitate mixed up and easy transportation of components, The centrifugal barrel has its plated work centrifugally compacted against the cathode ring for superior electrical contact with simultaneous rotary motion. This experiment has determined the effect of barrel vibration intensity to the plating thickness distribution. The procedures carried out in the experiment involved the overall plating process., cleaning, rinse, Nickel plating, Tin-Lead plating. Plating time was adjusted to meet the required specification. All other parameters were maintained constant. Two trials were performed to confirm the consistency of the result. The thickness data of the experiment conducted showed that the average mean value obtained from higher vibrational intensity is nearer to the standard mean. The distribution curve shown has a narrower specification limits and it has a reduced variation around the target value, Generally, intensity control in vi-barrel facilitates mixed up and easy transportation of components, However, it is desirable to maintain an optimum vibration intensity to prevent solution intrusion into the chips' internal electrode. A cathodic reaction can occur in the interface of the external and internal electrode. $2HD{\;}+{\;}e{\;}{\rightarrow}20H{\;}+{\;}H_2$ Hydrogen can penetrate into the body and create pressure which can cause cracks. At high intensity, the chip's motion becomes stronger, its contact between each other is delayed and so plating action is being controlled. However, the strong impact created by its collision can damage the external electrode's structure thereby resulting to bad plating condition. 1 lot of chip was divided into two equal partion. Each portion was loaded to the same barrel one after the other. Nickel plating and tin-lead plating was performed in the same station. Portion A maintained the normal barrel vibration intensity and portion B vibration intensity was increased two steps higher. All other parameters, current, solution condition were maintained constant. Generally, plating method find procedures were carried out in a best way to maintained the best plating condition. After plating, samples were taken out from each portion. molded and polished. Plating thickness was investigated for both. To check consistency of results. 2nd trial was done now using different lot of another characteristics.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.107-107
• /
• 2003

• Applied Chemistry for Engineering
• /
• v.17 no.4
• /
• pp.343-348
• /
• 2006

The object of this experiment is to recover precious metals from plating rinsed wastewater generated from Lead Frame manufacturing process using electrolysis coupled hybrid process. This was achieved from Amberlite IRA 400 at 1.15 V electrolysis potential using the oxide electrode and at 1.30 V using the Al electrode and from Amberlite IRA 402 at 1.10 V using the oxide electrode and at 1.20 V using the Al electrode. During the first 10~30 min of the process, 90~95% of the silver can be recovered.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.2
• /
• pp.29-32
• /
• 2013

The surface roughness and reflectivity of electroless-plated Sn-3.5 wt%Ag on a LED (light emitting diode) lead frame were investigated. Cu electroplating was carried out prior to electroless plating of Sn-3.5Ag to improve the reflectivity of the Sn-3.5Ag deposit. In order to investigate the effect of stirring speed and temperature of the plating solution, surface roughness and reflectivity was measured. The experimental results revealed that the thickness of the deposit layer increased with stirring speed and temperature of the plating solution. Stirring speed is increased from 100 to 300 rpm, the surface roughness was reduced from 0.513 to 0.266 ${\mu}m$, and the reflectivity increased from 1.67 to 1.84 GAM. As temperature of the plating solution increased from 25 to $45^{\circ}C$, the surface roughness reduced from 0.507 to 0.350 ${\mu}m$, and the reflectivity increased from 1.68 to 1.84 GAM.