• 한국농공학회논문집
• /
• 제50권6호
• /
• pp.49-60
• /
• 2008

This study were predicted the corrosion threshold reached at steel reinforcement in latex modified concrete(LMC) which were applied the agricultural hydraulic concrete structures. Accelerated testing was accomplished to the evaluate the diffusion coefficient of LMC mix, and the time dependent constants of diffusion. Also, the average chloride diffusion coefficient was estimated. From the average chloride ion diffusion coefficient, the time which critical chloride contents at depth of reinforcement steel was estimated. Test results indicated that the corrosion threshold reached at reinforcement in LMC were effected on the mix proportion factor including cement contents, latex content, and water-cement ratio. Especially, the average chloride diffusion coefficient, the corrosion threshold reached at reinforcement in LMC were affected by the all mix proportion factor.

• 자원리싸이클링
• /
• 제15권2호
• /
• pp.10-17
• /
• 2006

본 연구에서는 고로슬래그 미분말 혼입률에 따른 라텍스개질 콘크리트의 역학적 특성과 내구성에 관한 기초물성을 평가하였다. 이를 위해 라텍스 혼입률 변화(0%, 10%, 15%)와 고로슬래그 혼입률 변화(0%, 30%)를 실험변수로 하였으며, LMC와 BS-LMC의 특성분석을 위하여 압축강도, 휨강도 그리고 내약품성 시험을 실시하였다. 실험결과, 압축강도와 청강도에서 고로슬래그 미분말 혼입이 장기재령에서 강도 증진효과를 나타내는 것으로 평가되었다. 특히 라텍스 혼입률 10%이상에서의 고로슬래그 미분말의 사용은 매우 타당한 것으로 나타났다. 라텍스 혼입률 10%와 고로슬래그 미분말 혼입률 30%에서 BS-LMC의 투수저항성은 재령 90일에서 매우 높은 것으로 나타났다. 또한 고로슬래그 미분말이 OPC 및 LMC에 혼입되면 투수저항성 및 화학저항성의 향상을 가져오는 것으로 나타났다.

• 콘크리트학회논문집
• /
• 제14권3호
• /
• pp.299-306
• /
• 2002

본 연구에서는 기존 교량의 신속한 유지보수를 위한 교면포장 덧씌우기용 라텍스개질 초속경 콘크리트를 개발하고자 하였다. 실험변수로는 국내 생산 초속경 시멘트를 이용하여 혼화제 인자로 라텍스 및 소포제 혼입률 변화를 선정하여 작업성, 강도발현 및 투수 특성을 고찰하고자 한다. 실험결과 동일 물-시멘트비 조건에서의 라텍스 혼입은 콘크리트의 슬럼프를 증대시켜 작업성을 유지하기 위한 단위수량을 감소시키는 것으로 나타났다. 소포제를 혼입하지 않을 때는 공기량이 8~9%로 나타났으나, 소포제를 1.6~3.2% 혼입함으로써 공기량이 2.0~3.8%로 감소되었으며, 이로 인해 압축강도가 10~20%정도 증진하였다. 라텍스의 양이 증가함에 따라 콘크리트의 휨강도는 증진되나, 압축강도는 다소 저하되었다. 그러나, 소포제의 혼입으로 타설 후 3시간 만에 교통개방을 위한 압축강도와 휨강도를 얻을 수 있었다. 라텍스를 일정량 이상 첨가할 경우 콘크리트를 불투수성의 재료로 평가할 수 있을 정도의 낮은 통과전하량을 나타내었다. 따라서 라텍스 개질 초속경 콘크리트는 구조물, 교량 포장의 덧씌우기 또는 보수재료로서 사용되어 질 수 있을 것으로 사료된다.

• 대한토목학회논문집
• /
• 제34권6호
• /
• pp.1743-1751
• /
• 2014

라텍스 첨가는 콘크리트의 압축 및 휨거동, 부착강도, 염화물 저항성 및 동결융해 저항성의 향상을 유도할 수 있는 것으로 알려져 있다. 이러한 이유로, 기존 포장 콘크리트 보다 LMC에 관한 많은 연구가 진행되고 있다. 그러나 소음이나 공사비용등을 비롯한 문제점 때문에 LMC의 성능을 향상시키기 위한 새로운 방법들이 시도되고 있으며, 최근, LMC의 문제점을 해결하고자 레미콘 LMC가 개발되었다. 본 연구에서는 레미콘 LMC의 내구성을 라텍스와 광물질 첨가제의 혼입 비율에 따라 비교하였다. 실험결과, 레미콘LMC는 압축강도, 휨강도, 부착강도가 한국 도로공사 전문 시방서 기준을 만족하였으며, 레미콘LMC의 내구성은 우수한 것으로 나타났다. 또한, 레미콘LMC에 라텍스를 8% 이상 혼입해야 기존 LMC와 동등 이상의 내구성을 확보하는 것으로 나타났다.

• Advances in concrete construction
• /
• 제15권6호
• /
• pp.431-444
• /
• 2023

This study investigated the use of latex-modified sand concrete reinforced with sisal fibers (LMSC) as a repair material. Notably, no prior research has explored the application of LMSC for this purpose. This paper examines the interface bond strength and the type of failure between LMSC as a repair material and the normal concrete (NC) substrate utilising four different surfaces: without surface preparation as a reference (SR), hand hammer (HA), sandblasted (SB), and grooved (GR). The bond strength was measured by bi-surface shear, splitting tensile, and pull-off strength tests at 7, 28, and 90 days. Scanning electron microscopy analysis was also performed to study the microstructure of the interface between the normal concrete substrate and the latex-modified sand concrete reinforced with sisal fibers. The results of this study indicate that LMSC has bonding strength with NC, especially for HR and SB surfaces with high roughness. Therefore, substrate NC surface roughness is essential in increasing the bonding strength and adhesion. Eventually, The LMSC has the potential to repair and rehabilitate concrete structures.

• 산업기술연구
• /
• 제33권A호
• /
• pp.93-99
• /
• 2013

Shotcrete has been referred to as gunite, pneumatically applied mortar or concrete, sprayed concrete or mortar. There are sound reasons why sprayed mortar is one of the best portland cement based material for repairing old concrete structures. However, it is difficult to find the research results on the latex-modified mortar nevertheless on the impact of air onto the fresh and hardened properties of latex-modified mortar. So, the main experimental program included strength test, slump test, rapid chloride permeability test, image analysis for air void system, and chemical attacks with the main experimental variables of latex content, fine aggregate content, water-cement ratio, and air foamer content.

• 한국농공학회논문집
• /
• 제49권5호
• /
• pp.23-30
• /
• 2007

This research was to evaluate the shrinkage and durability performance of latex modified repair mortar and to improve the service lift of the agricultural concrete structures. The shrinkage characteristics of the repair material creates the delamination of repair materials and existing concrete. It may reduce the service life of structures. Also the reduction of durability performance of the repair materials induces the destruction of the repaired concrete structures at early stage. In this research, plastic and drying shrinkage, thermal expansion coefficient for shrinkage properties, durability performance, permeability, repeated freezing and thawing, and resistance of chemical solution test were performed. Test results showed that the latex modified repair mortar indicated the shrinkage amount which the delamination does not happen, and the latex modified repair mortar appeared excellent long-term durability performance which can increase the service life.

• 산업기술연구
• /
• 제25권A호
• /
• pp.49-56
• /
• 2005

Recently, very-early strength latex-modified concrete(below ; VES-LMC) has been developed for repairing and overlaying the old concrete bridge deck. VES-LMC provides the advantage of very-early-strength, as well as high flexural strength, bond strength, durability, resistance to corrosion, reduced water permeability and resistance to damage from freeze-thaw cycles. The compressive and flexural strength of VES-LMC are 21 MPa and 4.5 MPa at 3 hours after concrete placing, respectively. However, VES-LMC would have a relatively large shrinkage at early-age because of reduced water-cement ratio, big water self-dissipation, and rapid hydration reaction. Therefore, the purpose of this study was to evaluate the early-age and restrained shrinkage of VES-LMC, having an experimental variables such as latex contents and cement types. The latex contents included 0%, 5%, 10%, 15% and 20%, and the cement types included ordinary portland cement and very-early strength cement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 가을 학술발표회 논문집
• /
• pp.147-152
• /
• 2001

The purpose of this study is to ascertain the strength properties of water-permeable polymer concretes with SBR latex and redispersible polymer powder. The water-permeable polymer concretes using SBR latex and redispersible polymer powder with water-binder ratio of 29%, polymer-cement ratios of 0, 5, 10, 15 and 20% are prepared, and tested for compressive strength, tensile strength, flexural strength, water permeability. From the test results, improvements in the strength properties of the water-permeable polymer concretes due to the addition of the SBR latex and redispersible polymer powder are discussed.

• 한국공간구조학회논문집
• /
• 제9권4호
• /
• pp.61-72
• /
• 2009

건축물이 고층화 및 대형화 되어감에 따라 구조물 및 빌딩의 자중을 줄이는 것은 반드시 필요하게 되는데, 이러한 구조물 의 자중을 줄이기 위한 가장 효과적인 방법 중 하나는 경량콘크리트를 사용하는 것이다. 본 연구에서는 경량콘크리트의 단점인 강도를 보완하기 위하여 폴리머를 첨가하였으며, 폴리머 개질 경량콘크리트의 적절한 배합비율을 도출하기 위한 실험을 수행하였다. 또한 경화콘크리트 시험을 통하여 폴리머 개질 경량콘크리트의 물리적 특성을 고찰하였다. 그 결과 소량의 폴리머 첨가로도 휨강도가 증가하였으며, 실험결과를 바탕으로 회귀분석을 통한 압축강도 추정식을 제시하였다.