• Journal of the Korean institute of surface engineering
• /
• v.51 no.4
• /
• pp.243-248
• /
• 2018

All solid state thin film batteries with two types of cell structure, Pt / $LiCoO_2$ / LiPON / Cu and Pt / $LiCoO_2$ / LiPON / $LiCoO_2$ / Cu, are prepared and their electrochemical performances are investigated to evaluate the effect of $LiCoO_2$ interlayer at the interface of LiPON / Cu. The crystallinity of the deposited $LiCoO_2$ thin films is confirmed by XRD and Raman analysis. The crystalline $LiCoO_2$ cathode thin film is obtained and $LiCoO_2$ as the interlayer appears to be amorphous. The surface morphology of Cu current collector after cycling of the batteries is observed by AFM. The presence of a 10 nm-thick layer of $LiCoO_2$ at the interface of LiPON / Cu enhances the interfacial adhesion and reduces the interfacial resistance. As a result, Li plating / stripping at the interface of LiPON / Cu during charge/discharge reaction takes place more uniformly on Cu current collector, while without the interlayer of $LiCoO_2$ at the interface of LiPON / Cu, the Li plating / stripping is localized on current collector. The thin film batteries with the interlayer of $LiCoO_2$ at the interface of LiPON / Cu exhibits enhanced initial coulombic efficiency, reversible capacity and cycling stability. The thickness of the anode current collector Cu also appears to be crucial for electrochemical performances of all solid state thin film batteries.

• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.33-37
• /
• 2016

10 wt.% and 20 wt.%$Li-TiO_2$ composite powders are synthesized by a sol-gel method using titanium isopropoxide and $Li_2CO_3$ as precursors. The as-received amorphous 10 wt.%$Li-TiO_2$ composite powders crystallize into the anatase-type crystal structure upon calcination at $450^{\circ}C$, which then changes to the rutile phase at $750^{\circ}C$. The asreceived 20 wt%$Li-TiO_2$ composite powders, on the other hand, crystallize into the anatase-type structure. As the calcination temperature increases, the anatase $TiO_2$ phase gets transformed to the $LiTiO_2$ phase. The peaks for the samples obtained after calcination at $900^{\circ}C$ mainly exhibit the $LiTiO_2$ and $Li_2TiO_3$ phases. For a comparison of the photocatalytic activity, 10 wt.% and 20 wt.% $Li-TiO_2$ composite powders calcined at $450^{\circ}C$, $600^{\circ}C$, and $750^{\circ}C$ are used. The 20 wt.%$Li-TiO_2$ composite powders calcined at $600^{\circ}C$ show excellent efficiency for the removal of methylorange.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.10
• /
• pp.3682-3686
• /
• 2011

The electrochemical properties of lithium-sulfur batteries with binary electrolytes based on DME and DOL, TEGDME and DOL mixed solvent containing $LiClO_4$, LiTFSI, and LiTF salts were investigated. The ionic conductivity of 1M LiTFSI and $LiClO_4$ electrolytes based on TEGDME and DOL increased as the volume ratio of DOL solvent increased, because DOL effectively reduces the viscosity of the above electrolytes medium under the same salts concentration. The first discharge capacity of lithium-sulfur batteries in the DME and DOL-based electrolyte followed this order: LiTFSI (1,000 mAh/g) > LiTF (850 mAh/g) > $LiClO_4$ (750 mAh/g). In case of the electrolyte based on TEGDME and DOL, the first discharge capacity of batteries followed this order: $LiClO_4$ (1,030 mAh/g) > LiTF (770 mAh/g) > LiTFSI (750 mAh/g). The cyclic efficiency of lithium-sulfur batteries at 1M $LiClO_4$ electrolytes is higher than that of batteries at other lithium salts-based electrolytes. Lithium-sulfur battery showed discharge capacity of 550 mAh/g until 20 cycles at all electrolytes based on DME and DOL solvent. By contrast, the discharge capacity of batteries was about 450 mAh/g at 1M LiTFSI and LiTF electrolytes based on TEGDME and DOL solvent after 20 cycles.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.4 no.2
• /
• pp.16-21
• /
• 1967

This report describes actual fabrication mehod of Li drifted Ge detector. The gamma-ray spectrum from Cl(n, r) reaction measured by this Li drifted Ge detector are also shown. Energy resolution(FWHM) of this Li drifted Ge detector is 4.5KeV at the 122KeV( ), and 10KeV a the 1333KeV( ) respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.2
• /
• pp.166-176
• /
• 1996

The fundamental conditions for growing $CsLiB_{6}O_{10}$ crystal, new nonlinear optical material, were investigated. Stoichiometirc mixture of $CsLiB_{6}O_{10}$ composition resulted in the crystal of the same composition in the process of heating at the temperature above $600^{\circ}C$. No phase transition was observed in the $CsLiB_{6}O_{10}$ crystal in the temperature range of $600^{\circ}C~800^{\circ}C$, and $CsLiB_{6}O_{10}$ crystal melted congruently at $850^{\circ}C$. When the melt of this composition was cooled at rates of $1~150^{\circ}C/hr$, glass state ingot was formed regardless of cooling rates. However, $CsLiB_{6}O_{10}$ crystals were formed directly from the melt at any cooling rate in the presence of $CsLiB_{6}O_{10}$ seed crystal in the melt. Transparent $CsLiB_{6}O_{10}$ single crystal was grown from the melt using the seed crystal at the growing rate of 0.06 mm/hr in the furnace having the temperature gradient of $100^{\circ}C/cm$. Analysis of the single crystal showed that the crystal belonged to the noncentrosymmetric tetragonal space group 142d and unit cell dimensions were $a=10.467(1)\;{\AA},\;c=8.972(1)\;{\AA}\;and\;V=983.0(2)\;{\AA}^3$. Optical absorption edge of the crystal was observed at 180mm and the crystal showed a good optical transparency (70% transmittance, sample thickness 0.5 mm) in the wide wavelength range above 300 nm.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.10 no.4
• /
• pp.229-236
• /
• 2012

A molten salt technology using $Li_2O$-LiCl has been extensively investigated to recover uranium metal from spent fuels in the field of nuclear energy. In the reduction process, it is an important point to maintain the concentration of $Li_2O$. $ZrO_2$ is inevitably contained in the spent fuels because Zr is one of the main components of fuel rod hulls. Therefore, the fate of $ZrO_2$ in $Li_2O$-LiCl molten salt has been investigated. It was found that $Li_2ZrO_3$ and $Li_4ZrO_4$ were formed chemically and electrochemically and they were not reduced to Zr. The recycling of $Li_2O$ is the key mechanism ruling the total reaction in the electrolytic reduction process. However, $ZrO_2$ will have a role as a $Li_2O$ sink.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.121-124
• /
• 1998

The purpose of this study is to research and develop solid polymer electrolyte(SPE) for Li secondary battery. This paper describes temperature dependence of conductivity, impedance spectroscopy, electrochemical properties of PVDF electrolytes as a function of a mixed ratio. Polyvinylidene(PVDF) based polymer electrolyte films were prepared by thermal gellification method of preweighed PVDF, plasticizer and Li salt. The conductivity of PVDF electrolytes was 10$\^$-3/S/cm. 25PVDFPC$\_$10/EC$\_$10/LiClO$_4$ electrolyte shows the better conductivity of the others. 25PVDFPC$\_$10/EC$\_$10/LiClO$_4$electrolyte remains stable up to 4.7V vs. Li/Li$\^$+/. Steady state current method and ac impedance used for the determination of transference numbers in PVDFD electrolyte film. The transference number of 25PVDFPC$\_$10/EC$\_$10/LiClO$_4$electrolyte is 0.58.

• Journal of the Korean Ceramic Society
• /
• v.41 no.5
• /
• pp.388-394
• /
• 2004

LiCoO$_2$ as the cathode activity material for lithium secondary battery was prepared from a homogeneously mixed powder of LiNO$_3$/Co by SHS process under argon gas. The characteristics of powder including electrochemical properties were investigated according to various reaction conditions. The reaction temperature/velocity and the size of LiCoO$_2$ were controlled by Li/Co molar ratio and a cooling rate of the specimen, respectively. The maximum discharge capacity was 145 mAh/g on 1.05 Li/Co molar ratio and the relatively stable cycling characteristic with 6.4% of capacity fading was obtained after 10th charging-discharging test.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.3
• /
• pp.836-840
• /
• 2011

This study examines the effects of a carbon coating on the electrochemical performances of $LiFePO_4$. The results show that the capacity of bare $LiFePO_4$ decreased sharply, whereas the $LiFePO_4$/C shows a well maintained initial capacity. The Li ion diffusivity of the bare and carbon coated $LiFePO_4$ is calculated using cyclic voltammetry (CV) to determine the correlation between the electrochemical performance of $LiFePO_4$ and Li diffusion. The diffusion constants for $LiFePO_4$ and $LiFePO_4$/C measured from CV are $6.56{\times}10^{-16}$ and $2.48{\times}10^{-15}\;cm^2\;s^{-1}$, respectively, indicating considerable increases in diffusivity after modifications. The Li ion diffusivity (DLi) values as a function of the lithium content in the cathode are estimated by electrochemical impedance spectroscopy (EIS). The effects of the carbon coating as well as the mechanisms for the improved electrochemical performances after modification are discussed based on the diffusivity data.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.137.2-137.2
• /
• 2011

Poly (sodium 4-styrenesulfonate) (PSS) is ionomer based on polystyrene that is electrical conductivity and isoviscosity. LiFePO4 has been a promising electrode material however its poor conductivity limits practical application. To enhance the electronic conductivity of LiFePO4, in this study we prepared LiFePO4- PSS composite by the hydrothermal method. LiFePO4 was heated at $170^{\circ}C$ for 12h and then different wt% PSS (0%, 2.91%, 4.75%, 7.36%, 10%) are added to LiFePO4 and milled at 300rpm for 10h. And then the obtained powders were subsequently heated at $500^{\circ}C$ for 1h under argon flow. The cathode electrode were made from mixtures of LiFePO4-PSS: SP-270- PVDF in a weighting ratio 75%: 25%:5%. The electrochemical properties of LiFePO4- PSS/Li batteries were analyzed by cyclic voltammetry and charge/discharge tests. LiFePO4-C/Li battery with 4.75 wt% PSS displays discharge capacity of 128 mAh g-1 at room temperature that is considerably higher than pure LiFePO4/Li battery ( 113.48 mAhg-1).