• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.67 no.1
• /
• pp.142-147
• /
• 2018

Private electrical facilities are judged whether it is suitable for the insulation aging condition of their incoming underground cables using DC leakage current test method. In the case where the service point of utility is the secondary side of cut out switch installed in the electric pole, there is a problem that it is difficult to separate the lightning arresters(LA) because of their high position of the pole. Therefore, the field test voltage is applied at value lower than DC 30 kV, which are stated in the inspection guideline. However, this test could reduced the insulation performance of the LA by accelerating the electrical stress of the metal oxide varistor element in the pre-breakdown region. In this study, we analyzed the relationship between the DC test voltage and the leakage current using the non-destructive DC high voltage equipment with leakage current measurement function. The results show that the leakage current increases sharply above the specified test voltage. As a consequence, it could be contributed to improve insulation aging inspection method by selecting the possible test area on the VI characteristic curve of the pre-breakdown area of the LA.

• Journal of the Korean Ceramic Society
• /
• v.34 no.10
• /
• pp.1060-1066
• /
• 1997

In this paper, the effects of La addition of PLZT thin film prepared by sol-gel method on the capacitor characteristics are investigated for gigabit generation DRAM applications. The addition of La on the PLZT capacitor results in a trade-off between charge storage density(Qc') and leakage current density(Jl). As La content increases, Qc' and permeability(εr) at 0V are reduced while Jl is significantly decreased. It is demonstrated that 5% La doping of PZT can substantially reduce Jl and also improve resistance to fatigue while incurring only minimal degradation of Qc'. Very low leakage current density (5×10-7 A/㎠ even at 125℃) and high charge storage density (100fC/㎛2) under VDD/2=1V conditions are achieved using 5% La doped PZT thin films for gigabit DRAM capacitor dielectrics. In addition, the fatigue and TDDB measurements indicate good reliability of the PLZT capacitors.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.4
• /
• pp.189-195
• /
• 2006

The microstructure, electrical and dielectric properties, and stability against DC accelerated aging stress of the varistors, which are composed of quaternary system $ZnO-Pr_6O_{11}CoO-Cr_2O_3-based$ ceramics, were investigated for different $La_2O_3$ contents. The increase of $La_2O_3$ content led to more densified ceramics, whereas abruptly decreased the nonlinear properties by incorporating beyond 1.0mol%. The highest nonlinearity was obtained from 0.5mol% $La_2O_3$, with the nonlinear coefficient of 81.6 and the leakage current of $0.1{\mu}A$. The varistors doped with 0.5mol% $La_2O_3$ exhibited high stability, in which the variation rates of breakdown voltage, nonlinear coefficient, leakage current, dielectric constant, and dissipation factor were -1.1%, -3.7%, +100%, +1.4%, and +8.2%, respectively, for stressing state of $0.95V_{1mA}/150^{\circ}C/24h$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.422-425
• /
• 2001

The electrical properties of ZnO-$Pr_6O_{11}$-CoO-$Cr_2O_3-La_2O_3$ based varistors were investigated with sintering temperature in the range of $1240\sim1300^{\circ}C$. The varistors sintered at $1240\sim1260^{\circ}C$ exhibited high density, which was 5.50- $5.70g/cm^3$ corresponding to 95.2~98.6% of theoretical density. The varistor voltage was decreased in range of 718.47~108.00 V/mm with increasing sintering temperarture. The varistors sintered at $1240\sim1260^{\circ}C$ exhibited good electrical properties, in which the nonlinear exponent is in the range of 79.25~49.22 and leakage current is in the range of 0.26~$1.00 {\mu}A$ In particular, the varistor sintered at $1240^{\circ}C$ showed very excellent electrical properties, in which the nonlinear exponent is 79.25 and leakage current is $0.26{\mu}A$

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.422-425
• /
• 2001

The electrical properties of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-La$_2$O$_3$ based varistors were investigated with sintering temperature in the range of 1240~130$0^{\circ}C$. The varistors sintered at 1240~126$0^{\circ}C$ exhibited high density, which was 5.50~5.70 g/㎤ corresponding to 95.2~98.6% of theoretical density The varistor voltage was decreased in range of 718.47~108.00 V/mm with increasing sintering temperature. The varistors sintered at 1240~126$0^{\circ}C$ exhibited good electrical properties, in which the nonlinear exponent is in the range of 79.25~49.22 and leakage current is in the range of 0.26~1.00 $\mu$A. In particular, the varistor sintered at 1240\`c showed very excellent electrical properties, in which the nonlinear exponent is 79.25 and leakage current is 0.26 $\mu$A.A.A.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.415-418
• /
• 2001

The I-V characteristics and its stability of ZPCCL-based ceramic varistors doped with La$_2$O$_3$in the range of 0.0~4.0 mol% were investigated. The density of ceramics was increased in the range of 4.7~5.8 g/cm$^3$ with increasing La$_2$O$_3$content. As La$_2$O$_3$content is increased, the varistor voltage was decreased in the range of 503.49-9.42 V/mm up to 2.0 mol%, whereas increasing La$_2$O$_3$content further caused it to increase. The ZPCCL-based varistors were characterized by nonlinearity, in which the nonlinear exponent is in the range of 3.05~82.43 and leakage current is in the range of 0.24-100.22 $\mu$A. Among ZPCCL-based varistors, 0.5 mol% added-varistors exhibited an excellent nonlinearity, in which the nonlinear exponent is 82.43 and the leakage current is 0.24 $\mu$A. Furthermore, they exhibited a high stability, in which the variation rate of the varistor voltage and the nonlinear exponent was -1.11% and -6.72%, respectively, under DC stress, such as (0.80 V$_{1mA}$9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$115$^{\circ}C$//12h) +(0.90 V$_{1mA}$12$0^{\circ}C$//12h)+(0.95 V$_{1mA}$1$25^{\circ}C$//12h)+(0.95 V$_{1mA}$15$0^{\circ}C$//12h). Consequently, it was estimated that ZPCCL-based ceramics will be applied to development of Pr$_{6}$O$_{11}$ based ZnO varistors having a high performance.e.rformance.e.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.416-418
• /
• 2000

Thin films of phase-pure perovskite $(Pb_{0.72}La_{0.28})Ti_{0.93}O_3$ (PLT) were deposited in-situ onto Pt/Ti/$SiO_2$/Si substrates by pulsed laser deposition. We have systematically investigated the variation of grain sizes depending on the process condition. Both in-situ annealing and ex-situ annealing treatments have been compared depending on the annealing time. The grain sizes of PLT thin films were successfully controlled 260 to 350 nm by changing process parameters. Microstructural and electrical properties of the film were investigated by C-V measurement, leakage current measurement and SEM. Two-step process to grow $(Pb_{0.72}La_{0.28})Ti_{0.93}O_3$ (PLT) films was adopted and verified to be useful to enlarge the grain size of the film and to enhance the leakage current characteristics.

• Korean Journal of Materials Research
• /
• v.11 no.2
• /
• pp.151-154
• /
• 2001

The leakage current behaviors of PLZT capacitors with top electrodes of Pt, Ir, and $IrO_2$ are investigated before and after hydrogen forming gas anneal. The P-E hysteresis and fatigue properties of Pt/PLZT/Pt capacitors are almost recovered after recovery anneal in $O_2$ ambient. The leakage current mechanisms of PLZT capacitors with Pt and $IrO_2$ top electrodes are consistent with space-charge influenced injection model showing the strong time dependence irrespective of annealing conditions. On the other hand, the leakage current behavior of Ir/PLZT/Pt capacitor shows steady state independent of time because IrPb, conducting phase, formed at interface between Ir top and PLZT is a high conduction path. Teh leakage current mechanism of Ir/PLZT/Pt capacitor is consistent with Schottky barrier model.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.11
• /
• pp.969-974
• /
• 1998

The effects of $La_2O_3$on the microstructure and electrical characteristics of Pr-based ZnO varistors were investigated. The average grain size increased in the range of 21.9~56.3$\mu$ m with increasing $La_2O_3$additive content(0.0~2.0 mol%). La was, of course grain boundary, largely segregated at the nodal point. As $La_2O_3$additive content increases, threshold voltage and nonlinear coefficient decreased and leakage current increased. In particular, 2.0 mol% $La_2O_3$-added varistor exhibited low threshold voltage 17.0V/mm and nonlinear coefficient of about 6. Based on these results, this varistor can be said to be used as low-voltage varistor, if nonlinear coefficient is somewhat improved forward.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.383-386
• /
• 2004

DC accelerated aging characteristics of Zn-Pr-Co-Cr-La oxides-based varistors were investigated with various sintering temperatures. The varistors sintered at $1240^{\circ}C$ exhibited the highest nonlinearity, with a nonlinear exponent of 79.3 and a leakage current of $0.3\;{\mu}A$, whereas completely degraded because of thermal runaway owing to low sintered density. The varistors sintered at $1250^{\circ}C$ exhibited not only a high nonlinearity with the nonlinear exponent 61.4 and the leakage current 0.7 ${\mu}A$, but also a high stability with the variation rates of varistor voltage and nonlinear exponent are -1.01% and -10.67%, respectively, under DC stress condition such as $(0.85\;V_{1mA}/115^{\circ}C/24\;h)+(0.90\;V_{1mA}/120^{\circ}C/24\;h)+(0.95\;V_{1mA}/125^{\circ}C/24\;h)+(0.95\;V_{1mA}/150^{\circ}C/24\;h)$.