• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.215.2-215.2
• /
• 2015

We fabricated dual active layer (DAL) thin film transistors (TFTs) with indium tin zinc oxide (ITZO) and indium gallium zinc oxide (IGZO) thin film layers using solution process. The ITZO and IGZO layer were used as the front and back channel, respectively. In order to investigate the bias stress stability of ITZO SAL (single active layer) and ITZO/IGZO DAL TFT, a gate bias stress of 10 V was applied for 1500 s under the dark condition. The SAL TFT composed of ITZO layer shows a poor positive bias stability of ${\delta}VTH$ of 13.7 V, whereas ${\delta}VTH$ of ITZO/IGZO DAL TFT was very small as 2.6 V. In order to find out the evidence of improved bias stress stability, we calculated the total trap density NT near the channel/gate insulator interface. The calculated NT of DAL and SAL TFT were $4.59{\times}10^{11}$ and $2.03{\times}10^{11}cm^{-2}$, respectively. The reason for improved bias stress stability is due to the reduction of defect sites such as pin-hole and pores in the active layer.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.1
• /
• pp.112-116
• /
• 2007

We have investigated the hysteresis phenomenon of a hydrogenated amorphous silicon thin film transistor (a-Si:H TFT) and analyzed the effect of hysteresis phenomenon when a-Si:H TFT is a pixel element of active matrix organic light emitting diode (AMOLED). When a-Si:H TFT is addressed to different starting gate voltages, such as 10V and 5V, the measured transfer characteristics with 1uA at $V_{DS}$ = 10V shows that the gate voltage shift of 0.15V is occurred due to the different quantities of trapped charge. When the step gate-voltage in the transfer curve is decreased from 0.5V to 0.05V, the gate-voltage shift is decreased from 0.78V to 0.39V due to the change of charge do-trapping rate. The measured OLED current in the widely used 2-TFT pixel show that a gate-voltage of TFT in the previous frame can influence OLED current in the present frame by 35% due to the change of interface trap density induced by different starting gate voltages.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.354-357
• /
• 2002

Thermally grown gate oxide on 4H-SiC wafer was investigated. The oxide layers were grown at l150$^{\circ}C$ varying the carrier gas and post activation annealing conditions. Capacitance-Voltage(C-V) characteristic curves were obtained and compared using various gate electrode such as Al, Ni and poly-Si. The interface trap density can be reduced by using post oxidation annealing process in Ar atmosphere. All of the samples which were not performed a post oxidation annealing process show negative oxide effective charge. The negative oxide effective charges may come from oxygen radical. After the post oxidation annealing, the oxygen radicals fixed and the effective oxide charge become positive. The effective oxide charge is negative even in the annealed sample when we use poly silicon gate. Poly silicon layer was dope by POCl$_3$ process. The oxide layer may be affected by P ions in poly silicon layer due to the high temperature of the POCl$_3$ doping process.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.1 no.3
• /
• pp.158-166
• /
• 2001

Based on uniform hot carrier injection (optically assisted electron injection) across the $Si-SiO_2$ interface into the gate insulator of n-channel IGFETs, the threshold voltage shifts associated with electron injection of $1.25{\times}l0^{16}{\;}e/\textrm{cm}^2 between 0.5 and 7 MV/cm were found to decrease from positive to negative values, indicating both a decrease in trap cross section ($E_{ox}{\geq}1.5 MV/cm$) and the generation of FPC $E_{ox}{\geq}5{\;}MV/cm$). It was also found that FNC and large cross section NETs were generated for $E_{ox}{\geq}5{\;}MV/cm$. Continuous, uniform low-field (1MV/cm) electron injection up to $l0^{19}{\;}e/\textrm{cm}^2 is accompanied by a monatomic increase in threshold voltage. It was found that the data could be modeled more effectively by assuming that most of the threshold voltage shift could be ascribed to generated bulk defects which are generated and filled, or more likely, generated in a charged state. The injection method and conditions used in terms of injection fluence, injection density, and temperature, can have a dramatic impact on what is measured, and may have important implications on accelerated lifetime measurements.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.25-29
• /
• 2008

Reliability and performance in metal gate/high-k device with multiple gate dielectrics were investigated. MOSFETs with a thin $HfSiO_x$ layer on a thermal Si02 dielectric as gate dielectrics exhibit excellent mobility and low interface trap density. However, the distribution of threshold voltages of $HfSiO_x/SiO_2$ stack devices were wider than those of $SiO_2$ and $HfSiO_x$ single layer devices due to the penetration of Hf and/or intermixing of $HfSiO_x$ with underlying $SiO_2$. The results of TZDB and SILC characteristics suggested that a certain portion of $HfSiO_x$ layer reacted with the underlying thick $SiO_2$ layer, which in turn affected the reliability characteristics.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.1
• /
• pp.23-30
• /
• 1993

Hydrogenation on the top gate and bottom gate Poly-Si TET's was performed by using Nh$_{3}$ plasma and annealing SiN film deposited by PECVD and then the electric characteristics on Poly-Si TET were investigated. As the time of NA$_{3}$ plasma treatment increaes, on/off current ratio gradually increases and the swing value decreases. The trap densities of graim boundaries in Poly-Si decrease very much during the inital 20min of hydrogenation time, and the decreasing scale becomes smaller after 20 min. The electric characteristics of the top gate TFT are better than those of the bottom gate TFT, it is considered due to the defects at the interface between the Poly-Si and the underlayer, SiO$_{2}$. After NH$_{3}$ plasma was treated for 2 hours for the top gate TFT, as the aging time atroon temperature increases on current was not scacely changed and off current decreases more than 1 order. Gate current density recovers to original value after the aging treatment for 8 days and then the electric characteristics are finally improved. It is suggested that the degraded characteristics of gate oxide are improved, from the variations of C-V characteristics with aging time. For the hydrogenation of isothermal and isochronal annealing SiN film deposited by PECVD, the characteristics of Poly-Si TFT are improved with increasing annealing temperature and are not largely changed with increasing annealing time. This results is good in agreement with the hydrogen reduction in Sin film as variations of annealing temperature and time.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.6 no.1
• /
• pp.10-15
• /
• 2006

Various sizes of erbium/platinum silicided n/p-type Schottky barrier metal-oxide-semiconductor field effect transistors (SB-MOSFETs) are manufactured from $20{\mu}m$ to 10nm. The manufactured SB-MOSFETs show excellent DIBL and subthreshold swing characteristics due to the existence of Schottky barrier between source and channel. It is found that the minimization of trap density between silicide and silicon interface and the reduction of the underlap resistance are the key factors for the improvement of short channel characteristics. The manufactured 10 nm n-type SBMOSFET showed $550{\mu}A/um$ saturation current at $V_{GS}-V_T$ = $V_{DS}$ = 2V condition ($T_{ox}$ = 5nm) with excellent short channel characteristics, which is the highest current level compared with reported data.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.1
• /
• pp.20-23
• /
• 2012

In this paper, we investigated the device performance on fluorine implantation, hot carrier reliability and RTS (random telegraph signal) noise characteristics of NMOSFETs. The capacitance of the fluorine implanted NMOSFET decreased due to the increase of the gate oxide thickness. RTS noise characteristics of the fluorine implated NMOSFET was improved approximately by 46% due to the decrease of trap density at Si/$SiO_2$ interface. The improved gate oxide quality also results in the longer hot carrier life time.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.526-529
• /
• 2002

Various fluoride films on a glass substrate were prepared and characterized in order to determine the best seed layer for a microcrystalline silicon (${\mu}c$-Si) film growth. Among the various group-IIA-fluoride systems, the $CaF_2$films on glass substrates illustrated (220) preferential orientation and a lattice mismatch of less than 0.7% with Si. $CaF_2$ films exhibited a dielectric constant between $4.1{\sim}5.2$ and an interface trap density ($D_{it}$ as low as $1.8{\times}10^{11}\;cm^{-2}eV^1$. Using the $CaF_2$/glass structure, we were able to achieve an improved ${\mu}c$-Si film at a process temperature of 300 $^{\circ}C$. We have achieved the ${\mu}c$-Si films with a crystalline volume fraction of 65%, a grain size of 700 ${\AA}$, and an activation energy of 0.49 eV.

• Journal of the Korean Ceramic Society
• /
• v.32 no.11
• /
• pp.1262-1268
• /
• 1995

Photoelectrochemical properties of p-GaAs electrode have been investigated. I-V characteristic shows that the cathodic photocurrent is observed at -0.7 V vs. SCE. The photoresponse at near 870~880nm wavelength indicates that the photogenerated carriers contibuted to the observed current. The maximum converson efficiency of 35% is obtained for a Xe lamp light source at 400nm. In C-V relation, capacitance peaks appeared at the frequencies of 100Hz and 300Hz due to the activation of the interfacial states which exist at the energy level corresponding to the one-third of the GaAs band gap. The difference of about 1.1V between flatband potential (Vfb) from the Mott-Schottky method and onset voltage from I-V curve is observed due to the trap of carriers at the interfacial states in the boundary between GaAs and electrolyte. In case of WO3 deposited p-GaAs electrode, higher positive onset current and photocurent density are obtained. This can be explained by the fact that carriers are generated by light penetrated into the WO3 thin flm as well as p-GaAs substrate and then move into the electrolyte effectively.