• 대한치과보철학회지
• /
• 제34권2호
• /
• pp.309-319
• /
• 1996

This study was performed to evaluate the fracture toughness of seven commercially available dental ceramics by indentation fracture method. All specimens were fabricated to the final dimensions of approximately 12mm in diameter 2mm in thickness. The characte-ristic indentation dimensions of Vickers or Knoop indentation were measured to calculate the fracture toughness values and Young’s moduli. The results obtained were summarized as follows; 1. Young’s modulus and Vickers hardness of Vita In-Ceram showed the maximum values of $154.4{\pm}49.2$ Gpa and $12.60{\pm}0.71$Gpa, respectively. Results of Scheff test exhibited the significant difference between Vita In-Ceram group and others(p<0.01). 2. Maximum fracture toughness of $2.562{\pm}0.37 MPam^{1/2}$ for Vita In-Ceram and the maxi-mum one of $0.908{\pm}0.132MPam^{1/2}$ for Vitadur-N were calculated. Results of Scheff test showed the significant difference between Vita In-Ceram group and Vita Hi-Ceram(p<0.05) : also between Vita In-Ceram or Vita Hi-Ceram and others(p<0.01). 3. The alumina-based core ceramics showed the aspect of Palmqvist crack for the indentation load of 49.0N, but others showed the median/lateral crack for the indentation load of 9.8N.

• 대한기계학회논문집A
• /
• 제36권9호
• /
• pp.1081-1086
• /
• 2012

본 논문에서는 품질 검사 방법론이 적용된 계장화 압입시험을 수행하여 점용접부의 경도를 평가하였다. 먼저 정상 및 불량 용접조건하에서 제작된 점용접 샘플에 대해 로크웰 경도 및 계장화 압입시험을 실시하였다. 계장화 압입시험을 통해 구한 압입하중-변위선도를 이용하여 계산된 경도를, 동일한 조건의 동일위치에 대한 압입경도시험을 통하여 측정된 로크웰 경도와 확률론적 방법론을 이용하여 비교평가 하였다. 또한 계장화 압입시험을 통하여 추정한 경도 및 이에 대한 확률론적 해석을 수행하여 점용접부의 신뢰성 기반 품질 관리 기준 설정 가능성을 평가하였다.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.171-176
• /
• 2000

As huge energy transfer systems like a nuclear power plant, steam power plant and petrochemical plant are operated for a long time, mechanical properties are changed by degradation. The life time of the systems can be affected by the mechanical properties. BI(Ball Indentation) test has a potential to replace conventional fracture tests like a uniaxial tensile test, fracture toughness test, hardness test and so on. In this paper, we would like to present the aging evaluation technique by the BI method. The four classes of the thermally aged 1Cr-1Mo-0.25V specimens were prepared using an artificially accelerated aging method. Tensile tests, fracture toughness tests, hardness tests and BI tests were performed. The results of the BI tests were in good agreement with fracture characteristics by a standard fracture test method. The IDE(Indentation Deformation Energy) of a BI technique as a new parameter for evaluating a degradation was suggested and the new IDE parameter clearly depicts the degradation degree.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 1997년도 춘계학술대회논문집
• /
• pp.69-72
• /
• 1997

The indentation process in the Vickers hardness test is a kind of controlled local plastic deformation. Vickers hardness is defined as indenting force per unit area indented by a pyramid-shaped diamond at the hardness test. That is a measure of mechanical resistance against indentation of a rigid body into the deformable material. Therefore it is well known that Vickers hardness has a direct relation with the flow stress of the strain-hardened tmaterial. This relation is theoretically investigated and the result is given for use in practice.

• 대한의용생체공학회:의공학회지
• /
• 제26권2호
• /
• pp.117-122
• /
• 2005

The elastic modulus and the apparent density of the trabecular bone were evaluated from spherical indentation tests and Computed Tomography (CT) and their relationship was quantified. The femurs were prepared for trabecular bone analysis. Embedded with respect to their anatomical orientation, the transverse planes of the trabecular bone specimens were scanned at 1㎜ intervals using a CT scanner. The metaphyseal regions of femurs were sectioned with a diamond-blade saw, producing 8㎜ cubes. Using a specially made spherical indentation tester, the cubes were mechanically tested in the anterior-posterior (AP), medial-lateral (ML), and inferior-superior (IS) directions. After determination of modulus from the mechanical testing, the apparent densities of the specimens were measured. The results showed that the IS modulus was significantly greater than both the AP and ML moduli with the AP modulus greater than the ML modulus. This demonstrated that orthogonality was a structural characteristic of the trabecular bone. The power relationship between the modulus and the apparent density was also found to be statistically significant.

• Journal of Welding and Joining
• /
• 제27권6호
• /
• pp.43-48
• /
• 2009

In this study, Cu-based bulk metallic glass (BMG) coatings were deposited by atmospheric plasma spraying (APS) process with different process conditions (with- and without hydrogen gas). As adding the hydrogen gas, thermal energy in the plasma flame increased and induced difference in the melting state of the Cu-based BMG particles. The microstructure and mechanical properties of the coatings were analyzed using a scanning electron microscope (SEM) with an energy dispersive spectroscopy (EDS) and nano-indentation tester in the light of phase analysis. It was elucidated by the nano-indentation tests that un-melted region was a mainly amorphous phase which showed discrete plasticity observed as the flow serrations on the load.displacement (P - h) curves, and the curves of solidified region showed lower flow serrations as amorphous phase mingled with crystalline phase. Oxides produced during the spraying process had the highest hardness value among the phases and were well mixed with other phases resulted from the increase in melting degree.

• Journal of Mechanical Science and Technology
• /
• 제20권6호
• /
• pp.819-827
• /
• 2006

The stress-strain relation of aluminum (Al) alloy foam cell wall was evaluated by the instrumented sharp indentation method. The indentation in a few micron ranges was performed on the cell wall of Al-alloy foam having a composition or Al-3wt.%Si-2wt.%Cu-2wt.%Mg as well as its precursor (material prior to foaming). To extract the stress-stram relation in terms of yield stress ${\sigma}_y$, strain hardening exponent n and elastic modulus E, the closed-form dimensionless relationships between load-indentation depth curve and elasto-plastic property were used. The tensile properties of precursor material of Al-alloy foam were also measured independently by uni-axial tensile test. In order to verify the validity of the extracted stress-strain relation, it was compared with the results of tensile test and finite element (FE) analysis. A modified cubic-spherical lattice model was proposed to analyze the compressive behavior of the Al-alloy foam. The material parameters extracted by the instrumented nanoindentation method allowed the model to predict the compressive behavior of the Al-alloy foam accurately.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1997년도 춘계학술발표회논문집(2)
• /
• pp.129-136
• /
• 1997

The automated ball indentation(ABI) test was utilized to develop a semi-nondestructive method for estimating the fracture toughness( $K_{JC}$ ) in the transition temperature range. The key concept of the method is that the indentation deformation energy to the load at which the mean ball-specimen contact pressure reaches the fracture stress is related to the fracture energy of the material. ABI tests were performed for the reactor pressure vessel(RPV) base and weld metals at the temperatures of-15$0^{\circ}C$~$0^{\circ}C$ and the fracture toughness (estimated $K_{JC}$ ) was calculated from the indentation load-depth data. For all steels the temperature dependence of the estimated fracture toughness was almost the same as that ASTM $K_{JC}$ master curve The reference temperatures( $T_{o}$)of the steels were determined form the estimated $K_{JC}$ versus temperature curves. The reference temperature was well correlated with the index temperature of 41J Charpy impact energy( $T_{41J}$).).).

• 대한기계학회논문집A
• /
• 제25권12호
• /
• pp.1903-1910
• /
• 2001

The BI(Ball Indentation) method has a potential to assess the mechanical properties and to replace conventional fracture tests. In this study, the BI test system has been developed to evaluate material properties. Tensile tests, fracture toughness tests, hardness tests and BI tests were performed by the system using four classes of thermally aged specimens. The results of the BI tests were in good agreement with fracture characteristics from a standard fracture test method.

• 한국정밀공학회지
• /
• 제22권9호
• /
• pp.49-59
• /
• 2005

This paper describes a development of the extrusion process and estimation of the weldability for multi cell tubes used to cooling system of automobiles. A study on extrusion process is performed through the 3D FE simulation in non-steady state and extrusion experimentation. Also, nano-indentation test is employed to estimate the weldability of tubes. Especially, An evaluation of the weldability using the nano-indentation is accomplished as compared with nano-hardness in welded part and in the others. Finally, the pattern of the mandrel defection is investigated according to shapes of the porthole and/or chamber.