• Korean Journal of Materials Research
• /
• v.29 no.12
• /
• pp.757-763
• /
• 2019

A stacked high-voltage (900 V) Al electrolytic capacitor made with ZrO₂ coated anode foils, which has not been studied so far, is realized and the effects of Zr-Al-O composite layer on the electric properties are discussed. Etched Al foils coated with ZrO₂ sol are anodized in 2-methyl-1,3-propanediol (MPD)-boric acid electrolyte. The anodized Al foils are assembled with stacked structure to prepare the capacitor. The capacitance and dissipation factor of the capacitor with ZrO₂ coated anode foils increase by 41 % and decrease by 50 %, respectively, in comparison with those of Al anode foils. Zr-Al-O composite dielectric layer is formed between separate crystalline ZrO₂ with high dielectric constant and amorphous Al₂O₃ with high ionic resistivity. This work suggests that the formation of a composite layer by coating valve metal oxide on etched Al foil surface and anodizing it in MPD-boric acid electrolyte is a promising approach for high voltage and volume efficiency of capacitors.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.3
• /
• pp.143-148
• /
• 2004

This paper shows property conversion of water and removing characteristics of Escherichia coli for discharge tube with $ZrO_2$ beads. At the result of the removal characteristic experiments of Escherichia coli using the discharge tube with $ZrO_2$ beads, because the electric field is also increased when input voltage is increased, the removal characteristic of Escherichia coli was appeared relation connection to input voltage. And if a passing number of test water in discharge tube with $ZrO_2$beads is increased, the removal ratio of Escherichia coli is to be increased because passing number of electric field section is increased. And if diameter of $ZrO_2$beads is increased, the removal time of Escherichia coli is to be decreased because dielectric polalization of $ZrO_2$beads. Also, the removal ratio of Escherichia coli of the discharge tube with $ZrO_2$beads. is appeared higher than the removal ratio of the discharge tube without $ZrO_2$beads. And a satulation punt of ozone and $H_2$ $O_2$generation density inner water was appeared near 60[min].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.550-553
• /
• 2003

This paper was shown water properly conversion and removal characteristic of escherichia coli for discharge tube with $ZrO_2$ beads. At the result of the removal characteristic experiments of escherichia coli using the discharge tube with $ZrO_2$ beads, because the electric field is also increased when input voltage is increased, the removal characteristic of escherichia coli was appeared relation connection to input voltage. And if a passing number of test water in discharge tube with $ZrO_2$ beads is increased, the removal ratio of escherichia coli is to be increased because passing number of electric field section is increased. And if diameter of $ZrO_2$ beads is increased, the removal time of escherichia coli is to be decreased because dielectric polalization of $ZrO_2$ beads. Also, the removal ratio of escherichia coli of the discharge tube with $ZrO_2$ beads. is appeared higher than the removal ratio of the discharge tube without $ZrO_2$ beads. And a salutation point of ozone and $H_2O_2$ generation density inner water was appeared near 60[min].

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.377-383
• /
• 1997

Yttria-stabilized TZP alloyed with pentavalent oxides $(Ta_2O_5,\;Nb_2O_5)$ were fabricated by the conventional sintering method at $1500^{\circ}C$ in air to construct the simplified ternary phase diagram. The phase stability of tetragonal -$ZrO_2$ from the quasi-binary system $ZrO_2-YTa(Nb)O_4$, which do not transform to monoclinic-$ZrO_2$ even for a wide range of grain size and annealing temperature, was investigated to determine composition region of the non-transformable $t-ZrO_2$ solid solution$(NT_{ss})$. Phase stability of $NT_{ss}$ was probably due to the enhanced stability of $_YTa(Nb)O4$ having the tetragonal fergusonite structure. It was experimentally found that mixtures having $NT_{ss}$ alloyed with $T_{ss}$ by weight%% showed both excellent phase stability of $t-ZrO_2$ and fracture toughness even though the calculated composition of the mixture /was located outside $NT_{ss}$ composition region.

• Korean Chemical Engineering Research
• /
• v.52 no.4
• /
• pp.443-450
• /
• 2014

Selective catalytic reduction of nitrogen monoxide by hydrogen ($H_2$-SCR of NO) over platinum catalysts impregnated on zirconia-incorporated silica ($ZrO_2-SiO_2$) and manganese oxide ($MnO_x$) was investigated. $Pt-MnO_x$ catalyst showed low conversions and low yields of $N_2O$ and $NO_2$ at $100{\sim}350^{\circ}C$. On the other hand, NO conversions over $Pt/ZrO_2-SiO_2$ were very high, but $N_2O$ was predominantly produced at $100-150^{\circ}C$ and the yield of $NO_2$ increased with temperature at $200-300^{\circ}C$, resulting in poor $N_2$ yields. $Pt-MnO_x/ZrO_2-SiO_2$ exhibited a small enhancement in $N_2$ yield at $100-150^{\circ}C$ due to the synergy of $MnO_x$ and $ZrO_2-SiO_2$. The surface composition and oxidation state of the catalyst components and the acidity of the catalysts were examined. IR spectra of the adsorption of NO and their subsequent reactions with hydrogen on these catalysts were also recorded. The variations of conversion and product yield according to the catalyst components in the $H_2$-SCR of NO were discussed in relation to their catalytic roles.

• Journal of the Korean Ceramic Society
• /
• v.23 no.3
• /
• pp.87-93
• /
• 1986

Yttria-bismuth-stabilized zirconia was investigated with respect to the amount of $Bi_2O_3$ addition in the ran-ge of 0.5~5mol% to the base composition of $(ZrO_2)_{0.92}(Y_2O_3)_{0.08}.Bismuth was introduced into the ma-terial with $Bi_2O_3-SiO_2$ glasses in order to reduce the evaporation of components. The sinterbility evaporation of components phase formation and microstructure were evaluated depending on the amount of $Bi_2O_3-SiO_2$ glass addition. Two probe A. C conductivity measurement was subjected to all the specimens and the result was discussed on the possible substitution of $Bi^{3+}$ for $Zr^{4+}$ and interistial $Si^{4+}$ in the fluorite structure of zirconia crystal there-upon the possible change in the capability of oxygen transference within the material. It was found that the addition of $Bi_2O_3$ could improve the sinterbility of material very much while not so much.oxygen sensing material suitable for relative low temperature firing.

• Korean Journal of Materials Research
• /
• v.27 no.4
• /
• pp.179-183
• /
• 2017

$2ZrO_2{\cdot}P_2O_5$ powder, which is not synthesized by solid reaction method, was successfully synthesized through PVA solution method. In this process, the firing temperature and the PVA content strongly affected the crystallization behavior and final particle size. A stable ${\alpha}$-phase $2ZrO_2{\cdot}P_2O_5$ was synthesized at a firing temperature of $1200^{\circ}C$ and holding time of 4 h. ${\beta}$-phase $2ZrO_2{\cdot}P_2O_5$ was observed, with un-reacted $ZrO_2$ phases, for firing temperatures lower than $1200^{\circ}C$. In terms of the PVA content effect, the powder prepared with a PVA mixing ratio of 12:1 showed stable ${\alpha}$-phase $2ZrO_2{\cdot}P_2O_5$; however, the ${\beta}$-phase was found to co-exist at relatively higher PVA content. The synthesized ${\alpha}$-phase $2ZrO_2{\cdot}P_2O_5$ powder showed an average particle size of 100~250 nm and an average thermal expansion coefficient of $-2.5{\times}10^{-6}/^{\circ}C$ in the range of room temp. ${\sim}800^{\circ}C$.

• Economic and Environmental Geology
• /
• v.37 no.6 s.169
• /
• pp.603-612
• /
• 2004

Pyrochlore is known as one of the most promising materials for the immobilization of radionuclide in high level waste. This study included the synthesis, phase relation and characteristics of $pyrochlore(CaCeZr_xTi_{2-x}O_{7,\;x=0.2\~2.0)$ in the system of Ca-Ce-Zr-Ti-O. Using the CPS(Cold pressing and sintering) method, the mixtures of $CaCO3_,\;CeO_2,\;ZrO_2\;and\;TiO_2$ oxides were pressed, and sintered at $1100\~1600^{\circ}C$ for 20 hours. The optimal synthetic conditions at various compositions were differed from 1300 to $1600^{\circ}C$ Even in the optimal temperatures, pyrochlore or fluorite coexisted with minor amount of perovskite, $CeO_2\;or\;Ce_{0.75}Zr_{0.25}O_2$. It was confirmed that pyrochlore and fluorite structures were stable at $x\leq0.6\;and\;x\geq1.0$, respectively. Especially, the compositions of pyrochlore or fluorite showed non-stoichiometric compositions in that contents of Ca and Ti were more deficient and those of Zr and Ce were more excess than batch compositions with the increase of x value. These characteristics stemmed from the behavior of elements occupied at eight- and six-coordinated site, and then caused the coexistence of perovskite, $CeO_2\;or\;Ce_{0.75}Zr_{0.25}O_2$ along with pyrochlore or fluorite.

• Journal of the Korean Ceramic Society
• /
• v.42 no.1
• /
• pp.7-10
• /
• 2005

[ $TiO_{2}-ZrO_{2}$ ] powders were successfully synthesized by the sol-gel process using titanium iso-propoxide as a precursor. The amorphous $TiO_{2}$ particles, 70 nm in size, homogenously adhered to the surface of $ZrO_{2}$ the powders. After calcination at $450^{circ}C$, most of the $TiO_{2}$ powders appeared as an anatase type, whereas they changed to a rutile phase at $750^{circ}C$. For comparison of photocata­lytic activity, $TiO_{2}-ZrO_{2}$ nano-sized powders calcined at $450^{circ}C,\;600^{circ}C,\;and\;750^{circ}C$ were used. In the $TiO_{2}-20wt\%$ $ZrO_{2}$ powders cal­cined at $450^{circ}C$, there was excellent removal efficiency of Methyl Orange (MO). For the calcination temperature increased, $TiO_{2}­ZrO_{2}$ nano-sized powders increased $ZrO_{2}$ contents showed the good photoactivity for the photooxidation of MO.

• Journal of the Korean Ceramic Society
• /
• v.36 no.12
• /
• pp.1390-1395
• /
• 1999

Zr(Y,Ce)O2 TZP ceramics were prepared by sintering compacts of 3 mol% Y2O3-TZP(3Y-TZP) powders with different amount of 12 mol% CeO2-TZP(12Ce-TZP) in air at 140$0^{\circ}C$ for 2 h. The phase changes microstructure and mechanical properties of Zr(Y. Ce)O2 TZP after hydrothermal aging(20$0^{\circ}C$ 5h) were investigated. Although an addition of 12Ce-TZP accelerated the grain growth of Zr(Y, Ce)O2 TZP it restrained the transformation of tetragonal to the monoclinic phase during aging. The degradation in mechanical properties of sintered bodies was governed by the formed monoclinic phase and chemical composition. Induced Vickers indentation crack was propagated intergranually. From SEM observation of the fracture surfaces the pull-out of individual grain was confirmed.