• 한국표면공학회지
• /
• 제47권2호
• /
• pp.81-85
• /
• 2014

Ga doped ZnO (GZO)/Al bi-layered films were deposited on the glass substrate by RF and DC magnetron sputtering and then vacuum annealed at different temperatures of 100, 200 and $300^{\circ}C$ for 30 minutes to consider the effects of annealing temperature on the structural, electrical and optical properties of the films. For all depositions, the thicknesses of the GZO and Al films were kept constant at 95 and 5 nm, respectively, by controlling the deposition time. As-deposited GZO/Al bi-layered films showed a relatively low optical transmittance of 62%, while the films annealed at $300^{\circ}C$ showed a higher transmittance of 81%, compared to the other films. In addition, the electrical resistivity of the films was influenced by annealing temperature and the lowest resistivity of $9.8{\times}10^{-4}{\Omega}cm$ was observed in the films annealed at $300^{\circ}C$. Due to the increased carrier mobility, 2.35 $cm^2V^{-1}S^{-1}$ of the films. From the experimental results, it can be concluded that increasing the annealing temperature enhanced the optical and electrical properties of the GZO/Al films.

• 대한금속재료학회지
• /
• 제48권6호
• /
• pp.565-569
• /
• 2010

We report on the characteristics of indium-oxide-doped ZnO (IZO) ohmic contact to p-GaN. The IZO ohmic contact layer was deposited on p-GaN by a Roll-to-Roll (RTR) sputter method. IZO contact film with a thickness of 360, 230 and 100 nm yielded an ohmic contact resistance of $4.70{\times}10^{-4}$, $5.95{\times}10^{-2}$, $4.85{\times}10^{-1}\;{\Omega}cm^{2}$ on p-GaN when annealed at $600{^{\circ}C}$ for 1 min under a nitrogen ambient, respectively. While the transmittance of IZO film with a thickness of 360 nm slightly increased in the wavelength range of 380-800 nm after annealing, the transmittance rapidly increased up to 80% after annealing at $600{^{\circ}C}$ in the wavelength range of 380~430 nm because the crystallization of IZO film and created Ga vacancies near the p-GaN surface region were affected by the annealing. These results indicate that ohmic contact resistance and transmittance of the IZO films improved.

• 한국정보통신학회논문지
• /
• 제18권10호
• /
• pp.2497-2502
• /
• 2014

본 연구에서는 고주파 마그네트론 스퍼터링 법으로 RF 파워 (50~80 W) 를 변화시켜가며 PES 플라스틱 기판 위에 GZO ($Ga_2O_3$ : 5 wt %, ZnO : 95 wt %) 박막을 제작하여, 광학적 및 전기적 특성을 조사하였다. XRD 측정을 통해 공정 조건에 관계없이 모든 GZO 박막이 c 축으로 우선 성장함을 확인할 수 있었고, 70W에서 제작한 GZO 박막이 반가폭 $0.44^{\circ}$로 가장 우수한 결정성을 나타내었다. 박막의 표면을 AFM 으로 조사한 결과, 표면 거칠기 값은 RF 파워 70 W 에서 제작한 박막에서 가장 낮은 값인 0.20 nm 를 나타내었다. Hall 측정 결과, RF 파워 70 W에서 제작한 GZO 박막에서 가장 낮은 비저항 $6.93{\times}10^{-4}{\Omega}{\cdot}cm$ 값과 가장 높은 캐리어 농도 $7.04{\times}10^{20}cm^{-3}$ 및 이동도 $12.70cm^2/Vs$ 값을 나타내었다. 모든 GZO 박막은 RF 파워에 무관하게 가시광 영역에서 약 80 % 정도의 투과율을 나타냈으며, 캐리어 농도의 증가에 따라 에너지 밴드갭이 청색 편이 되는 Burstein-Moss 효과도 관찰할 수 있었다.