• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2006년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.69-70
• /
• 2006

The ITO thin films were prepared by Facing Targets Sputtering(FTS) method on polyethersulfon(PES) substrate. The ITO thin films were deposited with the film thickness of 100nm at room temperature and working gas pressure of 1 mTorr. As a function of sputtering conditions, electrical and optical properties of prepared ITO thin films were evaluated by Hall Effect Measurement(EGK) and UV-VIS spectrometer(HP), respectively. From the results, the ITO thin films was deposited was with a resistivity $8.3{\times}10^{-4}[{\Omega}-cm]$ and transmittance over 80% in the visible range.

• 한국세라믹학회지
• /
• 제44권6호
• /
• pp.313-318
• /
• 2007

ITO (Indium-tin oxide) thin films have been prepared by a sol-gel spinning coating method and fired and annealed in the temperature range of $450-600^{\circ}C$. The XRD patterns of the films indicated the main peak of (222) plane and showed higher crystallinity with increasing an annealing temperature. The surface of the ITO thin films were treated with 0.1 N HCl 20% solution at room temperature. The effects of surface treatment on electrical properties and surface morphologies of the ITO films were investigated with the results of sheet resistance and FE-SEM, AFM images. The samples, subsequently treated with acidic solution for 40 sec showed the sheet resistance of $0.982\;k{\Omega}/square$. The surface treatment using acidic solution diminished the RMS (root mean square) value and the residual carbon content of the ITO films. It seemed that the acid-cleaning of the ITO thin films lead to the decrease of surface roughness and sheet resistance.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.175-175
• /
• 2010

The etching characteristics with etch rate of ITO thin films in an $O_2/BCl_3$/Ar plasma were investigated. The etch rate of ITO thin films increased with increasing $O_2$ content from 0 to 10 % in $BCl_3$/Ar plasma, whereas that of ITO decreased with increasing $O_2$ content from 10 % to 30 % in $BCl_3$/Ar plasma. The maximum etch rate of 65.9 nm/min for the ITO thin films was obtained at 10 % $O_2$ addition. The etch conditions were the RF power of 500 W, bias power of 200 W, and process pressure of 2 Pa. The analysis of x-ray photoelectron spectroscopy (XPS) was carried out to investigate the chemical reactions between the surfaces of ITO thin films and etch species.

• 한국표면공학회지
• /
• 제38권5호
• /
• pp.179-182
• /
• 2005

Indium Tin Oxide (ITO) thin films were deposited from various target densities ($98.7\%\~99.6\%$) using RF magnetron sputtering. Effect of the sputtering target densities on the structural, electrical and optical properties of deposited ITO thin films was investigated. The preferable (400) crystalline orientation peak was observed on the films deposited from > $99.0\%$ target density. Higher target density produced films with higher roughness but lower resistivity. All of the deposited films showed optical transmittance more than $85\%$ in the visible wavelength region. It is necessary to use the highest target density for sputtering deposition of ITO thin films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.522-525
• /
• 2004

ITO thin films $({\sim}150\;nm)$ are deposited on glass substrates by different deposition condition. The sheet resistance of ITO thin films measured by using a four probe station. The microstructure of these films is determined using a X-ray diffractometer (XRD) and a scanning electron microscope (SEM) and a atomic force microscope (AFM). The sheet resistance of ITO thin films compared $s_{11}$ values by using a near field scanning microwave microscope.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.1042-1045
• /
• 2004

ITO thin films ($\sim150nm$) are deposited on glass substrates by different deposition condition. The sheet resistance of ITO thin films measured by using a four probe station. The microstructure of these films is determined using a X-ray diffractometer (XRD) and a scanning electron microscope (SEM) and a atomic force microscope (AEM). The sheet resistance of ITO thin films compared $s_11$ values by using a near field scanning microwave microscope.

• 한국반도체및디스플레이장비학회:학술대회논문집
• /
• 한국반도체및디스플레이장비학회 2006년도 추계학술대회 발표 논문집
• /
• pp.56-59
• /
• 2006

The ITO thin films were prepared by FTS (Facing Targets Sputtering) system on polycarbonate (PC) substrate. The ITO thin films were deposited with a film thickness of 100nm at room temperature. As a function of sputtering conditions, electrical and optical properties of prepared ITO thin films were measured. The electrical and optical characteristics of the ITO thin films were evaluated by Hall Effect Measurement (EGK) and UV-VIS spectrometer (HP), respectively. From the results, the ITO thin film was deposited with a resistivity $8{\times}10^{-4}[{\Omega}-cm]$ and transmittance over 80%.

• 대한기계학회논문집A
• /
• 제26권5호
• /
• pp.976-985
• /
• 2002

The purpose of this paper is that the roughness(Rrms = 31$\AA$, Rp-v = 270$\AA$) of ITO thin film deposited by sputtering method for OELD is improved to Rrms $\leq$ 10$\AA$, Rp-v $\leq$ 80$\AA$ by chemical mechanical polishing(CMP). First, ITO thin films are polished with a variety of consumables (Pads, Slurries) to choose proper some for the roughness improvement and the CMP mechanism of ITO thin films is demonstrated on the ground of the experiment results. Henceforth, the CMP characteristics (Removal rate, Non-uniformity) of chosen consumables are evaluated according to processing conditions (Polishing pressures, Table velocities) and suitable conditions for ITO film CMP are selected. Finally, the electrical and optical properties (Sheet resistance, Transmittance) of ITO thin films are investigated to verify whether or not ITO thin film are still suitable for OELD after polished.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 제5회 영호남 학술대회 논문집
• /
• pp.89-92
• /
• 2003

ITO thin films were deposited by RF-magnetron sputtering method and crystallization behavior of the films with and without external heating as a function of deposition time was examined. X-ray diffraction results indicated an amorphous state of the film when the deposition time is short about 10 min. When the deposition time was increased over 20 min development of crystallization of the films is observed. Because RF-sputtering transfers the high-energy to the growing film by energetic bombardment, it is believed that considerable activation energy for the crystallization of the film has transferred during deposition, which resulted in the crystallization of ITO thin films without external energy supply.

• 대한금속재료학회지
• /
• 제50권7호
• /
• pp.545-548
• /
• 2012

The optical and electronic properties of Indium Tin Oxide (ITO) thin films deposited on a RF-plasma treated glass substrate were investigated by X-Ray Photoelectron Spectroscopy (XPS), Ultra-violet Photoelectron Spectroscopy (UPS), Reflected Electron Energy Loss Spectroscopy (REELS). The modification of glass substrates was carried out by varying the time of the plasma surface treatment in an oxygen atmosphere. The focus of this research was to examine how the optical and electronic properties of ITO thin films change with the plasma treatment time. The surface energy increased since the carbon bonds were removed from the surface after the glass substrate received the surface treatment. The ITO thin films produced on the glass substrate with surface treatment showed that the high optical transmittance was approximately 85%. The measured band gap energy was as high as 3.23 eV when the plasma treatment time was 60 s and the work function after the treatment was increased by 0.5 eV in comparison to that before the treatment of 60 s. The ITO thin film exhibited an excellent sheet resistance of $2.79{\Omega}/{\Box}$. We found that the optical and electronic properties of ITO thin films can be improved by RF-plasma surface treatment.