• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 추계학술대회 논문집 Vol.19
• /
• pp.91-92
• /
• 2006

Aluminum-doped zinc oxide (AZO) films are attractive materials as transparent conductive electrode because they are inexpensive, nontoxic and abundant element compared with indium tin oxide (ITO). AZO films have been deposited on glass (corning 1737) substrates by RF magnetron sputtering system. The electrical resistivity of AZO films was $1.81{\times}10^{-2}{\Omega}cm$ and the average transmittance in the visible range 400-800 nm was more than 76% Organic light-emitting diodes (OLEDs) with AZO/TPD/$Alq_3$/Al configuration were fabricated. The current density-voltage properties of devices were studied and compared with ITO devices fabricated under the same conditions.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.273.2-273.2
• /
• 2014

Sputtering process has been widely used in Si-based semiconductor industry and it is also an ideal method to deposit transparent oxide materials for thin-film transistors (TFTs). The oxide films grown at low temperature by conventional RF sputtering process are typically amorphous state with low density including a large number of defects such as dangling bonds and oxygen vacancies. Those play a crucial role in the electron conduction in transparent electrode, while those are the origin of instability of semiconducting channel in oxide TFTs due to electron trapping. Therefore, post treatments such as high temperature annealing process have been commonly progressed to obtain high reliability and good stability. In this work, the scheme of electron-assisted RF sputtering process for high quality transparent oxide films was suggested. Through the additional electron supply into the plasma during sputtering process, the working pressure could be kept below $5{\times}10-4Torr$. Therefore, both the mean free path and the mobility of sputtered atoms were increased and the well ordered and the highly dense microstructure could be obtained compared to those of conventional sputtering condition. In this work, the physical properties of transparent oxide films such as conducting indium tin oxide and semiconducting indium gallium zinc oxide films grown by electron-assisted sputtering process will be discussed in detail. Those films showed the high conductivity and the high mobility without additional post annealing process. In addition, oxide TFT characteristics based on IGZO channel and ITO electrode will be shown.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2011년도 제40회 동계학술대회 초록집
• /
• pp.101-101
• /
• 2011

투명전도성산화물(transparent conducting oxides, TCOs) 박막으로써 널리 쓰이는 산화인듐주석(indium tin oxide, ITO)은 전기 전도성과 광 투과성이 우수하여 주로 유기발광다이오드(organic light-emitting diode, OLED)의 전극, 발광다이오드(light-emitting diode, LED)의 current spreading 층 및 태양전지(solar cell)의 윈도우층(window layer) 등의 광전자 소자로 응용되고 있으나, 고가의 indium 가격과 인체에 유해한 독성 등이 문제점으로 지적되고 있다. 따라서 indium의 함량을 저감한 새로운 조성의 TCO 또는 indium을 함유하지 않은 친환경적인 TCO 대체 재료 개발의 필요성이 증대되고 있다. 이러한 재료 중 하나인 AZO (Al-doped zinc oxide, $Al_2O_3$: 2 wt.%)는 3.82eV의 넓은 에너지 밴드갭을 가지며, 가시광선 및 근 적외선 파장 영역에 대하여 90% 이상의 높은 투과율을 나타낸다. 또한, 습식식각이 가능하며, 매우 풍부하여 원가가 매우 저렴하고, 독성이 없다. 본 연구에서는 박막 증착율이 높고, 제작과정의 조정이 용이한 RF magnetron 스퍼터를 이용하여 glass 기판 위에 AZO 박막을 성장하고, $N_2$ 분위기에서 다양한 온도 조건에서 열처리(rapid thermal annealing, RTA)하여 전기 및 광학적 특성에 대하여 비교 분석하였다. 또한, 이후에 기존의 성장방법과 달리 고가의 진공 장비를 사용하지 않고, 저온에서도 간단한 구조의 장비를 이용하여 균일한 나노구조를 성장시킬 수 있는 전기화학증착법(electrochemical deposition)으로 AZO 박막위에 ZnO 나노로드를 다양한 성장조건에 따라 성장시켜 광학적 특성을 비교 분석하였다.

• 반도체디스플레이기술학회지
• /
• 제14권3호
• /
• pp.33-36
• /
• 2015

It has increased several decades in the field of Indium Tin Oxide (ITO) transparent thin film, However, a major problem with this ITO thin film application is high cost compared with other transparent thin film materials[1]. So far, in order to overcome this disadvantage, we show that a transparent ITO/Ag/i-ZnO multilayer thin film electrode would be more cost-effective and it has not only highly transparent but also conductive properties. The aim of this research has therefore been to try and establish how ITO/Ag/i-ZnO multilayer thin film would be more effective than ITO thin film. Herein, we report the properties of ITO/Ag/i-ZnO multilayer thin film by using optical spectroscopic method and measuring sheet resistance. At a certain total thickness of thin film, sheet resistance of ITO/Ag/i-ZnO multilayer was drastically decreased than ITO layer approximately $40{\Omega}/{\Box}$ at same visible light transmittance. (minimal point $5.2{\Omega}/{\Box}$). Tendency, which shows lowly sheet resistive in a certain transmittance, has been observed, hence, it should be suitable for transparent electrode device.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2009년도 9th International Meeting on Information Display
• /
• pp.330-332
• /
• 2009

Highly stable bottom gate thin film transistors(TFTs) with a zinc indium tin oxide(Zn-In-Sn-O:ZITO) channel layer have been fabricated by rf-magnetron co-sputtering using a indium tin oxide(ITO:90/10), a tin oxide and a zinc oxide targets. The ZITO TFT (W/L=$40{\mu}m/20{\mu}m$) has a mobility of 24.6 $cm^2$/V.s, a subthreshold swing of 0.12V/dec., a turn-on voltage of -0.4V and an on/off ratio of >$10^9$. When gate field of $1.8{\times}10^5$ V/cm was applied with source-drain current of $3{\mu}A$ at $60^{\circ}C$, the threshold voltage shift was ~0.18 V after 135 hours. We fabricated AM-OLED driven by highly stable bottom gate Zn-In-Sn-O TFT array.

• 한국전기전자재료학회논문지
• /
• 제23권4호
• /
• pp.327-332
• /
• 2010

We report on the effect of PET substrate preheating on the characteristics of the flexible and transparent indium tin oxide (ITO) electrode grown by a specially designed roll-to-roll sputtering system for touch panel applications. It was found that electrical and optical properties of the roll-to-roll sputter grown ITO film were critically dependent on the preheating of the PET substrate. In addition, the roll-to-roll sputter-grown ITO film after post annealing test at $140^{\circ}C$ for 90 min showed stable electrical and optical properties. The low sheet resistance and high optical transmittance of the ITO film grown on the preheated PET substrate demonstrate that the preheating process before ITO sputtering is one of the effective way to improve the characteristics of ITO/PET film. Furthermore, the superior flexibility of the ITO electrode grown on the preheated PET substrate indicates that the preheating treatment is a promising technique to obtain robust ITO/PET sample for touch panel applications.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제44회 동계 정기학술대회 초록집
• /
• pp.581-581
• /
• 2013

ITO (Indium Tin oxide)는 비화학 양론적 조성을 띄는 n-type 반도체 특성이 있으며 가시광 영역(380~780 nm)의 파장에 대한 높은 광 투과도(>85%)를 가지며 비교적 높은 전도도(${\sim}10^4/{\Omega}-cm$)를 갖고 화학적 안정성이 우수하여 투명전극 박막으로 많이 사용되어왔다. 또한, PET film은 전기절연성, 내후성이 우수하고, 85%의 투과율을 보이는 특성에 의하여 Flexible display의 기판으로 많은 연구가 진행되고 있다. 이와 같은 PET film에 ITO를 증착하여 광 투과도와 전기전도도가 우수한 Flexible display의 투명전극으로 많은 연구 개발이 이루어지고 있다. Flexible ITO 박막의 특성을 향상하기 위해서는 $200^{\circ}C$ 이상의 열처리 공정이 필요하지만, PET는 약 $200^{\circ}C$ 이상에서 열 변형이 일어나므로 열처리 공정이 어렵고 이러한 문제점을 해결하기 위해 ITO/PET film에서 PET film의 변형 없이 ITO 박막의 표면에 전자빔 형태로 조사하여 박막의 물성을 개선하는 연구가 진행되고 있다 [1]. 본 연구에서는 ITO/$SiO_2$가 증착된 PET film에 전자빔을 조사하여 ITO 박막의 물성 변화를 관찰하였고, 전자빔 에너지 변화 및 전자빔 조사 시간에 따라 ITO film의 전기적, 광학적 특성 변화를 분석하였다. 구조적 특성은 XRD (X-ray diffraction), 전기적 특성은 4-point probe, Hall measurement를 이용하였으며, 가시광영역의 광 투과도는 UV-Vis spectrometer로 측정하였다. 전기 광학적 특성 변화는 Figure of Merit (FOM) 수치로 분석하였다. 이 실험으로 PET film에 직접적인 열을 가하지 않으면서 ITO 박막의 표면에 전자빔을 조사 하여, 박막의 전기전도도 및 광 투과율, 결정성 향상 등을 관찰할 수 있었다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 춘계학술발표강연 및 논문개요집
• /
• pp.130-130
• /
• 2003

일반적으로 Indium tin oxide (ITO)는 유기EL 소자 제작 공정에서 필수 불가결한 물질로 알려져 있다. ITO는 정공 수송의 기능을 하게 되는데 정공 주입의 효율을 향상시키기 위해서는 ITO 표면의 저 저항화와 ITO/유기박막 접합계면의 일함수 값의 적절한 균형이 중요하다. 그리고 현재 플라즈마를 이용한 ITO 기판의 세정은 산소 래디칼을 이용하여 표면을 산화하는 방식인 산소 플라즈마를 이용한 세정 방법이 널리 이용되고 있다. 본 연구에서는 ITO 표면의 탄소 오염물을 제거하여 저항특성을 향상시키기 위하여 원거리 산소와 수소 플라즈마 세정을 적용하였고, 그에 따른 탄소를 포함하는 오염물의 제거 효율과 산소와 수소 플라즈마로 처리된 ITO 표면의 특징을 기술하였다. 실험에 사용된 플라즈마 소스는 radio-frequency(RF) 플라즈마이고, 원거리 플라즈마 세정 시스템과 표면 분석 장비인 X-ray photoelectron spectroscopy(XPS)가 in-situ로 연결되어 있는 진공장비로 분석을 하였다 플라즈마 세정 전에 전처리 세정을 시행하지 알았으며, 세정 후 in-situ XPS에 의해서 화학 조성 및 결합 구조의 변화를 분석하였다. 또한 일함수와 면저항 값을 측정하고 그에 따른 표면의 저항 특성 및 표면 전위에 관하여 세정 효율과 연관지어 해석하였다. 원거리 산소/수소 플라즈마 세정 후 ITO 표면의 탄소오염물이 검출한계 이하로 효과적으로 제거된 것을 in-situ XPS 분석 결과로 확인하였고, 플라즈마 처리 순서 및 플라즈마 파워를 변화하여 그에 따른 표면의 결합 상태 및 화학 조성의 변화를 비교 분석하였다.

• 한국분말재료학회지
• /
• 제15권6호
• /
• pp.450-457
• /
• 2008

The objectives of this study were the development of a synthesis technique for highly active nanosized ITO powder and the understanding of the reaction mechanisms of the ITO precursors. The precipitation and agglomeration phenomena in ITO and $In_{2}O_{3}$ precursors are very sensitive to reaction temperature, pH, and coexisting ion species. Excessive $Cl^-$ ion and $Sn^{+4}$ ions had a negative effect an synthesizing highly active powders. However, with a relevant stabilizing treatment the shape and size of ITO and $In_{2}O_{3}$ precursors could be controlled and high density sintered products of ITO were obtained. By applying the reprecipitation process (or stabilization technique), highly active ITO and $In_{2}O_{3}$ powders were synthesized. Sintering these powders at $1500^{\circ}C$ for 5 hours produced 97% dense ITO bodies.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.417-417
• /
• 2009

Although a transparent conductive film (TCF) belongs to essential supporting materials for many device applications such as touch screens, flat panel displays, and sensors, a conventional transparent conductive material, indium-tin oxide (ITO), suffers from considerable drawback because the price of indium has soared since 2001. Despite a recent falloff, a demand of ITO is expected to increase sharply in the future due to the trend of flat panel display technologies toward flexible, paper-like features. There have been recently extensive studies to replace ITO with new materials, in particular, carbon nanotubes (CNTs) since CNTs possess excellent properties such as flexibility, electrical conductivity, optical transparency, mechanical strength, etc., which are prerequisite to TCFs. This study fabricated TCFs with single-walled carbon nanotubes (SWCNTs) produced by arc discharge. The SWCNTs were dispersed in water with a surfactant of sodium dodecyl benzene sulfonate (NaDDBS) under sonication. Carbon black and fullerene nanoparticles were added to the SWCNT-dispersed solution to enhance contact resistance between CNTs. TCFs were manufactured by a filtration and transfer method. TCFs added with carbon black and fullerene nanoparticles were characterized by scanning electron microscopy (SEM), UV-vis spectroscopy (optical transmittance), and four-point probe measurement (sheet resistance).