• Journal of Technologic Dentistry
• /
• v.42 no.2
• /
• pp.91-98
• /
• 2020

Purpose: This study is to compare the flexural strength and modulus by inserting a mesh and stick type fiberglass reinforcement into resin specimens. Methods: Wax specimens (length 64 mm, width 39 mm, thickness 5 mm) are prepared according to ISO 20795-1:2013. Mesh type and stick type glass fiber reinforcements were prepared. The prepared wax specimens were used plaster and flask for investment. The flask was separated and the wax was removed. The heat curing resin was injected into the flask, and then a mesh type and stick type fiberglass reinforcement were inserted. The prepared resin specimen was cut into three equal parts (length 64 mm, width 10 mm, thickness 3.3 mm). The mesh type glass fiber reinforcement (MT group) and the stick type glass fiber reinforcement (ST group) were classified into two groups. The prepared specimen was measured using a universal testing machine (UTM). The data were analyzed by Mann-Whitney U test, and the significance level was set to 0.05. Results: In the flexural strength, the ST group was higher than the MT group, and there was a significant difference between the two groups (p<0.05). In the flexural modulus, the ST group was higher than the MT group, and there was a significant difference between the two groups (p<0.05). Conclusion: The stick-type glass fiber inreased the flexural strength than the mesh-type glass fiber reinforcement.

• The Journal of Korean Academy of Prosthodontics
• /
• v.62 no.2
• /
• pp.95-103
• /
• 2024

Purpose. With the advancement of digital technology, 3D printing is being utilized in the fabrication of denture base. Nevertheless, increasing microbial adhesion to the surface of denture base has been reported as the disadvantage of 3D-printed denture base. The purpose of this study is to investigate the antifungal properties and flexural strength of 3D-printed denture base resin according to the different contents of titanium dioxide nanoparticles. Materials and methods. Titanium dioxide nanoparticles were mixed with the 3D printing resin at the ratios of 0.5, 1, 1.5, and 2 wt%. Twenty specimens per each group were printed in the form of cylindrical shape (diameter: 20 mm, height: 3 mm) to evaluate antifungal properties. Ten specimens from each group underwent polishing using autogrinder, while the remaining ten specimens did not. Candida albicans in hyphae form was inoculated onto each specimen, optical density and colony-forming unit were analyzed. The surface of the specimen was observed using scanning electron microscopy. To evaluate the flexural strength, twenty specimens per each group were 3D printed in the form of rectangular prism shape (length: 64 mm, height: 10 mm, width: 3 mm) and three-point bending tests were conducted using universal testing machine according to ISO 20795-1. Results. Colony-forming unit of C.albicans and optical density of culture medium showed no difference between non-polished groups, but decreased in the polished groups at concentration of 1, 1.5, 2 wt% titanium dioxide nanoparticles. Flexural strength increased with titanium dioxide nanoparticle at concentration of 0.5, 1, 1.5 wt%, but decreased at 2 wt% compared to 1.5 wt%. Conclusion. When 1.5 wt% of titanium dioxide nanoparticles were added to the 3D-printed denture base resin with polishing, antifungal properties were increased.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.3
• /
• pp.183-195
• /
• 2020

Purpose: The purpose of this study is to compare the flexural strength of CAD/CAM denture base resins with conventional denture base resins based on their thicknesses. Materials and Methods: For the conventional denture base resins, Lucitone 199^® (C-LC) was used. DIOnavi - Denture (P-DO) and DENTCA Denture Base II (P-DC) were taken for the 3D printing denture base resins. For the prepolymerized PMMA resins, Vipi Block Gum (M-VP) and M-IVoBase^® CAD (M-IV) were used. The final dimensions of the specimens were 65.0 mm x 12.7 mm x 1.6 mm / 2.0 mm / 2.5 mm. The 3-point bend test was implemented to measure the flexural strength and flexural modulus. Microscopic evaluation of surface of fractured specimen was conducted by using a scanning electron microscope (SEM). After testing the normality of the data, one-way ANOVA was adopted to evaluate the differences among sample groups with a significance level of P = 0.05. The Tukey HSD test was performed for post hoc analysis. Results: Under the same thicknesses, there are significant differences in flexural strength between CAD/CAM denture base resins and conventional denture base resins except for P-DO and C-LC. M-VP showed higher flexural strength than conventional denture base resins, P-DC and M-IV displayed lower flexural strength than conventional denture base resins. Flexural modulus was highest in M-VP, followed by C-LC, P-DO, P-DC, M-IV, significant differences were found between all materials. In the comparison of flexural strength according to thickness, flexural strength of 2.5 mm was significantly higher than that of 1.6 mm in C-LC. Flexural strength of 2.5 mm and 2.0 mm was significantly higher than that of 1.6 mm in P-DC and M-VP. In M-IV, as the thickness increases, significant increase in flexural strength appeared. SEM analysis illustrates different fracture surfaces of the specimens. Conclusion: The flexural strength of different CAD/CAM denture base resins used in this study varied according to the composition and properties of each material. The flexural strength of CAD/CAM denture base resins was higher than the standard suggested by ISO 20795-1:2013 at a thickness of 1.6 mm or more though the thickness decreased. However, for clinical use of dentures with lower thickness, further researches should be done regarding other properties at lower thickness of denture base resins.

• Journal of Technologic Dentistry
• /
• v.42 no.4
• /
• pp.355-361
• /
• 2020

Purpose: In this study, we added two kinds of photoinitiators (CQ and TPO) to prepare two kinds of denture base resins (Bis-GMA series and UDMA series) for three-dimensional (3D) printing to compare and analyze their mechanical and biological properties and to find the optimal composition. Methods: Control specimens were made using the mold made of polyvinyl siloxane of the same size. Light curing was performed twice for 20 seconds on both the upper and lower surfaces with LED (light emitting diode) light-curing unit (n=10). Experimental 3D printing dental resins were prepared, to which two photoinitiators were added. Digital light processing type 3D printer (EMBER, Autodesk, CA, USA) was used for 3D printing. The specimen size was 64 mm×10 mm×3.3 mm according to ISO 20795-1. The final specimens were tested for flexural strength and flexural modulus, and MTT test was performed. Furthermore, one-way analysis of variance was performed, and the post-test was analyzed by Duncan's test at α=0.05. Results: The flexural strength of both Bis-GMA+CQ (97.12±6.47 MPa) and UDMA+TPO (97.40±3.75 MPa) was significantly higher (p<0.05) in the experimental group. The flexural modulus in the experimental group of UDMA+TPO (2.56±0.06 GPa) was the highest (p<0.05). MTT test revealed that all the experimental groups showed more than 70% cell activity. Conclusion: The composition of UDMA+TPO showed excellent results in flexural strength, flexural modulus, and biocompatibility.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.1
• /
• pp.331-336
• /
• 2018

Oral health is an essential requirement for maintaining and promoting health and quality of life while aging. It is known that there is a deep connection with hygienic management of dentures. However, despite the emphasis on the importance of clean management of dentures, there is a lack of quantitative research on denture-related detergents. Therefore, the purpose of this study is to evaluate food stain removal performance of three denture cleansers containing proteolytic enzymes. In addition, this study provides basic data on self-cleaning methods using detergents and suggests ways to improve effective treatment for oral health of elders in domiciliary care. In order to obtain quantitative data concerning food stain removal performance of each proteinase denture cleaner, the test evaluation method proposed by the Korean Consumer Agency, ISO 20795, was used. A total of 18 specimens were discolored for 48 hours in water dissolved with turmeric, and then washed with each denture cleaner for 24 hours. The cleaned denture specimens were measured quantitatively using a spectrophotometer to measure the color values of the denture specimens before the discoloration as well as the color values of the discolored specimens after cleaning with the denture cleanser. The experimental values were analyzed through one-way ANOVA with post-hoc Tukey's test, and statistically significant differences were found among the experimental groups. It was found that C had statistically significant stain removal performance compared with A and B(p<.05). All experiments were conducted for a total of 21 days, from July 3- 23, 2017. This study confirms that denture cleansers is a beneficial self-denture management method for domiciliary seniors. Therefore, it is necessary to extend accessibility for denture cleansers in order to to optimize domiciliary care for elderly oral hygiene and health.

• The Journal of Advanced Prosthodontics
• /
• v.10 no.2
• /
• pp.113-121
• /
• 2018

PURPOSE. The aim of this preliminary study was to investigate, for the first time, the effects of addition of titania nanotubes ($n-TiO_2$) to poly methyl methacrylate (PMMA) on mechanical properties of PMMA denture base. MATERIALS AND METHODS. $TiO_2$ nanotubes were prepared using alkaline hydrothermal process. Obtained nanotubes were assessed using FESEM-EDX, XRD, and FT-IR. For 3 experiments of this study (fracture toughness, three-point bending flexural strength, and Vickers microhardness), 135 specimens were prepared according to ISO 20795-1:2013 (n of each experiment=45). For each experiment, PMMA was mixed with 0% (control), 2.5 wt%, and 5 wt% nanotubes. From each $TiO_2$:PMMA ratio, 15 specimens were fabricated for each experiment. Effects of $n-TiO_2$ addition on 3 mechanical properties were assessed using Pearson, ANOVA, and Tukey tests. RESULTS. SEM images of $n-TiO_2$ exhibited the presence of elongated tubular structures. The XRD pattern of synthesized $n-TiO_2$ represented the anatase crystal phase of $TiO_2$. Moderate to very strong significant positive correlations were observed between the concentration of $n-TiO_2$ and each of the 3 physicomechanical properties of PMMA (Pearson's P value ${\leq}.001$, correlation coefficient ranging between 0.5 and 0.9). Flexural strength and hardness values of specimens modified with both 2.5 and 5 wt% $n-TiO_2$ were significantly higher than those of control ($P{\leq}.001$). Fracture toughness of samples reinforced with 5 wt% $n-TiO_2$ (but not those of 2.5% $n-TiO_2$) was higher than control (P=.002). CONCLUSION. Titania nanotubes were successfully introduced for the first time as a means of enhancing the hardness, flexural strength, and fracture toughness of denture base PMMA.

• Journal of dental hygiene science
• /
• v.15 no.3
• /
• pp.259-264
• /
• 2015

For this experiment, specimen was manufactured by injecting polymer and monomer into silicon mold with volume ratio of 2.5:1 based on ISO 20795-2 so that average thickness, width and length of specimen would be maintained as 3.3 mm, 10.0 mm and 65.0 mm, respectively depending on spray on technique. Specimen was divided into 3 groups ($25^{\circ}C$, $40^{\circ}C$, $70^{\circ}C$) depending on polymerization temperature and 10 specimen was manufactured for each group and it was polymerized in water tank of ${\pm}1^{\circ}C$ under the setting condition of polymerization time of 15 minutes and pressure of 3 bar. After keeping specimen in distilled water of $37^{\circ}C$ for over 48 hours before experiment, flexural strength (FS) and elasticity modulus (EM) of specimen being tested by using Intron (3344; Instron; Instron). SPSS ver. 16.0 was used for analysis and post-hoc test of Scheffe was performed after using one-way ANOVA. When comparing mean value of FS of resin for orthodontics, it was represented in the range of 71.500 MPa for $25^{\circ}C$ group, 74.920 MPa for $40^{\circ}C$ group and 76.880 MPa for $70^{\circ}C$ group and difference was shown in the order of $25^{\circ}C$ group <$40^{\circ}C$ group <$70^{\circ}C$ group but such difference was not significant statistically (p=0.052). Result of EM mean value of resin for orthodontics was more polymerization temperature was high, the more was significant difference represented in the order of $25^{\circ}C$ group <$40^{\circ}C$ group <$70^{\circ}C$ group (p<0.039).