Comparison of flexural strength according to thickness between CAD/CAM denture base resins and conventional denture base resins  

Lee, Dong-Hyung (Department of Prosthodontics, College of Dentistry, Dankook University)
Lee, Joon-Seok (Department of Prosthodontics, College of Dentistry, Dankook University)
Publication Information
Journal of Dental Rehabilitation and Applied Science / v.36, no.3, 2020 , pp. 183-195 More about this Journal
Abstract
Purpose: The purpose of this study is to compare the flexural strength of CAD/CAM denture base resins with conventional denture base resins based on their thicknesses. Materials and Methods: For the conventional denture base resins, Lucitone 199® (C-LC) was used. DIOnavi - Denture (P-DO) and DENTCA Denture Base II (P-DC) were taken for the 3D printing denture base resins. For the prepolymerized PMMA resins, Vipi Block Gum (M-VP) and M-IVoBase® CAD (M-IV) were used. The final dimensions of the specimens were 65.0 mm x 12.7 mm x 1.6 mm / 2.0 mm / 2.5 mm. The 3-point bend test was implemented to measure the flexural strength and flexural modulus. Microscopic evaluation of surface of fractured specimen was conducted by using a scanning electron microscope (SEM). After testing the normality of the data, one-way ANOVA was adopted to evaluate the differences among sample groups with a significance level of P = 0.05. The Tukey HSD test was performed for post hoc analysis. Results: Under the same thicknesses, there are significant differences in flexural strength between CAD/CAM denture base resins and conventional denture base resins except for P-DO and C-LC. M-VP showed higher flexural strength than conventional denture base resins, P-DC and M-IV displayed lower flexural strength than conventional denture base resins. Flexural modulus was highest in M-VP, followed by C-LC, P-DO, P-DC, M-IV, significant differences were found between all materials. In the comparison of flexural strength according to thickness, flexural strength of 2.5 mm was significantly higher than that of 1.6 mm in C-LC. Flexural strength of 2.5 mm and 2.0 mm was significantly higher than that of 1.6 mm in P-DC and M-VP. In M-IV, as the thickness increases, significant increase in flexural strength appeared. SEM analysis illustrates different fracture surfaces of the specimens. Conclusion: The flexural strength of different CAD/CAM denture base resins used in this study varied according to the composition and properties of each material. The flexural strength of CAD/CAM denture base resins was higher than the standard suggested by ISO 20795-1:2013 at a thickness of 1.6 mm or more though the thickness decreased. However, for clinical use of dentures with lower thickness, further researches should be done regarding other properties at lower thickness of denture base resins.
Keywords
CAD/CAM denture base resins; pre-polymerized PMMA block; 3D printing denture base resins; flexural strength; thickness;
Citations & Related Records
연도 인용수 순위
  • Reference
1 Zarb GA, Fenton AH. Prosthodontic treatment for edentulous patients. 13th ed. St. Louis; Mosby/Elsevier; 2012. p. 133, 136, 140.
2 Anusavice KJ, Shen C, Rawls R. Phillips' science of dental materials. 12th ed. Philadelphia; Saunders/Elsevier; 2012. p. 94, 97, 480, 481, 483.
3 Ucar Y, Akova T, Aysan I. Mechanical properties of polyamide versus different PMMA denture base materials. J Prosthodont 2012;21:173-6.   DOI
4 Darbar UR, Huggett R, Harrison A. Denture fracture - a survey. Br Dent J 1994;176:342-5.   DOI
5 Sasaki H, Hamanaka I, Takahashi Y, Kawaguchi T. Effect of long-term water immersion or thermal shock on mechanical properties of high-impact acrylic denture base resins. Dent Mater J 2016;35:204-9.   DOI
6 Kim SH, Watts DC. The effect of reinforcement with woven E-glass fibers on the impact strength of complete dentures fabricated with high-impact acrylic resin. J Prosthet Dent 2004;91:274-80.   DOI
7 Infante L, Yilmaz B, McGlumphy E, Finger I. Fabricating complete dentures with CAD/CAM technology. J Prosthet Dent 2014;111:351-5.   DOI
8 John J, Gangadhar SA, Shah I. Flexural strength of heat-polymerized polymethyl methacrylate denture resin reinforced with glass, aramid, or nylon fibers. J Prosthet Dent 2001;86:424-7.   DOI
9 Huggett R, Bates JF, Packham DE. The effect of the curing cycle upon the molecular weight and properties of denture base materials. Dent Mater 1987;3:107-12.   DOI
10 El Ghazali S, Glantz PO, Strandman E, Randow K. On the clinical deformation of maxillary complete dentures. Influence of denture-base design and shape of denture-bearing tissue. Acta Odontol Scand 1989;47:69-76.   DOI
11 Neihart TR, Li SH, Flinton RJ. Measuring fracture toughness of high-impact poly(methyl methacrylate) with the short rod method. J Prosthet Dent 1988;60:249-53.   DOI
12 Murakami N, Wakabayashi N, Matsushima R, Kishida A, Igarashi Y. Effect of high-pressure polymerization on mechanical properties of PMMA denture base resin. J Mech Behav Biomed Mater 2013;20:98-104.   DOI
13 Kelly E. Fatigue failure in denture base polymers. J Prosthet Dent 1969;21:257-66.   DOI
14 Diaz-Arnold AM, Vargas MA, Shaull KL, Laffoon JE, Qian F. Flexural and fatigue strengths of denture base resin. J Prosthet Dent 2008;100:47-51.   DOI
15 Zappini G, Kammann A, Wachter W. Comparison of fracture tests of denture base materials. J Prosthet Dent 2003;90:578-85.   DOI
16 International Organization for Standardization. ISO 20795-1:2013. Dentistry - base polymers. Part 1: denture base polymers. Geneva: ISO;2015.
17 American Society for Testing and Materials International. ASTM D790. Standard test methods for flexural properties of unreinforced plastics and electrical insulating materials.
18 Bidra AS, Taylor TD, Agar JR. Computer-aided technology for fabricating complete dentures: systematic review of historical background, current status, and future perspectives. J Prosthet Dent 2013;109:361-6.   DOI
19 Gharechahi J, Asadzadeh N, Shahabian F, Gharechahi M. Flexural strength of acrylic resin denture bases processed by two different methods. J Dent Res Dent Clin Dent Prospects 2014;8:148-52.
20 Neumeier TT, Neumeier H. Digital immediate dentures treatment: a clinical report of two patients. J Prosthet Dent 2016;116:314-9.   DOI
21 Pereyra NM, Marano J, Subramanian G, Qeuk S, Leff D. Comparison of patient satisfaction in the fabrication of conventional dentures vs. DENTCA (CAD/CAM) dentures: A case report. J N J Dent Assoc 2015;86:26-33.
22 Goodacre CJ, Garbacea A, Naylor WP, Daher T, Marchack CB, Lowry J. CAD/CAM fabricated complete dentures: concepts and clinical methods of obtaining required morphological data. J Prosthet Dent 2012;107:34-46.   DOI
23 Al-Dwairi ZN, Tahboub KY, Baba NZ, Goodacre CJ. A comparison of the flexural and impact strengths and flexural modulus of CAD/CAM and conventional heat-cured polymethyl methacrylate (PMMA). J Prosthodont 2020;29:341-9.   DOI
24 Kydd WL. The comminuting efficiency of varied occlusal tooth form and the associated deformation of the complete denture base. J Am Dent Assoc 1960;61:465-71.   DOI
25 Steinmassl PA, Wiedemair V, Huck C, Klaunzer F, Steinmassl O, Grunert I, Dumfahrt H. Do CAD/CAM dentures really release less monomer than conventional dentures? Clin Oral Investig 2017;21:1697-705.   DOI
26 Aguirre BC, Chen JH, Kontogiorgos ED, Murchison DF, Nagy WW. Flexural strength of denture base acrylic resins processed by conventional and CAD-CAM methods. J Prosthet Dent 2020;123:641-6.   DOI
27 McLaughlin JB, Ramos V Jr. Complete denture fabrication with CAD/CAM record bases. J Prosthet Dent 2015;114:493-7.   DOI
28 Arslan M, Murat S, Alp G, Zaimoglu A. Evaluation of flexural strength and surface properties of prepolymerized CAD/CAM PMMA-based polymers used for digital 3D complete dentures. Int J Comput Dent 2018;21:31-40.
29 Steinmassl O, Offermanns V, Stockl W, Dumfahrt H, Grunert I, Steinmassl PA. In vitro analysis of the fracture resistance of CAD/CAM denture base resins. Materials (Basal) 2018;11:401.   DOI
30 Pacquet W, Benoit A, Hatege-Kimana C, Wulfman C. Mechanical properties of CAD/CAM denture base resins. Int J Prosthodont 2019;32:104-6.   DOI
31 Gajewski VE, Pfeifer CS, Froes-Salgado NR, Boaro LC, Braga RR. Monomers used in resin composites: degree of conversion, mechanical properties and water sorption/solubility. Braz Dent J 2012;23:508-14.   DOI
32 Peutzfeldt A. Resin composites in dentistry: the monomer systems. Eur J Oral Sci 1997;105:97-116.   DOI
33 Ruyter IE, Oysaed H. Composites for use in posterior teeth: Composition and conversion. J Biomed Mater Res 1987;21:11-23.   DOI
34 Lee YS, Choi KK, Park SJ. Effect of resin matrix on degree of conversion and fracture toughness of dental composites. J Korean Acad Conserv Dent 2002;27:77-86.   DOI
35 Peng L, Chen L, Harris BT, Morton D, Lin WS. Managing complications resulting from limited prosthetic space with a monolithic, multichromatic CAD/CAM implant-retained overdenture. J Prosthet Dent 2017;118:712-6.   DOI