• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.136-143
• /
• 2000

$SrBi_2Ta_2O_9;(SBT)$ films were deposited on p-type Si(100) at room temperature by rf magnetron sputtering method to confirm the possibility of application of $Pt/SBT/Pt/Ti/SiO_2/Si$ structure (MFM) for destructive read out ferroelectric RAM (random access memory). Their structural characteristics with the various annealing times and Ar/$O_2$ gas flow ratios in sputtering were observed by XRD (X-ray diffractometer) and the surface morphologies were observed by FE-SEM (field emission scanning electron microscopy), and their electrical properties were observed by P-V (polarization-voltage measurement) and I-V (current-voltage measurement). The Ar/$O_2$ gas flow ratios of sputtering gas were changed from 1 : 4 to 4 : 1 and SBT thin films were deposited at room temperature. The films show (105), (110) peaks of SBT by XRD measurement. SBT thin films deposited at room temperature were crystallized by furnace annealing at 80$0^{\circ}C$ in oxygen atmosphere during either one hour or two hours. Among their electrical properties, P-V curves showed shaped hysteresis curves, but the SBT thin films showed the asymmetric ferroelectric properties in P-V curves. When Ar/$O_2$ gas flow ratios are 1 : 1, 2: 1, the leakage current density values of SBT thin films are good, those values of 3 V, 5 V, and 7 V are respectively $3.11\times10^{-8} \textrm{A/cm}^2$, $5\times10^{-8}\textrm{A/cm}^2$, $7\times10^{-8}\textrm{A/cm}^2$.After two hours of annealing time, their electrical properties and crystallization are improved.

• Journal of Ecology and Environment
• /
• v.38 no.4
• /
• pp.505-515
• /
• 2015

The objectives of this study were to determine the effects of stream nutrient regime, N:P ratios and suspended solids on fish tolerance/trophic compositions and stream ecosystem health, based on multi-metric model, during 2008-2013. Also, stream ecosystem health was evaluated in relation to chlorophyll-a (CHL) as a measure of algal productivity or indicators of trophic state to water chemical parameters. Total number of sampled fish species were 50 and showed a decreasing trend from 2008 to 2013. The minnow of Zacco platypus, based on the catch per unit effort (CPUE), was the most dominant species (25.9%) among the all species. Spatial heterogeneity was evident in the fish tolerance guilds that showed the dominance of sensitive species (89%) in the headwaters (S1) and the dominance of tolerant species (57%) in the urban. These conditions were directly influenced by concentrations of nutrients and organic matter (COD). The N:P ratios, as a barometer of water pollution, had a negative linear function (R² = 0.40, P < 0.01) with CHL, and the ratios had an important role in changes of COD concentration (R² = 0.40, P < 0.01). Under the circumstances, the N:P ratio directly influenced the relative proportions of fish trophic/tolerance compositions. According to the regression analysis of omnivore (O_m) and insectivore sp. (I_n) on total nitrogen and total phosphorus, nitrogen had no significant influences (P > 0.05) to the two compositions, but phosphorus influenced directly the two guilds [slope (a) = -32.3, R² = 0.25, P < 0.01 in the I_n; a = 40.7, R² = 0.19, P < 0.01 in the O_m]. Such water chemistry and fish trophic guilds determined the stream ecosystem health, based on the multi-metric fish model.

• Journal of Environmental Science International
• /
• v.12 no.1
• /
• pp.35-40
• /
• 2003

With increasing population densities in cities, underground facilities and entertainment locations are proliferating at a rapid pace in efforts to maximize the use of land. The purpose of this study is to evaluate CO concentration level of subway stations having underground platforms in Busan Metropolitan City, from September to November 2000, over seven times. The places of inquiry include Yonsan-dong station, Somyon station, Busan station, Nampo-dong station and Dusil station. The samplings were conducted at three points of each station, i.e. gates, ticket gates, and platforms. The component of CO concentration is the main elements of indoor air quality evaluation. The total concentrations and average concentrations of CO were the higher at the Somyon station. The distribution of CO concentrations at each station, generally was higher at gate than ticket gates and platforms. The I/O ratios(I-platforms, 0-gates) were expressed highly than 1 at the Yonsan-dong station, Busan station, Nampo-dong station and were lower than 1 at the others.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.4
• /
• pp.1165-1169
• /
• 2011

Second-order rate constants ($k_N$) have been measured spectrophotometrically for nucleophilic substitution reactions of 2,4-dinitrophenyl phenyl thionocarbonate 4 with a series of Z-substituted pyridines in 80 mol % $H_2O$/20 mol % DMSO at $25.0{\pm}0.1^{\circ}C$. The Br${\o}$nsted-type plot for the reactions of 4 exhibits downward curvature (i.e., ${\beta}_1$ = 0.21 and ${\beta}_2$ = 1.04), indicating that the reactions proceed through a stepwise mechanism with a change in rate-determining step. It has been found that 4 is less reactive than its oxygen analogue, 2,4-dinitrophenyl phenyl carbonate 3, although the thionocarbonate is expected to be more electrophilic than its oxygen analogue. The $pK_a$ at the center of the Br${\o}$nsted curvature, defined as $pK_a^o$, has been analyzed to be 6.6 for the reactions of 4 and 8.5 for those of 3. Dissection of $k_N$ into the microscopic rate constants $k_1$ and $k_2/k_{-1}$ ratio has revealed that the reactions of 4 result in smaller $k_1$ values but larger $k_2/k_{-1}$ ratios than the corresponding reactions of 3. The larger $k_2/k_{-1}$ ratios have been concluded to be responsible for the smaller $pK_a^o$ found for the reactions of 4.

• Journal of Ocean Engineering and Technology
• /
• v.20 no.5 s.72
• /
• pp.77-81
• /
• 2006

In this study, monolithic liquid phase sintered SiC (LPS-SiC) was made by the hot pressing method with nano-SiC powder, whose particle size is 30 nm and less on the average. Alumina ($Al_{2}O_{3}$), yttria ($Y_{2}O_{3}$), and silica ($S_{i}O_{2}$) were used for sintering additives. To investigate the effects of $S_{i}O_{2}$, the $Al_{2}O_{3}/Y_{2}O_{3}$ composition was fixed and the ratio of $S_{i}O_{2}$ was changed, with seven different ratios tested. And to investigate the effects of the sintering temperature, the sintering temperature was changed, with $1760^{\circ}C,\;1780_{\circ}C$, and $1800_{\circ}C$ being used with a $S_{i}O_{2}$ ratio of 3 wt%. The materials were sintered for 1 hour at $1760^{\circ}C,\;1780^{\circ}C$ and $1800^{\circ}C$ under a pressure of 20 MPa. The effects on sintering from the sintering system used, as well as from the composition of the sintering additives, were investigated by density measurements. Mechanical properties, such as flexural strength, were investigated to ensure the optimum conditions for a matrix of SiCf/SiC composites. Sintered densityand the flexural strength of fabricated LPS-SiC increased with an increase in sintering temperature. Particularly, the relative density of a sintered body at $1800^{\circ}C$ with a non-content of $S_{i}O_{2}$, a specimen of AYSO-1800, was 95%. Also, flexural strength was about 750MPa.

• Applied Chemistry for Engineering
• /
• v.7 no.4
• /
• pp.623-632
• /
• 1996

The reactivity ratios, melting temperature and polymer morphology in propylene/butene-1 and propylene/hexene-1 copolymerization reactions were studied by examining comonomer compositions of resulting polymers. The catalysts used here are different in their supports which are silica(catalyst I) and magnesium(catalyst II). As the content of comonomer(butene-1 and hexene-1) increased in the copolymer, the melting temperature of the copolymer decreased. The morphology of polymer was amorphous in the range of comonomer(butene-1) composition over 40% in the propylene/butene-1 copolymerization and comonomer(hexene-1) composition over 80% in the propylene/hexene-1 copolymerization. The reactivity ratios were obtained by the Fineman-Ross and Kelen-$T{\ddot{u}}d{\tilde{o}}s$ methods.

• Korean Journal of Materials Research
• /
• v.21 no.9
• /
• pp.509-514
• /
• 2011

In this study, optical emission spectroscopy was used to monitor the plasma produced during the RF magnetron sputtering of a $BaTiO_3$ target. The intensities of chemical species were measured by real time monitoring with various discharge parameters such as RF power, pressure, and discharge gas. The emission lines of elemental and ionized species from $BaTiO_3$ and Ti targets were analyzed to evaluate the film composition and the optimized growth conditions for $BaTiO_3$ films. The emissions from Ar(I, II), Ba(I, II) and Ti(I) were found during sputtering of the $BaTiO_3$ target in Ar atmosphere. With increasing RF power, all the line intensities increased because the electron density increased with increasing RF power. When the Ar pressure increased, the Ba(II) and Ti(I) line intensity increased, but the $Ar^+$ line intensity decreased with increasing pressure. This result shows that high pressure is of greater benefit for the ionization of Ba than for that of Ar. Oxygen depressed the intensity of the plasma more than Ar did. When the Ar/$O_2$ ratio decreased, the intensity of Ba decreased more sharply than that of Ti. This result indicates that the plasma composition strongly depends on the discharge gas atmosphere. When the oxygen increased, the Ba/Ti ratio and the thickness of the films decreased. The emission spectra showed consistent variation with applied power to the Ti target during co-sputtering of the $BaTiO_3$ and Ti targets. The co-sputtered films showed a Ba/Ti ratio of 1.05 to 0.73 with applied power to the Ti target. The films with different Ba/Ti ratios showed changes in grain size. Ti excess films annealed at $600^{\circ}C$ did not show the second phase such as $BaTi_2O_5$ and $TiO_2$.

• Bulletin of the Korean Mathematical Society
• /
• v.53 no.6
• /
• pp.1741-1751
• /
• 2016

We prove the boundary Harnack principle and the Carleson type estimate for ratios of solutions u/v of non-divergence second order elliptic equations $Lu=a_{ij}D_{ij}+b_iD_iu=0$ in a bounded domain ${\Omega}{\subset}R_n$. We assume that $b_i{\in}L^n({\Omega})$ and ${\Omega}$ is a $H{\ddot{o}}lder$ domain of order ${\alpha}{\in}$ (0, 1) satisfying a strong regularity condition.

• Journal of the Korean Ceramic Society
• /
• v.24 no.1
• /
• pp.23-32
• /
• 1987

Synthesis of high purity ultrafine Si3N4 and ${\beta}$-Sialon powders was investigated via the simultaneous reduction and nitriding of amorphous SiO2, SiO2-Al2O3 system prepaerd by hydrolysis of alkoxides, using carbonablack as a reducing agent. In Si(OC2H5)4-C2H5 OH-H2 O-NH4OH system, hydrolysis rate increased with increasing reaction temperature and pH. Pure ${\alpha}$-Si3N4 was formed at 1350$^{\circ}C$ for 5 hrs in N2 atmosphere. In Si(OC2H5)4-Al(OC3H7)3-C6H6-H2 O-NH4OH system, weight loss increased as Si/Al ratio decreased. Single phase ${\beta}$-Sialon consisted of Si/Al=2 was formed at 1350$^{\circ}C$ in N2 and minor phases of ${\alpha}$-Si3N4, AIN, and X-phase were existed besides theSialon phase at other Si/Al ratios. The Si3N4 and Sialon powders synthesized from alkoxides consisted of uniform find particles of 0.05-0.2$\mu\textrm{m}$ in diameter, respectively.

• Steel and Composite Structures
• /
• v.9 no.5
• /
• pp.419-444
• /
• 2009

Flange and web local buckling in beam plastic hinge regions of steel moment frames can prevent beam-column connections from achieving adequate plastic rotations under earthquake-induced forces. Reducing the flange-web slenderness ratios (FSR/WSR) of beams is the most effective way in mitigating local member buckling as stipulated in the latest seismic design specifications. However, existing steel moment frame buildings with beams that lack the adequate slenderness ratios set forth for new buildings are vulnerable to local member buckling and thereby system-wise instability prior to reaching the required plastic rotation capacities specified for new buildings. This paper presents results from a research study investigating the cyclic behavior of steel I-beams modified by a welded haunch at the bottom flange and reinforced with glass fiber reinforced polymers at the plastic hinge region. Cantilever I-sections with a triangular haunch at the bottom flange and flange slenderness ratios higher then those stipulated in current design specifications were analyzed under reversed cyclic loading. Beam sections with different depth/width and flange/web slenderness ratios (FSR/WSR) were considered. The effect of GFRP thickness, width, and length on stabilizing plastic local buckling was investigated. The FEA results revealed that the contribution of GFRP strips to mitigation of local buckling increases with increasing depth/width ratio and decreasing FSR and WSR. Provided that the interfacial shear strength of the steel/GFRP bond surface is at least 15 MPa, GFRP reinforcement can enable deep beams with FSR of 8-9 and WSR below 55 to maintain plastic rotations in the order of 0.02 radians without experiencing any local buckling.