• Journal of the Korean Ceramic Society
• /
• v.26 no.1
• /
• pp.73-80
• /
• 1989

Preparation and characteristics of electroless Ni-P and Ni-B systems for semiconducting ceramics have been investigated as a function of deposit rate, reducing agent and pH variation. The effect of DMAB as ruducing agent is greater than that of sodium hypophosphite. The nickel electrode prepared from the nickel-phosphorus system with sodium hypophosphite shows low contact resistance of 0.99ohm compared with the resistance of 10chm in the electrode prepared from the nickel-boron system with DMAB. The contact resistance increases with increasing pH valuein the nickel-phosphorus system with sodium hypophosphite. The ratio of Ni to P is about 76.0/24.0 for the contact resistance of 0.99ohm in the above system.

• Journal of Powder Materials
• /
• v.22 no.4
• /
• pp.260-265
• /
• 2015

Spherical fine cobalt powders were fabricated by new liquid reduction method. Commercial cobalt sufate heptahydrate was used as raw material. Also ethylene glycol was used as solvent and hydrazine-sodium hypophosphite mixture was used as reduction agent for the new liquid reduction method. A plate shaped cobalt powders with an approximately 300 nm were prepared by a traditional wet ruduction method using distilled water as solvent and hydrazine. Spherical fine cobalt powders with an average size of $1-3{\mu}m$ were synthesized by a new liquid reduction method in 0.3M cobalt sulfate and 1.5M hydrazine-0.6M sodium hypophosphite mixture at 333K.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.3
• /
• pp.263-271
• /
• 2003

Optimal conditions of electroless nickel plating in acid baths has been studied for industrial applications of a developed EN solution. The phosphorus content in the deposition ranges from 8 to $12\;wt.\%$. The investigated EN plating parameters are ion concentrations of nickel and hypophosphite, concentration of reducing and complexing agent, temperature, and pH. The average plating rate of Ni-P deposition was ca. $14{\mu}m/h$. The EN solution used shows a deposition rate of $10{\mu}m/h$ up to seven metal turnovers.

• Bulletin of the Korean Chemical Society
• /
• v.24 no.1
• /
• pp.15-16
• /
• 2003

• Journal of Power System Engineering
• /
• v.5 no.2
• /
• pp.71-78
• /
• 2001

Using sodium hypophosphite as reducing agent, bath composition and plating condition of electroless copper plating on plating rate have been studied. The followings were determined as optimum, bath composition; $CuSO_4\;0.025M,\;NiSO_4\;0.002M,\;NaH_2PO_2\;0.4M$, sodium citrate 0.06M, $H_3BO_3$ 0.6M, thiourea or 2-MBT $0.2mg/{\ell}$, and operation conditions; pH $9{\sim}10$ at bath temperature rage of $60{\sim}70^{\circ}C$. A small amount of nickel ion($Ni^{2+}/Cu^{2+}$=0.002/0.025) to the hypophosphite reduced solution promotes autocatalysis and continuous plating. An additive such as thiourea or 2-MBT of a small amount($0.2mg/{\ell}$) can be used to stabilize the solution without changing plating rate much. The attivation energy between $20^{\circ}C\;and\;70^{\circ}C$ were calculated to be 11.3kcal/mol for deposition weight. Plating reaction had been ceased by the adjustment of pH above 13, temperature higher than $90^{\circ}C\;and\;under\;20^{\circ}C$. Deposited surface became worse in the case of increment of bath temperature above $80^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.2
• /
• pp.126-134
• /
• 2000

This study investigated the bath compositions and plating conditions and crystal structure used for achieving nickel-thallium-phosphorus deposits by means electroless plating. The electroless nickel-thallium-phosphorus deposits were achieved with a bath using sodium hypophosphite as the reducing agent and sodium citrate as the complexing agent. The depositing rate was 10.5mg.$cm^{2-1}$ .$hr^{-1 }$ from the optimistic bath composition, 0.1M nickel sulfate, 0.005M thallium sulfate, 0.2M sodium hypophosphite, and 0.05M sodium citrat and the recommended plating conditions, pH 5.5 and $90^{\circ}C$. The composition of alloy deposits determined by X-ray analysis (EDS) that the Thallium was increased with major increasing concentration of complexing agent and thallium ion in bath solution, it decreased according to the increasing concentrations of reduction agent in the bath solution, Bit Phosphorus showed a contrary to the thallium. It was observed from X-ray diffraction analysis, Scanning Electron Microscopy and Transmission Electron Microscopy. The crystalline structure of deposits was amorphous at the first deposited state but it was changed $Ni-T1-Ni_{5}$ $P_2$ polycrystalline when subjected to 1 hour heat treatment of more than $350^{\circ}C$. TEM observation demonstrated that the microstructure was identical to the result of the XRD at as deposited but it became $Ni-Tl-Ni_{5}$ $P_2$ polycrystalline when heated. And grain size was 10-50nm.

• Fibers and Polymers
• /
• v.1 no.2
• /
• pp.116-121
• /
• 2000

It has been considered that malic acid, $\alpha$-hydroky succinic acid, could not form crosslinks in the cellulosic materials unless activated by other polycarboxylic acids such as butanetetracarboxylic acid or citric acid because there are only two carboxylic acids per molecule available fur the formation of one anhydride intermediate. However we found that the dicarboxylic malic acid with sodium hypophosphite catalyst without the addition of other crosslinkers was able to improve wrinkle resistance of cotton up to $294^{\circ}$(dry WRA) and $285^{\circ}$ (wet WRA), which is a measure of crosslinking level in cotton. $^1$H FT-NMR, FT-IR and GPC analysis indicated the in-situ formation of an trimeric $\alpha$, $\beta$-rnalic acid with a composition of 1:3 through the esterification between hydroxyl group and one of carboxylic groups in malic acid during curing. The crosslinking of cotton was attributed to the trimeric $\alpha$, $\beta$-malic acid, a tetracarboxylic acid, which can form two anhydride rings during curing. The influence of crosslinking conditions such as concentrations of malic acid and catalyst, pH of the formulation bath, and curing temperature were investigated in terms of imparted wrinkle resistance and whiteness. The addition of reactive polyurethane resin in the formulation slightly increased the mechanical strength retention of crosslinked fabric coupled with additional increase in wrinkle resistance.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.393-397
• /
• 2003

The effects of the composition and additives on the blackening and deposition rate of electroless Ni-Zn plating have been examined. Hydrazine resulted in lower sheet resistance of the deposit than sodium hypophosphite. Zinc concentration more than 15 wt% and small amount of ammonium sulfate in the deposits were needed in obtaining Ni-Zn deposit with a black color. An optimum condition was obtained for the black Ni-Zn deposit at an appreciable deposition rate.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.331-335
• /
• 1999

Electroless plating nickel has superior mechanical property to electroplated nickel. Furthermore nickel can be coated on nonconducting substrate. In this research, electroless plating of nickel were conducted in different bath condition to find optimum conditions of electroless nickel plating for MEMS applications. The selectivity of activation method on several substrates was investigated. The effects of nickel concentration, reducing agent concentration and inhibitor on deposition rate were investigated. The effect of pH on deposition rate and content of phosphorous in deposited nickel was also investigated.

• Asian-Australasian Journal of Animal Sciences
• /
• v.15 no.11
• /
• pp.1646-1652
• /
• 2002

Si-Raw is a raw cured meat (raw, cured meat fermented with steamed rice) produced by the aboriginal people of Taiwan. In order to prevent food poisoning or intoxication from botulism, new methods of monitoring the production base on hurdle technology were investigated. New methods investigated incorporated citric acid, sodium hypophosphite, Monascus anka mash, plum paste or lactic acid bacteria inoculum added separately to meat with steamed rice and salt to lower the Aw (water activity) and pH values of the products to control the microbial growth. Results showed that anaerobic bacterial counts, lactic acid bacterial counts and aerobic bacterial counts for the products of all treatments were less than $10^6$, $10^5$ and $10^2cfu/g$, respectively. Sodium chloride content of all products was above 5.46%, water activity was below 0.939 and pH value was below 4.27. IMP was lower and ATP and hypoxanthine were higher. ATP concentrations were higher in the samples which contained the anka mash. Result of sensory panel test indicated that most people preferred the products with added sodium hypophosphite. Except for the fact that the content of tryptamine in the sample with Monascus anka mash was higher, the amine concentrations for all treatments were lower than those of other fermented meat products. The amino acid nitrogen content was higher in the product made from raw meat treated with citric acid, but lower in the other products. Neither Clostridium botulinum nor Trichinella spiralis were detected in any of the treatments. The result may indicate that hurdle technology is effective for hygiene and safe producing Si-Raw.