• Advances in nano research
• /
• v.6 no.1
• /
• pp.1-19
• /
• 2018

Iron oxide nanoparticles excite researcher interest in biomedical applications due to their low cost, biocompatibility and superparamagnetism properties. Magnetic iron oxide especially magnetite ($Fe_3O_4$) possessed a superparamagnetic behaviour at certain nanosize which beneficial for drug and gene delivery, diagnosis and imaging. The properties of nanoparticles mainly depend on their synthesis procedure. There has been a massive effort in developing the best synthetic strategies to yield appropriate physico-chemical properties namely co-precipitation, thermal decomposition, microemulsions, hydrothermal and sol-gel. In this review, it is discovered that magnetite nanoparticles are best yielded by co-precipitation method owing to their simplicity and large production. However, its magnetic saturation is within range of 70-80 emu/g which is lower than thermal decomposition and hydrothermal methods (80-90 emu/g) at 100 nm. Dimension wise, less than 100 nm is produced by co-precipitation method at $70^{\circ}C-80^{\circ}C$ while thermal decomposition and hydrothermal methods could produce less than 50 nm but at very high temperature ranging between $200^{\circ}C$ and $300^{\circ}C$. Thus, co-precipitation is the optimum method for pre-compliance magnetite nanoparticles preparation (e.g., 100 nm is fit enough for biomedical applications) since thermal decomposition and hydrothermal required more sophisticated facilities.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.5
• /
• pp.185-189
• /
• 2001

Amorphous aluminium phosphate powders were synthesized as a single phase by neutralization reaction of a stoichiometric mixture of $Al_2(SO_4)_3$ and $H_3PO_4$ using the NaOH or KOH solution and subsequently by the hydrothermal precipitation method. The synthesis conditions were as follows : starting materials; $Al_2(SO_4)_3$ and $H_3PO_4$,pH ranges of neutralization reaction; between 5.6 and 6.0, temperature ranges of hydrothermal reaction; between 170 and $180^{\circ}C$,time ranges of hydrothermal reaction; between 4 and 5hs. Under such synthesis conditions, the products are obtained as amorphous aluminium phosphate powders of 0.1~0.3$\mu\textrm{m}$ in size and are Eitted to USP (United Standard Pharmacopoeia) test.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.223-227
• /
• 2009

$BaCO_3$ crystals with various morphology were prepared using precipitation, hydrothermal and ligand-assisted methods. An irregular structure of $BaCO_3$ microparticle was obtained by simple precipitation method from $Ba(NO_3)_2$ and $Na_2CO_3$ in aqueous solution. Hexagonal pyramidals of $BaCO_3$ were synthesized using a hydrothermal method between $Ba(NO_3)_2$ and urea. Hexagonal rods of $BaCO_3$ were also synthesized using the ligand-assisted hydrothermal method. The aspect ratio of $BaCO_3$ hexagonal rods was increased with the concentration of ligand.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.3
• /
• pp.95-100
• /
• 2016

In this work, tin oxides were obtained by the liquid reduction precipitation method and hydrothermal process using $SnCl_2{\cdot}2H_2O$, $N_2H_4$, and NaOH. Tin oxide crystals having different sizes and morphologies could be achieved. The powders were characterized by X-ray diffraction (XRD) and Field Emission Scanning Electron Microscopy (FE-SEM). Depending on the molar ratio of the raw materials, tin oxide crystalline with the spherical and rectangular plate-like shape could be obtained, the crystal phase was SnO and $Sn_6O_4(OH)_4$. And the obtained SnO crystals by a hydrothermal reaction showed various shapes, such as, spherical, plate-like and flower-like architectures depending on the temperature conditions.

• Korean Chemical Engineering Research
• /
• v.50 no.5
• /
• pp.808-814
• /
• 2012

Photocatalytic zinc oxide powders were prepared from precursor zinc acetate and ammonia solution at elevated temperature, $80^{\circ}C$, by hydrothermal precipitation method. The effect of operating parameters, pH of ammonia solution and concentration of zinc acetate solution, on the characteristics of zinc oxide powders were experimentally examined. Zinc oxide powders prepared at the conditions of pH 11, zinc acetate concentration of 1.0 M, precipitation temperature of $80^{\circ}C$, showed smallest average particle diameter of $3{\mu}m$. SEM and XRD analysis confirmed that prepared zinc oxide has hexagonal rods structure, and Anatase type crystallinity. In addition, DRS and PL analysis showed that the zinc oxide has activity at the range of 200~400 nm of UV light. And the zinc oxide decomposed 57% of a food-color stamp Brilliant blue FCF for 3 hours under the UV radiation.

• Journal of Powder Materials
• /
• v.18 no.6
• /
• pp.546-551
• /
• 2011

Ag spot-coated Cu nanopowders were synthesized by a hydrothermal-attachment method (HA) using oleic acid capped Ag hydrosol. Cu nano powders were synthesized by pulsed wire exploding method using 0.4 mm in diameter of Cu wire (purity 99.9%). Synthesized Cu nano powders are seen with comparatively spherical shape having range in 50 nm to 150 nm in diameter. The oleic acid capped Ag hydrosol was synthesized by the precipitation-redispersion method. Oleic acid capped Ag nano particles showed the narrow size distribution and their particle size were less than 20 nm in diameter. In the case of nano Ag-spot coated Cu powders, nanosized Ag particles were adhered in the copper surface by HAA method. The components of C, O and Ag were distributed on the surface of copper powder.

• Journal of Powder Materials
• /
• v.19 no.6
• /
• pp.424-428
• /
• 2012

Nano Pd spot-coated active carbon powders were synthesized by a hydrothermal-attachment method (HAA) using PVP capped Pd colloid in a high pressure bomb at $250^{\circ}C$, 450 psi, respectively. The PVP capped Pd colloid was synthesized by the precipitation-redispersion method. PVP capped Pd nano particles showed the narrow size distribution and their particle sizes were less than 8nm in diameter. In the case of nano Pd-spot coated active carbon powders, nano-sized Pd particles were adhered in the active carbon powder surface by HAA method. The component of Pd was homogeneously distributed on the active carbon surface.

• Korean Journal of Materials Research
• /
• v.21 no.8
• /
• pp.425-431
• /
• 2011

The industrial manufacturing of YSZ products can be summarized as a three step process: a) hydrolysis of zirconyl chloride and mixing of other solutions, b) precipitation, and c) calcination. The addition of ammonia or OH- is essential in the precipitation process. However, a strong agglomeration was observed in the results of an ammonia or OH- addition. Thus, it is necessary to disperse the powders smoothly in order to improve the mechanical strength of YSZ. In this study, YSZ was synthesized using the urea stabilizer and hydrothermal method. YSZ powders were synthesized using a hydrothermal method with Teflon Vessels at $180^{\circ}C$ for 24 h. The mole ratio of urea to Zr was 0, 0.5, 1, and 2. The crystal phase, particle size, and morphologies were analyzed. Rectangular specimens ($33\;mm{\times}8\;mm{\times}1{\pm}0.5\;mm$) for three-point bend tests were used in the mechanical properties evaluation. The crystalline of YSZ powders observed a tetragonal phase in the sample with a ratio of Zr:urea = 1:2 addition and a hydrothermal reaction time of 24 h. The average primary particle size of YSZ was measured to be 9 nm to 11 nm. The agglomerated particle size was measured from 15 nm to 30 nm. The three-point bending strength of the YSZ samples was 142.47 MPa, which is the highest value obtained for the Zr:urea = 1:2 ratio addition YSZ sample.

• Bulletin of the Korean Chemical Society
• /
• v.20 no.8
• /
• pp.869-874
• /
• 1999

In this paper, electrochemical techniques are used to investigate hydrothermal-electrochemically formation of barium titanate (BT) ceramic films. For comparison, the electrochemical behaviors of anodic titanium oxide films formed in alkaline solution were also investigated both at room temperature and in hydrothermal condition at 150.0 ℃. Film structure and morphology were identified by scanning electron microscopy (SEM) and atomic force microscopy (AFM). Titanium oxide films produced at different potentials exhibit different film morphology. The breakdown of titanium oxide films anodic growth on Ti electrode plays an important roles in the formation of BT films. BT films can grow on anodic oxide/metal substrate interface by short-circuit path, and the dissolution-precipitation processes on the ceramic film/solution interface control the film structure and morphology. Based upon the current experimental results and our previous work, extensively schematic proce-dures are proposed to model the mechanism of ceramic film formation by hydrothermal-electrochemical method.

• Korean Chemical Engineering Research
• /
• v.49 no.6
• /
• pp.752-757
• /
• 2011

The effects of reaction temperature, reactant concentration, pH of solution and mixing order of reactants on the particle shape and size distribution of zinc oxide were investigated in the preparation of zinc oxide from ammonium hydroxide and zinc acetate by the method of aqueous hydrothermal precipitation method, and the photocatalytic ability of zinc oxide synthesized was measured from the degradation of tartrazine under UV irradiation. The average particle size was increased with pH of solution but decreased with zinc acetate concentration and reaction temperature. The optimum condition for the synthesis of minimum sized zinc oxide was pH 11.2, concentration of zinc acetate 0.6 M and reaction temperature $90^{\circ}C$, and its average particle size was 3.133 ${\mu}$m. 97% of tartrazine was degraded by zinc oxide in sixty minutes.